“Examination of Vincent van Gogh's paintings and pigments by means of state-of-the-art analytical methods”. Janssens K, Alfeld M, Van der Snickt G, De Nolf W, Vanmeert F, Monico L, Legrand S, Dik J, Cotte M, Falkenberg G, van der Loeff L, Leeuwestein M, Hendriks E page 373 (2014).
Abstract: Recent studies in which X-ray beams of macroscopic to (sub) microscopic dimensions were used for non-destructive analysis and characterization of pigments, paint micro samples and/or entire paintings by Vincent van Gogh are concisely reviewed. The overview presented encompasses the use of laboratory and synchrotron radiation-based instrumentation and deals with the use of several variants of X-ray fluorescence (XRF) as a method of elemental analysis and imaging as well as with the combined use of X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS). Microscopic and macroscopic XRF are variants of the method that are well suited to visualize the elemental distribution of key elements, mostly metals, present in paint multi layers, either on the length scale from 1–100 μm inside micro samples taken from paintings or on the 1–100 cm length scale when the (subsurface) distribution of specific pigments in entire paintings is concerned. In the context of the characterization of van Gogh's pigments subject to natural degradation, the use of methods limited to elemental analysis or imaging usually is not sufficient to elucidate the chemical transformations that have taken place. However, at synchrotron facilities, combinations of μ-XRF with related methods such as μ-XAS and μ-XRD have proven themselves to be very suitable for such studies. Their use is often combined with microscopic Fourier transform infra-red (μ-FTIR) spectroscopy since this method delivers complementary information at more or less the same length scale as the X-ray microprobe techniques. Also in the context of macroscopic imaging of works of art, the complementary use of X-ray based and infra-red based imaging appears very promising; some recent developments are discussed.
Keywords: H2 Book chapter; Art; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1039/9781839161957-00373
|
de Nolf W (2013) Imaging of crystalline phase distributions by means of scanning and tomographic X-ray powder diffraction. 407 p
Keywords: Doctoral thesis; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Influence of Bridgman process conditions on microstructure and porosity of single crystal Ni-base superalloy CMSX-4”. Matuszewski K, Matysiak H, Jaroszewicz J, de Nolf W, Kubiak K, Kurzydlowski KJ, International journal of cast metals research 27, 329 (2014). http://doi.org/10.1179/1743133614Y.0000000112
Abstract: Synchrotron radiation micro-X-ray fluorescence and micro-X-ray diffraction analysis, micro-computed tomography and transmission electron microscopy were used to investigate the microstructure of turbine blades made of a second generation nickel based superalloy CMSX-4 manufactured by investment casting process via Bridgman technique. The dependence of microstructure on process parameters, among others, on the withdrawal rate was analysed. The results set the stage for optimising the microstructure of the blades in terms of their mechanical properties.
Keywords: A1 Journal article; Engineering sciences. Technology; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1179/1743133614Y.0000000112
|
“2θ-resolution obtainable during – XRPD experiments at Beamline L”. de Nolf W, Jaroszewicz J, Janssens K, Falkenberg G page 1655 (2008).
Keywords: H3 Book chapter; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Assessing the origin and fate of Cr, Ni, Cu, Zn, Pb, and V in an industrial polluted soil by combined micro-spectroscopic techniques and bulk extraction methods”. Terzano R, Spagnuolo M, Vekemans B, de Nolf W, Janssens K, Falkenberg G, Fiore S, Ruggiero P (2008).
Keywords: H3 Book chapter; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Assessing the origin and fate of CR, Ni, Cu, Zn, Ph, and V in industrial polluted soil by combined microspectroscopic techniques and bulk extraction methods”. Terzano R, Spagnuolo M, Vekemans B, de Nolf W, Janssens K, Falkenberg G, Ruggiero P, Environmental science &, technology 41, 6762 (2007). http://doi.org/10.1021/ES070260H
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Times cited: 61
DOI: 10.1021/ES070260H
|
“Characterization of carcinogenic Ni-rich dust particles by scanning micro-XRF/XRD at BL L”. de Nolf W, Janssens K, Rickers K (2005).
Keywords: H3 Book chapter; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Characterization of Yenisey River U-particles using a combination of μ-XRF, μ-XRD and U-LIII μ-XANES”. Lind OC, Claussen-Kjerre L, de Nolf W, Falkenberg G, Jaroszewicz J, Janssens K, Salbu B page 1279 (2008).
