“Focused ion beam/scanning electron microscopy tomography and conventional transmission electron microscopy assessment of Ni4Ti3 morphology in compression-aged Ni-rich Ni-Ti single crystals”. Cao S, Somsen C, Croitoru M, Schryvers D, Eggeler G, Scripta materialia 62, 399 (2010). http://doi.org/10.1016/j.scriptamat.2009.11.040
Abstract: The size, morphology and configuration of Ni4Ti3 precipitates in a single-crystal NiTi alloy have been investigated by two-dimensional transmission electron microscopy-based image analysis and three-dimensional reconstruction from slice-and-view images obtained in a focused ion beam/scanning electron microscopy (FIB/SEM) dual-beam system. Average distances between the precipitates measured along the compression direction correlate well between both techniques, while particle shape and configuration data is best obtained from FIB/SEM. Precipitates form pockets of B2 of 0.54 ìm in the compression direction and 1 ìm perpendicular to the compression direction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 3.747
Times cited: 16
DOI: 10.1016/j.scriptamat.2009.11.040
|
|
“On the relationship between the twin internal structure and the work-hardening rate of TWIP steels”. Idrissi H, Renard K, Schryvers D, Jacques PJ, Scripta materialia 63, 961 (2010). http://doi.org/10.1016/j.scriptamat.2010.07.016
Abstract: FeMnC and FeMnSiAl TWIP steels deformed under the same conditions exhibit different work-hardening rates. The present study investigates the microstructure of plastically deformed FeMnC and FeMnSiAl samples, particularly the internal structure of the mechanically generated twins and their topology at the grain scale. Twins in the FeMnC steel are finer and full of sessile dislocations, rendering this material distinctly stronger with an improved work-hardening rate.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 145
DOI: 10.1016/j.scriptamat.2010.07.016
|
|
“Is there a relationship between the stacking fault character and the activated mode of plasticity of FeMn-based austenitic steels?”.Idrissi H, Ryelandt L, Veron M, Schryvers D, Jacques PJ, Scripta materialia 60, 941 (2009). http://doi.org/10.1016/j.scriptamat.2009.01.040
Abstract: By changing the testing temperature, an austenitic FeMnAlSi alloy presents either å-martensite transformation or mechanical twinning during straining. In order to understand the nucleation and growth mechanisms involved in both phenomena, defects and particularly stacking faults, were characterized by transmission electron microscopy. It is observed that the character of the stacking faults also changes (from extrinsic to intrinsic) together with the temperature and the activated mode of plasticity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 84
DOI: 10.1016/j.scriptamat.2009.01.040
|
|
“Transmission electron microscopy investigation of microstructures in low-hysteresis alloys with special lattice parameters”. Delville R, Schryvers D, Zhang Z, James RD, Scripta materialia 60, 293 (2009). http://doi.org/10.1016/j.scriptamat.2008.10.025
Abstract: A sharp drop in hysteresis is observed for shape memory alloys satisfying the compatibility condition between austenite and martensite, i.e. ë2 = 1, where ë2 is the middle eigenvalue of the transformation strain matrix. The present work investigates the evolution of microstructure by transmission electron microscopy as the composition of the Ti50Ni50−xPdx system is systemically tuned to achieve the condition ë2 = 1. Changes in morphology, twinning density and twinning modes are reported along with twinless martensite and exact austenitemartensite interfaces.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 56
DOI: 10.1016/j.scriptamat.2008.10.025
|
|
“Microstructure and precipitates in as-cast Co38Ni33Al29 shape memory alloy”. Bartova B, Schryvers D, Yang Z, Ignacova S, Sittner P, Scripta materialia 57, 37 (2007). http://doi.org/10.1016/j.scriptamat.2007.03.007
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 22
DOI: 10.1016/j.scriptamat.2007.03.007
|
|
“Analytical TEM investigations on concentration gradients surrounding Ni4Ti3 precipitates in Ni-Ti shape memory material”. Yang Z, Tirry W, Schryvers D, Scripta materialia 52, 1129 (2005). http://doi.org/10.1016/j.scriptamat.2005.02.013
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 49
DOI: 10.1016/j.scriptamat.2005.02.013
|
|
“Effect of amorphous-crystalline interfaces on the martensitic transformation in Ti50Ni25Cu25”. Santamarta R, Schryvers D, Scripta materialia 50, 1423 (2004). http://doi.org/10.1016/j.scriptamat.2004.03.013
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 29
