“Improvement of the oxidation stability and the mechanical properties of flexible graphite foil by boron oxide impregnation”. Savchenko DV, Serdan AA, Morozov VA, Van Tendeloo G, Ionov SG, New carbon materials 27, 12 (2012). http://doi.org/10.1016/S1872-5805(12)60001-8
Abstract: Flexible graphite foil produced by rolling expanded graphite impregnated with boron oxide was analyzed by laser mass spectroscopy, X-ray photoelectron spectroscopy, scanning electron microscopy and thermogravimetry. It was shown that the modification of the graphite foil by boron oxide increases the onset temperature of oxidation by ∼ 150 °C. Impregnation of less than 2 mass% boron oxide also increased the tensile strength of the materials. The observed improvement was attributed to the blocking of active sites by boron oxide, which is probably chemically bonded to the edges of graphene sheets in expanded graphite particles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 5
DOI: 10.1016/S1872-5805(12)60001-8
|
|
|
“Intersublevel absorption in stacked n-type doped self-assembled quantum dots”. Veljkovic D, Tadić, M, Peeters FM, Materials science forum 494, 37 (2005)
Abstract: The intersublevel absorption in n-doped InAs/GaAs self-assembled quantum-dot molecules composed of three quantum dots is theoretically considered. The transition matrix elements and the transition energies are found to vary considerably with the spacer thickness. For s polarized light, decreasing the thickness of the spacer between the dots brings about crossings between the transition matrix elements, but the overall absorption is not affected by the variation of the spacer thickness. For p-polarized light and thick spacers, there are no available transitions in the single quantum dot, but a few of them emerge as a result of the electron state splitting in the stacks of coupled quantum dots, which leads to a considerable increase of the transition matrix elements, exceeding by an order of magnitude values of the matrix elements for s-polarized light.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
|
|
|
“Magnetoexcitons in type-II self-assembled quantum dots and quantum-dot superlattices”. Veljkovic D, Tadić, M, Peeters FM, Recent developments in advanced materials and processes 518, 51 (2006)
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
|
|
|
“Magnetoplasma excitations in vertically coupled quantum dot systems”. Partoens B, Matulis A, Peeters FM, Materials science forum 297/298, 225 (1999)
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
|
|
|
“Measurement of the mean inner potential of ZnO nanorods by transmission electron holography”. Müller E, Kruse P, Gerthsen D, Schowalter M, Rosenauer A, Lamoen D, Kling R, Microscopy of Semiconducting Materials 107SPRINGER PROCEEDINGS IN PHYSICS, 303 (2005)
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT)
|
|
|
“A microstructural study of the thermal stability of atomic layer deposited Al2O3 thin films”. Nistor LC, Richard O, Zhao O, Bender H, Stesmans A, Van Tendeloo G, Institute of physics conference series
T2 –, Microscopy of semiconducting materials , 397 (2003)
Abstract: The thermal stability of amorphous Al2O3 films (similar to8 and 80 nut thick) deposited by atomic layer deposition on HF-last and thin SiO2 covered (001) Si substrates is studied by transmission electron microscopy. The layers are in- and ex-situ annealed in the same temperature range.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Microstructure of artificial [100] 45 degrees twist grain boundaries in YBa2Cu3O7-delta”. Verbist K, Tafuri F, Granozio FM, Di Chiara S, Van Tendeloo G, Electron Microscopy 1998, Vol 2: Materials Science 1 , 593 (1998)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Misfit accommodation of epitaxial La1-xAxMnO3 (A=Ca, Sr) thin films”. Lebedev OI, Van Tendeloo G, Amelinckx S, International journal of inorganic materials 3, 1331 (2001). http://doi.org/10.1016/S1466-6049(01)00155-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1016/S1466-6049(01)00155-6
|
|
|
“Molecular terms and optical transitions of C60n+/- molecular ions”. Nikolaev AV, Michel KH, AIP conference proceedings
T2 –, 16th International Winterschool on Electronic Properties of Novel, Materials, MAR 02-09, 2002, KIRCHBERG, AUSTRIA , 417 (2002)
Abstract: We have studied the molecular energy terms of the hole configurations (h(u)(+))(m), m=2,3,4,5 of C-60(m+) cations and the electronic configurations (t(1u))(n) n=2,3,4, as well as (t(1u))(n-1)t(1g) of the C-60(n-) anions. The lowest terms (within an energy span of 0.03 eV) for C-60(2+) are three triplets T-3(1g), (3)G(g), T-3(2g) and for C-60(3+) are three quartets T-4(1u), (4)G(u), T-4(2u), which favor Jahn-Teller distortions. For the ground state of C-60(2-) we find a triplet T-3(1g) in agreement with Hund's rules. Our method takes into account intramolecular direct and exchange multipolar Coulomb interactions.