Keywords: H3 Book chapter; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Combined micro-XRF/XRPD tomography on historical and modern paint multilayer samples at Beamline L”. de Nolf W, Jaroszewicz J, van der Snickt G, Janssens K, Farnell S, Klaassen L page 1633 (2008).
Keywords: H3 Book chapter; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Combined use of μ-XRF and μ-XRD for characterization of radioactive particle clusters released during the Chernobyl reactor incident”. Jaroszewicz J, de Nolf W, Janssens K, Claussen-Kjerre L, Lind OC, Salbu B, Falkenberg G (2007).
Keywords: H3 Book chapter; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Combined use of μ-XRF and μ-XRD to determine the heterogeneity, the chemical and phase composition of Ti-B-C ceramics prepared by the pulse plasma sintering (PPS) method”. Jaroszewicz J, de Nolf W, Janssens K, Michalski A, Falkenberg G (2007).
Keywords: H3 Book chapter; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Confocal μ-XRF and μ-XAFS studies of fractured granite following a radiotracer migration experiment”. Denecke MA, Janssens K, Brendebach B, Falkenberg G, de Nolf W, Römer J (2007).
Keywords: H3 Book chapter; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Confocal mu-XRF, mu-XAFS, and mu-XRD studies of sediment from a nuclear waste disposal natural analogue site and fractured granite following a radiotracer migration experiment”. Denecke MA, Janssens K, Brendebach B, de Nolf W, Falkenberg G, Rothe J, Simon R, Somogyi A, Vekemans B, Noseck U, AIP conference proceedings 882, 187 (2007)
Abstract: Combined mu-XRF, mu-XAFS, and mu-XRD investigations of a uranium-rich tertiary sediment, from a nuclear repository natural analogue site, and a fractured granite bore core section after a column tracer experiment using a Np(V) containing cocktail have been performed. Most mu-XRF/mu-XAFS measurements are recorded in a confocal geometry to provide added depth information. The U-rich sediment results show uranium to be present as a tetravalent phosphate and that U(IV) is associated with As(V). Arsenic present is either As(V) or As(0). The As(0) form thin coatings on the surface of pyrite nodules. A hypothesis for the mechanism of uranium immobilization is proposed, where arsenopyrite acted as reductant of ground water dissolved U(VI) leading to precipitation of less soluble U(IV) and thereby forming As(V). Results for the granite sample show the immobilized Np to be tetravalent and associated with facture material.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Disclosing the binding medium effects and the pigment solubility in the (photo)reduction process of chrome yellows (PbCrO4/PbCr1-xSxO4)”. Monico L, Sorace L, Cotte M, de Nolf W, Janssens K, Romani A, Miliani C, ACS Omega 4, 6607 (2019). http://doi.org/10.1021/ACSOMEGA.8B03669
Abstract: The darkening due to chemical alteration of chrome yellows (PbCrO4/PbCr1-xSxO4) is a phenomenon threatening a large number of 19th-20th century paintings, including the Amsterdam Sunflowers by Vincent van Gogh. Our earlier studies have proven that the alteration is due to a Cr(VI) -> Cr(III) reduction with Cr(V)-species that are formed as long-lived intermediates and that bCr(1-x)S(x)O(4) (0 < x <= 0.8) types undergo reduction more readily than monoclinic, S-free, PbCrO4. In this context, there is still lack of knowledge about the effects of the chemical properties of the binding medium (i.e., chemical composition and drying process) and the solubility of chrome yellows on the overall reduction pathways. Here, we study a series of naturally and photochemically aged mock-up paints prepared by mixing chrome yellow powders (PbCrO4/PbCr0.2S0.8O4) with either linseed oil or a water-based acrylic emulsion as the binding medium. Equivalent paints made up of the highly soluble K2CrO4 were also investigated and used as benchmarks to provide a more in-depth understanding of the influence of the solubility on the chromate reduction pathways in the two different binders. A combination of synchrotron radiation-based Cr K-edge X-ray absorption near edge structure (XANES), electron paramagnetic resonance (EPR), and UV-Visible spectroscopy measurements shows that: (1) the Cr(VI) reduction results from the interaction between the pigment and the binder; (2) the process is more significant in oil, giving rise to Cr(V)- and Cr(III)-species as well as oxidized organic compounds; (3) the lightfastness of the chrome yellow pigment is enhanced in the acrylic binder; and (4) the tendency toward chromium reduction increases with increasing solubility of the pigment. Based on our findings, we propose a scheme for the mechanism of the (photo)reduction process of chrome yellows in the oil and acrylic binder. Overall, our results provide new insights into the factors driving the degradation of lead chromate-based paints in artworks and contribute to the development of strategies for preserving them over time.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Times cited: 4
