“Laser-induced periodic annular surface structures on fused silica surface”. Liu Y, Brelet Y, He Z, Yu L, Forestier B, Deng Y, Jiang H, Houard A, Applied physics letters 102, 251103 (2013). http://doi.org/10.1063/1.4812354
Abstract: We report on the formation of laser-induced periodic annular surface structures on fused silica irradiated with multiple femtosecond laser pulses. This surface morphology emerges after the disappearance of the conventional laser induced periodic surface structures, under successive laser pulse irradiation. It is independent of the laser polarization and universally observed for different focusing geometries. We interpret its formation in terms of the interference between the reflected laser field on the surface of the damage crater and the incident laser pulse. (C) 2013 AIP Publishing LLC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 19
DOI: 10.1063/1.4812354
|
|
“Local bond length variations in boron-doped nanocrystalline diamond measured by spatially resolved electron energy-loss spectroscopy”. Lu Y-G, Turner S, Verbeeck J, Janssens SD, Haenen K, Van Tendeloo G, Applied physics letters 103, 032105 (2013). http://doi.org/10.1063/1.4813842
Abstract: Variations in local bond length and coordination in boron-doped nanocrystalline diamond (NCD) films have been studied through changes in the fine structure of boron and carbon K-edges in electron energy-loss spectra, acquired in a scanning transmission electron microscope. The presence of high concentrations of B in pristine diamond regions and enrichment of B at defects in single NCD grains is demonstrated. Local bond length variations are evidenced through an energy shift of the carbon 1s → σ* edge at B-rich defective regions within single diamond grains, indicating an expansion of the diamond bond length at sites with local high B content.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 15
DOI: 10.1063/1.4813842
|
|
“Microstructure of bilayer manganite PrCa2Mn2O7 showing charge/orbital ordering”. He Z, Tian H, Deng G, Xu Q, Van Tendeloo G, Applied physics letters 102, 212902 (2013). http://doi.org/10.1063/1.4807758
Abstract: The microstructure of the charge/orbital ordering Ruddleden-Popper phase PrCa2Mn2O7 was studied by transmission electron microscopy along both the [001] and the [110] orientation. Three coexisting charge/orbital ordering phases CO1, CO2, and CO3 were observed along the [001] orientation at room temperature. Different from the one-dimensional modulation in the CO1 and CO2 phase, the CO3 phase is characterized by two sets of mutually perpendicular structural modulations. From [110] high angle annular dark field-scanning transmission electron microscopy, we found that the Pr atoms locate in-between the bilayer MnO6 octahedra, which is different from the previous reports.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 4
DOI: 10.1063/1.4807758
|
|
“Towards rapid nanoscale measurement of strain in III-nitride heterostructures”. Jones E, Cooper D, Rouvière J-L, Béché, A, Azize M, Palacios T, Gradecak S, Applied Physics Letters 103, 231904 (2013). http://doi.org/10.1063/1.4838617
Abstract: We report the structural and compositional nanoscale characterization of InAlN/GaN nanoribbon-structured high electron mobility transistors (HEMTs) through the use of geometric phase analysis (GPA) and nanobeam electron diffraction (NBED). The strain distribution in the HEMT layer is quantified and compared to the expected strain profile for the nominal structure predicted by finite element analysis (FEA). Using the experimental strain results, the actual structure is determined and used to modify the FEA model. The improved fit of the model demonstrates that GPA and NBED provide a powerful platform for routine and rapid characterization of strain in III-V semiconducting device systems leading to insights into device evolution during processing and future device optimization.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 6
DOI: 10.1063/1.4838617
|
|
“Improved strain precision with high spatial resolution using nanobeam precession electron diffraction”. Rouvière J-L, Béché, A, Martin Y, Denneulin T, Cooper D, Applied physics letters 103, 241913 (2013). http://doi.org/10.1063/1.4829154
