“Direct-synthesis method towards copper-containing periodic mesoporous organosilicas : detailed investigation of the copper distribution in the material”. Lin F, Meng, Kukueva E, Altantzis T, Mertens M, Bals S, Cool P, Van Doorslaer S, Journal of the Chemical Society : Dalton transactions 44, 9970 (2015). http://doi.org/10.1039/c4dt03719g
Abstract: Three-dimensional cubic Fm (3) over barm mesoporous copper-containing ethane-bridged PMO materials have been prepared through a direct-synthesis method at room temperature in the presence of cetyltrimethylammonium bromide as surfactant. The obtained materials have been unambiguously characterized in detail by several sophisticated techniques, including XRD, UV-Vis-Dr, TEM, elemental mapping, continuous- wave and pulsed EPR spectroscopy. The results show that at lower copper loading, the Cu2+ species are well dispersed in the Cu-PMO materials, and mainly exist as mononuclear Cu2+ species. At higher copper loading amount, Cu2+ clusters are observed in the materials, but the distribution of the Cu2+ species is still much better in the Cu-PMO materials prepared through the direct-synthesis method than in a Cu-containing PMO material prepared through an impregnation method. Moreover, the evolution of the copper incorporation during the PMO synthesis has been followed by EPR. The results show that the immobilization of the Cu2+ ion/complex and the formation of the PMO materials are taking place simultaneously. The copper ions are found to be situated on the inner surface of the mesopores of the materials and are accessible, which will be beneficial for the catalytic applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 4.029
Times cited: 11
DOI: 10.1039/c4dt03719g
|
|
|
“Landfill taxes and enhanced waste management : combining valuable practices with respect to future waste streams”. Hoogmartens R, Eyckmans J, Van Passel S, Waste Management 55, 345 (2016). http://doi.org/10.1016/J.WASMAN.2016.03.052
Abstract: Both landfill taxes and Enhanced Waste Management (EWM) practices can mitigate the scarcity issue of landfill capacity by respectively reducing landfilled waste volumes and valorising future waste streams. However, high landfill taxes might erode incentives for EWM, even though EWM creates value by valorising waste. Concentrating on Flanders (Belgium), the paper applies dynamic optimisation modelling techniques to analyse how landfill taxation and EWM can reinforce each other and how taxation schemes can be adjusted in order to foster sustainable and welfare maximising ways of processing future waste streams. Based on the Flemish simulation results, insights are offered that are generally applicable in international waste and resource management policy. As shown, the optimal Flemish landfill tax that optimises welfare in the no EWM scenario is higher than the one in the EWM scenario (93 against (sic)50/ton). This difference should create incentives for applying EWM and is driven by the positive external effects that are generated by EWM practices. In Flanders, as the current landfill tax is slightly lower than these optimal levels, the choice that can be made is to further increase taxation levels or show complete commitment to EWM. A first generally applicable insight that was found points to the fact that it is not necessarily the case that the higher the landfill tax, the more effective waste management improvements can be realised. Other insights are about providing sufficient incentives for applying EMW practices and formulating appropriate pleas in support of technological development. By these insights, this paper should provide relevant information that can assist in triggering the transition towards a resource efficient, circular economy in Europe. (C) 2016 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering Management (ENM)
Impact Factor: 4.03
Times cited: 5
DOI: 10.1016/J.WASMAN.2016.03.052
|
|
|
“Eliciting stakeholder needs : an anticipatory approach assessing enhanced landfill mining”. Einhäupl PV, Krook J, Svensson N, Van Acker K, Van Passel S, Waste Management 98, 113 (2019). http://doi.org/10.1016/J.WASMAN.2019.08.009
Abstract: Landfill owners, governmental institutions, technology providers, academia and local communities are important stakeholders involved in Enhanced Landfill Mining (ELFM). This concept of excavating and processing historical waste streams to higher added values can be seen as a continuation of traditional landfill mining (LFM) and seems to be an innovative and promising idea for potential environmental and societal benefits. However, ELFM's profitability is still under debate, and environmental as well as societal impacts have to be further investigated. This study provides a first step towards an anticipatory approach, assessing ELFM through stakeholder integration. In the study, semi-structured interviews were conducted with various stakeholders, involved in a case study in Flanders, Belgium. Participants were selected across a quadruple helix (QH) framework, i.e. industrial, governmental, scientific, and local community actors. The research comprises 13 interviews conducted with an aim to elicit stakeholder needs for ELFM implementation using a general inductive approach. In total 18 different stakeholder needs were identified. The paper explains how the stakeholder needs refer to the different dimensions of sustainability, which groups of stakeholders they primarily affect, and what types of uncertainty could be influenced by their implementation. The stakeholder needs are structured into societal, environmental, regulatory and techno-economic needs. Results show additional economic, environmental, and societal aspects of ELFM to be integrated into ELFM research, as well as a need for the dynamic modeling of impacts. (C) 2019 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Engineering Management (ENM)
Impact Factor: 4.03
Times cited: 3
DOI: 10.1016/J.WASMAN.2019.08.009
|
|
|
“Non-invasive and non-destructive examination of artistic pigments, paints, and paintings by means of X-Ray methods”. Janssens K, van der Snickt G, Vanmeert F, Legrand S, Nuyts G, Alfeld M, Monico L, Anaf W, de Nolf W, Vermeulen M, Verbeeck J, De Wael K, Topics in Current Chemistry 374, 81 (2016). http://doi.org/10.1007/S41061-016-0079-2