DOI: 10.1016/j.scriptamat.2004.03.013
|
|
“On the crystal structure of TiNi-Cu martensite”. Potapov P, Shelyakov A, Schryvers D, Scripta materialia 44, 1 (2001). http://doi.org/10.1016/S1359-6462(00)00555-8
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 36
DOI: 10.1016/S1359-6462(00)00555-8
|
|
“Unit cell determination in CuZr martensite by EM and X-ray diffraction”. Schryvers D, Firstov GS, Seo JW, van Humbeeck J, Koval YN, Scripta materialia 36, 1119 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 76
|
|
“Orientation relationship of the austenite-to-ferrite transformation in austenitic stainless steels due to dissolution corrosion in contact with liquid Pb-Bi eutectic”. Charalampopoulou E, Cautaerts N, Van der Donck T, Schryvers D, Lambrinou K, Delville R, Scripta materialia 167, 66 (2019). http://doi.org/10.1016/J.SCRIPTAMAT.2019.03.035
Abstract: The orientation relationship of an austenite-to-ferrite phase transformation in 316L stainless steels induced by the loss of austenite stabilizers resulting from the steel dissolution corrosion in liquid Pb-Bi eutectic was studied by means of electron backscatter diffraction. The misorientations at the austenite/ferrite interface were compared to the prevailing orientation relationship models in steels. The Pitsch orientation relationship model was found to be predominant, which is unusual for austenite-to-ferrite bulk transformations in steels. The nature of this particular transformation, which involves loss of steel alloying elements and the presence of an interfacial liquid metal layer, is discussed to explain this finding. (C) 2019 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 3
DOI: 10.1016/J.SCRIPTAMAT.2019.03.035
|
|
“Anomalous stress-strain behavior of NiTi shape memory alloy close to the border of superelastic window”. Wang X, Yao X, Schryvers D, Verlinden B, Wang G, Zhao G, Van Humbeeck J, Kustov S, Scripta Materialia 204, 114135 (2021). http://doi.org/10.1016/J.SCRIPTAMAT.2021.114135
Abstract: In this work, we report an anomalous phenomenon on superelastic cycling of NiTi shape memory alloys when deforming at the temperature close to the border of superelastic window. New unexpected effects are found-(i) critical stress for inducing martensite transformation during the second loading cycle is higher than that of the first cycle; ( ii ) the plateau stress of the second cycle decreases to the original level when the strain overcomes the limit of the first cycle; ( iii ) transition from good superelasticity in the first cycle to fully irreversible strain in the second. We propose that defects generated during the first superelastic cycle close to the border of superelastic window impede following stress-induced martensitic transformations, leading to the increase of critical stress beyond yield stress of the B2 matrix, and thus functional fatigue of NiTi alloys. (c) 2021 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
DOI: 10.1016/J.SCRIPTAMAT.2021.114135
|
|
“Effect of structural defects on the hydriding kinetics of nanocrystalline Pd thin films”. Delmelle R, Amin-Ahmadi B, Sinnaeve M, Idrissi H, Pardoen T, Schryvers D, Proost J, International journal of hydrogen energy 40, 7335 (2015). http://doi.org/10.1016/j.ijhydene.2015.04.017
Abstract: While the microstructure of a metal is well-known to affect its equilibrium hydrogen uptake and therefore the hydriding thermodynamics, microstructural effects on the hydriding kinetics are much less documented. Moreover, for thin film systems, such microstructural effects are difficult to separate from the internal stress effect, since most defects generate internal stresses. Such a decoupling has been achieved in this paper for nanocrystalline Pd thin film model systems through the use of a high-resolution, in-situ curvature measurement set-up during Pd deposition, annealing and hydriding. This set-up allowed producing Pd thin films with similar internal stress levels but significantly different microstructures. This was evidenced from detailed defect statistics obtained by transmission electron microscopy, which showed that the densities of grain boundaries, dislocations and twin boundaries have all been lowered by annealing. The same set-up was then used to study the hydriding equilibrium and kinetic behaviour of the resulting films at room temperature. A full quantitative analysis of their hydriding cycles showed that the rate constants of both the adsorption- and absorption-limited kinetic regimes were strongly affected by microstructure. Defect engineering was thereby shown to increase the rate constants for hydrogen adsorption and absorption in Pd by a factor 40 and 30, respectively. Copyright (C) 2015, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.582