Abstract: NanoBeam Electron Diffraction is a simple and efficient technique to measure strain in nanostructures. Here, we show that improved results can be obtained by precessing the electron beam while maintaining a few nanometer probe size, i.e., by doing Nanobeam Precession Electron Diffraction (N-PED). The precession of the beam makes the diffraction spots more uniform and numerous, making N-PED more robust and precise. In N-PED, smaller probe size and better precision are achieved by having diffraction disks instead of diffraction dots. Precision in the strain measurement better than 2 × 10−4 is obtained with a probe size approaching 1 nm in diameter.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 53
DOI: 10.1063/1.4829154
|
|
“3Y-TZP ceramics with improved hydrothermal degradation resistance and fracture toughness”. Zhang F, Vanmeensel K, Inokoshi M, Batuk M, Hadermann J, Van Meerbeek B, Naert I, Vleugels J, Journal of the European Ceramic Society 34, 2453 (2014). http://doi.org/10.1016/j.jeurceramsoc.2014.02.026
Abstract: Different factors such as the way of incorporating the Y2O3 stabilizer, alumina addition and sintering temperature were assessed with the goal to improve the low temperature degradation (LTD) resistance of 3Y-TZP without compromising on the mechanical properties. The degradation of hydrothermally treated specimens was studied by X-ray diffraction, micro-Raman spectroscopy and scanning electron microscopy. Decreasing the sintering temperature decreased the LTD susceptibility of 3Y-TZPs but did not allow to obtain a LTD resistant 3Y-TZP with optimized mechanical properties. Alumina addition along with the use of Y2O3 stabilizer coated starting powder allowed to combine both an excellent toughness and LTD resistance, as compared to alumina-free and stabilizer co-precipitated powder based equivalents. Transmission electron microscopy revealed that the improved LTD resistance could be attributed to the segregation of Al3+ at the grain boundary and the heterogeneously distributed Y3+ stabilizer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 48
DOI: 10.1016/j.jeurceramsoc.2014.02.026
|
|
“Atomic layer epitaxy of Ruddlesden-Popper SrO(SrTiO3)n films by means of metalorganic aerosol deposition”. Jungbauer M, Huehn S, Egoavil R, Tan H, Verbeeck J, Van Tendeloo G, Moshnyaga V, Applied physics letters 105, 251603 (2014). http://doi.org/10.1063/1.4905055
Abstract: We report an atomic layer epitaxial growth of Ruddlesden-Popper (RP) thin films of SrO(SrTiO3)(n) (n = infinity, 2, 3, 4) by means of metalorganic aerosol deposition (MAD). The films are grown on SrTiO3(001) substrates by means of a sequential deposition of Sr-O/Ti-O-2 atomic monolayers, monitored in-situ by optical ellipsometry. X-ray diffraction and transmission electron microscopy (TEM) reveal the RP structure with n = 2-4 in accordance with the growth recipe. RP defects, observed by TEM in a good correlation with the in-situ ellipsometry, mainly result from the excess of SrO. Being maximal at the film/substrate interface, the SrO excess rapidly decreases and saturates after 5-6 repetitions of the SrO(SrTiO3)(4) block at the level of 2.4%. This identifies the SrTiO3 substrate surface as a source of RP defects under oxidizing conditions within MAD. Advantages and limitations of MAD as a solution-based and vacuum-free chemical deposition route were discussed in comparison with molecular beam epitaxy. (C) 2014 AIP Publishing LLC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 32
DOI: 10.1063/1.4905055
|
|
“Microstructural analysis of 9.7% efficient Cu2ZnSnSe4 thin film solar cells”. Buffière M, Brammertz G, Batuk M, Verbist C, Mangin D, Koble C, Hadermann J, Meuris M, Poortmans J, Applied physics letters 105, 183903 (2014). http://doi.org/10.1063/1.4901401