DOI: 10.1021/ACSOMEGA.8B03669
|
“Examination of historical paintings by state-of-the-art hyperspectral imaging methods : from scanning infra-red spectroscopy to computed X-ray laminography”. Legrand S, Vanmeert F, van der Snickt G, Alfeld M, de Nolf W, Dik J, Janssens K, Heritage science 2, 13 (2014). http://doi.org/10.1186/2050-7445-2-13
Abstract: The development of advanced methods for non-destructive selective imaging of painted works of art at the macroscopic level based on radiation in the X-ray and infrared range of the electromagnetic spectrum are concisely reviewed. Such methods allow to either record depth-selective, element-selective or species-selective images of entire paintings. Camera-based full field methods (that record the image data in parallel) can be discerned next to scanning methods (that build up distributions in a sequential manner by scanning a beam of radiation over the surface of an artefact). Six methods are discussed: on the one hand, macroscopic X-ray fluorescence and X-ray diffraction imaging and X-ray laminography and on the other hand macroscopic Mid and Near Infrared hyper- and full spectral imaging and Optical Coherence Tomography. These methods can be considered to be improved versions of the well-established imaging methods employed worldwide for examination of paintings, i.e., X-ray radiography and Infrared reflectography. Possibilities and limitations of these new imaging techniques are outlined.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1186/2050-7445-2-13
|
“Identification of the geochemical forms of CR, Zn, Ni, Pb, V, and Cu in an industrial polluted soil by combined μ-XRF/μ-XRD and μ-XANES”. Terzano R, Spagnuolo M, Ruggiero P, Vekemans B, de Nolf W, Janssens K, Fiore S, Falkenberg G (2008).
Keywords: H3 Book chapter; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Pigment identification by scanning μ-XRF/μ-XRD”. de Nolf W, Vekemans B, Janssens K, van der Snickt G, Falkenberg G (2007).
Keywords: H3 Book chapter; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Reexamination of U and Pu in particles from Thule and Palomares by μ-XRD”. Lind O-C, Salbu B, de Nolf W, Jaroszewicz J, Janssens K, Falkenberg G page 1297 (2008).
Keywords: H3 Book chapter; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“Study of the degradation on historical documents induced by iron gall ink by means of scanning μ-XRF/μ-XRD”. de Nolf W, Janssens K, Rouchon V, Falkenberg G (2007).
Keywords: H3 Book chapter; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
|
“XRDUA : crystalline phase distribution maps by two-dimensional scanning and tomographic (micro) X-ray powder diffraction”. de Nolf W, Vanmeert F, Janssens K, Journal of applied crystallography 47, 1107 (2014). http://doi.org/10.1107/S1600576714008218
Abstract: Imaging of crystalline phase distributions in heterogeneous materials, either plane projected or in virtual cross sections of the object under investigation, can be achieved by scanning X-ray powder diffraction employing X-ray micro beams and X-ray-sensitive area detectors. Software exists to convert the two-dimensional powder diffraction patterns that are recorded by these detectors to one-dimensional diffractograms, which may be analysed by the broad variety of powder diffraction software developed by the crystallography community. However, employing these tools for the construction of crystalline phase distribution maps proves to be very difficult, especially when employing micro-focused X-ray beams, as most diffraction software tools have mainly been developed having structure solution in mind and are not suitable for phase imaging purposes. XRDUA has been developed to facilitate the execution of the complete sequence of data reduction and interpretation steps required to convert large sequences of powder diffraction patterns into a limited set of crystalline phase maps in an integrated fashion.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Times cited: 62
DOI: 10.1107/S1600576714008218
|
“Non-invasive and non-destructive examination of artists’ pigments, paints and paintings by means of X-ray imaging methods”. Vanmeert F, De Meyer S, Gestels A, Clerici EA, Deleu N, Legrand S, Van Espen P, Van der Snickt G, Alfeld M, Dik J, Monico L, De Nolf W, Cotte M, Gonzalez V, Saverwyns S, Depuydt-Elbaum L, Janssens K page 317 (2022).
