“Microstructure of quenched Ni-rich Ni-Ti shape memory alloys”. Somsen C, Kästner J, Wassermann EF, Boullay P, Schryvers D, Journal de physique: 4
T2 –, 8th European Symposium on Martensitic Transformations (ESOMAT2000), SEP 04-08, 2000, COMO, ITALY 11, 445 (2001). http://doi.org/10.1051/jp4:2001874
Abstract: Microstructural investigations with transmission electron microscopy were carried out on quenched Ni-Ti alloys with 52 and 54.5 at% Ni. For the Ni52Ti48 specimen long time exposed diffraction patterns of a single grain show besides the expected reflections of the B2-phase, two sets of extra reflections in different zones. The first type of spots is explained by lattice displacement waves, which are regarded as precursors of the martensitic Ni-Ti phases, B 19' and R-phase, respectively. The second set of reflection with more diffuse intensity than the other reflections is related to Ni4Ti3 precipitates in an early state of formation. For the Ni-richer Ni54.5Ti45.5 alloy only Ni4Ti3 precipitates in an early state of formation are found but no precursors of the B 19'- and R-phase.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1051/jp4:2001874
|
|
|
“Microstructure of tough polycrystalline natural diamond”. Chen JH, Van Tendeloo G, Journal of electron microscopy 48, 121 (1999). http://doi.org/10.1093/oxfordjournals.jmicro.a023658
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.9
Times cited: 9
DOI: 10.1093/oxfordjournals.jmicro.a023658
|
|
|
“Misfit accommodation of epitaxial La1-xAxMnO3 (A=Ca, Sr) thin films”. Lebedev OI, Van Tendeloo G, Amelinckx S, International journal of inorganic materials 3, 1331 (2001). http://doi.org/10.1016/S1466-6049(01)00155-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1016/S1466-6049(01)00155-6
|
|
|
Batuk D (2014) Modular structures with lone electron pair cations. Antwerpen
Keywords: Doctoral thesis; Electron microscopy for materials research (EMAT)
|
|
|
“Modulated structures in KAISi3O8: a study by high resolution electron microscopy and 29Si MAS-NMR spectroscopy”. Sanchez-Munoz L, Nistor L, Van Tendeloo G, Sanz J, Journal of electron microscopy 47, 17 (1998). http://doi.org/10.1093/oxfordjournals.jmicro.a023555
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.9
Times cited: 10
DOI: 10.1093/oxfordjournals.jmicro.a023555
|
|
|
“Morphology and defects in shallow trench isolation structures”. Stuer C, van Landuyt J, Bender H, Rooyackers R, Badenes G, Conference series of the Institute of Physics 164, 443 (1999)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
|
|
|
“Multi-functional copper oxide nanosystems for H2 sustainable production and sensing”. Gasparotto A, Barreca D, Fornasiero P, Gombac V, Lebedev O, Maccato C, Montini T, Tondello E, Van Tendeloo G, Comini E, Sberveglieri G, ECS transactions 25, 1169 (2009)
Abstract: This work focuses on the use of tailored copper oxide nanoarchitectures as multi-functional materials for the sustainable production of hydrogen and its on-line detection. An innovative copper(II) precursor, Cu(hfa)2TMEDA, was adopted in the CVD of CuxO (x=1,2) nanosystems under both O2 and O2+H2O atmospheres on Si(100) and Al2O3 substrates. A multi-technique characterization indicates that both the phase composition (from Cu2O to CuO) and morphology (from continuous films to entangled quasi-1D nanosystems) can be tailored by varying the growth temperature and reaction atmosphere. The obtained CuxO nanodeposits are active in the photocatalytic H2 production from aqueous solutions under UV-Vis irradiation and display interesting gas sensing performances towards hydrogen detection even at moderate temperatures.
