“Ti surface doping of LiNi0.5Mn1.5O4−δpositive electrodes for lithium ion batteries”. Ulu Okudur F, D'Haen J, Vranken T, De Sloovere D, Verheijen M, Karakulina OM, Abakumov AM, Hadermann J, Van Bael MK, Hardy A, RSC advances 8, 7287 (2018). http://doi.org/10.1039/C7RA12932G
Abstract: The particle surface of LiNi0.5Mn1.5O4−δ (LNMO), a Li-ion battery cathode material, has been modified by Ti cation doping through a hydrolysis–condensation reaction followed by annealing in oxygen. The effect of different annealing temperatures (500–850 °C) on the Ti distribution and electrochemical performance of the surface modified LNMO was investigated. Ti cations diffuse from the preformed amorphous ‘TiOx’ layer into the LNMO surface during annealing at 500 °C. This results in a 2–4 nm thick Ti-rich spinel surface having lower Mn and Ni content compared to the core of the LNMO particles, which was observed with scanning transmission electron microscopy coupled with compositional EDX mapping. An increase in the annealing temperature promotes the formation of a Ti bulk doped LiNi(0.5−w)Mn(1.5+w)−tTitO4 phase and Ti-rich LiNi0.5Mn1.5−yTiyO4 segregates above 750 °C. Fourier-transform infrared spectrometry indicates increasing Ni–Mn ordering with annealing temperature, for both bare and surface modified LNMO. Ti surface modified LNMO annealed at 500 °C shows a superior cyclic stability, coulombic efficiency and rate performance compared to bare LNMO annealed at 500 °C when cycled at 3.4–4.9 V vs. Li/Li+. The improvements are probably due to suppressed Ni and Mn dissolution with Ti surface doping.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 9
DOI: 10.1039/C7RA12932G
|
|
|
“Fabrication, microstructure, and enhanced thermionic electron emission properties of vertically aligned nitrogen-doped nanocrystalline diamond nanorods”. Sankaran KJ, Deshmukh S, Korneychuk S, Yeh C-J, Thomas JP, Drijkoningen S, Pobedinskas P, Van Bael MK, Verbeeck J, Leou K-C, Leung K-T, Roy SS, Lin I-N, Haenen K, MRS communications 8, 1311 (2018). http://doi.org/10.1557/MRC.2018.158
Abstract: Vertically aligned nitrogen-doped nanocrystalline diamond nanorods are fabricated from nitrogen-doped nanocrystalline diamond films using reactive ion etching in oxygen plasma. These nanorods show enhanced thermionic electron emission (TEE) characteristics, viz.. a high current density of 12.0 mA/cm(2) and a work function value of 4.5 eV with an applied voltage of 3 Vat 923 K. The enhanced TEE characteristics of these nanorods are ascribed to the induction of nanographitic phases at the grain boundaries and the field penetration effect through the local field enhancement from nanorods owing to a high aspect ratio and an excellent field enhancement factor.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.01
Times cited: 1
DOI: 10.1557/MRC.2018.158
|
|
|
“The superconducting proximity effect in epitaxial Al/Pb nanocomposites”. Wang H, Picot T, Houben K, Moorkens T, Grigg J, Van Haesendonck C, Biermans E, Bals S, Brown SA, Vantomme A, Temst K, Van Bael MJ;, Superconductor science and technology 27, 015008 (2014). http://doi.org/10.1088/0953-2048/27/1/015008
Abstract: We have investigated the superconducting properties of Pb nanoparticles with a diameter ranging from 8 to 20 nm, synthesized by Pb+ ion implantation in a crystalline Al matrix. A detailed structural characterization of the nanocomposites reveals the highly epitaxial relation between the Al crystalline matrix and the Pb nanoparticles. The Al/Pb nanocomposites display a single superconducting transition, with the critical temperature T-c increasing with the Pb content. The dependence of T-c on the Pb/Al volume ratio was compared with theoretical models of the superconducting proximity effect based on the bulk properties of Al and Pb. A very good correspondence with the strong-coupling proximity effect model was found, with an electron-phonon coupling constant in the Pb nanoparticles slightly reduced compared to bulk Pb. Our result differs from other studies on Pb nanoparticle based proximity systems where weak-coupling models were found to better describe the T-c dependence. We infer that the high interface quality resulting from the ion implantation synthesis method is a determining factor for the superconducting properties. Critical field and critical current measurements support the high quality of the nanocomposite superconducting films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 2