Abstract: Recent studies are concisely reviewed, in which X-ray beams of (sub)micrometre to millimetre dimensions have been used for non-destructive analysis and characterization of pigments, minute paint samples, and/or entire paintings from the seventeenth to the early twentieth century painters. The overview presented encompasses the use of laboratory and synchrotron radiation-based instrumentation and deals with the use of several variants of X-ray fluorescence (XRF) as a method of elemental analysis and imaging, as well as with the combined use of X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS). Microscopic XRF is a variant of the method that is well suited to visualize the elemental distribution of key elements, mostly metals, present in paint multi-layers, on the length scale from 1 to 100 μm inside micro-samples taken from paintings. In the context of the characterization of artists pigments subjected to natural degradation, the use of methods limited to elemental analysis or imaging usually is not sufficient to elucidate the chemical transformations that have taken place. However, at synchrotron facilities, combinations of μ-XRF with related methods such as μ-XAS and μ-XRD have proven themselves to be very suitable for such studies. Their use is often combined with microscopic Fourier transform infra-red spectroscopy and/or Raman microscopy since these methods deliver complementary information of high molecular specificity at more or less the same length scale as the X-ray microprobe techniques. Since microscopic investigation of a relatively limited number of minute paint samples, taken from a given work of art, may not yield representative information about the entire artefact, several methods for macroscopic, non-invasive imaging have recently been developed. Those based on XRF scanning and full-field hyperspectral imaging appear very promising; some recent published results are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 4.033
Times cited: 50
DOI: 10.1007/S41061-016-0079-2
|
|
|
“Scalable synthesis of one-dimensional Na2Li2Ti6O14 nanofibers as ultrahigh rate capability anodes for lithium-ion batteries”. Wang C, Xin X, Shu M, Huang S, Zhang Y, Li X, Inorganic Chemistry Frontiers 6, 646 (2019). http://doi.org/10.1039/C8QI00973B
Abstract: Carbon anode materials for Li-ion batteries have been operated close to their theoretical rate and cycle limits. Therefore, titanium-based materials have attracted great attention due to their high stability. Here, Na2Li2Ti6O14 nanofibers as anode materials were prepared through a controlled electrospinning method. The Na2Li2Ti6O14 nanofibers presented superior electrochemical performance with high rate capability and long cycle life and can be regarded as a competitive anode candidate for advanced Li-ion batteries. One-dimensional (1D) Na2Li2Ti6O14 nanofibers are able to deliver a capacity of 128.5 mA h g(-1) at 0.5C, and demonstrate superior high-rate charge-discharge capability and cycling stability (the reversible charge capacity is 77.8 mA h g(-1) with a capacity retention of 99.45% at the rate of 10C after 800 cycles). The 1D structure is considered to contribute remarkably to increased rate capability and stability. This simple and scalable method indicates that the Na2Li2Ti6O14 nanofibers have a practical application potential for high performance lithium-ion batteries.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.036
Times cited: 3
DOI: 10.1039/C8QI00973B
|
|
|
“Virtual archaeology of altered paintings : multiscale chemical imaging tools”. Janssens K, Legrand S, van der Snickt G, Vanmeert F, Elements 12, 39 (2016). http://doi.org/10.2113/GSELEMENTS.12.1.39
Abstract: Understanding how painted works of art were constructed, layer-by-layer, requires a range of macroscopic and microscopic X-ray and infrared-based analytical methods. Deconstructing complex assemblies of paints horizontally across a picture and vertically through it provides insight into the detailed production process of the art work and on the painting techniques and styles of its maker. The unwanted chemical transformations that some paint pigments undergo are also detectable; these changes can alter the paint's optical properties. Understanding the chemistry behind such paint degradation gives conservators vital clues to counter these effects and is an invaluable asset in protecting these cultural artefacts for future generations.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 4.038
Times cited: 12
DOI: 10.2113/GSELEMENTS.12.1.39
|
|
|
“Environmental and economic performance of plasma gasification in Enhanced Landfill Mining”. Danthurebandara M, Van Passel S, Vanderreydt I, Van Acker K, Waste Management 45, 458 (2015). http://doi.org/10.1016/J.WASMAN.2015.06.022
Abstract: This paper describes an environmental and economic assessment of plasma gasification, one of the viable candidates for the valorisation of refuse derived fuel from Enhanced Landfill Mining. The study is based on life cycle assessment and life cycle costing. Plasma gasification is benchmarked against conventional incineration, and the study indicates that the process could have significant impact on climate change, human toxicity, particulate matter formation, metal depletion and fossil depletion. Flue gas emission, oxygen usage and disposal of residues (plasmastone) are the major environmental burdens, while electricity production and metal recovery represent the major benefits. Reductions in burdens and improvements in benefits are found when the plasmastone is valorised in building materials instead of landfilling. The study indicates that the overall environmental performance of plasma gasification is better than incineration. The study confirms a trade-off between the environmental and economic performance of the discussed scenarios. Net electrical efficiency and investment cost of the plasma gasification process and the selling price of the products are the major economic drivers.
Keywords: A1 Journal article; Economics; Engineering sciences. Technology; Engineering Management (ENM)
Impact Factor: 4.03
Times cited: 12
DOI: 10.1016/J.WASMAN.2015.06.022
|
|
|
“Assessment of environmental and economic feasibility of Enhanced Landfill Mining”. Danthurebandara M, Van Passel S, Vanderreydt I, Van Acker K, Waste Management 45, 434 (2015). http://doi.org/10.1016/J.WASMAN.2015.01.041
Abstract: This paper addresses the environmental and economic performance of Enhanced Landfill Mining (ELFM). Based on life cycle assessment and life cycle costing, a detailed model is developed and is applied to a case study, i.e. the first ELFM project in Belgium. The environmental and economic analysis is performed in order to study the valorisation of different waste types in the landfill, such as municipal solid waste, industrial waste and total waste. We found that ELFM is promising for the case study landfill as greater environmental benefits are foreseen in several impact categories compared to the landfills current situation (the Do-nothing scenario). Among the considered processes, the thermal treatment process dominates both the environmental and economic performances of ELFM. Improvements in the electrical efficiency of thermal treatment process, the calorific value of refuse derived fuel and recovery efficiencies of different waste fractions lead the performance of ELFM towards an environmentally sustainable and economically feasible direction. Although the environmental and economic profiles of ELFM will differ from case to case, the results of this analysis can be used as a benchmark for future ELFM projects.
