“Precursor phenomena in a quenched and aged Ni52Ti48 shape memory alloy”. Somsen C, Wassermann EF, Kästner J, Schryvers D, Journal de physique: 4
T2 –, 10th International Conference on Martensitic Transformations, JUN 10-14, 2002, ESPOO, FINLAND 112, 777 (2003). http://doi.org/10.1051/jp4:2003997
Abstract: We measured the electrical resistivity R(T) and specific heat C-p(T) between room temperature (RT) and 4.2 K as well as the microstructure by transmission electron microscopy (TEM) of a Ni-52 Ti-48 SMA quenched from 1000degreesC (B2-Phase range) to RT and then annealed for 1h at T=380degreesC, 550degreesC and 650degreesC. In the “as quenched” and the “650degreesC annealed” state no martensitic transformations (MT's) occur. The diffraction patterns show faint reflections originating from coherent Ni4Ti3 precipitates in an early state of formation. Additional reflections of the type 1/2 <110>, 1/2 <111> and 1/3 <110> result from various lattice displacement waves, which are precursors of the MT's to the B19' and R-phase, respectively. Indeed, high resolution TEM micrographs of the [001] zone of the “as quenched” sample reveal transverse 1/2 <110> <110> lattice displacement waves, precursors of the B19' martensite. The coherent Ni4Ti3 precipitates, homogeneously distributed on a small length scale, binder the MT's in the “as quenched” and the “650degreesC annealed” state, and thus only the precursors appear. When annealed at T=380degreesC, however, coherent Ni4Ti3 precipitates with a length of 10nm are clearly visible in TEM. These precipitates trigger the NIT from the B2 to the R-phase on cooling, as evidenced also by anomalies in R(T) and C-p(T). Annealing at T-550degreesC leads to the well known two step MT's from the B2 to the R-phase and then into the B19'-phase. These martensitic transitions are clearly seen as additional peaks in the specific heat and anomalies in the resistance, while the “as quenched” and 650degreesC annealed samples show weak features in R(T) and C-p(T).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1051/jp4:2003997
|
|
|
“Special microstructures and twin features in Ti50Ni50-x(Pd,Au)x at small hysteresis”. Delville R, Shi H, James RD, Schryvers D, Diffusion and defect data : solid state data : part B : solid state phenomena 172/174, 105 (2011). http://doi.org/10.4028/www.scientific.net/SSP.172-174.105
Abstract: The breaking of symmetry due to atomic displacements in the austenite-martensite phase transformation generally leads to their crystallographic incompatibility. Energy minimizing accommodation mechanisms such as martensite twinning have been recently shown to be a source of hysteresis and irreversible plastic deformation. Compatibility between the two phases can however be achieved by carefully tuning lattice parameters through composition change. A dramatic drop in hysteresis and novel microstructures such as a lowering of the amount of twin lamella are then observed. Related theoretical and simulation works also support the existence of such microstructures including peculiar self-accommodating configurations at near-compatibility. We present the transmission electron microscopy (TEM) study of these novel microstructures for the alloy systems Ti50Ni50-xPdx and Ti50Ni50-xAux where the composition was systemically tuned to approach perfect compatibility. High resolution imaging of the interface between austenite and martensite supplies evidences of compatibility at the atomic level.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 3
DOI: 10.4028/www.scientific.net/SSP.172-174.105
|
|
|
“Structural characterisation of melt-spun Ti-Ni-Cu-ribbons”. Schryvers D, Potapov P, Ledda A, Shelyakov A, Journal de physique: 4 11, 363 (2001). http://doi.org/10.1051/jp4:2001861
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1051/jp4:2001861
|
|
|
“Structural characterisation of nanostructured Ni3Al processed by inert gas condensation”. Yandouzi M, Pauwels B, Schryvers D, van Swygenhoven H, Van Tendeloo G, Defects and diffusion in metals 213/215, 19 (2003)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Structural characterization of nanostructured Ni3Al processed by inert gas condensation”. Yandouzi M, Pauwels B, Schryvers D, Van Swygenhoven H, Van Tendeloo G, Diffusion and defect data : solid state data : part A : defect and diffusion forum 213, 19 (2003)
Abstract: High-resolution transmission electron microscopy was performed on compacted Ni(3)Al nanostructured material prepared by the inert gas condensation technique. From electron diffraction data an incomplete L1(2) ordering of the crystallites is observed in the free particles as well as in the room temperature compacted samples. However, a completely ordered L1(2) structure with much bigger and well-defined crystallites exhibiting several defects is observed in material compacted and annealed at 773 K. Sharp crystallite boundaries as well as amorphous material and voids are observed in between crystallites in all samples, the former being dominant in the annealed material, the latter in the as-prepared one.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“TEM study of the mechanism of Ni ion release from Nitinol wires with original oxides”. Tian H, Schryvers D, Shabalovskaya S, van Humbeeck J, , 05027 (2009). http://doi.org/10.1051/esomat/200905027