Keywords: A2 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Nano- and microcrystal investigations of precipitates, interfaces and strain fields in Ni-Ti-Nb by various TEM techniques”. Schryvers D, Shi H, Martinez GT, Van Aert S, Frenzel J, Van Humbeeck J, Materials science forum
T2 –, 9th European Symposium on Martensitic Transformations (ESOMAT 2012), SEP 09-16, 2012, St Petersburg, RUSSIA 738/739, 65 (2013). http://doi.org/10.4028/www.scientific.net/MSF.738-739.65
Abstract: In the present contribution several advanced electron microscopy techniques are employed in order to describe chemical and structural features of the nano- and microstructure of a Ni45.5Ti45.5Nb9 alloy. A line-up of Nb-rich nano-precipitates is found in the Ni-Ti-rich austenite of as-cast material. Concentration changes of the matrix after annealing are correlated with changes in the transformation temperatures. The formation of rows and plates of larger Nb-rich precipitates and particles is described. The interaction of a twinned martensite plate with a Nb-rich nano-precipitate is discussed and the substitution of Nb atoms on the Ti-sublattice in the matrix is confirmed.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.4028/www.scientific.net/MSF.738-739.65
|
|
|
“Nanodesign of combined micro- and mesoporous materials for specific applications in adsorption and catalysis”. Meynen V, Busuioc AM, Beyers E, Cool P, Vansant EF, Bilba N, Mertens M, Lebedev O, Van Tendeloo G Nova, New York (2007).
Keywords: H3 Book chapter; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
|
|
|
“Nanoparticles in glass and glazes”. Frederickx P, De Vis K, Wouters H, Helary D, Schryvers D, (2005)
Keywords: P3 Proceeding; Art; Electron microscopy for materials research (EMAT)
|
|
|
“Nanoparticles in lustre reconstructions”. Frederickx P, Verbeeck J, Schryvers D, Helary D, Darque-Ceretti E, , 169 (2005)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Nanoscale inhomogeneities in melt-spun Ni-Al”. Potapov P, Ochin P, Pons J, Schryvers D, Journal de physique: 4 11, 439 (2001). http://doi.org/10.1051/jp4:2001873
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1051/jp4:2001873
|
|
|
“Nanoscale morphology of a piece of ruby red Kunckel glass”. Fredrickx P, Schryvers D, Janssens K, Physics and chemistry of glasses 43, 176 (2002)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
|
|
Goorden L, Van Tendeloo G, Lenaerts S, Deblonde M, et al. (2009) Nanotechnologie: gewikt en gewogen. NanoSoc
Keywords: Minutes and reports; Engineering sciences. Technology; Engineering Management (ENM); Sustainable Energy, Air and Water Technology (DuEL); Electron microscopy for materials research (EMAT)
|
|
|
Goorden L, Van Tendeloo G, Lenaerts S, Deblonde M, van Oudheusden M, et al. (2009) Nanotechnologie op de agenda. NanoSoc
Keywords: Minutes and reports; Engineering sciences. Technology; Engineering Management (ENM); Society and Environment; Sustainable Energy, Air and Water Technology (DuEL); Electron microscopy for materials research (EMAT)
|
|
|
“'Natural' and 'man-made' platelets in type-la diamonds”. Kiflawi I, Bruley J, Luyten W, Van Tendeloo G, Philosophical magazine: B: physics of condensed matter: electronic, optical and magnetic properties 78, 299 (1998). http://doi.org/10.1080/13642819808205733
Abstract: 'Natural' platelets are planar defects in {001} planes found in natural type-IaA/B diamonds. 'Man-made' platelets are platelets formed in the laboratory by annealing type-IaA diamonds at temperatures over 2500 degrees C. Careful study shows that the infrared (IR) spectra of the 'man-made' platelets are different from the IR spectra of 'natural' platelets. High-temperature (T greater than or equal to 2000 degrees C) annealing of platelets containing type-IaA/B diamonds modifies the IR absorption spectrum owing to the 'natural' platelets and makes it similar to the IR spectrum of the 'man-made' platelets. It is suggested that such high-temperature annealing changes the structure of the 'natural' platelets. The changes are too subtle to be detected by electron microscopy techniques. Topographic electron-energy-loss spectroscopy shows that platelets contain nitrogen at an average density of 0.7 atoms per a(0)(2); however, high-temperature annealing does not seem to affect the concentration of the nitrogen in the platelets.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 13
DOI: 10.1080/13642819808205733
|
|
|