Keywords: A1 Journal article; Economics; Engineering Management (ENM)
Impact Factor: 4.03
Times cited: 30
DOI: 10.1016/J.WASMAN.2015.01.041
|
|
|
“Indoor environmental quality index for conservation environments : the importance of including particulate matter”. Marchetti A, Pilehvar S, 't Hart L, Leyva Pernia D, Voet O, Anaf W, Nuyts G, Otten E, Demeyer S, Schalm O, De Wael K, Building and environment 126, 132 (2017). http://doi.org/10.1016/J.BUILDENV.2017.09.022
Abstract: It is commonly known that the conservation state of works of arts exhibited inside museums is strongly influenced by the indoor environmental quality (IEQ). Heritage institutions traditionally record and evaluate their IEQ by monitoring temperature, relative humidity, and -more rarely-light. However, smart use of technology enables monitoring other parameters that give a more complete insight in environmental air aggressiveness. One of this parameters is particulate matter (PM) and especially its concentration, size distribution and chemical composition. In this work, we present a selection of data sets which were obtained in a measuring campaign performed in the War Heritage Institute in Brussels, Belgium. A continuous monitoring of PM concentration with a light scattering based particle counter was performed. In addition the daily mass concentration and size distribution of airborne PM was monitored by means of Harvard impactors. The chemical composition of sampled PM was inferred from the results of XRF and IC analysis. The insights from these datasets are combined with the results of traditional environmental monitoring (temperature, relative humidity and light intensity), and assessed against the recommended guidelines for conservation environments. By using an integrated approach based on the calculation of an IEQ-index, we present a straightforward methodology to evaluate and visualize the IEQ including also continuous PM monitoring. It is clear from the results of this study how including PM in IEQ analysis allows to identify potential risks for museum collections that remain invisible when only traditional parameters are considered.
Keywords: A1 Journal article; Engineering sciences. Technology; Antwerp Systems and software Modelling (AnSyMo); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Antwerp Cultural Heritage Sciences (ARCHES)
Impact Factor: 4.053
Times cited: 10
DOI: 10.1016/J.BUILDENV.2017.09.022
|
|
|
“The impact of street canyon morphology and traffic volume on NO₂, values in the street canyons of Antwerp”. Voordeckers D, Meysman FJR, Billen P, Tytgat T, Van Acker M, Building And Environment 197, 107825 (2021). http://doi.org/10.1016/J.BUILDENV.2021.107825
Abstract: Air pollution remains a major environmental and health concern in urban environments, especially in street canyons that show increased pollution levels due to a lack of natural ventilation. Previous studies have investigated the relationship between street canyon morphology and in-canyon pollution levels. However, these studies are typically limited to the scale of a single street canyon and city-wide assessments on this matter are scarce. In 2018, NO2 concentrations were measured in 321 street canyons in the city of Antwerp (Belgium) as part of the large-scale citizen-science project “CurieuzeNeuzen”. In our research, this data was used to study the correlation between morphological indices (e.g. aspect ratio (AR), lateral aspect ratio (LAR), presence of trees) and the traffic volumes on a city-wide scale. The maximum hourly traffic volume (TVmax) and AR correlated significantly with the measured NO2 values, making them useful indicators for air quality in street canyons. For street canyons with AR > 0.65, a TVmax of 300 vehicles/hour was found as a threshold value to guarantee acceptable air quality. No significant correlations were found for the other parameters. Finally, a number of typical street canyon types were defined, which can be of fundamental interest for further research and spatial policy making.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL); Research Group for Urban Development; Intelligence in PRocesses, Advanced Catalysts and Solvents (iPRACS)
Impact Factor: 4.053
DOI: 10.1016/J.BUILDENV.2021.107825
|
|
|
“Quantifying inflow uncertainties for CFD simulations of the flow in downtown Oklahoma City”. García-Sánchez C, Philips DA, Gorlé, C, Building and environment 78, 118 (2014). http://doi.org/10.1016/j.buildenv.2014.04.013
Abstract: Computational Fluid Dynamics (CFD) methods are widely used to investigate wind flow and dispersion in urban environments. Validation with field experiments that represent the full complexity of the problem should be performed to assess the predictive capabilities of the computations. In this context it will be necessary to quantify the effect of uncertainties in simulations of the full-scale problem. The present study aims at quantifying the uncertainty related to the variability in the inflow boundary conditions for Reynolds-averaged Navier-Stokes (RANS) simulations of the flow in downtown Oklahoma City to address validation with the Joint Urban 2003 field measurements. Three uncertain inflow parameters were defined: the wind speed and wind direction at a reference height, and the aerodynamic roughness in the logarithmic velocity inlet profile. An ensemble of 729 RANS simulations were performed to determine the polynomial chaos expansion coefficients that define the response surfaces for the velocity magnitude and direction at 13 field measurement stations, and the results are compared to the experimental data. For the velocity magnitude the mean experimental velocity magnitude is encompassed within the 95% confidence interval for the magnitudes predicted by the Uncertainty Quantification study in all stations. For the velocity direction this holds in 11 out of 13 locations. The study demonstrates the significant potential of applying advanced uncertainty quantification methods to address validation with field measurements and to develop a more realistic approach to the definition of inflow boundary conditions in atmospheric CFD simulations. (C) 2014 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.053
