Author |
Penders, A.G.; Konstantinović, M.J.; Van Renterghem, W.; Bosch, R.-W.; Schryvers, D.; Somville, F. |
|
|
Title |
Characterization of IASCC crack tips extracted from neutron-irradiated flux thimble tube specimens in view of a probabilistic fracture model |
Type |
A1 Journal article |
|
Year |
2022 |
Publication |
Journal of nuclear materials |
Abbreviated Journal |
J Nucl Mater |
|
|
Volume |
571 |
Issue |
|
Pages |
154015-154016 |
|
|
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
This study reports the properties of irradiation assisted stress corrosion crack tips extracted by means of focused-ion beam from 60 to 80 dpa neutron-irradiated O-ring specimens tested under straining conditions under a pressurized-water reactor environment. Various crack tip morphologies and surrounding deformation features were analyzed as a function of applied stress, surface oxidation state and loading form – constant versus cyclic. All investigated cracks exhibit grain boundary oxidation in front of the crack tip, with the extent of oxidation being proportional to applied stress. These findings clearly demonstrate that, under the subcritical crack propagation regime, the grain boundary oxide grows faster than the crack. On the other hand, crack tips appertaining to specimens with removed oxide layer at the outer surface show comparatively less oxidation at the crack tip, which could indicate towards crack initiation from regions that exemplify lower stress, such as the O-ring inner surface. Cyclic loading is found to have a more pronounced effect on the crack tip microstructure, demonstrating increased deformation twinning and -martensitic transformation, which signifies towards an increased susceptibility to intergranular failure. Still, the extent of crack tip grain boundary oxidation in this case agrees well with expected values for maximum stress applied during cyclic loading. All results are interpreted based on the probabilistic subcritical crack propagation mechanism and provide strong support to a stress-driven internal oxidation model. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
|
Editor |
|
|
|
Language |
|
Wos |
000872389200009 |
Publication Date |
2022-09-06 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0022-3115 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
3.1 |
Times cited |
|
Open Access |
OpenAccess |
|
|
Notes |
|
Approved |
Most recent IF: 3.1 |
|
|
Call Number |
UA @ admin @ c:irua:190375 |
Serial |
7135 |
|
Permanent link to this record |
|
|
|
|
Author |
Penders, A.; Konstantinovic, M.J.; Van Renterghem, W.; Bosch, R.W.; Schryvers, D. |
|
|
Title |
TEM investigation of SCC crack tips in high Si stainless steel tapered specimens |
Type |
A1 Journal article |
|
Year |
2021 |
Publication |
Corrosion Engineering Science And Technology |
Abbreviated Journal |
Corros Eng Sci Techn |
|
|
Volume |
|
Issue |
|
Pages |
|
|
|
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
The stress corrosion cracking (SCC) mechanism is investigated in high Si duplex stainless steel in a simulated PWR environment based on TEM analysis of FIB-extracted SCC crack tips. The microstructural investigation in the near vicinity of SCC crack tips illustrates a strain-rate dependence in SCC mechanisms. Detailed analysis of the crack tip morphology, that includes crack tip oxidation and surrounding deformation field, indicates the existence of an interplay between corrosion- and deformation-driven failure as a function of the strain rate. Slow strain-rate crack tips exhibit a narrow cleavage failure which can be linked to the film-induced failure mechanism, while rounded shaped crack tips for faster strain rates could be related to the strain-induced failure. As a result, two nominal strain-rate-dependent failure regimes dominated either by corrosion or deformation-driven cracking mechanisms can be distinguished. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
|
Editor |
|
|
|
Language |
|
Wos |
000695956400001 |
Publication Date |
2021-09-14 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
1478-422x |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
0.879 |
Times cited |
|
Open Access |
OpenAccess |
|
|
Notes |
|
Approved |
Most recent IF: 0.879 |
|
|
Call Number |
UA @ admin @ c:irua:181533 |
Serial |
6892 |
|
Permanent link to this record |
|
|
|
|
Author |
Penders, A.G.; Konstantinovic, M.J.; Yang, T.; Bosch, R.-w.; Schryvers, D.; Somville, F. |
|
|
Title |
Microstructural investigation of IASCC crack tips extracted from thimble tube O-ring specimens |
Type |
A1 Journal article |
|
Year |
2022 |
Publication |
Journal of nuclear materials |
Abbreviated Journal |
J Nucl Mater |
|
|
Volume |
565 |
Issue |
|
Pages |
153727-16 |
|
|
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
The microstructural features of intergranular irradiation-assisted stress corrosion crack tips from a redeemed neutron-irradiated flux thimble tube (60 dpa) have been investigated using focused-ion beam analysis and (scanning) transmission electron microscopy. The current work presents a close examination of the deformation field and oxide assembly associated with intergranular cracking, in addition to the analysis of radiation-induced segregation at leading grain boundaries. Evidence of stress induced martensitic transformation extending from the crack tips is presented. Intergranular crack arrest is demonstrated on the account of the external tensile stress orientation, and as a consequence of MnS inclusion particles segregating close to the fractured grain boundary. Exclusive observations of grain boundary oxidation prior to the cracking are presented, which is in full-agreement with the internal oxidation model.(c) 2022 Elsevier B.V. All rights reserved. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
|
Editor |
|
|
|
Language |
|
Wos |
