Abstract: The post-growth modification of diamond-like amorphous hydrogenated carbon a-C:H films by laser treatment has been studied by transmission electron microscopy and Raman spectroscopy. a-C:H films grown on Si substrates by benzene decomposition in a rf glow discharge were irradiated with 15 ns pulses of a KrF-excimer laser with fluences in the ran e of E = 50-700 mJ/cm(2). At fluences below 100 mJ/cm(2) an increase in the number of graphitic clusters and in their ordering was evidenced from Raman spectra, while the film structure remained amorphous according to electron microscopy and electron diffraction observations. At higher fluences the appearance of diamond particles of 2-7 nm size, embedded into the lower crystallized graphitic matrix, was observed and simultaneously a progressive growth of graphite nanocrystals with dimensions from 2 nm to 4 nm was deduced from Raman measurements. The maximum thickness of the crystallized surface layer (approximate to 400 nm) and the degree of laser annealing are limited by the film ablation which starts at E > 250 mJ/cm(2). The laser-treated areas lose their chemical inertness. In particular, chemical etching in chromium acid becomes possible, which may be used for patterning the highly inert carbon films.

Abstract: A far-infrared absorption study of electrons in lightly-doped GaAs/Al0.3Ga0.7As superlattices is presented. Both weakly and strongly coupled superlattices are investigated, and the difference between intersubband transitions and transitions between extended minibands is demonstrated. At low temperatures, the absorption spectra are dominated by donor transitions. The 1s-2p(z) transition, which is intimately related to the intersubband transition, is observed. All experimental data are compared to an envelope function calculation for the miniband structure and a variational calculation for the donor energies. Excellent agreement between experiment and theory is achieved.

Abstract: In this work, photoelectric yield and electrical properties of several types of epitaxial erbium silicide on silicon Schottky diodes are studied, Different preparation conditions are used simultaneously on n- and p-Si(111) substrates for the 200 Angstrom thick silicide films. A last type of sample consists in 1.3 monolayer of epitaxial silicide with root 3 X root 3 superstructure on the Si substrate and covered by silver on the top. Photocurrent measurements are done as a function of photon energy at several temperatures. All these samples show barrier heights near 1 eV on p-type Si, even for the interface comprising only 1.3 monolayer of silicide whereas barrier heights on n-rype Si span the range from 0.28 to 0.67 eV for this last kind of sample, the sum of the barriers always exceeding the silicon band gap, These photoelectric results are confirmed by electrical characterisations, All these results show that the Fermi level is pinned 0.1 eV below the conduction band edge on p-type Si but shifts to various positions lower within the band gap on n-type Si. This fact leads to the hypothesis of a density of -7 interface states close to the charge change in the Si depletion zone from p- to n-type, namely 10(12) eV(-1) cm(-2). Although some inhomogeneities and defects at the interface are detected by electron microscopy for samples annealed at 750 degrees C, Fermi level position seems rather insensitive to the structural details of the interface while the silicide thickness plays a role on n-type Si.