Times cited: 29
DOI: 10.1016/j.buildenv.2014.04.013
|
|
|
“Elucidation of the Growth Mechanism of Sputtered 2D Hexagonal Boron Nitride Nanowalls”. Hoang D-Q, Pobedinskas P, Nicley SS, Turner S, Janssens SD, Van Bael MK, D'Haen J, Haenen K, Crystal growth &, design 16, 3699 (2016). http://doi.org/10.1021/ACS.CGD.6B00191
Abstract: Hexagonal boron nitride nanowall thin films were deposited on Si(100) substrates using a Ar(51%)/N-2(44%)/H-2(5%) gas mixture by unbalanced radio frequency sputtering. The effects of various target-to-substrate distances, substrate temperatures, and substrate tilting angles were investigated. When the substrate is close to the target, hydrogen etching plays a significant role in the film growth, while the effect is negligible for films deposited at a farther distance. The relative quantity of defects was measured by a non-destructive infrared spectroscopy technique that characterized the hydrogen incorporation at dangling nitrogen bonds at defect sites in the deposited films. Despite the films deposited at different substrate tilting angles, the nanowalls of those films were found to consistently grow vertical to the substrate surface, independent of the tilting angle. This implies that chemical processes, rather than physical ones, govern the growth of the nanowalls. The results also reveal that the degree of nanowall crystallization is tunable by varying the growth parameters. Finally, evidence of hydrogen desorption during vacuum annealing is given based on measurements of infrared stretching (E-1u) and bending (A(2u)) modes of the optical phonons, and the H-N vibration mode.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 8
DOI: 10.1021/ACS.CGD.6B00191
|
|
|
“On the Origin of Diamond Plates Deposited at Low Temperature”. Drijkoningen S, Pobedinskas P, Korneychuk S, Momot A, Balasubramaniam Y, Van Bael MK, Turner S, Verbeeck J, Nesladekt M, Haenen K, Crystal growth &, design 17, 4306 (2017). http://doi.org/10.1021/ACS.CGD.7B00623
Abstract: The crucial requirement for diamond growth at low temperatures, enabling a wide range of new applications, is a high plasma density at a low gas pressure, which leads to a low thermal load onto sensitive substrate materials. While these conditions are not within reach for resonance cavity plasma systems, linear antenna microwave delivery systems allow the deposition of high quality diamond films at temperatures around 400 degrees C and at pressures below 1 mbar. In this work the codeposition of high quality plates and octahedral diamond grains in nanocrystalline films is reported. In contrast to previous reports claiming the need for high temperatures (T >= 850 degrees C), low temperatures (320 degrees C <= T <= 410 degrees C) were sufficient to deposit diamond plate structures. Cross-sectional high resolution transmission electron microscopy studies show that these plates are faulty cubic diamond terminated by large {111} surface facets with very little sp(2) bonded carbon in the grain boundaries. Raman and electron energy loss spectroscopy studies confirm a high diamond quality, above 93% sp(3) carbon content. Three potential mechanisms, that can account for the initial development of the observed plates rich with stacking faults, and are based on the presence of impurities, are proposed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 23
DOI: 10.1021/ACS.CGD.7B00623
|
|
|
“Controlled Growth of Supported ZnO Inverted Nanopyramids with Downward Pointing Tips”. Barreca D, Carraro G, Maccato C, Altantzis T, Kaunisto K, Gasparotto A, Crystal growth &, design , acs.cgd.8b00198 (2018). http://doi.org/10.1021/acs.cgd.8b00198
Abstract: High purity porous ZnO nanopyramids with controllable properties are grown on their tips on
Si(100) substrates by means of a catalyst-free vapor phase deposition route in a wet oxygen
reaction environment. The system degree of preferential [001] orientation, as well as
nanopyramid size, geometrical shape and density distribution, can be finely tuned by varying the
growth temperature between 300 and 400°C, whereas higher temperatures lead to more compact
systems with a three-dimensional (3D) morphology. A growth mechanism of the obtained ZnO
nanostructures based on a self-catalytic vapor-solid (VS) mode is proposed, in order to explain
the evolution of nanostructure morphologies as a function of the adopted process conditions. The
results obtained by a thorough chemico-physical characterization enable to get an improved
control over the properties of ZnO nanopyramids grown by this technique. Taken together, they
are of noticeable importance not only for fundamental research on ZnO nanomaterials with
controlled nano-organization, but also to tailor ZnO functionalities in view of various potential
applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 6
DOI: 10.1021/acs.cgd.8b00198
|
|
|
“CVD of copper oxides from a \beta-diketonate diamine precursor: tailoring the nano-organization”. Barreca D, Gasparotto A, Maccato C, Tondello E, Lebedev OI, Van Tendeloo G, Crystal growth &, design 9, 2470 (2009). http://doi.org/10.1021/cg801378x
Abstract: A copper(II) hexafluoroacetylacetonate (1,1,1,5,5,5-hexafluoro-2,4-pentanedionate, hfa) adduct with N,N,N¡ä,N¡ä-tetramethylethylenediamine (TMEDA) [Cu(hfa)2¡¤TMEDA] is used for the first time as precursor for the chemical vapor deposition (CVD) of copper oxide nanosystems. The syntheses are carried out under both O2 and O2+H2O reaction atmospheres on Si(100) substrates, at temperatures ranging between 250 and 550 ¡ãC. Subsequently, the interrelations between the preparative conditions and the system composition, nanostructure, and morphology are elucidated by means of complementary analytical techniques [Fourier transform infrared spectroscopy (FT-IR), X-ray photoelectron and X-ray excited auger electron spectroscopies (XPS and XE-AES), glancing incidence X-ray diffraction (GIXRD), field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM)]. The obtained data revealed a gradual transformation from Cu2O, to Cu2O + CuO, to CuO nanosystems upon increasing the deposition temperature from 250 to 550 ¡ãC under both growth atmospheres. Such a phenomenon was accompanied by a progressive morphological evolution from continuous films to 1D hyperbranched nanostructures. Water vapor introduction in the deposition environment enabled to lower the deposition temperature and resulted in a higher aggregate interconnection, attributed to a higher density of nucleation centers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 60