Times cited: 13
DOI: 10.1016/j.ijhydene.2015.04.017
|
|
“Plasticity mechanisms in ultrafine grained freestanding aluminum thin films revealed by in-situ transmission electron microscopy nanomechanical testing”. Idrissi H, Kobler A, Amin-Ahmadi B, Coulombier M, Galceran M, Raskin J-P, Godet S, Kuebel C, Pardoen T, Schryvers D, Applied physics letters 104, 101903 (2014). http://doi.org/10.1063/1.4868124
Abstract: In-situ bright field transmission electron microscopy (TEM) nanomechanical tensile testing and in-situ automated crystallographic orientation mapping in TEM were combined to unravel the elementary mechanisms controlling the plasticity of ultrafine grained Aluminum freestanding thin films. The characterizations demonstrate that deformation proceeds with a transition from grain rotation to intragranular dislocation glide and starvation plasticity mechanism at about 1% deformation. The grain rotation is not affected by the character of the grain boundaries. No grain growth or twinning is detected. (C) 2014 AIP Publishing LLC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 24
DOI: 10.1063/1.4868124
|
|
“High resolution transmission electron microscopy characterization of fcc ->, 9R transformation in nanocrystalline palladium films due to hydriding”. Amin-Ahmadi B, Idrissi H, Delmelle R, Pardoen T, Proost J, Schryvers D, Applied physics letters 102, 071911 (2013). http://doi.org/10.1063/1.4793512
Abstract: Sputtered nanocrystalline palladium thin films with nanoscale growth twins have been subjected to hydriding cycles. The evolution of the twin boundaries has been investigated using high resolution transmission electron microscopy. Surprisingly, the Sigma 3{112} incoherent twin boundaries dissociate after hydriding into two phase boundaries bounding a 9R phase. This phase which corresponds to single stacking faults located every three {111} planes in the fcc Pd structure was not expected because of the high stacking fault energy of Pd. This observation is connected to the influence of the Hydrogen on the stacking fault energy of palladium and the high compressive stresses building up during hydriding. (C) 2013 American Institute of Physics. [http://dx.doi.org/10.1063/1.4793512]
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 14
DOI: 10.1063/1.4793512
|
|
“Quantitative Landau potentials for the martensitic transformation in Ni-Al”. Salje EKH, Zhang H, Schryvers D, Bartova B, Applied physics letters 90, 221903 (2007). http://doi.org/10.1063/1.2743927
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 9
DOI: 10.1063/1.2743927
|
|
“The colour of silver stained glass : analytical investigations carried out with XRF, SEM/EDX, TEM and IBA”. Jembrih-Simbürger D, Neelmeijer C, Schalm O, Fredrickx P, Schreiner M, De Vis K, Mäder M, Schryvers D, Caen J, Journal of analytical atomic spectrometry 17, 321 (2002). http://doi.org/10.1039/b111024c
Abstract: Glass treated on its surface with silver compounds and an aluminosilicate, such as ochre or clay, at higher temperatures (between 550 and 650 °C) accepts a wide variety of a yellow colour. It is the aim of this study to investigate the parameters of the manufacturing process affecting the final colour of silver stained glass and to correlate them with the final colour and colour intensity. Therefore, defined mixtures of ochre and a silver compound (AgCl, AgNO3, Ag2SO4, Ag3PO4, Ag2O) were prepared and applied on soda-lime glass. The firing process was modified within the range from 563 to 630 °C and glass samples were analysed after treatment with energy dispersive X-ray fluorescence analysis (EDXRF), scanning electron microscopy (SEM/EDX), transmission electron microscopy (TEM), as well as ion beam analysis (IBA) with an external beam. Within the scope of IBA simultaneous measurements using particle-induced X-ray emission (PIXE), particle-induced gamma-ray emission (PIGE), and Rutherford backscattering spectrometry (RBS) were carried out in order to obtain the thickness of the Ag-rich surface layer and the depth distribution of Ag. By means of TEM the microstructure of the silver particles was visualised. XRF results show that the lowest amount of Ag could be detected on glass samples treated with silver stain mixtures containing AgCl and Ag2O. A low kiln temperature (e.g. 563 °C) results in a higher silver concentration at the surface and lower penetration depths. Furthermore, the results obtained with SEM/EDX at cross-sections of the glass samples could be confirmed by PIXE, PIGE, RBS, and TEM.