Abstract: The surface of commercial Nitinol wires with original oxides and a thickness in the 30-190 nm range was investigated by different state of art TEM techniques. The oxide surface layer was identified as a combination of TiO and TiO2 depending on the processing of the wire. Between the core of the wires and the oxidized surface, an interfacial Ni3Ti nanolayer was observed while Ni nanoparticles are found inside the original oxide. The particle sizes, their distribution in the surface and the Ti-O stoichiometry were deduced from the analysis of the obtained data. Molecular dynamics calculations performed for evaluation of the stability of Ni particles relative to the atomic state revealed that a pure Ni particle has a lower energy than free Ni atoms inside the TiO2 lattice. The obtained results are discussed with respect to surface stability and Ni release in the human body.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1051/esomat/200905027
|
|
|
“Ni4Ti3 precipitates and their influence on the surrounding NiTi matrix”. Schryvers D, Tirry W, Yang Z, , 205 (2005)
Abstract: The properties of the shape memory behaviour of Ni-rich binary NiTi are strongly dependant on the thermal history of the material. In this respect the changing of transformation temperatures of the underlying martensitic transformation and the occurrence of multiple step transformations are the most important phenomena. Part of the explanation is found in the presence of Ni4Ti3 precipitates in the B2 matrix after particular heat treatments. The formation of these precipitates changes the Ni concentration of the matrix and induces a strain field, with both of these aspects expected to be of importance. In this work atomic resolution and analytical TEM (transmission electron microscopy) techniques are used to obtain quantitative information concerning these two main features. Furthermore, the known structure of Ni4Ti3 is refined by a least squares optimization of quantitative electron diffraction data. The high-resolution TEM results show that there are strains up to 2% in the matrix surrounding the precipitates and they gradually increase until a maximum is reached when moving away from the interface. Analytical results reveal a global decrease of Ni content in the matrix when sufficient precipitates are present and a gradient in their close vicinity. The refinement of the structure shows atomic displacements, thereby increasing our understanding of the shrinking of the precipitate lattice with respect to the matrix.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“The analysis of macrotwins in NiAl martensite”. Ball JM, Schryvers D, Journal de physique: 4
T2 –, 10th International Conference on Martensitic Transformations, JUN 10-14, 2002, ESPOO, FINLAND 112, 159 (2003). http://doi.org/10.1051/jp4:2003855
Abstract: We present a theoretical study of macrotwins arising in cubic to tetragonal martensitic transformations. The results help to explain some features of such macrotwins observed in Ni65Al35.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 11
DOI: 10.1051/jp4:2003855
|
|
|
“The influence of the precipitation method on defect formation in multishell AgBrI (111) tabular crystals”. Van Renterghem W, Karthauser S, Schryvers D, van Landuyt J, De Keyzer R, Van Roost C, , 167 (2000)
Abstract: Multishell tabular grains have a higher speed than pure AgBr tabular grains. Usually the shells differ in size and iodide content, but also the precipitation method for the iodide containing shells has an influence on the iodide incorporation. A TEM investigation was performed to determine the defect structure of multishell AgBr (111) tabular crystals containing a shell with a low iodide concentration and one with a high iodide concentration. The twins that induce tabular growth and stacking fault contrast in the region of the iodide shells have been observed, similar to previously studied AgBr/Ag(Br,I) coreshell crystals. Moreover in some of the crystals dislocations have been observed, sometimes even an entire network. The number of dislocations formed varies for the different methods of iodide addition. Also variations in average thickness between the different iodide addition methods have been observed. A higher number of dislocations and thicker crystals point towards a higher local concentration of iodide. These observations allow deciding which iodide incorporation method is most useful for a preferred dislocation pattern.