DOI: 10.1021/cg801378x
|
|
|
“An effective morphology control of hydroxyapatite crystals via hydrothermal synthesis”. Neira IS, Kolen'ko YV, Lebedev OI, Van Tendeloo G, Gupta HS, Guitián F, Yoshimura M, Crystal growth &, design 9, 466 (2009). http://doi.org/10.1021/cg800738a
Abstract: A facile urea-assisted hydrothermal synthesis and systematic characterization of hydroxyapatite (HA) with calcium nitrate tetrahydrate and diammonium hydrogen phosphate as precursors are reported. The advantage of the proposed technique over previously reported synthetic approaches is the simple but precise control of the HA crystals morphology, which is achieved by employing an intensive, stepwise, and slow thermal decomposition of urea as well as varying initial concentrations of starting reagents. Whereas the plate-, hexagonal prism- and needle-like HA particles preferentially growth along the c-axis, the smaller and fine-plate-like HA crystals demonstrate crystal growth along the (102) and (211) directions, uncommon for HA. Furthermore, it was established that the hydrothermally derived powdered products are phase-pure HA containing CO32− anions in the crystal lattice, that is, AB-type carbonated hydroxyapatite. Transmission electron microscopy (TEM) and electron diffraction (ED) of selected samples reveal that the as-prepared HA crystals are single-crystalline and exhibit a nearly defect-free microstructure. The hardness and elastic modulus of the hexagonal prism-like HA crystals have been investigated on a nanoscale using the nanoindentation technique; the observed trends are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 183
DOI: 10.1021/cg800738a
|
|
|
“Differences between ultrananocrystalline and nanocrystalline diamond growth: theoretical investigation of CxHy species at diamond step edges”. Eckert M, Neyts E, Bogaerts A, Crystal growth &, design 10, 4123 (2010). http://doi.org/10.1021/cg100804v
Abstract: The behavior of hydrocarbon species at step edges of diamond terraces is investigated by means of combined molecular dynamics−Metropolis Monte Carlo simulations. The results show that the formation of ballas-like diamond films (like UNCD) and well-faceted diamond films (like NCD) can be related to the gas phase concentrations of CxHy in a new manner: Species that have high concentrations above the growing UNCD films suppress the extension of step edges through defect formation. The species that are present above the growing NCD film, however, enhance the extension of diamond terraces, which is believed to result in well-faceted diamond films. Furthermore, it is shown that, during UNCD growth, CxHy species with x ≥ 2 play an important role, in contrast to the currently adopted CVD diamond growth mechanism. Finally, the probabilities for the extension of the diamond (100) terrace are much higher than those for the diamond (111) terrace, which is in full agreement with the experimental observation that diamond (100) facets are more favored than diamond (111) facets during CVD diamond growth.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 4.055
Times cited: 11
DOI: 10.1021/cg100804v
|
|
|
“Highly oriented ZnO nanorod arrays by a novel plasma chemical vapor deposition process”. Bekermann D, Gasparotto A, Barreca D, Bovo L, Devi A, Fischer RA, Lebedev OI, Maccato C, Tondello E, Van Tendeloo G, Crystal growth &, design 10, 2011 (2010). http://doi.org/10.1021/cg1002012
Abstract: Strongly c-axis oriented ZnO nanorod arrays were grown on Si(100) by plasma enhanced-chemical vapor deposition (PE-CVD) starting from two volatile bis(ketoiminato) zinc(II) compounds Zn[(R′)NC(CH3)═C(H)C(CH3)═O]2, with R′ = -(CH2)xOCH3 (x = 2, 3). A systematic investigation of process parameters enabled us to obtain the selective formation of ZnO nanorods with tailored features, and provided an important insight into their growth mechanism. The morphology, structure, and composition of the synthesized ZnO nanosystems were thoroughly analyzed by field emission-scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDXS), glancing incidence X-ray diffraction (GIXRD), X-ray photoelectron spectroscopy (XPS), and transmission electron microscopy (TEM). Photoluminescence (PL) measurements were carried out to gain information on the optical properties. Specifically, one-dimensional (1D) ZnO architectures could be grown on Si(100) substrates at temperatures as low as 200−300 °C and radio frequency (RF)-power values of 20 W, provided that a sufficiently high mass supply to the growth surface was maintained. To the best of our knowledge, the present work reports the mildest preparation conditions ever appeared in the literature for the PE-CVD of ZnO nanorods, a key result in view of potential large-scale technological applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 75
DOI: 10.1021/cg1002012
|
|
|
“Insight into the growth of multiple branched MnOOH nanorods”. Li Y, Tan H, Lebedev O, Verbeeck J, Biermans E, Van Tendeloo G, Su B-L, Crystal growth &, design 10, 2969 (2010). http://doi.org/10.1021/cg100009k
Abstract: Multiple branched manganese oxide hydroxide (MnOOH) nanorods prepared by a hydrothermal process were extensively studied by transmission electron microscopy (TEM). A model of the branch formation is proposed together with a study of the interface structure. The sword-like tip plays a crucial role for the nanorods to form different shapes. Importantly, the branching occurs at an angle of around either 57 degrees or 123 degrees. Specifically, a (111) twin plane can only be formed at the interface with a 123 degrees angle. The interfaces formed with a 57 degrees angle usually contain edge dislocations. Electron energy loss spectroscopy (EELS) demonstrates that the whole crystal has a uniform chemical composition. Interestingly, an epitaxial growth of Mn3O4 at the radial surface was also observed under electron beam irradiation; this is because of the rough purification of the products. The proposed mechanism is expected to shed light on the branched/dendrite nanostructure growth and to provide opportunities for further novel nanomaterial structure growth and design.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.055