Keywords: A1 Journal article; Art; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.379
Times cited: 42
DOI: 10.1039/b111024c
|
|
“Enamels in stained glass windows: preparation, chemical composition, microstructure and causes of deterioration”. Schalm O, van der Linden V, Frederickx P, Luyten S, van der Snickt G, Caen J, Schryvers D, Janssens K, Cornelis E, van Dyck D, Schreiner M, Spectrochimica acta: part B : atomic spectroscopy 64, 812 (2009). http://doi.org/10.1016/j.sab.2009.06.005
Abstract: Stained glass windows incorporating dark blue and purple enamel paint layers are in some cases subject to severe degradation while others from the same period survived the ravages of time. A series of dark blue, greenblue and purple enamel glass paints from the same region (Northwestern Europe) and from the same period (16early 20th centuries) has been studied by means of a combination of microscopic X-ray fluorescence analysis, electron probe micro analysis and transmission electron microscopy with the aim of better understanding the causes of the degradation. The chemical composition of the enamels diverges from the average chemical composition of window glass. Some of the compositions appear to be unstable, for example those with a high concentration of K2O and a low content of CaO and PbO. In other cases, the deterioration of the paint layers was caused by the less than optimal vitrification of the enamel during the firing process. Recipes and chemical compositions indicate that glassmakers of the 1617th century had full control over the color of the enamel glass paints they made. They mainly used three types of coloring agents, based on Co (dark blue), Mn (purple) and Cu (light-blue or greenblue) as coloring elements. Bluepurple enamel paints were obtained by mixing two different coloring agents. The coloring agent for redpurple enamel, introduced during the 19th century, was colloidal gold embedded in grains of lead glass.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Vision lab
Impact Factor: 3.241
Times cited: 28
DOI: 10.1016/j.sab.2009.06.005
|
|
“Cavity nucleation and growth in Cu-Zn-Al irradiated with Cu+ ions at different temperatures”. Zelaya E, Schryvers D, Tolley A, Fitchner PFP, Intermetallics 18, 493 (2010). http://doi.org/10.1016/j.intermet.2009.09.010
Abstract: The effects of high dose ion irradiation in β CuZnAl were investigated between room temperature and 150 °C. Single crystal samples with surface normal close to [001]β were irradiated with 300 keV Cu+ ions. Microstructural changes were characterized using transmission electron microscopy. Irradiation induced cavities located on the surface exposed to the irradiation were observed. The morphology, size and density distribution of these cavities were analyzed as a function of different irradiation conditions. The shape and location of the cavities with respect to the irradiation surface were not affected by irradiation temperature or irradiation dose. Instead, the cavity size distribution showed a bi-modal shape for a dose of 15 dpa, regardless of irradiation temperature. For a dose of 30 dpa the bi-modal distribution was only observed after room temperature irradiation. The diffusion effects of vacancies produced by irradiation are analyzed in shape memory CuZnAl alloys, which main characteristic is the diffusionless martensitic transformation. Particularly, the cavity size distributions were analyzed in terms of nucleation, growth and coalescence.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 1
DOI: 10.1016/j.intermet.2009.09.010
|
|
“Transmission electron microscopy study of combined precipitation of Ti2Ni(Pd) and Ti2Pd(Ni) in a Ti50Ni30Pd20 alloy”. Delville R, Schryvers D, Intermetallics 18, 2353 (2010). http://doi.org/10.1016/j.intermet.2010.08.006