DOI: 10.1088/0953-2048/27/1/015008
|
|
|
“Tuning of the size and the lattice parameter of ion-beam synthesized Pb nanoparticles embedded in Si”. Wang H, Cuppens J, Biermans E, Bals S, Fernandez-Ballester L, Kvashnina KO, Bras W, van Bael MJ, Temst K, Vantomme A, Journal of physics: D: applied physics 45, 035301 (2012). http://doi.org/10.1088/0022-3727/45/3/035301
Abstract: The size and lattice constant evolution of Pb nanoparticles (NPs) synthesized by high fluence implantation in crystalline Si have been studied with a variety of experimental techniques. Results obtained from small-angle x-ray scattering showed that the Pb NPs grow with increasing implantation fluence and annealing duration. The theory of NP growth kinetics can be applied to qualitatively explain the size evolution of the Pb NPs during the implantation and annealing processes. Moreover, the lattice constant of the Pb NPs was evaluated by conventional x-ray diffraction. The lattice dilatation was observed to decrease with increasing size of the Pb NPs. Such lattice constant tuning can be attributed to the pseudomorphism caused by the lattice mismatch between the Pb NPs and the Si matrix.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.588
Times cited: 5
DOI: 10.1088/0022-3727/45/3/035301
|
|
|
“Analytical TEM study of CVD diamond growth on TiO2 sol-gel layers”. Lu Y-G, Verbeeck J, Turner S, Hardy A, Janssens SD, De Dobbelaere C, Wagner P, Van Bael MK, Van Tendeloo G, Diamond and related materials 23, 93 (2012). http://doi.org/10.1016/j.diamond.2012.01.022
Abstract: The early growth stages of chemical vapor deposition (CVD) diamond on a solgel TiO2 film with buried ultra dispersed diamond seeds (UDD) have been studied. In order to investigate the diamond growth mechanism and understand the role of the TiO2 layer in the growth process, high resolution transmission electron microscopy (HRTEM), energy-filtered TEM and electron energy loss spectroscopy (EELS) techniques were applied to cross sectional diamond film samples. We find evidence for the formation of TiC crystallites inside the TiO2 layer at different diamond growth stages. However, there is no evidence that diamond nucleation starts from these crystallites. Carbon diffusion into the TiO2 layer and the chemical bonding state of carbon (sp2/sp3) were both extensively investigated. We provide evidence that carbon diffuses through the TiO2 layer and that the diamond seeds partially convert to amorphous carbon during growth. This carbon diffusion and diamond to amorphous carbon conversion make the seed areas below the TiO2 layer grow and bend the TiO2 layer upwards to form the nucleation center of the diamond film. In some of the protuberances a core of diamond seed remains, covered by amorphous carbon. It is however unlikely that the remaining seeds are still active during the growth process.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 16
DOI: 10.1016/j.diamond.2012.01.022
|
|
|
“CVD diamond growth from nanodiamond seeds buried under a thin chromium layer”. Degutis G, Pobedinskas P, Turner S, Lu Y-G, Al Riyami S, Ruttens B, Yoshitake T, D'Haen J, Haenen K, Verbeeck J, Hardy A, Van Bael MK, Diamond and related materials 64, 163 (2016). http://doi.org/10.1016/j.diamond.2016.02.013
Abstract: This work presents a morphological and structural analysis of CVD diamond growth on silicon from nanodiamond seeds covered by a 50 nm thick chromium layer. The role of carbon diffusion as well as chromium and carbon silicide formation is analyzed. The local diamond environment is investigated by scanning transmission electron microscopy in combination with electron energy-loss spectroscopy. The evolution of the diamond phase composition (sp3/sp2) is evaluated by micro-Raman spectroscopy. Raman and X-ray diffraction analysis are used to identify the interfacial phases formed during CVD growth. Based upon the observed morphological and structural evolution, a diamond growth model from nanodiamond seeds buried beneath a thin Cr layer is proposed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 11