Keywords: P1 Proceeding; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
|
|
|
“Multiscale investigation of quasi-brittle fracture characteristics in a 9Cr–1Mo ferritic–martensitic steel embrittled by liquid lead–bismuth under low cycle fatigue”. Gong X, Marmy P, Volodin A, Amin-Ahmadi B, Qin L, Schryvers D, Gavrilov S, Stergar E, Verlinden B, Wevers M, Seefeldt M, Corrosion science 102, 137 (2016). http://doi.org/10.1016/j.corsci.2015.10.003
Abstract: Liquid metal embrittlement (LME) induced quasi-brittle fracture characteristics of a 9Cr–1Mo ferritic–martensitic steel (T91) after fatigue cracking in lead–bismuth eutectic (LBE) have been investigated at various length scales. The results show that the LME fracture morphology is primarily characterized by quasi-brittle translath flat regions partially covered by nanodimples, shallow secondary cracks propagating along the martensitic lath boundaries as well as tear ridges covered by micro dimples. These diverse LME fracture features likely indicate a LME mechanism involving multiple physical processes, such as weakening induced interatomic decohesion at the crack tip and plastic shearing induced nano/micro voiding in the plastic zone.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Times cited: 16
DOI: 10.1016/j.corsci.2015.10.003
|
|
|
“Transmission electron microscopy study of low-hysteresis shape memory alloys”. Delville R, James RD, Salman U, Finel A, Schryvers D, , 02005 (2009). http://doi.org/10.1051/esomat/200902005
Abstract: Recent findings have linked low hysteresis in shape memory alloys with phase compatibility between austenite and martensite. In order to investigate the evolution of microstructure as the phase compatibility increases and the hysteresis is reduced, transmission electron microscopy was used to study the alloy system Ti50Ni50-xPdx where the composition is systemically tuned to approach perfect compatibility. Changes in morphology, twinning density and twinning modes are reported along with special microstructures occurring when the compatibility is achieved. In addition, the interface between austenite and a single variant of martensite was studied by high-resolution and conventional electron microscopy. The atomically sharp, defect free, low energy configuration of the interface suggests that it plays an important role in the lowering of hysteresis. Finally, dynamical modeling of the martensitic transformation using the phase-field micro-elasticity model within the geometrically linear theory succeeded in reproducing the change in microstructure as the compatibility condition is satisfied. Latest results on the extension of these findings in other Ni-Ti based ternary/quaternary systems are also reported.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 3
DOI: 10.1051/esomat/200902005
|
|
|
“Transmission electron microscopy study of microstructural evolution in nanograined Ni-Ti microwires heat treated by electric pulse”. Delville R, Malard B, Pilch J, Sittner P, Schryvers D, Diffusion and defect data : solid state data : part B : solid state phenomena 172/174, 682 (2011). http://doi.org/10.4028/www.scientific.net/SSP.172-174.682
Abstract: Transmission electron microscopy and mechanical testing were employed to investigate the evolution of microstructure and functional superelastic properties of 0.1mm diameter as-drawn Ni-Ti wires subjected to a non-conventional heat treatment by controlled electric pulse current. This method enables a finer control of the recovery and recrystallisation processes taking place during the heat treatment and accordingly a better control on the final microstructure. The best functional properties were obtained for heat-treated Ni-Ti wires having a nanograined microstructure (20-50 nm) partially recovered through polygonization and partially recrystallized. Such microstructure is highly resistant against dislocation slip upon cycling, while microstructures annealed for longer time and showing mostly recrystallized grains were prone to dislocation slip, particularly as the grain size exceeds 100 nm. The density of dislocation defects increased significantly with increasing grain size of the microstructure. The activity of three <100>/{011} slip systems was identified in the largest grains of 500-1200 nm. An additional mode of plastic deformation, {114} compound austenite twinning, was observed in the largest grains of fully recrystallized microstructures. It is proposed that dislocation slip (and possibly deformation twinning) occurring in superelastic cycling is coupled with the stress-induced martensitic transformation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 3