Abstract: Recent studies in which X-ray beams of (sub)micrometre to millimetre dimensions have been used for non-destructive analysis and characterization of pigments, minute paint samples and/or entire paintings from fifteenth to twentieth century artists are discussed. The overview presented encompasses the use of laboratory and synchrotron radiation-based instrumentation and deals with the use of several variants of X-ray fluorescence (XRF) as a method of elemental analysis and imaging as well as with the combined use with X-ray diffraction (XRD). Microscopic XRF (μ-XRF) is a variant of the XRF method able to visualize the elemental distribution of key elements, mostly metals, on the scale from 1 μm to 100 μm present inside multi-layered micro samples taken from paintings. In the context of the characterization of artists’ pigments subjected to natural degradation, in many cases the use of methods limited to elemental analysis or imaging does not suffice to elucidate the chemical transformations that have taken place. However, at synchrotron facilities, combinations of μ-XRF with related methods such as μ-XAS (microscopic X-ray absorption spectroscopy) and μ-XRD have proven themselves to be very suitable for such studies. Since microscopic investigation of a relatively limited number of minute paint samples may not yield representative information about the complete artefact they were taken from, several methods for macroscopic, non-invasive imaging have recently been developed. Combined macroscopic XRF/XRD scanning is able to provide a fairly complete overview of the inorganic pigments employed to create a work of art, to answer questions about ongoing degradation phenomena and about its authenticity. As such these newly developed non-invasive and highly specific imaging methods are of interest for many cultural heritage stakeholders.
Keywords: H1 Book chapter; Art; Antwerp Cultural Heritage Sciences (ARCHES); Antwerp X-ray Imaging and Spectroscopy (AXIS)
DOI: 10.1007/978-3-030-86865-9_11
|
“Stable Rh particles in hydrotalcite-derived catalysts coated on FeCrAlloy foams by electrosynthesis”. Benito P, Nuyts G, Monti M, de Nolf W, Fornasari G, Janssens K, Scavetta E, Vaccari A, Applied catalysis : B : environmental 179, 321 (2015). http://doi.org/10.1016/J.APCATB.2015.05.035
Abstract: Rh-based structured catalysts for the Catalytic Partial Oxidation of CH4 to syngas were prepared by electrosynthesis of Rh/Mg/Al hydrotalcite-type compounds on FeCrAlloy foams and calcination. The effects of Rh content, total metal concentration, and partial replacement of Mg2+ by Ni2+ in the electrolytic solution on coating thickness, Rh speciation, metallic particle size, and catalytic activity were investigated by SEM/EDS, mu-XRF/XANES and tests under diluted and concentrated reaction conditions. The amount of Rh species, present as Mg (RhxAl1-x)(2)O-4, depended on the thickness of the electrosynthesised layer as well as the Rh particle size and dispersion. Smaller and more dispersed particles were obtained by decreasing the Rh concentration in the electrolytic solution from Rh/Mg/Al=11/70/19 to 5/70/25 and 2/70/28 atomic ratio% (a.r.%) and in thinner rather than thicker layers. Despite the improvement in metallic particles features, the CH4 conversion was negatively affected by the low amount of active sites in the coating, the high metal support interaction and possibly the oxidation of metallic particles and carbon formation. A larger amount of solid containing well dispersed Rh particles was deposited by increasing the total metal concentration from 0.03 M to 0.06 M with the Rh/Mg/Al=5/70/25 a.r.%, and the catalytic performances were enhanced. The partial replacement of Mg2+ by Ni2+ gave rise to a very active bimetallic Rh/Ni catalyst, CH4 conversion and selectivity to syngas were above 90%, however, it slightly deactivated with time-on-stream. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 9.446
Times cited: 14
DOI: 10.1016/J.APCATB.2015.05.035
|
“Recent trends in quantitative aspects of microscopic X-ray fluorescence analysis”. Janssens K, de Nolf W, van der Snickt G, Vincze L, Vekemans B, Terzano R, Brenker FE, Trends in analytical chemistry 29, 464 (2010). http://doi.org/10.1016/J.TRAC.2010.03.003
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 8.442
Times cited: 48
DOI: 10.1016/J.TRAC.2010.03.003
|
“The use of synchrotron radiation for the characterization of artists' pigments and paintings”. Janssens K, Alfeld M, van der Snickt G, de Nolf W, Vanmeert F, Radepont M, Monico L, et al, Annual review of analytical chemistry 6, 399 (2013). http://doi.org/10.1146/ANNUREV-ANCHEM-062012-092702