Abstract: This work presents a detailed analysis of the microstructure and the composition of our record Cu 2ZnSnSe4 (CZTSe)-CdS-ZnO solar cell with a total area efficiency of 9.7%. The average composition of the CZTSe crystallites is Cu 1.94 Zn 1.12Sn0.95Se3.99. Large crystals of ZnSe secondary phase (up to 400 nm diameter) are observed at the voids between the absorber and the back contact, while smaller ZnSe domains are segregated at the grain boundaries and close to the surface of the CZTSe grains. An underlying layer and some particles of Cu xSe are observed at the Mo-MoSe2-Cu2ZnSnSe4 interface. The free surface of the voids at the back interface is covered by an amorphous layer containing Cu, S, O, and C, while the presence of Cd, Na, and K is also observed in this region.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 17
DOI: 10.1063/1.4901401
|
|
“Optimal experimental design for the detection of light atoms from high-resolution scanning transmission electron microscopy images”. Gonnissen J, de Backer A, den Dekker AJ, Martinez GT, Rosenauer A, Sijbers J, Van Aert S, Applied physics letters 105, 063116 (2014). http://doi.org/10.1063/1.4892884
Abstract: We report an innovative method to explore the optimal experimental settings to detect light atoms from scanning transmission electron microscopy (STEM) images. Since light elements play a key role in many technologically important materials, such as lithium-battery devices or hydrogen storage applications, much effort has been made to optimize the STEM technique in order to detect light elements. Therefore, classical performance criteria, such as contrast or signal-to-noise ratio, are often discussed hereby aiming at improvements of the direct visual interpretability. However, when images are interpreted quantitatively, one needs an alternative criterion, which we derive based on statistical detection theory. Using realistic simulations of technologically important materials, we demonstrate the benefits of the proposed method and compare the results with existing approaches.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 3.411
Times cited: 12
DOI: 10.1063/1.4892884
|
|
“Plasticity mechanisms in ultrafine grained freestanding aluminum thin films revealed by in-situ transmission electron microscopy nanomechanical testing”. Idrissi H, Kobler A, Amin-Ahmadi B, Coulombier M, Galceran M, Raskin J-P, Godet S, Kuebel C, Pardoen T, Schryvers D, Applied physics letters 104, 101903 (2014). http://doi.org/10.1063/1.4868124
Abstract: In-situ bright field transmission electron microscopy (TEM) nanomechanical tensile testing and in-situ automated crystallographic orientation mapping in TEM were combined to unravel the elementary mechanisms controlling the plasticity of ultrafine grained Aluminum freestanding thin films. The characterizations demonstrate that deformation proceeds with a transition from grain rotation to intragranular dislocation glide and starvation plasticity mechanism at about 1% deformation. The grain rotation is not affected by the character of the grain boundaries. No grain growth or twinning is detected. (C) 2014 AIP Publishing LLC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 24
DOI: 10.1063/1.4868124
|
|
“Critical influence of alumina content on the low temperature degradation of 2-3 mol% yttria-stabilized TZP for dental restorations”. Zhang F, Vanmeensel K, Inokoshi M, Batuk M, Hadermann J, Van Meerbeek B, Naert I, Vleugels J, Journal of the European Ceramic Society 35, 741 (2015). http://doi.org/10.1016/j.jeurceramsoc.2014.09.018
Abstract: The influence of 0.25, 2 and 5 wt.% alumina addition on the mechanical properties and low temperature degradation (LTD) of 3, 2.5 and 2 mol% yttria-stabilized TZP ceramics was investigated. The amount of alumina addition was observed to have a crucial impact on the degradation of Y-TZP ceramics. Independent on the yttria stabilizer content, 0.25 wt.% alumina had a higher degradation retarding effect to Y-TZP ceramics than 2 and 5 wt.% of alumina addition, which had a comparable effect. The apparent activation energy for the degradation process was increased by adding alumina, but it was the same for 0.255 wt.% alumina doped 3Y-TZP ceramics. For Y-TZPs containing a small amount of alumina addition, only the segregated Al3+ at the grain boundaries of the zirconia grains was effective to retard the degradation of Y-TZPs. The secondary phase Al2O3 grains increased the degradation kinetics, which might be attributed to the residual stresses.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 37