DOI: 10.4028/www.scientific.net/SSP.172-174.682
|
|
|
“Optimization of Automated Crystal Orientation and Phase Mapping in TEM Applied to Ni-Ti All Round Shape Memory Alloy”. Yao X, Li Y, Cao S, Ma X, Zhang X-ping, Schryvers D, MATEC web of conferences
T2 –, Proceedings of ESOMAT 2015 10th European Symposium on Martensitic Transformations, September 14-18, 2015, Antwerp, Belgium 33, 03022 (2015). http://doi.org/10.1051/matecconf/20153303022
Abstract: A new application which focuses on an artificial sphincter fabricated by Ni-Ti SMAs for human implantation is under investigation by applying the all-round shape memory effect with precise control of the phase transformation temperatures. In this study, a Ni51at.%-Ti alloy was fabricated by arc melting with fast solidification, followed by a proper strained aging which induces the two way shape memory effect needed for this particular application. Differential scanning calorimetry was used to investigate the thermal behavior and transmission electron microscopy was used for studying the microstructure of the alloys. With the latter the novel technique of automated crystal orientation microscopy is used and optimized to obtain phase and orientation mapping of the various structures.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1051/matecconf/20153303022
|
|
|
“Microstructural Characterization and Transformation Behavior of Porous Ni50.8Ti49.2”. Yao X, Cao S, Zhang XP, Schryvers D, Materials Today: Proceedings 2, S833 (2015). http://doi.org/10.1016/j.matpr.2015.07.411
Abstract: Porous Ni50.8Ti49.2 bulk material was prepared by powder metallurgy sintering. Solid solution and aging treatments were applied to improve the phase homogeneity and phase transformation behavior. Scanning and transmission electron microscopy, aided by energy dispersive X-ray analysis, were used to study the microstructure and chemical phase content of the alloys. In-situ cooling was carried out to observe the phase transformation behavior. As-received material contains dispersed Ni2Ti4O particles while Ni4Ti3 precipitates appear after aging. Close to pore edges, the latter have a preferential orientation due to the induced stress fields in the matrix.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
DOI: 10.1016/j.matpr.2015.07.411
|
|
|
“Low-temperature plasticity of olivine revisited with in situ TEM nanomechanical testing”. Idrissi H, Bollinger C, Boioli F, Schryvers D, Cordier P, Science Advances 2, e1501671 (2016). http://doi.org/10.1126/sciadv.1501671
Abstract: The rheology of the lithospheric mantle is fundamental to understanding how mantle convection couples with plate tectonics. However, olivine rheology at lithospheric conditions is still poorly understood because experiments are difficult in this temperature range where rocks and mineral become very brittle. We combine techniques of quantitative in situ tensile testing in a transmission electron microscope and numerical modeling of dislocation dynamics to constrain the low-temperature rheology of olivine. We find that the intrinsic ductility of olivine at low temperature is significantly lower than previously reported values, which were obtained under strain-hardened conditions. Using this method, we can anchor rheological laws determined at higher temperature and can provide a better constraint on intermediate temperatures relevant for the lithosphere. More generally, we demonstrate the possibility of characterizing the mechanical properties of specimens, which can be available in the form of submillimeter-sized particles only.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Times cited: 32
DOI: 10.1126/sciadv.1501671
|
|
|
“Optimization of Automated Crystal Orientation Mapping in a TEM for Ni4Ti3 Precipitation in All-Round SMA”. Yao X, Amin-Ahmadi B, Li Y, Cao S, Ma X, Zhang X-P, Schryvers D, Shape memory and superelasticity 2, 286 (2016). http://doi.org/10.1007/s40830-016-0082-z
Abstract: Automated crystal orientation and phase mapping in TEM are applied to the quantification of Ni4Ti3 precipitates in Ni–Ti shape memory alloys which will be used for the implantation of artificial sphincters operating using the all-round shape memory effect. This paper focuses on the optimization process of the technique to obtain best values for all major parameters in the acquisition of electron diffraction patterns as well as template generation. With the obtained settings, vast statistical data on nano- and microstructures essential to the operation of these shape memory devices become available.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1007/s40830-016-0082-z