Abstract: We report a new mode of precipitation in a B19 martensitic Ti50Ni30Pd20 shape memory alloy consisting of a central Ti2Ni(Pd) precipitate surrounded by an austenite area containing Ti2Pd(Ni) precipitates. The morphology and crystallography of the precipitation area is investigated using conventional and high resolution electron microscopy. In particular, the orientation relationship and the coherency strain between the Ti2Pd(Ni) precipitate and the surrounding retained B2 matrix are discussed. A study of local composition in relation with a ternary phase diagram using X-ray energy dispersive spectroscopy with a nanoprobe gives evidences of the formation mechanism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 9
DOI: 10.1016/j.intermet.2010.08.006
|
|
“Grain growth and precipitation in an annealed cold-rolled Ni50.2Ti49.8 alloy”. Srivastava AK, Schryvers D, van Humbeeck J, Intermetallics 15, 1538 (2007). http://doi.org/10.1016/j.intermet.2007.06.003
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 37
DOI: 10.1016/j.intermet.2007.06.003
|
|
“Twinned b.c.c. sherical particles in a partially crystallised Ti50Ni25Cu25 melt-spun ribbon”. Santamarta R, Schryvers D, Intermetallics 12, 341 (2004). http://doi.org/10.1016/j.intermet.2003.12.002
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 14
DOI: 10.1016/j.intermet.2003.12.002
|
|
“Phase transformations and precipitation in amorphous Ti50Ni25Cu25 ribbons”. Satto C, Ledda A, Potapov P, Janssens JF, Schryvers D, Intermetallics 9, 395 (2001). http://doi.org/10.1016/S0966-9795(01)00015-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 16
DOI: 10.1016/S0966-9795(01)00015-2
|
|
“Austenite and martensite microstructures in splat-cooled Ni-Al”. Schryvers D, Holland-Moritz D, Intermetallics 6, 427 (1998). http://doi.org/10.1016/S0966-9795(97)00091-5
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 13
DOI: 10.1016/S0966-9795(97)00091-5
|
|
“Recrystallization and grain growth in a B2 iron aluminide alloy”. Samajdar I, Ratchev P, Verlinden B, Schryvers D, Intermetallics 6, 419 (1998). http://doi.org/10.1016/S0966-9795(97)00092-7
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 17
DOI: 10.1016/S0966-9795(97)00092-7
|
|
“Determination of the atomic width of an APB in ordered CoPt using quantified HAADF-STEM”. Akamine H, Van den Bos KHW, Gauquelin N, Farjami S, Van Aert S, Schryvers D, Nishida M, Journal of alloys and compounds 644, 570 (2015). http://doi.org/10.1016/j.jallcom.2015.04.205
Abstract: Anti-phase boundaries (APBs) in an ordered CoPt alloy are planar defects which disturb the ordered structure in their vicinity and decrease the magnetic properties. However, it has not yet been clarified to what extend the APBs disturb the ordering. In this study, high-resolution HAADF-STEM images are statistically analysed based on the image intensities estimated by the statistical parameter estimation theory. In the procedure, averaging intensities, fitting the intensity profiles to specific functions, and assessment based on a statistical test are performed. As a result, the APBs in the stable CoPt are found to be characterised by two atomic planes, and a contrast transition range as well as the centre of an inclined APB is determined. These results show that the APBs are quite sharp and therefore may have no notable effect on the net magnetic properties due to their small volume fraction. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 12
DOI: 10.1016/j.jallcom.2015.04.205
|
|
“Microstructural dependence on middle eigenvalue in Ti-Ni-Au”. Shi H, Delville R, Srivastava V, James RD, Schryvers D, Journal of alloys and compounds 582, 703 (2013). http://doi.org/10.1016/j.jallcom.2013.08.132
Abstract: The microstructure of various compounds of the Ti-Ni-Au alloy system is investigated by transmission electron microscopy in relation with changing lattice parameters improving the compatibility conditions between austenite and martensite expressed by the lambda(2) = 1 equation based on the Geometrically NonLinear Theory of Martensite (GNLTM). Although local differences in microstructure are observed, when increasing the gold content compound twins are replaced by Type I twins, while twinned lamellar structures are replaced by untwinned plates and self-accommodating structures when lambda(2) = 1 is approached, all confirming the predictions of the GNLTM. (c) 2013 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 8