DOI: 10.1016/j.jeurceramsoc.2014.09.018
|
|
“Influence of defect distribution on the reducibility of CeO2-x nanoparticles”. Spadaro MC, Luches P, Bertoni G, Grillo V, Turner S, Van Tendeloo G, Valeri S, D'Addato S, Nanotechnology 27, 425705 (2016). http://doi.org/10.1088/0957-4484/27/42/425705
Abstract: Ceria nanoparticles (NPs) are fundamental in heterogeneous catalysis because of their ability to store or release oxygen depending on the ambient conditions. Their oxygen storage capacity is strictly related to the exposed planes, crystallinity, density and distribution of defects. In this work a study of ceria NPs produced with a ligand-free, physical synthesis method is presented. The NP films were grown by a magnetron sputtering based gas aggregation source and studied by high resolution- and scanning-transmission electron microscopy and x-ray photoelectron spectroscopy. In particular, the influence of the oxidation procedure on the NP reducibility has been investigated. The different reducibility has been correlated to the exposed planes, crystallinity and density and distribution of structural defects. The results obtained in this work represent a basis to obtain cerium oxide NP with desired oxygen transport properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 11
DOI: 10.1088/0957-4484/27/42/425705
|
|
“Achieving independent control of core diameter and carbon shell thickness in Pd-C core–shell nanoparticles by gas phase synthesis”. Singh V, Mehta BR, Sengar SK, Karakulina OM, Hadermann J, Kaushal A, Nanotechnology 28, 295603 (2017). http://doi.org/10.1088/1361-6528/aa7660
Abstract: Pd-C core–shell nanoparticles with independently controllable core size and shell thickness are grown by gas phase synthesis. First, the core size is selected by electrical mobility values of charged particles, and second, the shell thickness is controlled by the concentration of carbon precursor gas. The carbon shell grows by adsorption of carbon precursor gas molecules on the surface of nanoparticles, followed by sintering. The presence of a carbon shell on Pd nanoparticles is potentially important in hydrogen-related applications operating at high temperatures or in catalytic reactions in acidic/aqueous environments.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 1
DOI: 10.1088/1361-6528/aa7660
|
|
“Preparation and structure analysis of Gd(OH)3 nanorods”. Du G, Van Tendeloo G, Nanotechnology 16, 595 (2005). http://doi.org/10.1088/0957-4484/16/4/043
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 28
DOI: 10.1088/0957-4484/16/4/043
|
|
“Controllable synthesis of novel one-dimensional carbon nanomaterials on an alkali-element-modified Cu catalyst”. Tao XY, Zhang XB, Cheng J-P, Liu F, Li Y, Van Tendeloo G, Nanotechnology 17, 224 (2006). http://doi.org/10.1088/0957-4484/17/1/037
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 4
DOI: 10.1088/0957-4484/17/1/037
|
|
“Structural characterization and luminescence properties of nanostructured lanthanide-doped Sc2O3 prepared by propellant synthesis”. Krsmanovic R, Lebedev OI, Speghini A, Bettinelli M, Polizzi S, Van Tendeloo G, Nanotechnology 17, 2805 (2006). http://doi.org/10.1088/0957-4484/17/11/013
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 22
DOI: 10.1088/0957-4484/17/11/013
|
|
“CdSe quantum dot formation: alternative paths to relaxation of a strained CdSe layer and influence of the capping conditions”. Robin I-C, Aichele T, Bougerol C, André, R, Tatarenko S, Bellet-Amalric E, van Daele B, Van Tendeloo G, Nanotechnology 18, 265701 (2007). http://doi.org/10.1088/0957-4484/18/26/265701
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 8
DOI: 10.1088/0957-4484/18/26/265701
|
|
“Structural and luminescence investigation on gadolinium gallium garnet nanocrystalline powders prepared by solution combustion synthesis”. Krsmanovic R, Morozov VA, Lebedev OI, Polizzi S, Speghini A, Bettinelli M, Van Tendeloo G, Nanotechnology 18, 325604 (2007). http://doi.org/10.1088/0957-4484/18/32/325604