Keywords: P1 Proceeding; Condensed Matter Theory (CMT)
|
|
|
“Nano- and microcrystal investigations of precipitates, interfaces and strain fields in Ni-Ti-Nb by various TEM techniques”. Schryvers D, Shi H, Martinez GT, Van Aert S, Frenzel J, Van Humbeeck J, Materials science forum
T2 –, 9th European Symposium on Martensitic Transformations (ESOMAT 2012), SEP 09-16, 2012, St Petersburg, RUSSIA 738/739, 65 (2013). http://doi.org/10.4028/www.scientific.net/MSF.738-739.65
Abstract: In the present contribution several advanced electron microscopy techniques are employed in order to describe chemical and structural features of the nano- and microstructure of a Ni45.5Ti45.5Nb9 alloy. A line-up of Nb-rich nano-precipitates is found in the Ni-Ti-rich austenite of as-cast material. Concentration changes of the matrix after annealing are correlated with changes in the transformation temperatures. The formation of rows and plates of larger Nb-rich precipitates and particles is described. The interaction of a twinned martensite plate with a Nb-rich nano-precipitate is discussed and the substitution of Nb atoms on the Ti-sublattice in the matrix is confirmed.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.4028/www.scientific.net/MSF.738-739.65
|
|
|
“Natural mineral-marine manganese nodule as a novel catalyst for the synthesis of carbon nanotubes”. Cheng JP, Zhang XB, Ye Y, Tao XY, Liu F, Li Y, Van Tendeloo G, Journal of Wuhan University of Technology: materials science edition 21, 29 (2006)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Nickel/carbon composite materials based on expanded graphite”. Afanasov IM, Lebedev OI, Kolozhvary BA, Smirnov AV, Van Tendeloo G, New carbon materials 26, 335 (2011). http://doi.org/10.1016/S1872-5805(11)60085-1
Abstract: Monolithic nickel/carbon (Ni/C) composites were prepared from coal tar pitch-impregnated compressed expanded graphite pre-decorated with NiO particles (EGNiO) by pyrolysis at 550 °C and subsequent steam activation at 800 °C. The microstructural arrangement of the Ni-comprising nanoparticles in the composites was investigated using transmission electron microscopy. The specific surface area and porosity of the composites were analyzed by nitrogen adsorption. The catalytic activity of the composites was compared with the material obtained by the conventional H2 treatment of EGNiO using hydrocracking of 2,2,3-trimethylpentane as a model reaction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 7
DOI: 10.1016/S1872-5805(11)60085-1
|
|
|
“On estimation of the dielectric function of Ag(Br,I) nanocrystals by cryo-EELS (addendum)”. Oleshko VP, Gijbels RH, van Daele AJ, Jacob WA, Nanostructered materials 11, 687 (1999)
Keywords: A3 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
|
|
|
“Pd@MOF-5: limitations of gas-phase infiltration and solution impregnation of [Zn4O(bdc)3] (MOF-5) with metalorganic palladium precursors for loading with Pd nanoparticles”. Esken D, Zhang X, Lebedev OI, Schröder F, Fischer RA, Journal of materials chemistry 19, 1314 (2009). http://doi.org/10.1039/b815977g
Abstract: The limitations of the loading of the porous metalorganic framework [Zn4O(bdc)3] (bdc = benzene-1,4-dicarboxylate; MOF-5 or IRMOF-1) with Pd nanoparticles was investigated. First, the volatile organometallic precursor [Pd(5-C5H5)(3-C3H5)] was employed to get the inclusion compound [Pd(5-C5H5)(3-C3H5)]x@MOF-5 via gas-phase infiltration at 10-3 mbar. A loading of four molecules of [Pd(5-C5H5)(3-C3H5)] per formula unit of MOF-5 (x = 4) can be reached (35 wt.% Pd). Second, the metalorganic precursor [Pd(acac)2] (acac = 2,4-pentanedionate) was used and the inclusion materials [Pd(acac)2]x@MOF-5 of different Pd loadings were obtained by incipient wetness infiltration. However, the maximum loading was lower as compared with the former case with about two precursor molecules per formula unit of MOF-5. Both loading routes are suitable for the synthesis of Pd nanoparticles inside the porous host matrix. Homogeneously distributed nanoparticles with diameter of 2.4(±0.2) nm can be achieved by photolysis of the inclusion compounds [Pd(5-C5H5)(3-C3H5)]x@MOF-5 (x 4), while the hydrogenolysis of [Pd(acac)2]x@MOF-5 (x 2) leads to a mixture of small particles inside the network (< 3 nm) and large Pd agglomerates (40 nm) on the outer surface of the MOF-5 specimens. The pure Pdx@MOF-5 materials proved to be stable under hydrogen pressure (2 bar) at 150 °C over many hours. Neither hydrogenation of the bdc linkers nor particle growth was observed. The new composite materials were characterized by 1H/13C-MAS-NMR, powder XRD, ICP-AES, FT-IR, N2 sorption measurements and high resolution TEM. Raising the Pd loading of a representative sample Pd4@MOF-5 (35 wt.% Pd) by using [Pd(5-C5H5)(3-C3H5)] as precursor in a second cycle of gas-phase infiltration and photolysis was accompanied by the collapse of the long-range crystalline order of the MOF.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 100