DOI: 10.1016/j.jallcom.2013.08.132
|
|
“Microstructure and precipitates in annealed Co38Ni33Al29 ferromagnetic shape memory alloy”. Lu JB, Shi H, Sedlakova-Ignacova S, Espinoza R, Kopeček J, Sittner P, Bártová, B, Schryvers D, Journal of alloys and compounds 572, 5 (2013). http://doi.org/10.1016/j.jallcom.2013.03.228
Abstract: Transmission electron microscopy was performed to investigate the microstructure and precipitates in the annealed Co38Ni33Al29 ferromagnetic shape memory alloy. Apart from the dendritic secondary phase in the austenite matrix, micron-sized (up to 100 μm) fcc-based precipitates with partial γ′ L12 ordering and containing none, one or three {1 1 1}p parallel twin planes were found. The orientation relationship between the precipitates and matrix was found to be KurdjumovSachs. STEMEDX analysis indicates that twinned and non-twinned precipitates are Co-rich and Al- and Ni-deficient with respect to the matrix and with a lower Co/Al ratio for the latter. The 3D morphologies of precipitates were reconstructed with focused ion beam/scanning electron microscope dual-beam slice-and-view imaging, showing that the single {1 1 1}p plane twinned precipitates have a plate-like shape while the non-twinned precipitates are lath-like and often bent.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 10
DOI: 10.1016/j.jallcom.2013.03.228
|
|
“Morphological characterization and distribution of autocatalytic-grown Ni4Ti3 precipitates in a Ni-Ti single crystal”. Cao S, Ke CB, Zhang XP, Schryvers D, Journal of alloys and compounds 577, 215 (2013). http://doi.org/10.1016/j.jallcom.2012.02.013
Abstract: The 3D size, morphology and distribution of autocatalytic-grown Ni4Ti3 precipitates in a Ni51Ti49 single crystal were characterized via a FIB/SEM Slice-and-View procedure and phase-field simulation. Important parameters on size and shape of the precipitates were measured. The pair distribution function and the minimum distance between two precipitates from different variants were calculated to describe the 3D distribution of the autocatalytic-grown Ni4Ti3 precipitates in single crystal Ni-Ti, with a comparison to the polycrystalline Ni50.8Ti49.2 alloy. Phase-field simulation was conducted to study the nucleation behavior of precipitates in the single crystal Ni-Ti. (C) 2012 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 5
DOI: 10.1016/j.jallcom.2012.02.013
|
|
“Recent EM investigations on nano-and micro-defect structures in SMAs”. Schryvers D, Cao S, Pourbabak, Shi H, Lu, Journal of alloys and compounds 577, S705 (2013). http://doi.org/10.1016/j.jallcom.2011.10.112
Abstract: The present contribution reviews some recent electron microscopy investigations on different shape memory systems in which a variety of nano- and micro-defect structures play an essential role in the functional behaviour of the material. (NiTi3)-Ti-4 precipitates in Ni-Ti are a well-known example for which the focus is now on the 3D configurations, in Ni-Ti-Nb Nb-rich nanoprecipitates are thought to have a large impact on the hysteresis, in Co-Ni-Al an Al-enriched zone nearby the y'-precipitates yields a small sandwiched austenite while some first signs of quasidynamical lattice deformation in non-frozen Ni-Ti strain glass are measured by Cs-aberration-corrected transmission electron microscopy. (C) 2011 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 7
DOI: 10.1016/j.jallcom.2011.10.112
|
|
“Unexpected ordering behaviour of Pt3Al intermetallic precipitates”. Douglas A, Neethling JH, Santamarta R, Schryvers D, Cornish LA, Journal of alloys and compounds 432, 96 (2007). http://doi.org/10.1016/j.jallcom.2006.05.106
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 18
DOI: 10.1016/j.jallcom.2006.05.106
|