Times cited: 41
DOI: 10.1021/cg100009k
|
|
|
“Insights into the growth of (ultra)nanocrystalline diamond by combined molecular dynamics and Monte Carlo simulations”. Eckert M, Neyts E, Bogaerts A, Crystal growth &, design 10, 3005 (2010). http://doi.org/10.1021/cg100063c
Abstract: In this paper, we present the results of combined molecular dynamics−Metropolis Monte Carlo (MD-MMC) simulations of hydrocarbon species at flat diamond (100)2 × 1 and (111)1 × 1 surfaces. The investigated species are considered to be the most important growth species for (ultra)nanocrystalline diamond ((U)NCD) growth. When applying the MMC algorithm to stuck species at monoradical sites, bonding changes are only seen for CH2. The sequence of the bond breaking and formation as put forward by the MMC simulations mimics the insertion of CH2 into a surface dimer as proposed in the standard growth model of diamond. For hydrocarbon species attached to two adjacent radical (biradical) sites, the MMC simulations give rise to significant changes in the bonding structure. For UNCD, the combinations of C3 and C3H2, and C3 and C4H2 (at diamond (100)2 × 1) and C and C2H2 (at diamond (111)1 × 1) are the most successful in nucleating new crystal layers. For NCD, the following combinations pursue the diamond structure the best: C2H2 and C3H2 (at diamond (100)2 × 1) and CH2 and C2H2 (at diamond (111)1 × 1). The different behaviors of the hydrocarbon species at the two diamond surfaces are related to the different sterical hindrances at the diamond surfaces.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 4.055
Times cited: 13
DOI: 10.1021/cg100063c
|
|
|
“Understanding the surface diffusion processes during magnetron sputter-deposition of complex oxide Mg-Al-O thin films”. Georgieva V, Voter AF, Bogaerts A, Crystal growth &, design 11, 2553 (2011). http://doi.org/10.1021/cg200318h
Abstract: It is known that film structure may change dramatically with the extent of surface diffusion during the film growth process. In the present work, surface diffusion, induced thermally or activated by energetic impacts, is investigated theoretically under conditions appropriate for magnetron sputter-deposition of MgAlO thin films with varying stoichiometry. The distribution of surface diffusion energy barriers available to the system was determined for each stoichiometry, which allowed assessing in a qualitative way how much surface diffusion will take place on the time scale available between deposition events. The activation energy barriers increase with the Al concentration in the film, and therefore, the surface diffusion rates in the time frame of typical deposition rates drop, which can explain the decrease in crystallinity in the film structure and the transition to amorphous structure. The deposition process and the immediate surface diffusion enhanced by the energetic adatoms are simulated by means of a molecular dynamics model. The longer-time thermal surface diffusion and the energy landscape are studied by the temperature accelerated dynamics method, applied in an approximate way. The surface diffusion enhanced by the energetic impacts appears to be very important for the film structure in the low-temperature deposition regime.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 4.055
Times cited: 14
DOI: 10.1021/cg200318h
|
|
|
“Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations”. Zhang F, Inokoshi M, Batuk M, Hadermann J, Naert I, Van Meerbeek B, Vleugels J, Dental Materials 32, e327 (2016). http://doi.org/10.1016/j.dental.2016.09.025
Abstract: OBJECTIVE: The aim was to evaluate the optical properties, mechanical properties and aging stability of yttria-stabilized zirconia with different compositions, highlighting the influence of the alumina addition, Y2O3 content and La2O3 doping on the translucency. METHODS: Five different Y-TZP zirconia powders (3 commercially available and 2 experimentally modified) were sintered under the same conditions and characterized by X-ray diffraction with Rietveld analysis and scanning electron microscopy (SEM). Translucency (n=6/group) was measured with a color meter, allowing to calculate the translucency parameter (TP) and the contrast ratio (CR). Mechanical properties were appraised with four-point bending strength (n=10), single edge V-notched beam (SEVNB) fracture toughness (n=8) and Vickers hardness (n=10). The aging stability was evaluated by measuring the tetragonal to monoclinic transformation (n=3) after accelerated hydrothermal aging in steam at 134 degrees C, and the transformation curves were fitted by the Mehl-Avrami-Johnson (MAJ) equation. Data were analyzed by one-way ANOVA, followed by Tukey's HSD test (alpha=0.05). RESULTS: Lowering the alumina content below 0.25wt.% avoided the formation of alumina particles and therefore increased the translucency of 3Y-TZP ceramics, but the hydrothermal aging stability was reduced. A higher yttria content (5mol%) introduced about 50% cubic zirconia phase and gave rise to the most translucent and aging-resistant Y-TZP ceramics, but the fracture toughness and strength were considerably sacrificed. 0.2mol% La2O3 doping of 3Y-TZP tailored the grain boundary chemistry and significantly improved the aging resistance and translucency. Although the translucency improvement by La2O3 doping was less effective than for introducing a substantial amount of cubic zirconia, this strategy was able to maintain the mechanical properties of typical 3Y-TZP ceramics. SIGNIFICANCE: Three different approaches were compared to improve the translucency of 3Y-TZP ceramics.