“Natural mineral-marine manganese nodule as a novel catalyst for the synthesis of carbon nanotubes”. Cheng JP, Zhang XB, Ye Y, Tao XY, Liu F, Li Y, Van Tendeloo G, Journal of Wuhan University of Technology: materials science edition 21, 29 (2006)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“New intermediate defect configuration in Si studied by in situ HREM irradiation”. Fedina L, Gutakovskii A, Aseev A, van Landuyt J, Vanhellemont J, Conference series of the Institute of Physics 157, 43 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
Batuk M (2013) New perovskite-based homologous series : AnBnO3n-2 and An+1BnO3n-1Cl. Antwerpen
Keywords: Doctoral thesis; Electron microscopy for materials research (EMAT)
|
|
|
“Nickel/carbon composite materials based on expanded graphite”. Afanasov IM, Lebedev OI, Kolozhvary BA, Smirnov AV, Van Tendeloo G, New carbon materials 26, 335 (2011). http://doi.org/10.1016/S1872-5805(11)60085-1
Abstract: Monolithic nickel/carbon (Ni/C) composites were prepared from coal tar pitch-impregnated compressed expanded graphite pre-decorated with NiO particles (EGNiO) by pyrolysis at 550 °C and subsequent steam activation at 800 °C. The microstructural arrangement of the Ni-comprising nanoparticles in the composites was investigated using transmission electron microscopy. The specific surface area and porosity of the composites were analyzed by nitrogen adsorption. The catalytic activity of the composites was compared with the material obtained by the conventional H2 treatment of EGNiO using hydrocracking of 2,2,3-trimethylpentane as a model reaction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 7
DOI: 10.1016/S1872-5805(11)60085-1
|
|
|
“The notion of resolution”. Van Aert S, den Dekker AJ, van Dyck D, van den Bos A Springer, Berlin, page 1228 (2008).
Keywords: H3 Book chapter; Electron microscopy for materials research (EMAT); Vision lab
|
|
|
“The notion of resolution”. Van Aert S, den Dekker AJ, van Dyck D, van den Bos A Springer, Berlin, page 1228 (2007).
Keywords: H3 Book chapter; Electron microscopy for materials research (EMAT); Vision lab
|
|
|
“Observations of intermetallic compound formation of hot dip aluminized steel”. Kee-Hyun K, van Daele B, Van Tendeloo G, Jong-Kyu Y, Aluminium alloys: part 1-2 519-521, 1871 (2006)
Abstract: A hot dip aluminizing process to simulate the continuous galvanizing line (CGL) was carried out in three successive steps by a hot dip simulator: the pre-treatment for removing scales on the 200 x 250 mm(2) and 1mm in thickness cold rolled steel sheet, the dipping in 660 degrees C Al-Si melt for 3s and the cooling. In a pre-treatment, the steel specimen was partly coated by Au to confirm the mechanism of intermetallic compound (IMC) formation. Scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), and transmission electron microscopy (TEM) analyses were followed to observe the cross-section and the distribution of the elements. The specimen was analyzed in the boundary of the dipped-undipped part to see the formation mechanism of the aluminized steel. An intermetallic compound (IMC) is rapidly developed and grown in the steel-liquid interface. It has been usually reported that the IMC was formed by the dissolution of iron in the steel substrate toward the melt and the diffusion of aluminum in an opposite direction. The specimen is covered with aluminum-10 wt.% silicon, forms the IMC in the part that was not Au coated. However, IMC is not formed in the Au-coated part. The interface of the dipped-undipped is also analyzed by EDX. At the interface of the steel-IMC, it is clearly shown that the IMC is only formed in the dipped part and exists in the steel substrate as well, and contributes by iron, aluminum and silicon. The result clearly shows that only aluminum diffuses into the steel substrate without the dissolution of iron and forms the IMC between the steel substrate and the melt. Au coating and the short dipping time prevent the iron from dissolving into the aluminum melt. By TEM combined with focused ion beam (FIB) sample preparation, the IMC is confirmed as Fe2SiAl8, a hexagonal structure with space group P6(3)/mmc.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Obstacles on the road towards atomic resolution tomography”. van Dyck D, Van Aert S, Croitoru MD, Microscoy and microanalysis 11, 238 (2005)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT); Vision lab
|
|
|