DOI: 10.1039/b815977g
|
|
|
“Phase transitions in AC60 (A=Rb, Cs) fullerides”. Nikolaev AV, Prassides K, Michel KH, Recent advances in the chemistry and physics of fullerenes and related materials 5, 450 (1997)
Keywords: A3 Journal article; Condensed Matter Theory (CMT)
|
|
|
“Positron annihilation study of nanocrystalline Ni3Al : simulations and measurements”. Kuriplach J, van Petegem S, Hou M, Van Tendeloo G, Schryvers D, et al, Materials science forum
T2 –, 12th International Conference on Positron Annihilation (ICPA-12), AUG 06-12, 2000, UNIV BUNDERSWEHR MUNCHEN, NEUBIBERG, GERMANY 363-3, 94 (2001)
Abstract: A positron lifetime experiment is performed on samples produced by the compaction of nanocrystalline Ni3Al powder synthesized by the inert-gas condensation technique. In the lifetime spectrum we observe two components corresponding to defects. Computer (virtual) samples of n-Ni3Al are obtained using molecular dynamics combined with the Metropolis Monte Carlo technique. Positron lifetime calculations are then performed on selected regions of simulated samples. For this purpose, a new computational technique based on a generalization of the atomic superposition method for non-periodic systems was developed. Lifetimes calculated in this way are compared to experiment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Preparation of nanocrystalline titania powder by aerosol pyrolysis of titanium alkoxide”. Ahonen PP, Kauppinen EI, Deschanvres JL, Joubert JC, Van Tendeloo G, Materials Research Society symposium proceedings 520, 109 (1998)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 2
|
|
|
“Production and structure of exfoliated graphite/coke composites modified by ZrO2 nanoparticles”. Afanasov IM, Van Tendeloo G, Mateev AT, New carbon materials 25, 255 (2010). http://doi.org/10.1016/S1872-5805(09)60032-9
Abstract: Exfoliated graphite/coke composites modified by ZrO2 nanoparticles were produced using two different techniques and characterized by means of X-ray diffraction, scanning and transmission electron microscopy. In the first, low-density exfoliated graphite/coke blocks were dipped repeatedly and alternately in ZrO(NO3)2 and NH4OH solutions and subsequently heat treated at 1200°C in nitrogen to deposit thin layers of ZrO2 nanoparticles on the free surfaces of the carbon matrix. In the second, a mixture of expandable graphite, phenol-formaldehyde resin powder, and ZrOC2O4-modified fibrous cellulose in a sealed container was submitted to thermal shock at 900 °C followed by heat treatment at 1 200 °C in nitrogen to obtain the modified composites. The ZrO2 nanoparticles formed in the second technique were incorporated into the composites in three length scales: 6-30 nm-isolated nanoparticles and small blobs, 200-1000 nm-lengthy dendrite-like structures, and thin layer adhering to the surface of the 1-40 μm long cellulose carbon fibers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1016/S1872-5805(09)60032-9
|
|
|
“Rapid microwave-assisted synthesis of benzene bridged periodic mesoporous organosilicas”. Smeulders G, Meynen V, van Baelen G, Mertens M, Lebedev OI, Van Tendeloo G, Maes BUW, Cool P, Journal of materials chemistry 19, 3042 (2009). http://doi.org/10.1039/b820792e
Abstract: Following extended use in organic chemistry, microwave-assisted synthesis is gaining more importance in the field of inorganic chemistry, especially for the synthesis of nanoporous materials. It offers some major advantages such as a significant shortening of the synthesis time and an improved promotion of nucleation. In the research here reported, microwave technology is applied for the synthesis of benzene bridged PMOs (periodic mesoporous organosilicas). PMOs are one of the latest innovations in the field of hybrid ordered mesoporous materials and have attracted much attention because of their feasibility in electronics, catalysis, separation and sorption applications. The different synthesis steps (stirring, aging and extraction) of the classical PMO synthesis are replaced by microwave-assisted synthesis steps. The characteristics of the as-synthesized materials are evaluated by X-ray diffraction, N2-sorption, thermogravimetric analysis, scanning- and