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 4.07
DOI: 10.1016/j.dental.2016.09.025
|
|
|
“Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations”. Zhang F, Inokoshi M, Batuk M, Hadermann J, Naert I, Van Meerbeek B, Vleugels J, Dental materials 32, E327 (2016). http://doi.org/10.1016/J.DENTAL.7016.09.075
Abstract: Objective. The aim was to evaluate the optical properties, mechanical properties and aging stability of yttria-stabilized zirconia with different compositions, highlighting the influence of the alumina addition, Y2O3 content and La2O3 doping on the translucency. Methods. Five different Y-TZP zirconia powders (3 commercially available and 2 experimentally modified) were sintered under the same conditions and characterized by X-ray diffraction with Rietveld analysis and scanning electron microscopy (SEM). Translucency (n = 6/group) was measured with a color meter, allowing to calculate the translucency parameter (TP) and the contrast ratio (CR). Mechanical properties were appraised with four-point bending strength (n = 10), single edge V-notched beam (SEVNB) fracture toughness (n = 8) and Vickers hardness (n = 10). The aging stability was evaluated by measuring the tetragonal to monoclinic transformation (n = 3) after accelerated hydrothermal aging in steam at 134 degrees C, and the transformation curves were fitted by the Mehl-Avrami-Johnson (MAJ) equation. Data were analyzed by one-way ANOVA, followed by Tukey's HSD test (alpha = 0.05). Results. Lowering the alumina content below 0.25 wt.% avoided the formation of alumina particles and therefore increased the translucency of 3Y-TZP ceramics, but the hydrothermal aging stability was reduced. A higher yttria content (5 mol%) introduced about 50% cubic zirconia phase and gave rise to the most translucent and aging-resistant Y-TZP ceramics, but the fracture toughness and strength were considerably sacrificed. 0.2 mol% La2O3 doping of 3Y-TZP tailored the grain boundary chemistry and significantly improved the aging resistance and translucency. Although the translucency improvement by La2O3 doping was less effective than for introducing a substantial amount of cubic zirconia, this strategy was able to maintain the mechanical properties of typical 3Y-TZP ceramics. Significance. Three different approaches were compared to improve the translucency of 3YTZP ceramics. (C) 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.07
Times cited: 47
DOI: 10.1016/J.DENTAL.7016.09.075
|
|
|
“Towards a more structured selection process for attributes and levels in choice experiments : a study in a Belgian protected area”. Jeanloz S, Lizin S, Beenaerts N, Brouwer R, Van Passel S, Witters N, Ecosystem Services 18, 45 (2016). http://doi.org/10.1016/J.ECOSER.2016.01.006
Abstract: The process of selecting attributes for inclusion in choice experiments frequently involves qualitative methods such as focus groups and interviews. In order for a choice experiment to be successful and the results to be valid, this qualitative selection process is essential. It often lacks rigour and is poorly described, particularly in environmental choice experiments. We propose a meticulous attribute and attribute-level selection process consisting of a scoring exercise and an interactive discussion. This paper provides a case study describing how attributes and attribute-levels were identified and selected for the National Park Hoge Kempen in Belgium. We carried out four focus groups and thirteen semi-structured interviews with various park stakeholders to select attributes from six categories: the four categories of ecosystem services (supporting, provisioning, regulating, cultural), infrastructure, and land use types. The top-ranked characteristics were nature conservation, natural forests, biodiversity refuge, wetlands, landscape variety, heathlands, air purification, and education. Both the scoring exercise and the interactive discussion contributed to the attributes selected for the CE. Following these, an ultimate expert consultation stage is recommended to approve both the attribute and attribute-level selection. The semi-qualitative protocol proposed in this paper can help practitioners and demonstrates how the results guide choice experiment design.
Keywords: A1 Journal article; Engineering Management (ENM)
Impact Factor: 4.072
Times cited: 10
DOI: 10.1016/J.ECOSER.2016.01.006
|
|
|
“Fostering crack deviation via local internal stresses in Al/NiTi composites and its correlation with fracture toughness”. Zhao L, Ding L, Soete J, Idrissi H, Kerckhofs G, Simar A, Composites: part A: applied science and manufacturing 126, 105617 (2019). http://doi.org/10.1016/J.COMPOSITESA.2019.105617
Abstract: In the framework of metal matrix composites, a research gap exists regarding tailoring damage mechanisms. The present work aims at developing an Al/NiTi composite incorporating internal stresses in the vicinity of reinforcements. The composite is manufactured by friction stir processing which allows a homogenous NiTi distribution and a good Al/NiTi interface bonding. The internal stresses are introduced via shape memory effect of the embedded NiTi particles. The induced internal strain field is confirmed by digital image correlation and the corresponding stress field is evaluated by finite element simulation. It is found that the damage mechanism is modified in the presence of internal stresses. The consequent enhancement of fracture toughness arises by the fact that the internal stresses foster discrete damages shifted from the fracture ligament line. These damages release the stress concentration at the main crack tip and lead to a deviated crack path when coalescing to accommodate fracture propagation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.075
DOI: 10.1016/J.COMPOSITESA.2019.105617
|
|
|
“Control of the interfacial wettability to synthesize highly dispersed PtPd nanocrystals for efficient oxygen reduction reaction”. Wei H, Hu Z-Y, Xiao Y-X, Tian G, Ying J, Van Tendeloo G, Janiak C, Yang X-Y, Su B-L, Chemistry: an Asian journal 13, 1119 (2018). http://doi.org/10.1002/ASIA.201800191
Abstract: Highly dispersed PtPd bimetallic nanocrystals with enhanced catalytic activity and stability were prepared by adjusting the interfacial wettability of the reaction solution on a commercial carbon support. This approach holds great promise for the development of high-performance and low-cost catalysts for practical applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.083
Times cited: 3
DOI: 10.1002/ASIA.201800191
|
|
|
“Hierarchical MoS2@TiO2 heterojunctions for enhanced photocatalytic performance and electrocatalytic hydrogen evolution”. Dong Y, Chen S-Y, Lu Y, Xiao Y-X, Hu J, Wu S-M, Deng Z, Tian G, Chang G-G, Li J, Lenaerts S, Janiak C, Yang X-Y, Su B-L, Chemistry: an Asian journal 13, 1609 (2018). http://doi.org/10.1002/ASIA.201800359
Abstract: Hierarchical MoS2@TiO2 heterojunctions were synthesized through a one-step hydrothermal method by using protonic titanate nanosheets as the precursor. The TiO2 nanosheets prevent the aggregation of MoS2 and promote the carrier transfer efficiency, and thus enhance the photocatalytic and electrocatalytic activity of the nanostructured MoS2. The obtained MoS2@TiO2 has significantly enhanced photocatalytic activity in the degradation of rhodamineB (over 5.2times compared with pure MoS2) and acetone (over 2.8times compared with pure MoS2). MoS2@TiO2 is also beneficial for electrocatalytic hydrogen evolution (26times compared with pure MoS2, based on the cathodic current density). This work offers a promising way to prevent the self-aggregation of MoS2 and provides a new insight for the design of heterojunctions for materials with lattice mismatches.