Abstract: Nanocrystalline powders of undoped and lanthanide (Pr3+, Tm3+)- doped gadolinium gallium garnet, Gd3Ga5O12 (GGG), were prepared by propellant synthesis and studied by x-ray powder diffraction (XRD), electron diffraction (ED), high-resolution electron microscopy (HREM) and luminescence spectroscopy. The x-ray diffraction patterns of the GGG samples were analysed using the Rietveld method. The Rietveld refinement reveals the existence of two garnet-type phases: both are cubic (space group Ia $(3) over bar $d) with a slightly different lattice parameter and probably a slightly different composition. Electron diffraction and electron microscopy measurements confirm the x-ray diffraction results. EDX measurements for lanthanide-doped samples show that stable solid solutions with composition Gd(3-x)Ln(x)Ga(5)O(12), x approximate to 0.3 ( Ln = Pr; Tm) have been obtained. The luminescence properties of the Tm3+ -doped nanocrystalline GGG samples were measured and analysed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 33
DOI: 10.1088/0957-4484/18/32/325604
|
|
“Carbon nanotube TiO2 hybrid films for detecting traces of O2”. Llobet E, Espinosa EH, Sotter E, Ionescu R, Vilanova X, Torres J, Felten A, Pireaux JJ, Ke X, Van Tendeloo G, Renaux F, Paint Y, Hecq M, Bittencourt C;, Nanotechnology 19, 375501 (2008). http://doi.org/10.1088/0957-4484/19/37/375501
Abstract: Hybrid titania films have been prepared using an adapted sol-gel method for obtaining well-dispersed hydrogen plasma-treated multiwall carbon nanotubes in either pure titania or Nb-doped titania. The drop-coating method has been used to fabricate resistive oxygen sensors based on titania or on titania and carbon nanotube hybrids. Morphology and composition studies have revealed that the dispersion of low amounts of carbon nanotubes within the titania matrix does not significantly alter its crystallization behaviour. The gas sensitivity studies performed on the different samples have shown that the hybrid layers based on titania and carbon nanotubes possess an unprecedented responsiveness towards oxygen (i.e. more than four times higher than that shown by optimized Nb-doped TiO(2) films). Furthermore, hybrid sensors containing carbon nanotubes respond at significantly lower operating temperatures than their non-hybrid counterparts. These new hybrid sensors show a strong potential for monitoring traces of oxygen (i.e. <= 10 ppm) in a flow of CO(2), which is of interest for the beverage industry.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 48
DOI: 10.1088/0957-4484/19/37/375501
|
|
“Surface enhanced Raman scattering of silver sensitized cobalt nanoparticles in metaldielectric nanocomposites”. Margueritat J, Gonzalo J, Afonso CN, Hörmann U, Van Tendeloo G, Mlayah A, Murray DB, Saviot L, Zhou Y, Hong MH, Luk'yanchuk BS, Nanotechnology 19, 375701 (2008). http://doi.org/10.1088/0957-4484/19/37/375701
Abstract: We report the preparation of a new type of nanocomposite containing cobalt and silver nanoparticles organized in parallel layers with a well controlled separation. This arrangement allows the observation of an enhanced low-frequency Raman signal at the vibration frequency of cobalt nanoparticles excited through the surface plasmons of silver nanoparticles. Numerical simulations of the electric field confirm the emergence of hot spots when the separation between silver and cobalt nanoparticles is small enough.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 11
DOI: 10.1088/0957-4484/19/37/375701
|
|
“Synthesis of few-layer graphene via microwave plasma-enhanced chemical vapour deposition”. Malesevic A, Vitchev R, Schouteden K, Volodin A, Zhang L, Van Tendeloo G, Vanhulsel A, van Haesendonck C, Nanotechnology 19, 305604 (2008). http://doi.org/10.1088/0957-4484/19/30/305604
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 309
DOI: 10.1088/0957-4484/19/30/305604
|
|
“Structure and defect characterization of multiferroic <tex>ReMnO$3 films and multilayers by TEM”. Jehanathan N, Lebedev O, Gélard I, Dubourdieu C, Van Tendeloo G, Nanotechnology 21, 075705 (2010). http://doi.org/10.1088/0957-4484/21/7/075705