transmission electron microscopy. The microwave-assisted synthesis drastically reduces the synthesis time by more than 40 hours without any loss in structural properties, such as mesoscale and molecular ordering. The porosity of the PMO materials has even been improved by more than 25%. Moreover, the number of handling/transfer steps and amounts of chemicals and waste are drastically reduced. The study also shows that there is a clear time (1 to 3 hours) and temperature frame (373 K to 403 K) wherein synthesis of benzene bridged PMO is optimal. In conclusion, the microwave-assisted synthesis pathway allows an improved material to be obtained in a more economical way i.e. a much shorter time with fewer chemicals and less waste.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY)
Times cited: 20
DOI: 10.1039/b820792e
|
|
|
“Reduced dimensionality in different forms of carbon”. Van Tendeloo G, Bernaerts D, Amelinckx S, Fullerenes and carbon based materials , 487 (1998)
Abstract: Several TEM techniques are used to characterise the local structure of low dimensional forms of carbon. HREM is particularly useful to describe the defect structure of thin films of diamond or fullerenes and C-60-C-70 nanoclusters. A columnar form of graphite is analysed, mainly by electron diffraction which allowed us to propose a growth mechanism. Diffraction contrast dark field microscopy, in combination with electron diffraction, allows a detailed characterisation of carbon nanotubes; e.g. the chirality distribution of tubes in ropes of single wall tubes is studied by selected area electron diffraction. (C) 1998 Elsevier Science Ltd. All rights reserved.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Shallow donor near a semiconductor surface in the presence of locally spherical scanning tunneling microscope tip”. Djotyan AP, Avetisyan AA, Hao YL, Peeters FM, Proceedings of the Society of Photo-optical Instrumentation Engineers
T2 –, Conference on Photonics and Micro and Nano-structured Materials, JUN 28-30, 2011, Yerevan, ARMENIA , 84140 (2012). http://doi.org/10.1117/12.923562
Abstract: We developed a variational approach to investigate the ground state energy and the extend of the wavefunction of a neutral donor located near a semiconductor surface in the presence of scanning tunneling microscope (STM) metallic tip. We apply the effective mass approximation and use a variational wavefunction that takes into account the influence of all image charges that arise due to the presence of a metallic tip. The behavior of the ground state energy when the tip approaches the semiconductor surface is investigated.
Keywords: P1 Proceeding; Engineering sciences. Technology; Condensed Matter Theory (CMT)
DOI: 10.1117/12.923562
|
|
|
“Stable polyoxometalate insertion within the mesoporous metal organic framework MIL-100(Fe)”. Canioni R, Roch-Marchal C, Sécheresse F, Horcajada P, Serre C, Hardi-Dan M, Férey G, Grenèche J-M, Lefebvre F, Chang J-S, Hwang Y-K, Lebedev O, Turner S, Van Tendeloo G, Journal of materials chemistry 21, 1226 (2011). http://doi.org/10.1039/c0jm02381g
Abstract: Successful encapsulation of polyoxometalate (POM) within the framework of a mesoporous iron trimesate MIL-100(Fe) sample has been achieved by direct hydrothermal synthesis in the absence of fluorine. XRPD, 31P MAS NMR, IR, EELS, TEM and 57Fe Mössbauer spectrometry corroborate the insertion of POM within the cavities of the MOF. The experimental Mo/Fe ratio is 0.95, in agreement with the maximum theoretical amount of POM loaded within the pores of MIL-100(Fe), based on steric hindrance considerations. The POM-MIL-100(Fe) sample exhibits a pore volume of 0.373 cm3 g−1 and a BET surface area close to 1000 m2 g−1, indicating that small gas molecules can easily diffuse inside the cavities despite the presence of heavy phosphomolybdates. These latter contribute to the decrease in the overall surface area, due to the increase in molar weight, by 65%. Moreover, the resulting Keggin containing MIL-100(Fe) solid is stable in aqueous solution with no POM leaching even after more than 2 months. In addition, no exchange of the Keggin anions by tetrabutylammonium perchlorate in organic media has been observed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 158
DOI: 10.1039/c0jm02381g
|
|
|
“Structural and analytical characterization of Ag(Br,I) nanocrystals by cryo-AEM techniques”. Oleshko VP, van Daele A, Gijbels RH, Jacob WA, Journal of nanostructured materials 10, 1225 (1998). http://doi.org/10.1016/S0965-9773(99)00003-3
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Times cited: 5