|
|
|
“Transmission electron microscopy study of complex oxide scales on DIN 1.4970 steel exposed to liquid Pb-Bi eutectic”. Charalampopoulou E, Delville R, Verwerft M, Lambrinou K, Schryvers D, Corrosion science 147, 22 (2019). http://doi.org/10.1016/j.corsci.2018.10.018
Abstract: The deployment of Gen-IV lead-cooled fast reactors requires a good compatibility between the selected structural/cladding steels and the inherently corrosive heavy liquid metal coolant. An effective liquid metal corrosion mitigation strategy involves the in-situ steel passivation in contact with the oxygen-containing Pb-alloy coolant. Transmission electron microscopy was used in this work to study the multi-layered oxide scales forming on an austenitic stainless steel fuel cladding exposed to oxygen-containing (CO ≈ 10−6 mass%) static liquid leadbismuth eutectic (LBE) for 1000 h between 400 and 500 °C. The oxide scale constituents were analyzed, including the intertwined phases comprising the innermost biphasic layer.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Times cited: 5
DOI: 10.1016/j.corsci.2018.10.018
|
|
|
“In-Situ TEM Stress Induced Martensitic Transformation in Ni50.8Ti49.2 Microwires”. Pourbabak S, Orekhov A, Samaee V, Verlinden B, Van Humbeeck J, Schryvers D, Shape memory and superelasticity 5, 154 (2019). http://doi.org/10.1007/s40830-019-00217-6
Abstract: In-situ transmission electron microscopy tensile straining is used to study the stress induced martensitic transformation in Ni50.8Ti49.2. Two microwire samples with different heat treatment are investigated from which one single crystal and three polycrystalline TEM specimens, the latter with micro- and nano-size grains, have been produced. The measured Young’s modulus for all TEM specimens is around 70 GPa, considerably higher than the averaged 55 GPa of the original microwire sample. The height of the superelastic stress plateau shows an inverse relationship with the specimen thickness for the polycrystalline specimens. Martensite starts nucleating within the elastic region of the stress–strain curve and on the edges of the specimens while also grain boundaries act as nucleation sites in the polycrystalline specimens. When a martensite plate reaches a grain boundary in the polycrystalline specimen, it initiates the transformation in the neighboring grain at the other side of the grain boundary. In later stages martensite plates coalesce at higher loads in the stress plateau. In highly strained specimens, residual martensite remains after release.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1007/s40830-019-00217-6
|
|
|
“Datasets for the analysis of dislocations at grain boundaries and during vein formation in cyclically deformed Ni micropillars”. Sandfeld S, Samaee V, Idrissi H, Groten J, Pardoen T, Schwaiger R, Schryvers D, Data in Brief 27, 104724 (2019). http://doi.org/10.1016/J.DIB.2019.104724
Abstract: The dataset together with the corresponding Python scripts and Jupyter notebooks presented in this article are supplementary data for the work presented in Samaee et al., 2019 [1]. The data itself consists of two parts: the simulation data that was used in [1] to analyze the effect of a particular grain boundary on curved dislocations and the precession electron diffraction (PED) strain maps together with post-processed data for analyzing details of the observed dislocation vein structures. Additionally, the complete stress tensor components, which are not shown in [1], have also been included. The data sets are accompanied by Python code explaining the file formats and showing how to post-process the data. (c) 2019 The Author(s). Published by Elsevier Inc. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.DIB.2019.104724
|
|
|
“Analysis of internal stress build-up during deposition of nanocrystalline Ni thin films using transmission electron microscopy”. Lumbeeck G, Delvaux A, Idrissi H, Proost J, Schryvers D, Thin solid films : an international journal on the science and technology of thin and thick films 707, 138076 (2020). http://doi.org/10.1016/j.tsf.2020.138076