000799256300004 |
Publication Date |
2022-04-11 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0022-3115 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
3.1 |
Times cited |
|
Open Access |
OpenAccess |
|
|
Notes |
|
Approved |
Most recent IF: 3.1 |
|
|
Call Number |
UA @ admin @ c:irua:188609 |
Serial |
7086 |
|
Permanent link to this record |
|
|
|
|
Author |
Penders, A.; Konstantinovic, M.J.; Bosch, R.W.; Schryvers, D. |
|
|
Title |
Crack initiation in tapered high Si stainless steel specimens : stress threshold analyses |
Type |
A1 Journal article |
|
Year |
2020 |
Publication |
Corrosion Engineering Science And Technology |
Abbreviated Journal |
Corros Eng Sci Techn |
|
|
Volume |
|
Issue |
|
Pages |
1-8 |
|
|
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
Tapered specimens were used for an accelerated test technique to study the crack initiation of high Si stainless steel by means of constant elongation rate tensile testing in a simulated pressurised water reactor environment. Detailed crack density distributions were obtained by applying an advanced crack detection algorithm on iteratively displaced scanning electron microscopy pictures featuring stress corrosion cracks along the specimen's gauge length. By means of finite-element analysis, prominent peaks in the crack density graphs are demonstrated to be related to stress relief and stress build-up during the crack initiation phase. Intrinsic scatter related to the crack detection suggests that stress corrosion cracking is independent of the strain-rate for strain-rates lower than 10(-6 )s(-1). Based on the extrapolation to constant load conditions, the critical threshold value for the duplex high Si stainless steel is estimated to be around 580 MPa. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
|
Editor |
|
|
|
Language |
|
Wos |
000549651600001 |
Publication Date |
2020-06-30 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
1478-422x |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
1.8 |
Times cited |
1 |
Open Access |
Not_Open_Access |
|
|
Notes |
; We would like to acknowledge ENGIE Electrabel for the financial support of this work under the contract number BSUEZ5500. ; |
Approved |
Most recent IF: 1.8; 2020 IF: 0.879 |
|
|
Call Number |
UA @ admin @ c:irua:171292 |
Serial |
6478 |
|
Permanent link to this record |
|
|
|
|
Author |
Penders, A.G. |
|
|
Title |
Microstructural investigation of irradiation assisted stress corrosion cracking mechanisms based on focused ion beam analysis of tested and industrial specimens |
Type |
Doctoral thesis |
|
Year |
2022 |
Publication |
|
Abbreviated Journal |
|
|
|
Volume |
|
Issue |
|
Pages |
xxxviii, 226 p. |
|
|
Keywords |
Doctoral thesis; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
Irradiation assisted stress corrosion cracking (IASCC) is an intergranular cracking effect which can occur in heavily irradiated internal structural components of nuclear reactor cores. It is a complex phenomenon which is not yet fully understood because it occurs through an interplay of several material degradation processes. The factors that influence IASCC susceptibility include irradiation damage (neutrons and other irradiation particles stemming from the nuclear fission reaction), the operating temperature of the nuclear reactor, water corrosion, operating stresses, and the composition of materials susceptible to IASCC. Such materials are typically fabricated from austenitic stainless steels because of their relatively high strength, ductility, and fracture toughness. However, besides excellent metallurgical and corrosion resistant qualities, the operating conditions may still cause severe material degradation and component failure, which is extremely important for nuclear power plant safety and lifetime managements. Despite much accumulated data in the literature, both crack initiation and crack propagation mechanisms still need to be further elucidated. To that end, a probabilistic fracture model entitled the subcritical crack propagation (SCP) was recently developed, which assumes that the oxidized part of stainless steel in front of the crack plays an essential role in the crack initiation and crack propagation in sample failures. Still, despite a very good agreement with experimental observations, the SCP model but also other contemporary models favoured within the literature, require further experimental verification to what concerns the investigation of (IA)SCC. To that end, the main objective of this doctorate was to utilize experimental instrumentations like SEM, FIB-SEM and (S)TEM to conduct the investigation of the crack initiation and propagation processes in both tested and industrial specimens. Some of the investigated materials were retrieved within a nuclear reactor and are thus considered as unique test material to investigate the material degradation processes relevant for cracking. Other specimens were tailor-made to simulate the cracking processes of irradiated materials in otherwise un-irradiated materials. The newly acquired experimental results in this doctorate help rationalize existing models and methodologies used in the literature to analyse the IASCC failures of structural materials of reactor components. These results also facilitate in the development of predictive methodologies and mitigation strategies towards IASCC cracking and provide more information on IASCC from a microstructural perspective. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
|
Editor |
|
|
|
Language |
|
Wos |
|
Publication Date |
|
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
|
ISBN |
|
Additional Links |
UA library record |
|
|
Impact Factor |
|
Times cited |
|
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: NA |
|
|
Call Number |
UA @ admin @ c:irua:192431 |
Serial |
7323 |
|
Permanent link to this record |