DOI: 10.1016/S0965-9773(99)00003-3
|
|
|
“Structural characterization of erbium doped LAS glass ceramics obtained by glass melting technique”. Krsmanovic R, Bertoni G, Van Tendeloo G, Materials science forum 555, 377 (2007)
Abstract: Samples of transparent glass-ceramics in the ternary system Li2O-Al2O3-SiO2 (LAS), with Er2O3 as a luminescent dopant, are investigated. The initial glass is obtained by the classical melting technique. In order to induce ceramization of the glass, TiO2 and ZrO2 are added in small amount as nucleating agents. The thermal treatments at 730 and 770 degrees C are carried out to promote formation of titanium zirconate solid solution precipitates. The spatial distribution of the precipitates in the material, their morphology, and their composition are investigated with TEM, HRTEM, HAADF-STEM, EELS and EFTEM. The results demonstrate that with the glass-melting preparation technique it is possible to achieve small nanoparticles with uniform distribution and higher number density than with the sol-gel glass preparation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Structural studies of nanocrystalline diamond thin films”. Nistor LC, van Landuyt J, Ralchenko VG, Obratzova ED, Korothushenko KG, Smolin AA, Materials science forum 239-241, 115 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Structural transformation in fluorinated LaACuGaO5 (A=Ca, Sr) brownmillerites”. Hadermann J, Van Tendeloo G, Abakumov AM, Pavlyuk BP, Rozova MG, Antipov EV, International journal of inorganic materials 2, 493 (2000). http://doi.org/10.1016/S1466-6049(00)00072-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 13
DOI: 10.1016/S1466-6049(00)00072-6
|
|
|
“Structure and magnetotransport properties of La2/3Ca1/3MnO3 thin films prepared by pulsed laser deposition”. Lebedev OI, Van Tendeloo G, Amelinckx S, Leibold B, Habermeier HU, Phillipp F, Materials Research Society symposium proceedings
T2 –, Symposium on Advances in Laser Ablation of Materials at the 1998 MRS, Spring Meeting, April 13-16, 1998, San Francisco, Calif. , 219 (1998). http://doi.org/10.1557/PROC-526-219
Abstract: La1-xCaxMnO3-delta (LCMO) thin films are grown by pulsed laser deposition on a (100) SrTiO3 substrate at temperatures between 530 degrees C and 890 degrees C. The magnetotransport properties show a high negative magnetoresistance and a shift of the maximum of the R(T) curve as function of temperature. The Curie temperature changes with deposition temperature and film quality in the range of 100-220K. The film quality is characterised by X-ray diffraction and transmission electron microscopy (TEM); film and target compositions were verified by atomic emission spectroscopy. The local structure of the film depends on the growth conditions and substrate temperature. TEM reveals a slight distortion of the film leading to a breakdown of the symmetry from orthorhombic to monoclinic. At the highest growth temperatures, a well defined interface is observed within the LCMO film, parallel to the substrate surface; this interface divides the film into two lamellae with a different microstructure. The lamella close to the substrate is perfectly coherent with the substrate, suggesting that it is strained as a result of the lattice parameter mismatch; the upper lamella shows a typical domain structure with unusual translation interfaces characterised by a displacement vector of the type 1/2[010](m) and 1/2[001](m) when referred ten the monoclinic lattice.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
DOI: 10.1557/PROC-526-219
|
|
|
“Study of the packing of double-walled carbon nanotubes into bundles by transmission electron microscopy and electron diffraction”. Colomer J-F, Henrard L, Van Tendeloo G, Lucas A, Lambin P, Journal of materials chemistry 14, 603 (2004). http://doi.org/10.1039/b311551h
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 27
DOI: 10.1039/b311551h
|
|
|
“Synthesis and charactreization of the new Ln(2)FeMoO(7) (Ln = Y, Dy, Ho) compounds”. Veith GM, Lobanov MV, Emge TJ, Greenblatt M, Croft M, Stowasser F, Hadermann J, Van Tendeloo G, Journal of materials chemistry 14, 1623 (2004). http://doi.org/10.1039/b315028c
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 17
DOI: 10.1039/b315028c
|
|
|
“Synthesis and crystal structure of novel CaRMnSnO6(R = La, Pr, Nd, Sm-Dy) double perovskites”. Abakumov AM, Rossell MD, Seryakov SA, Rozova MG, Markina MM, Van Tendeloo G, Antipov EV, Journal of materials chemistry 15, 4899 (2005). http://doi.org/10.1039/b510242a
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 8
DOI: 10.1039/b510242a
|
|