DOI: 10.1016/j.diamond.2016.02.013
|
|
|
“Crystal structure and magnetic properties of the Cr-doped spiral antiferromagnet BiMnFe2O6”. Batuk D, de Dobbelaere C, Tsirlin AA, Abakumov AM, Hardy A, van Bael MK, Greenblatt M, Hadermann J, Materials research bulletin 48, 2993 (2013). http://doi.org/10.1016/j.materresbull.2013.04.038
Abstract: We report the Cr3+ for Mn3+ substitution in the BiMnFe2O6 structure. The BiCrxMn1-xFe2O6 solid solution is obtained by the solution-gel synthesis technique for the x values up to 0.3. The crystal structure investigation using a combination of X-ray powder diffraction and transmission electron microscopy demonstrates that the compounds retain the parent BiMnFe2O6 structure (for x = 0.3, a = 5.02010(6)angstrom, b = 7.06594(7)angstrom, c = 12.6174(1)angstrom, S.G. Pbcm, R-1 = 0.036, R-p = 0.011) with only a slight decrease in the cell parameters associated with the Cr3+ for Mn3+ substitution. Magnetic susceptibility measurements suggest strong similarities in the magnetic behavior of BiCrxMn1-xFe2O6 (x = 0.2; 0.3) and parent BiMnFe2O6. Only T-N slightly decreases upon Cr doping that indicates a very subtle influence of Cr3+ cations on the magnetic properties at the available substitution rates. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 3
DOI: 10.1016/j.materresbull.2013.04.038
|
|
|
“Properties and thermal stability of solution processed ultrathin, high-k bismuth titanate (Bi2Ti2O7) films”. Hardy A, Van Elshocht S, De Dobbelaere C, Hadermann J, Pourtois G, De Gendt S, Afanas'ev VV, Van Bael MK, Materials research bulletin 47, 511 (2012). http://doi.org/10.1016/j.materresbull.2012.01.001
Abstract: Ultrathin bismuth titanate films (Bi2Ti2O7, 5-25 nm) are deposited onto SiO2/Si substrates by aqueous chemical solution deposition and their evolution during annealing is studied. The films crystallize into a preferentially oriented, pure pyrochlore phase between 500 and 700 degrees C, depending on the film thickness and the total thermal budget. Crystallization causes a strong increase of surface roughness compared to amorphous films. An increase of the interfacial layer thickness is observed after anneal at 600 degrees C, together with intermixing of bismuth with the substrate as shown by TEM-EDX. The band gap was determined to be similar to 3 eV from photoconductivity measurements and high dielectric constants between 30 and 130 were determined from capacitance voltage measurements, depending on the processing conditions. (C) 2012 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.446
DOI: 10.1016/j.materresbull.2012.01.001
|
|
|
“Toward unlocking the Mn3+/Mn2+ redox pair in alluaudite-type Na2+2zMn2-z(SO4)3-x(SeO4)x cathodes for sodium-ion batteries”. Kirsanova MA, De Sloovere D, Karakulina OM, Hadermann J, Van Bael MK, Hardy A, Abakumov AM, Journal of solid state chemistry 277, 804 (2019). http://doi.org/10.1016/J.JSSC.2019.07.032
Abstract: In polyanion cathodes, the inductive effect alters the potential of a M(n+1)+/Mn+ redox couple (M – transition metal) according to the electronegativity of the X cation in the polyanion groups (XO4m+). To manipulate the operating potential, we synthesized a series of mixed sulfate-selenate alluaudites, with structure formulas Na2+2zMn2-z(SO4)(3-x)(SeO4)(x) and Na2.81Ni1.60(SO4)(1.43)(SeO4)(1.57). Their crystal structure was determined from powder X-ray diffraction data, revealing that the Mn-based alluaudites form solid solutions with the same crystal structure for x = 0.75; 1.125 and 1.5. Na2.81Ni1.60(SO4)(1.43)(SeO4)(1.57) is isostructural to the Mn-based alluaudites. Although the Na2+2zMn2-z(SO4)(3-x)(SeO4)(x) compound with the highest selenium content demonstrates a reversible discharge capacity of 60 mAh g(-1), only a small part of this electrochemical activity can be ascribed to the Mn3+/Mn2+ redox couple. The redox potential of the Mn3+/Mn2+ pair in Na2+2zMn2-z(SO4)(3-)x(SeO4)(x) decreases with increasing values of x, in agreement with the lower electronegativity of Se compared to that of S.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