Abstract: We review methods and recent studies in which macroscopic to (sub)microscopic X-ray beams were used for nondestructive analysis and characterization of pigments, paint microsamples, and/or entire paintings. We discuss the use of portable laboratory- and synchrotron-based instrumentation and describe several variants of X-ray fluorescence (XRF) analysis used for elemental analysis and imaging and combined with X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS). Macroscopic and microscopic (μ-)XRF variants of this method are suitable for visualizing the elemental distribution of key elements in paint multilayers. Technical innovations such as multielement, large-area XRF detectors have enabled such developments. The use of methods limited to elemental analysis or imaging usually is not sufficient to elucidate the chemical transformations that take place during natural pigment alteration processes. However, synchrotron-based combinations of μ-XRF, μ-XAS, and μ-XRD are suitable for such studies.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 7.435
Times cited: 46
DOI: 10.1146/ANNUREV-ANCHEM-062012-092702
|
“Combined use of synchrotron radiation based micro-X-ray fluorescence, micro-X-ray diffraction, micro-X-ray absorption near-edge, and micro-fourier transform infrared spectroscopies for revealing an alternative degradation pathway of the pigment cadmium yellow in a painting by Van Gogh”. van der Snickt G, Janssens K, Dik J, de Nolf W, Vanmeert F, Jaroszewicz J, Cotte M, Falkenberg G, Van der Loeff L, Analytical chemistry 84, 10221 (2012). http://doi.org/10.1021/AC3015627
Abstract: Over the past years a number of studies have described the instability of the pigment cadmium yellow (CdS). In a previous paper we have shown how cadmium sulfide on paintings by James Ensor oxidizes to CdSO4 center dot H2O. The degradation process gives rise to the fading of the bright yellow color and the formation of disfiguring white crystals that are present on the paint surface in approximately 50 mu m sized globular agglomerations. Here, we study cadmium yellow in the painting “Flowers in a blue vase” by Vincent van Gogh. This painting differs from the Ensor case in the fact that (a) a varnish was superimposed onto the degraded paint surface and (b) the CdS paint area is entirely covered with an opaque crust. The latter obscures the yellow color completely and thus presents a seemingly more advanced state of degradation. Analysis of a cross-sectioned and a crushed sample by combining scanning microscopic X-ray diffraction (mu-XRD), microscopic X-ray absorption near-edge spectroscopy (mu-XANES), microscopic X-ray fluorescence (mu-XRF) based chemical state mapping and scanning microscopic Fourier transform infrared (mu-FT-IR) spectrometry allowed unravelling the complex alteration pathway. Although no crystalline CdSO4 compounds were identified on the Van Gogh paint samples, we conclude that the observed degradation was initially caused by oxidation of the original CdS pigment, similar as for the previous Ensor case. However, due to the presence of an overlying varnish containing lead-based driers and oxalate ions, secondary reactions took place. In particular, it appears that upon the photoinduced oxidation of its sulfidic counterion, the Cd2+ ions reprecipitated at the paint/varnish interface after having formed a complex with oxalate ions that themselves are considered to be degradation products of the resin and/or oil in the varnish. The SO42- anions, for their part, found a suitable reaction partner in Pb2+ ions stemming from a dissolved lead-based siccative that was added to the varnish to promote its drying. The resulting opaque anglesite compound in the varnish, in combination with the underlying CdC2O4 layer at the paint/varnish interface, account for the orange-gray crust that is disfiguring the painting on a macroscopic level. In this way, the results presented in this paper demonstrate how, through a judicious combined use of several microanalytical methods with speciation capabilities, many new insights can be obtained from two minute, but highly complex and heterogeneous paint samples.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 59
DOI: 10.1021/AC3015627
|
“Degradation process of lead chromate in paintings by Vincent van Gogh studied by means of synchrotron X-ray spectromicroscopy and related methods : 1 : artificially aged model samples”. Monico L, van der Snickt G, Janssens K, de Nolf W, Miliani C, Verbeeck J, Tian H, Tan H, Dik J, Radepont M, Cotte M, Analytical chemistry 83, 1214 (2011). http://doi.org/10.1021/ac102424h