Abstract: Ni thin films sputter-deposited at room temperature with varying Ar pressures were investigated with automated crystal orientation mapping in a transmission electron microscope to uncover the mechanisms controlling the internal stress build-up recorded in-situ during deposition. Large grains were found to induce behaviour similar to a stress-free nucleation layer. The measurements of grain size in most of the Ni thin films are in agreement with the island coalescence model. Low internal stress was observed at low Ar pressure and was explained by the presence of large grains. Relaxation of high internal stress was also noticed at the highest Ar pressure, which was attributed to a decrease of Σ3 twin boundary density due to a low deposition rate. The results provide insightful information to better understand the relationship between structural boundaries and the evolution of internal stress upon deposition of thin films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1016/j.tsf.2020.138076
|
|
|
Cautaerts N, Lamm S, Stergar E, Pakarinen J, Yang Y, Hofer C, Schnitzer R, Felfer P, Verwerft M, Delville R, Schryvers D (2020) Atom probe tomography data collection from DIN 1.4970 (15-15Ti) austenitic stainless steel irradiated with Fe ions
Abstract: This dataset comprises a large collection of atom probe tomography datasets collected from DIN 1.4970 alloy that was irradiated with Fe ions at different conditions. The DIN 1.4970 alloy is an austenitic stainless steel with 15 wt% Cr, 15 wt% Ni, a small addition of Ti. The full composition and characterization of our material can be found published elsewhere [1,2]. Some of our material was subjected to ageing heat treatments at different temperatures for different times. Small samples of our original material and aged material was irradiated at the Michigan Ion Beam Laboratory in 2017 with 4.5 MeV Fe ions up to 40 dpa at an average dose rate of 2×10−4 dpa/s. This was done at three different temperatures: 300, 450, and 600 ºC. Atom probe samples were made of the irradiated layers (approximately 1.5 micron deep) with focused ion beam and mounted on Microtip coupons. APT measurements took place on three CAMECA LEAP-HR systems located at CAES in Idaho Falls, USA (files beginning with R33), at Montanuniversität Leoben in Leoben, Austria (R21) and at Friedrich–Alexander University in Erlangen, Germany (R56).
Keywords: Dataset; Electron microscopy for materials research (EMAT)
DOI: 10.5281/ZENODO.3407832
|
|
|
“DSC cycling effects on phase transformation temperatures of micron and submicron grain Ni50.8Ti49.2 microwires”. Pourbabak S, Verlinden B, Van Humbeeck J, Schryvers D, Shape memory and superelasticity , 1 (2020). http://doi.org/10.1007/S40830-020-00278-Y
Abstract: The effect of thermal cycling parameters on the phase transformation temperatures of micron and submicron grain size recrystallized Ni-Ti microwires was investigated. The suppression of martensitic transformation by thermal cycling was found to enhance when combined with room temperature aging between the cycles and enhances even more when aged at elevated temperature of 100 degrees C. While aging at room temperature alone has no clear effect on the martensitic transformation, elevated temperature aging at 100 degrees C alone suppresses the martensitic transformation. All aforementioned effects were found to be stronger in large grain samples than in small grain samples. Martensitic transformation suppression in all cases was in line with the formation of Ni4Ti3 precursors in the form of < 111 & rang;(B2) Ni clusters as concluded from the observed diffuse intensity in the electron diffraction patterns revealing short-range ordering enhancement. Performing thermal cycling in some different temperature ranges to separate the effect of martensitic transformation and high temperature range of DSC cycling revealed that both high temperature- and martensitic transformation-included cycles enhance the short-range ordering.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1007/S40830-020-00278-Y
|
|
|
Samaeeaghmiyoni V, Cordier P, Demouchy S, Bollinger C, Gasc J, Mussi A, Schryvers D, Idrissi H (2020) Research data supporting for Stress-induced amorphization triggers deformation in the lithospheric mantle
Keywords: Dataset; Electron microscopy for materials research (EMAT)
DOI: 10.5281/zenodo.3893661
|
|
|
“Electronic and chemical properties of nickel oxide thin films and the intrinsic defects compensation mechanism”. Poulain R, Lumbeeck G, Hunka J, Proost J, Savolainen H, Idrissi H, Schryvers D, Gauquelin N, Klein A, ACS applied electronic materials 4, 2718 (2022). http://doi.org/10.1021/ACSAELM.2C00230