DOI: 10.1016/J.JSSC.2019.07.032
|
|
|
“Gaining new insight into low-temperature aqueous photochemical solution deposited ferroelectric PbTiO3 films”. De Dobbelaere C, Lourdes Calzada M, Bretos I, Jimenez R, Ricote J, Hadermann J, Hardy A, Van Bael MK, Materials chemistry and physics 174, 28 (2016). http://doi.org/10.1016/J.MATCHEMPHYS.2016.02.047
Abstract: The nature of the low-temperature photochemical assisted formation process of ferroelectric lead titanate (PbTiO3) films is studied in the present work. Films are obtained by the deposition of an aqueous solution containing citric acid based (citrato) metal ion complexes with intrinsic UV activity. This UV activity is crucial for the aqueous photochemical solution deposition (aqueous PCSD) route being used. UV irradiation enhances the early decomposition of organics and results in improved electrical properties for the crystalline oxide film, even if the film is crystallized at low temperature. GATR-FTIR shows that UV irradiation promotes the decomposition of organic precursor components, resulting in homogeneous films if applied in the right temperature window during film processing. The organic content, morphology and crystallinity of the irradiated films, achieved at different processing atmospheres and temperatures, is studied and eventually correlated to the functional behavior of the obtained films. This is an important issue, as crystalline films obtained at low temperatures often lack ferroelectric responses. In this work, the film prepared in pure oxygen at the very low temperature of 400 degrees C and after an optimized UV treatment presents a significant remanent polarization value of P-r = 8.8 mu C cm(-2). This value is attributed to the better crystallinity, the larger grain size and the reduced porosity obtained thanks to the early film crystallization effectively achieved through the UV treatment in oxygen. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.084
Times cited: 4
DOI: 10.1016/J.MATCHEMPHYS.2016.02.047
|
|
|
“Anisotropic magnetism and spin-dependent transport in Co nanoparticle embedded ZnO thin films”. Li DY, Zeng YJ, Pereira LMC, Batuk D, Hadermann J, Zhang YZ, Ye ZZ, Temst K, Vantomme A, Van Bael MJ, Van Haesendonck C;, Journal of applied physics 114, 033909 (2013). http://doi.org/10.1063/1.4815877
Abstract: Oriented Co nanoparticles were obtained by Co ion implantation in crystalline ZnO thin films grown by pulsed laser deposition. Transmission electron microscopy revealed the presence of elliptically shaped Co precipitates with nanometer size, which are embedded in the ZnO thin films, resulting in anisotropic magnetic behavior. The low-temperature resistance of the Co-implanted ZnO thin films follows the Efros-Shklovskii type variable-range-hopping. Large negative magnetoresistance (MR) exceeding 10% is observed in a magnetic field of 1 T at 2.5K and the negative MR survives up to 250K (0.3%). The negative MR reveals hysteresis as well as anisotropy that correlate well with the magnetic properties, clearly demonstrating the presence of spin-dependent transport. (C) 2013 AIP Publishing LLC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 10
DOI: 10.1063/1.4815877
|
|
|
“Diamond nucleation by carbon transport from buried nanodiamond TiO2 sol-gel composites”. Doenen M, Zhang L, Erni R, Williams OA, Hardy A, van Bael MK, Wagner P, Haenen K, Nesladek M, Van Tendeloo G, Advanced materials 21, 670 (2009). http://doi.org/10.1002/adma.200802305
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 20
DOI: 10.1002/adma.200802305
|
|
|