Abstract: On several paintings by artists of the end of the 19th century and the beginning of the 20th Century a darkening of the original yellow areas, painted with the chrome yellow pigment (PbCrO4, PbCrO4·xPbSO4, or PbCrO4·xPbO) is observed. The most famous of these are the various Sunflowers paintings Vincent van Gogh made during his career. In the first part of this work, we attempt to elucidate the degradation process of chrome yellow by studying artificially aged model samples. In view of the very thin (1−3 μm) alteration layers that are formed, high lateral resolution spectroscopic methods such as microscopic X-ray absorption near edge (μ-XANES), X-ray fluorescence spectrometry (μ-XRF), and electron energy loss spectrometry (EELS) were employed. Some of these use synchrotron radiation (SR). Additionally, microscopic SR X-ray diffraction (SR μ-XRD), μ-Raman, and mid-FTIR spectroscopy were employed to completely characterize the samples. The formation of Cr(III) compounds at the surface of the chrome yellow paint layers is particularly observed in one aged model sample taken from a historic paint tube (ca. 1914). About two-thirds of the chromium that is present at the surface has reduced from the hexavalent to the trivalent state. The EELS and μ-XANES spectra are consistent with the presence of Cr2O3·2H2O (viridian). Moreover, as demonstrated by μ-XANES, the presence of another Cr(III) compound, such as either Cr2(SO4)3·H2O or (CH3CO2)7Cr3(OH)2 [chromium(III) acetate hydroxide], is likely.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 113
DOI: 10.1021/ac102424h
|
“Degradation process of lead chromate in paintings by Vincent van Gogh studied by means of synchrotron X-ray spectromicroscopy and related methods : 2 : original paint layer samples”. Monico L, van der Snickt G, Janssens K, de Nolf W, Miliani C, Dik J, Radepont M, Hendriks E, Geldof M, Cotte M, Analytical chemistry 83, 1224 (2011). http://doi.org/10.1021/AC1025122
Abstract: The darkening of the original yellow areas painted with the chrome yellow pigment (PbCrO4, PbCrO4·xPbSO4, or PbCrO4·xPbO) is a phenomenon widely observed on several paintings by Vincent van Gogh, such as the famous different versions of Sunflowers. During our previous investigations on artificially aged model samples of lead chromate, we established for the first time that darkening of chrome yellow is caused by reduction of PbCrO4 to Cr2O3·2H2O (viridian green), likely accompanied by the presence of another Cr(III) compound, such as either Cr2(SO4)3·H2O or (CH3CO2)7Cr3(OH)2 [chromium(III) acetate hydroxide]. In the second part of this work, in order to demonstrate that this reduction phenomenon effectively takes place in real paintings, we study original paint samples from two paintings of V. van Gogh. As with the model samples, in view of the thin superficial alteration layers that are present, high lateral resolution spectroscopic methods that make use of synchrotron radiation (SR), such as microscopic X-ray absorption near edge (μ-XANES) and X-ray fluorescence spectrometry (μ-XRF) were employed. Additionally, μ-Raman and mid-FTIR analyses were carried out to completely characterize the samples. On both paint microsamples, the local presence of reduced Cr was demonstrated by means of μ-XANES point measurements. The presence of Cr(III) was revealed in specific areas, in some cases correlated to the presence of Ba(sulfate) and/or to that of aluminum silicate compounds.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 84
DOI: 10.1021/AC1025122
|
“Room-temperature study of iron gall ink impregnated paper degradation under various oxygen and humidity conditions : time-dependent monitoring by viscosity and X-ray absorption near-edge spectrometry measurements”. Rouchon V, Duranton M, Burgaud C, Pellizzi E, Lavédrine B, Janssens K, de Nolf W, Nuyts G, Vanmeert F, Hellemans K, Analytical chemistry 83, 2589 (2011). http://doi.org/10.1021/AC1029242
Abstract: Many western manuscripts were written using iron gall inks. These inks can damage the paper via two major mechanisms: (a) acid hydrolysis, enhanced by humidity, and (b) oxidative depolymerization provoked by the presence of oxygen and free iron(II) ions. The degradation of unsized Whatman paper impregnated with different combinations of iron sulfate, gallic acid, and gum arabic was studied at room temperature in order to assess the relative importance of each mechanism. The samples were stored in various environments including a dry and/or an oxygen-free atmosphere. The cellulose depolymerization was monitored by viscometry and related to changes in the oxidation state of iron, determined by X-ray absorption near-edge spectrometry. The results indicate that residual amounts of oxygen (less than 0.1%) promote cellulose depolymerization, whereas the level of relative humidity has no impact. The cellulose depolymerization also appears closely correlated to oxidative mechanisms. Regarding the oxidation of iron, it only occurs in the simultaneous presence of oxygen and moisture, suggesting the occurrence of rustlike oxidative mechanisms. Finally, the presence of gallic acid has a strong influence, which is only partially explained by its capacity to reduce iron(III) to iron(II).