Abstract: Although largely studied, contradictory results on nickel oxide (NiO) properties can be found in the literature. We herein propose a comprehensive study that aims at leveling contradictions related to NiO materials with a focus on its conductivity, surface properties, and the intrinsic charge defects compensation mechanism with regards to the conditions preparation. The experiments were performed by in situ photo-electron spectroscopy, electron energy loss spectroscopy, and optical as well as electrical measurements on polycrystalline NiO thin films prepared under various preparation conditions by reactive sputtering. The results show that surface and bulk properties were strongly related to the deposition temperature with in particular the observation of Fermi level pinning, high work function, and unstable oxygen-rich grain boundaries for the thin films produced at room temperature but not at high temperature (>200 degrees C). Finally, this study provides substantial information about surface and bulk NiO properties enabling to unveil the origin of the high electrical conductivity of room temperature NiO thin films and also for supporting a general electronic charge compensation mechanism of intrinsic defects according to the deposition temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1021/ACSAELM.2C00230
|
|
|
“Displacive and diffusive components in the formation of the Ni2Al structure studied by HREM, SAED and micro-ED”. Muto S, Merk N, Schryvers D, Tanner LE, Monterey Institute for Advances Studies , 101 (1992)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Displacive-replacive phase transformation in a Ni62.5Al37.5 phase studies by HREM and microdiffraction”. Muto S, Merk N, Schryvers D, Tanner LE, Philosophical magazine: B: physics of condensed matter: electronic, optical and magnetic properties 67, 673 (1993). http://doi.org/10.1080/13642819308219316
Abstract: The structure of the metastable Ni2Al phase, which has long been a matter of controversy, has been carefully re-examined by means of high-resolution transmission electron microscopy (HREM) and electron microdiffraction. First, it is concluded that theas-quenched NixAl100-x(60 less-than-or-equal-to x less-than-or-equal-to 65) material already exhibits a partial omega-type collapse in a one-dimensional fashion which and is consistent with the anomalous dip in the phonon dispersion curve. Ni2Al precipitates are formed on annealing by thermal decomposition of the high-temperature NixAl100-xB2 phase and still retain the small omega-type shuffle. The amount of displacement in the well developed Ni2Al phase was estimated to be between 20 and 50% of the ideal omega collapse; this was determined by means of a combined technique of HREM and microdiffraction together with dynamical calculations of HREM images and diffraction intensities.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 16
DOI: 10.1080/13642819308219316
|
|
|
“Electron diffraction evidence for ordering of interstitial silver ions in silver bromide microcrystals”. Goessens C, Schryvers D, van Dyck D, van Landuyt J, de Keyzer R, Icem 13 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
|
|
|
“Electron-diffraction evidence for ordering of interstitial silver ions in silver bromide microcrystals”. Goessens C, Schryvers D, van Dyck D, van Landuyt J, de Keyzer R, Physica status solidi: A 143, 277 (1994). http://doi.org/10.1002/pssa.2211430211
Abstract: The occurrence and origin of diffuse intensity contours in electron micrographs of AgBr crystals are investigated. The observations are interpreted in terms of a model, which attributes diffuse scattering to the presence of predominant atom or vacancy clusters of a particular polyhedral type. It is shown that irrespective of the crystal morphology, interstitial Ag ions order in AgBr material in clusters of finite size along 001 type planes. A different geometry of the diffuse intensity locus observed for triangular and hexagonal tabular grains is explained in terms of the different twin plane morphology of these grains.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Times cited: 7
DOI: 10.1002/pssa.2211430211
|
|
|
“Electron-irridation-induced martensitic transformation in a Ni63Al37 observed in-situ by HREM”. Muto S, Schryvers D, MRS Japan: shape memory materials 18, 853 (1993)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Electron microscopy and diffraction study of the composition dependency of the 3R microtwinned martensite in Ni-Al”. Schryvers D, de Saegher B, van Landuyt J, Materials research bulletin 26, 57 (1991)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.288
Times cited: 11
|
|