Abstract: Epitaxial rare earth manganite thin films (ReMnO3; Re = Tb, Ho, Er, and Y) and multilayers were grown by liquid injection metal organic chemical vapor deposition (MOCVD) on YSZ(111) and the same systems were grown c-oriented on Pt(111) buffered Si substrates. They have been structurally investigated by electron diffraction (ED) and high resolution transmission electron microscopy (HRTEM). Nanodomains of secondary orientation are observed in the hexagonal YMnO3 films. They are related to a YSZ(111) and Pt(111) misorientation. The epitaxial film thickness has an influence on the defect formation. TbO2 and Er2O3 inclusions are observed in the TbMnO3 and ErMnO3 films respectively. The structure and orientation of these inclusions are correlated to the resembling symmetry and structure of film and substrate. The type of defect formed in the YMnO3/HoMnO3 and YMnO3/ErMnO3 multilayers is also influenced by the type of substrate they are grown on. In our work, atomic growth models for the interface between the film/substrate are proposed and verified by comparison with observed and computer simulated images.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 15
DOI: 10.1088/0957-4484/21/7/075705
|
|
“Defect controlled room temperature ferromagnetism in Co-doped barium titanate nanocrystals”. Ray S, Kolen'ko YV, Kovnir KA, Lebedev OI, Turner S, Chakraborty T, Erni R, Watanabe T, Van Tendeloo G, Yoshimura M, Itoh M, Nanotechnology 23, 025702 (2012). http://doi.org/10.1088/0957-4484/23/2/025702
Abstract: Defect mediated high temperature ferromagnetism in oxide nanocrystallites is the central feature of this work. Here, we report the development of room temperature ferromagnetism in nanosized Co-doped barium titanate particles with a size of around 14 nm, synthesized by a solvothermal drying method. A combination of x-ray diffraction with state-of-the-art electron microscopy techniques confirms the intrinsic doping of Co into BaTiO3. The development of the room temperature ferromagnetism was tracked down to the different donor defects, namely hydroxyl groups at the oxygen site (\mathrm {OH}\mathrm {(O)}
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 19
DOI: 10.1088/0957-4484/23/2/025702
|
|
“Electrical tomography using atomic force microscopy and its application towards carbon nanotube-based interconnects”. Schulze A, Hantschel T, Dathe A, Eyben P, Ke X, Vandervorst W, Nanotechnology 23, 305707 (2012). http://doi.org/10.1088/0957-4484/23/30/305707
Abstract: The fabrication and integration of low-resistance carbon nanotubes (CNTs) for interconnects in future integrated circuits requires characterization techniques providing structural and electrical information at the nanometer scale. In this paper we present a slice-and-view approach based on electrical atomic force microscopy. Material removal achieved by successive scanning using doped ultra-sharp full-diamond probes, manufactured in-house, enables us to acquire two-dimensional (2D) resistance maps originating from different depths (equivalently different CNT lengths) on CNT-based interconnects. Stacking and interpolating these 2D resistance maps results in a three-dimensional (3D) representation (tomogram). This allows insight from a structural (e.g. size, density, distribution, straightness) and electrical point of view simultaneously. By extracting the resistance evolution over the length of an individual CNT we derive quantitative information about the resistivity and the contact resistance between the CNT and bottom electrode.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 29
DOI: 10.1088/0957-4484/23/30/305707
|
|
“Monodisperse spherical mesoporous silica particles : fast synthesis procedure and fabrication of photonic-crystal films”. Trofimova EY, Kurdyukov DA, Yakovlev SA, Kirilenko DA, Kukushkina YA, Nashchekin AV, Sitnikova AA, Yagovkina MA, Golubev VG, Nanotechnology 24, 155601 (2013). http://doi.org/10.1088/0957-4484/24/15/155601