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 28
DOI: 10.1021/AC1029242
|
“Characterization of a degraded cadmium yellow (CdS) pigment in an oil painting by means of synchrotron radiation based X-ray techniques”. van der Snickt G, Dik J, Cotte M, Janssens K, Jaroszewicz J, de Nolf W, Groenewegen J, van der Loeff L, Analytical chemistry 81, 2600 (2009). http://doi.org/10.1021/AC802518Z
Abstract: On several paintings of James Ensor (1860−1949), a gradual fading of originally bright yellow areas, painted with the pigment cadmium yellow (CdS), is observed. Additionally, in some areas exposed to light, the formation of small white-colored globules on top of the original paint surface is observed. In this paper the chemical transformation leading to the color change and to the formation of the globules is elucidated. Microscopic X-ray absorption near-edge spectroscopy (ì-XANES) experiments show that sulfur, originally present in sulfidic form (S2−), is oxidized during the transformation to the sulfate form (S6+). Upon formation (at or immediately below the surface), the highly soluble cadmium sulfate is assumed to be transported to the surface in solution and reprecipitates there, forming the whitish globules. The presence of cadmium sulfate (CdSO4·2H2O) and ammonium cadmium sulfate [(NH4)2Cd(SO4)2] at the surface is confirmed by microscopic X-ray diffraction measurements, where the latter salt is suspected to result from a secondary reaction of cadmium sulfate with ammonia. Measurements performed on cross sections reveal that the oxidation front has penetrated into the yellow paint down to ca. 1−2 ìm. The morphology and elemental distribution of the paint and degradation product were examined by means of scanning electron microscopy equipped with an energy-dispersive spectrometer (SEM-EDS) and synchrotron radiation based micro-X-ray fluorescence spectrometry (SR ì-XRF). In addition, ultraviolet-induced visible fluorescence photography (UIVFP) revealed itself to be a straightforward technique for documenting the occurrence of this specific kind of degradation on a macroscale by painting conservators.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 91
DOI: 10.1021/AC802518Z
|
“Macroscopic X-ray powder diffraction scanning, a new method for highly selective chemical imaging of works of art : instrument optimization”. Vanmeert F, de Nolf W, De Meyer S, Dik J, Janssens K, Analytical chemistry 90, 6436 (2018). http://doi.org/10.1021/ACS.ANALCHEM.8B00240
Abstract: In the past decade macroscopic X-ray fluorescence imaging (MA-XRF) has become established as a method for the noninvasive investigation of flat painted surfaces, yielding large scale elemental maps. MA-XRF is limited by a lack of specificity, only allowing for indirect pigment identification based on the simultaneous presence of chemical elements. The high specificity of X-ray powder diffraction (XRPD) mapping is already being exploited at synchrotron facilities for investigations at the (sub)microscopic scale, but the technique has not yet been employed using lab sources. In this paper we present the development of a novel MA-XRPD/XRF instrument based on a laboratory X-ray source. Several combinations of X-ray sources and area detectors are evaluated in terms of their spatial and angular resolution and their sensitivity. The highly specific imaging capability of the combined MA-XRPD/XRF instrument is demonstrated on a 15th/16th century illuminated manuscript directly revealing the distribution of a large number of inorganic pigments, including the uncommon yellow pigment massicot (o-PbO). The case study illustrates the wealth of new mapping information that can be obtained in a noninvasive manner using the laboratory MA-XRPD/XRF instrument.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 6.32
Times cited: 11
DOI: 10.1021/ACS.ANALCHEM.8B00240
|