Abstract: Recently discovered series of high Tc superconductors, characterized by the existence of two types of cations within the same layer, are presented. The first family concerns the mercury based cuprates, Hg(1-x)M(x)A(2)Ca(m-1)Cu(m)O(2m+2+delta), with A = Ba and/or Sr, which exhibit structures closely related to that of the thallium cuprates TlBa2Cam-1CumO2m+3. They differ from the thallium cuprates by a high oxygen deficiency at the level of the mercury layer. It is shown that cations such as M = Cu, Pb, Tl, Bi, Ce, Pr, Cr, V, Mo, W, Ti, Sr, Ca,... can partially substitute for mercury ions, stabilizing the structures. The cationic composition of the layer depends indeed on the nature of the M cation but also on that of the alkaline earth A. For given A and M cations, the a: value remains unchanged even when the number of copper layers varies. M and Hg cations are either statistically distributed over the same site or ordered. Different types of ordering have been detected. Another way of generating mixed layers is to shear periodically the structure, leading to the formation of the so called ''collapsed phase''. In the collapsed bismuth cuprates, bismuth and copper segments, a few octahedra long, alternate in strongly waving layers. In the collapsed oxycarbonates, carbonate groups and M cations are ordered within the intermediate layer so that they can be simply described from a partial and ordered substitution of carbon for Hg,TI, Bi and other M cations building the intermediate layer. The oxycarbonitrates (Y1-xCax)(n)Ba2nCu3n-1(C,N)O3O7n-3 can also be described as an ordered substitution of carbon for copper in the 123 matrix. The different families of superconducting materials which are generated by such mechanisms are described as well as the way the different species are distributed within the mixed layers. Their influence on the physical properties are discussed.

Abstract: The nucleation and growth mechanisms of Ni5Al3 precipitates and microtwinned plates in B2 austenite and 2M (3R) martensite phases are described on the basis of conventional and high resolution electron microscopy. In the Ni62.5Al37.5 B2 austenite matrix short annealings at 550 degrees C introduce three-pointed star shaped precipitates consisting of twin related parts of different variants of the Ni5Al3 structure. Longer annealings result in plates growing separately from these wings and developing microtwinning in order to accommodate stress built-up at the interfaces with the surrounding matrix. Annealing of Ni65Al35 2M martensite plates induces simple reordering into the Ni5Al3 phase, increasing the fct c/a ratio by about 1%. As a result stracking faults are introduced in the smallest twin variants.

Abstract: A model for superstructure ordering in the <<chain>> layers of Ga (Co) substituted YBCO intergrowths with general formula (REO2)NSr2MCu2O5 (M = Co, Ga; n = 1, 2, ...) is proposed. By Ga or Co substitution for Cu, the structure of the <<chain>> layer changes : instead of the CuO4 planar squares, the chains consist of MO4 tetrahedra (M = Ga, Co) running along the [110] perovskite direction. The existing model for the Ga substituted <<123>> implies that all the chains are the same. Our new model is based on the results of Electron diffraction and High-resolution electron microscopy investigations. The model reveals the occurrence of two types of chains as a consequence of <<opposite>> ordering between neighbouring tetrahedra. The comer linked tetrahedra in each chain appear as alternatingly rotated in opposite sense, and a chain itself, as being displaced with respect to the underlying structure in one of two senses ; either forth (right) or back (left) along the chain direction. The regular alternation of chains of opposite type doubles the periodicity within a layer and induces the possibility for intrinsic disorder in the chain layer stacking sequence. The planar superstructure and a staggered stacking of the tetrahedral chain layers is found irrespective of the rest of the intergrowth structure. Superstructure ordering in the case of Co substitution is more perfect than for the Ga substitution.