“Atomic scale dynamics of ultrasmall germanium clusters”. Bals S, Van Aert S, Romero CP, Lauwaet K, Van Bael MJ, Schoeters B, Partoens B, Yuecelen E, Lievens P, Van Tendeloo G, Nature communications 3, 897 (2012). http://doi.org/10.1038/ncomms1887
Abstract: Starting from the gas phase, small clusters can be produced and deposited with huge flexibility with regard to composition, materials choice and cluster size. Despite many advances in experimental characterization, a detailed morphology of such clusters is still lacking. Here we present an atomic scale observation as well as the dynamical behaviour of ultrasmall germanium clusters. Using quantitative scanning transmission electron microscopy in combination with ab initio calculations, we are able to characterize the transition between different equilibrium geometries of a germanium cluster consisting of less than 25 atoms. Seven-membered rings, trigonal prisms and some smaller subunits are identified as possible building blocks that stabilize the structure.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 12.124
Times cited: 90
DOI: 10.1038/ncomms1887
|
|
|
“Increasing the solubility limit for tetrahedral aluminium in ZnO:Al nanorods by variation in synthesis parameters”. Kelchtermans A, Adriaensens P, Slocombe D, Kuznetsov VL, Hadermann J, Riskin A, Elen K, Edwards PP, Hardy A, Van Bael MK, Journal of nanomaterials 2015, 1 (2015). http://doi.org/10.1155/2015/546041
Abstract: Nanocrystalline ZnO:Al nanoparticles are suitable building blocks for transparent conductive layers. As the concentration of substitutional tetrahedral Al is an important factor for improving conductivity, here we aim to increase the fraction of substitutional Al. To this end, synthesis parameters of a solvothermal reaction yielding ZnO:Al nanorods were varied. A unique set of complementary techniques was combined to reveal the exact position of the aluminium ions in the ZnO lattice and demonstrated its importance in order to evaluate the potential of ZnO:Al nanocrystals as optimal building blocks for solution deposited transparent conductive oxide layers. Both an extension of the solvothermal reaction time and stirring during solvothermal treatment result in a higher total tetrahedral aluminium content in the ZnO lattice. However, only the longer solvothermal treatment effectively results in an increase of the substitutional positions aimed for.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.871
Times cited: 2
DOI: 10.1155/2015/546041
|
|
|
“Morphological TEM studies and magnetoresistance analysis of sputtered Al-substituted ZnO films : the role of oxygen”. Van Gompel M, Atalay AY, Gaulke A, Van Bael MK, D'Haen J, Turner S, Van Tendeloo G, Vanacken J, Moshchalkov VV, Wagner P, Physica status solidi : A : applications and materials science 212, 1191 (2015). http://doi.org/10.1002/pssa.201431888
Abstract: In this article, we report on the synthesis of thin, epitaxial films of the transparent conductive oxide Al:ZnO on (0001)-oriented synthetic sapphire substrates by DC sputtering from targets with a nominal 1 at.% Al substitution. The deposition was carried out at an unusually low substrate temperature of only 250 °C in argonoxygen mixtures as well as in pure argon. The impact of the processgas composition on the morphology was analysed by transmission electron microscopy, revealing epitaxial growth in all the cases with a minor impact of the process parameters on the resulting grain sizes. The transport properties resistivity, Hall effect and magnetoresistance were studied in the range from 10 to 300 K in DC and pulsed magnetic fields up to 45 T. While the carrier density and mobility are widely temperature independent, we identified a low fieldlow temperature regime in which the magnetoresistance shows an anomalous, negative behaviour. At higher fields and temperatures, the magnetoresistance exhibits a more conventional, positive curvature with increasing field strength. As a possible explanation, we propose carrier scattering at localised magnetic trace impurities and magnetic correlations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.775
DOI: 10.1002/pssa.201431888
|
|