Keywords: A1 Journal article; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 4.083
Times cited: 22
DOI: 10.1002/ASIA.201800359
|
|
|
“MOTIFS : a monitoring tool for integrated farm sustainability”. Meul M, Van Passel S, Nevens F, Dessein J, Rogge E, Mulier A, Van Hauwermeiren A, Agronomy For Sustainable Development 28, 321 (2008). http://doi.org/10.1051/AGRO:2008001
Abstract: Indicator-based monitoring tools are frequently applied for sustainability assessments, also in agriculture. However, many indicators focus on a rather restricted number of sustainability aspects such as economy or ecology. Moreover the choice of the indicator is rarely explained. The aim of our study was to develop an indicator-based monitoring tool for integrated farm sustainability – i.e. taking into account economic and ecological and social aspects – based on a supported vision of sustainable agriculture and using a set of relevant indicators. Hereby, specific attention was paid to aspects of communication and user-friendliness. Four methodological steps were considered: (i) translating the major principles of a supported vision of sustainable Flemish agriculture into concrete and relevant themes; (ii) designing indicators to monitor progress towards sustainability for each of those themes; (iii) aggregating the indicators into an integrated farm sustainability monitoring tool and (iv) applying the monitoring tool on a practical farm, as a first attempt at end-use validation. Stakeholder participation and expert consulting played an important part in each of these methodological steps. As a case study, the methodology was applied to Flemish dairy farms. As a result, we developed MOTIFS, a user-friendly and strongly communicative indicator-based monitoring tool that allows the measurement of progress towards integrated sustainable dairy farming systems and fits within a well-founded methodological framework. MOTIFS is based on the equality of the economic, ecological and social sustainability dimensions, and this equality is inherently built into the system. Through the applied methodology, we founded the selected themes and indicators and we avoided using indicators that are not relevant to the problem at hand.
Keywords: A1 Journal article; Economics
Impact Factor: 4.101
Times cited: 97
DOI: 10.1051/AGRO:2008001
|
|
|
“Higher sustainability performance of intensive grazing versus zero-grazing dairy systems”. Meul M, Van Passel S, Fremaut D, Haesaert G, Agronomy For Sustainable Development 32, 629 (2012). http://doi.org/10.1007/S13593-011-0074-5
Abstract: Although grazing of dairy cows is an integral part of dairy farming in many European countries, farmers today more often choose for zero-grazing systems, where cows are housed throughout the year. Some studies already compared grazing and zero-grazing systems for specific issues such as labor efficiency, environmental impact, or animal welfare. In our study, we perform a more integrated evaluation, considering relevant ecological, economic, and social aspects. This allows for a balanced and more complete comparison of the sustainability performance of the two production methods. We evaluated ten intensive grazing and ten zero-grazing specialized Flemish dairy farms on the use of nutrients and energy, productivity and profitability, labor input, and animal welfare. In addition, we put special effort in formulating useful management advice for farmers. Therefore, we combined a detailed analysis of the sustainability indicators with an intensive interaction and discussion with farmers and farm advisors. Results show that, on average, the zero-grazing farms performed significantly worse from an ecological and economic point of view. This fact is explained mainly due to a less efficient use of concentrates and byproducts. Social sustainability performance did not differ significantly between the two groups. As a result, the integrated sustainability performance was significantly lower for the zero-grazing group. This finding shows that a further shift from intensive grazing to zero-grazing can move dairy farming in Flanders further away from sustainability. An important advice to improve the ecological and economic performance of zero-grazing farms is to optimize cows' rations to include more forages and optimize forage production and use. More detailed site- and case-specific management advice for farmers of both groups was provided during a discussion meeting. We consider this an essential additional step to any sustainability evaluation, since progress can only be made when monitoring results are translated into practical measures.
Keywords: A1 Journal article; Engineering sciences. Technology; Engineering Management (ENM)
Impact Factor: 4.101
Times cited: 26
DOI: 10.1007/S13593-011-0074-5
|
|
|
“The role of hydrogen during Pt-Ga nanocatalyst formation”. Filez M, Redekop EA, Galvita VV, Poelman H, Meledina M, Turner S, Van Tendeloo G, Bell AT, Marin GB, Physical chemistry, chemical physics 18, 3234 (2016). http://doi.org/10.1039/c5cp07344h
Abstract: Hydrogen plays an essential role during the in situ assembly of tailored catalytic materials, and serves as key ingredient in multifarious chemical reactions promoted by these catalysts. Despite intensive debate for several decades, the existence and nature of hydrogen-involved mechanisms – such as hydrogen-spillover, surface migration – have not been unambiguously proven and elucidated up to date. Here, Pt-Ga alloy formation is used as a probe reaction to study the behavior and atomic transport of H and Ga, starting from Pt nanoparticles on hydrotalcite-derived Mg(Ga)(Al)Ox supports. In situ XANES spectroscopy, time-resolved TAP kinetic experiments, HAADF-STEM imaging and EDX mapping are combined to probe Pt, Ga and H in a series of H2 reduction experiments up to 650 degrees C. Mg(Ga)(Al)Ox by itself dissociates hydrogen, but these dissociated hydrogen species do not induce significant reduction of Ga3+ cations in the support. Only in the presence of Pt, partial reduction of Ga3+ into Gadelta+ is observed, suggesting that different reaction mechanisms dominate for Pt- and Mg(Ga)(Al)Ox-dissociated hydrogen species. This partial reduction of Ga3+ is made possible by Pt-dissociated H species which spillover onto non-reducible Mg(Al)Ox or partially reducible Mg(Ga)(Al)Ox and undergo long-range transport over the support surface. Moderately mobile Gadelta+Ox migrates towards Pt clusters, where Gadelta+ is only fully reduced to Ga0 on condition of immediate stabilization inside Pt-Ga alloyed nanoparticles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.123
Times cited: 10
DOI: 10.1039/c5cp07344h
|
|