Abstract: A procedure for the synthesis of monodisperse spherical mesoporous silica particles (MSMSPs) via the controlled coagulation of silica/surfactant clusters into spherical aggregates with mean diameters of 250-1500 nm has been developed. The synthesis is fast (taking less than 1 h) because identical clusters are simultaneously formed in the reaction mixture. The results of microscopic, x-ray diffraction, adsorption and optical measurements allowed us to conclude that the clusters are similar to 15 nm in size and have hexagonally packed cylindrical pore channels. The channel diameters in MSMSPs obtained with cethyltrimethylammonium bromide and decyltrimethylammonium bromide as structure-directing agents were 3.1 +/- 0.15 and 2.3 +/- 0.12 nm, respectively. The specific surface area and the pore volume of MSMSP were, depending on synthesis conditions, 480-1095 m(2) g(-1) and 0.50-0.65 cm(3) g(-1). The MSMSP were used to grow opal-like photonic-crystal films possessing a hierarchical macro-mesoporous structure, with pores within and between the particles. A selective filling of mesopore channels with glycerol, based on the difference between the capillary pressures in macro- and mesopores, was demonstrated. It is shown that this approach makes it possible to control the photonic bandgap position in mesoporous opal films by varying the degree of mesopore filling with glycerol. Online supplementary data available from stacks.iop.org/Nano/24/155601/mmedia
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 49
DOI: 10.1088/0957-4484/24/15/155601
|
|
“Interplay of strain and indium incorporation in InGaN/GaN dot-in-a-wire nanostructures by scanning transmission electron microscopy”. Woo SY, Gauquelin N, Nguyen HPT, Mi Z, Botton GA, Nanotechnology 26, 344002 (2015). http://doi.org/10.1088/0957-4484/26/34/344002
Abstract: The interplay between strain and composition is at the basis of heterostructure design to engineer new properties. The influence of the strain distribution on the incorporation of indium during the formation of multiple InGaN/GaN quantum dots (QDs) in nanowire (NW) heterostructures has been investigated, using the combined techniques of geometric phase analysis of atomic-resolution images and quantitative elemental mapping from core-loss electron energy-loss spectroscopy within scanning transmission electron microscopy. The variation in In-content between successive QDs within individual NWs shows a dependence on the magnitude of compressive strain along the growth direction within the underlying GaN barrier layer, which affects the incorporation of In-atoms to minimize the local effective strain energy. Observations suggest that the interfacial misfit between InGaN/GaN within the embedded QDs is mitigated by strain partitioning into both materials, and results in normal stresses inflicted by the presence of the surrounding GaN shell. These experimental measurements are linked to the local piezoelectric polarization fields for individual QDs, and are discussed in terms of the photoluminescence from an ensemble of NWs.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 19
DOI: 10.1088/0957-4484/26/34/344002
|
|
“Hydrophilic Pt nanoflowers: synthesis, crystallographic analysis and catalytic performance”. Mourdikoudis S, Altantzis T, Liz-Marzan LM, Bals S, Pastoriza-Santos I, Perez-Juste J, CrystEngComm 18, 3422 (2016). http://doi.org/10.1039/C6CE00039H
Abstract: Water-soluble Pt nanoflowers (NFs) were prepared by a diethylene glycol-mediated reduction of Pt acetylacetonate
(Pt(acac)2) in the presence of polyethyleneimine. Advanced electron microscopy analysis showed that NFs consist of
multiple branches with truncated cubic morphology and different crystallographic orientations. We demonstrate that the
nature of the solvent strongly influences the resulting morphology. The catalytic performance of Pt NFs in 4–nitrophenol
reduction was found to be superior to that of other nanoparticle-based catalysts. Additionally, Pt NFs display good
catalytic reusability with no loss of activity after five consecutive cycles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.474
Times cited: 30
DOI: 10.1039/C6CE00039H
|
|
“Influence of annealing conditions on the structure and luminescence properties of KGd1-xEux(MoO4)2(0\leq x\leq1)”. Morozov VA, Posokhova SM, Deyneko D V, Savina AA, Morozov A V, Tyablikov OA, Redkin BS, Spassky DA, Hadermann J, Lazoryak B I, CrystEngComm 21, 6460 (2019). http://doi.org/10.1039/C9CE01244C