“On the mechanism of {111}-defect formation in silicon studies by in situ electrin irradiation in a high resolution electron microscope”. Fedina L, Gutakovskii A, Aseev A, van Landuyt J, Vanhellemont J, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 77, 423 (1998)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 23
|
|
|
“Optimization of the amount of catalyst and reaction time in single wall nanotube production”. Horvath ZE, Biro LP, Van Tendeloo G, Tondeur C, Bister G, Pierard N, Fonseca A, Nagy JB, Diffusion and defect data : solid state data : part B : solid state phenomena 94, 271 (2003)
Abstract: The influence of the amount of catalyst and the reaction time on the quantity and quality of catalytically grown single wall carbon nanotubes (SWNT) was investigated. The aim was to optimize some of the SWNT growth parameters using TEM and HRTEM. The thickness of catalyst layer influences the synthesis of the nanotube because the gas composition can differ between top and bottom. Microscopic investigation of the grown SWNT samples showed that the thicker the catalyst layer the lower relative nanotube content, so the deeper parts of the catalyst layer are less effective: The optimum time for the reaction was found to be 10 minutes. This may be understood assuming that nanotube growth needs an initial incubation time while the activity of the catalyst decreases steadily until the nariotube growth stops.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Oxygen and fluorine doping in Sr2MnGaO5 brownmillerite”. Antipov EV, Abakumov AM, Alekseeva AM, Rozova MG, Hadermann J, Lebedev OI, Van Tendeloo G, Physica status solidi: A: applied research 201, 1403 (2004). http://doi.org/10.1002/pssa.200304428
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 9
DOI: 10.1002/pssa.200304428
|
|
|
“Pd@MOF-5: limitations of gas-phase infiltration and solution impregnation of [Zn4O(bdc)3] (MOF-5) with metalorganic palladium precursors for loading with Pd nanoparticles”. Esken D, Zhang X, Lebedev OI, Schröder F, Fischer RA, Journal of materials chemistry 19, 1314 (2009). http://doi.org/10.1039/b815977g
Abstract: The limitations of the loading of the porous metalorganic framework [Zn4O(bdc)3] (bdc = benzene-1,4-dicarboxylate; MOF-5 or IRMOF-1) with Pd nanoparticles was investigated. First, the volatile organometallic precursor [Pd(5-C5H5)(3-C3H5)] was employed to get the inclusion compound [Pd(5-C5H5)(3-C3H5)]x@MOF-5 via gas-phase infiltration at 10-3 mbar. A loading of four molecules of [Pd(5-C5H5)(3-C3H5)] per formula unit of MOF-5 (x = 4) can be reached (35 wt.% Pd). Second, the metalorganic precursor [Pd(acac)2] (acac = 2,4-pentanedionate) was used and the inclusion materials [Pd(acac)2]x@MOF-5 of different Pd loadings were obtained by incipient wetness infiltration. However, the maximum loading was lower as compared with the former case with about two precursor molecules per formula unit of MOF-5. Both loading routes are suitable for the synthesis of Pd nanoparticles inside the porous host matrix. Homogeneously distributed nanoparticles with diameter of 2.4(±0.2) nm can be achieved by photolysis of the inclusion compounds [Pd(5-C5H5)(3-C3H5)]x@MOF-5 (x 4), while the hydrogenolysis of [Pd(acac)2]x@MOF-5 (x 2) leads to a mixture of small particles inside the network (< 3 nm) and large Pd agglomerates (40 nm) on the outer surface of the MOF-5 specimens. The pure Pdx@MOF-5 materials proved to be stable under hydrogen pressure (2 bar) at 150 °C over many hours. Neither hydrogenation of the bdc linkers nor particle growth was observed. The new composite materials were characterized by 1H/13C-MAS-NMR, powder XRD, ICP-AES, FT-IR, N2 sorption measurements and high resolution TEM. Raising the Pd loading of a representative sample Pd4@MOF-5 (35 wt.% Pd) by using [Pd(5-C5H5)(3-C3H5)] as precursor in a second cycle of gas-phase infiltration and photolysis was accompanied by the collapse of the long-range crystalline order of the MOF.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 100
DOI: 10.1039/b815977g
|
|
|
“Periodic microtwinning as a possible mechanism for the accommodation of the epitaxial film-substrate mismatch in the La1-xSrxMnO3/SrTiO3 system”. Lebedev OI, Van Tendeloo G, Amelinckx S, Razavi F, Habermeier H-U, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 81, 797 (2001)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Phase boundaries of superconducting mesoscopic square loops”. Fomin VM, Misko VR, Devreese JT, Moshchalkov VV, 249/251, 476 (1998)
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
|
|