Abstract: This study describes the influence of annealing temperature on the structure and luminescence properties of KGd1-xEux(MoO4)(2) (0 <= x <= 1). Compounds with the general formula (A ', A '')(n)[(W, Mo)O-4](m) are investigated as luminescent materials for photonic applications such as phosphor-converted LEDs (light-emitting diodes). Herein, the KGd0.8Eu0.2(MoO4)(2) light-rose crystal was grown by the Czochralski technique. Moreover, three polymorphs of KGd1-xEux(MoO4)(2) were present in the 923-1223 K range of annealing temperatures under ambient pressure: a triclinic alpha-phase, a disproportionately modulated monoclinic beta-phase and an orthorhombic gamma-phase with a KY(MoO4)(2)-type structure. The different behaviors of KGd(MoO4)(2) and KEu(MoO4)(2) were revealed by DSC studies. The number and the character of phase transitions for KGd1-xEux(MoO4)(2) depended on the elemental composition. The formation of a continuous range of solid solutions with the triclinic alpha-KEu(MoO4)(2)-type structure and ordering of K+ and Eu3+/Gd3+ cations were observed only for alpha-KGd1-xEux(MoO4)(2) (0 <= x <= 1) prepared at 923 K. The structures of gamma-KGd1-xEux(MoO4)(2) (x = 0 and 0.2) were studied using electron diffraction and refined using the powder X-ray diffraction data. The luminescence properties of KGd1-xEux(MoO4)(2) prepared at different annealing temperatures were studied and related to their different structures. The maxima of the D-5(0) -> F-7(2) integral emission intensities were found under excitation at lambda(ex) = 300 nm and lambda(ex) = 395 nm for triclinic scheelite-type alpha-KGd0.6Eu0.4(MoO4)(2) and monoclinic scheelite-type beta-KGd0.4Eu0.6(MoO4)(2) prepared at 1173 K, respectively. The latter shows the brightest red light emission among the KGd1-xEux(MoO4)(2) phosphors. The maximum and integral emission intensity of beta-KGd0.4Eu0.6(MoO4)(2) in the D-5(0) -> F-7(2) transition region is similar to 20% higher than that of the commercially used red phosphor Gd2O2S:Eu3+. Thus, beta-KGd0.4Eu0.6(MoO4)(2) is very attractive for application as a near-UV convertible red-emitting phosphor for LEDs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.474
DOI: 10.1039/C9CE01244C
|
|
“Controlled vapor-phase synthesis of cobalt oxide nanomaterials with tuned composition and spatial organization”. Barreca D, Gasparotto A, Lebedev OI, Maccato C, Pozza A, Tondello E, Turner S, Van Tendeloo G, CrystEngComm 12, 2185 (2010). http://doi.org/10.1039/b926368n
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.474
Times cited: 85
DOI: 10.1039/b926368n
|
|
“Fe2O3-TiO2 nanosystems by a hybrid PE-CVD/ALD approach : controllable synthesis, growth mechanism, and photocatalytic properties”. Barreca D, Carraro G, Warwick MEA, Kaunisto K, Gasparotto A, Gombac V, Sada C, Turner S, Van Tendeloo G, Maccato C, Fornasiero P;, CrystEngComm 17, 6219 (2015). http://doi.org/10.1039/c5ce00883b
Abstract: Supported Fe2O3–TiO2 nanocomposites are fabricated by an original vapor phase synthetic strategy, consisting of the initial growth of Fe2O3 nanosystems on fluorine-doped tin oxide substrates by plasma enhanced-chemical vapor deposition, followed by atomic layer deposition of TiO2 overlayers with variable thickness, and final thermal treatment in air. A thorough characterization of the target systems is carried out by X-ray diffraction, atomic force microscopy, field emission-scanning electron microscopy, energy dispersive X-ray spectroscopy, transmission electron microscopy, and X-ray photoelectron spectroscopy. High purity nanomaterials characterized by the co-presence of Fe2O3 (hematite) and TiO2 (anatase), with an intimate Fe2O3–TiO2 contact, are successfully obtained. In addition, photocatalytic tests demonstrate that, whereas both single-phase oxides do not show appreciable activity, the composite systems are able to degrade methyl orange aqueous solutions under simulated solar light, and even visible light, with an efficiency directly dependent on TiO2 overlayer thickness. This finding opens attractive perspectives for eventual applications in wastewater treatment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.474
Times cited: 25
DOI: 10.1039/c5ce00883b
|