“Ba2Y(Nb/Ta)O6–Doped YBCO Films on Biaxially Textured Ni–5at.% W Substrates”. Sieger M, Pahlke P, Hanisch J, Sparing M, Bianchetti M, MacManus-Driscoll J, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Nast R, Schultz L, Holzapfel B, Huhne R, IEEE transactions on applied superconductivity 26, 1 (2016). http://doi.org/10.1109/TASC.2016.2539254
Abstract: The incorporation of nanoscaled pinning centers in superconducting YBa2Cu3O7-d (YBCO) films is one of the core topics to enhance the critical current density Jc(B, Q) of coated conductors. The mixed double-perovskite Ba2Y(Nb/Ta)O6 (BYNTO) can be grown in nanosized columns parallel the YBCO c-axis and in step-like patterns, making it customizable to meet specific working conditions (T, B, Q). We compare a 1.6 μm thick film of pure YBCO and a similar film with additional 5 mol% of BYNTO, grown by pulsed laser deposition with a growth rate of 1.6 nm/s on buffered biaxially textured Ni-5at.% W tape. Our doped sample shows nanosized BYNTO columns parallel cYBCO and plates in the ab-plane containing Y, Nb and Ta. An improved homogeneity of the critical current density Jc over the sample was evaluated from trapped field profiles measured with a scanning Hall probe microscope. The mean Jc in rolling direction of the tape is 1.8 MA/cm² (77 K, self-field) and doubles the value of the undoped sample. Angular dependent measurements of the critical current density, Jc(Q), show a decreased anisotropy of the doped film for various magnetic fields at 77 K as well as 64 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 6
DOI: 10.1109/TASC.2016.2539254
|
|
|
“Synthesis of aluminum-containing hierarchical mesoporous materials with columnar mesopore ordering by evaporation induced self assembly”. Kurttepeli M, Locus R, Verboekend D, de Clippel F, Breynaert E, Martens J, Sels B, Bals S, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 234, 186 (2016). http://doi.org/10.1016/J.MICROMESO.2016.07.002
Abstract: The incorporation of aluminum into the silica columns of hierarchical mesoporous materials (HMMs) was studied. The HMMs were synthesized by a combination of hard and soft templating methods, forming mesoporous SBA-15-type silica columns inside the pores of anodic aluminum oxide membranes via evaporation induced self-assembly (EISA). By adding Al-isopropoxide to the EISA-mixture a full tetrahedral incorporation of Al and thus the creation of acid sites was achieved, which was proved by nuclear magnetic resonance spectroscopy. Electron microscopy showed that the use of Al-isopropoxide as an Al source for the HMMs led to a change in the mesopore ordering of silica material from circular hexagonal (donut-like) to columnar hexagonal and a 37% increase in specific surface (BET surface). These results were confirmed by a combination of nitrogen physisorption and small-angle X-ray scattering experiments and can be attributed to a swelling of the P123 micelles with isopropanol. The columnar mesopore ordering of silica is advantageous towards the pore accessibility and therefore preferential for many possible applications including catalysis and adsorption on the acid tetrahedral Al-sites. (C) 2016 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 5
DOI: 10.1016/J.MICROMESO.2016.07.002
|
|
|
“KSm(MoO4)2, an incommensurately modulated and partially disordered scheelite-like structure”. Arakcheeva A, Pattison P, Chapuis G, Rossell M, Filaretov A, Morozov V, Van Tendeloo G, Acta crystallographica: section B: structural science 64, 160 (2008). http://doi.org/10.1107/S0108768108001870
Abstract: The incommensurately modulated scheelite-like KSm( MoO4)(2) structure has been refined in the monoclinic superspace group I2/b(alpha beta 0)00 by the Rietveld method on the basis of synchrotron radiation powder diffraction data. The systematic broadening of satellite reflections has been accounted for by applying anisotropic microstrain line-broadening. The microstructure has been studied by transmission electron microscopy (TEM). The partial disorder of the K and Sm cations in the A position is best approximated by a combination of harmonic and complex crenel functions with (0.952Sm + 0.048K) and (0.952K + 0.048Sm) atomic domains. This combination yields a compositional wave distribution from {KMoO4} to {SmMoO4} observed in the ab structure projection along q. The specific features of KSm(MoO4)(2) and degree of the A-cation ordering are discussed in comparison with the previously reported structure of KNd(MoO4)(2).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 23
DOI: 10.1107/S0108768108001870
|
|
|
“Encapsulation of Noble Metal Nanoparticles through Seeded Emulsion Polymerization as Highly Stable Plasmonic Systems”. Scarabelli L, Schumacher M, Jimenez de Aberasturi D, Merkl J‐P, Henriksen‐Lacey M, Milagres de Oliveira T, Janschel M, Schmidtke C, Bals S, Weller H, Liz‐Marzán LM, Advanced functional materials 29, 1809071 (2019). http://doi.org/10.1002/adfm.201809071
Abstract: The implementation of plasmonic nanoparticles in vivo remains hindered by important limitations such as biocompatibility, solubility in biological fluids, and physiological stability. A general and versatile protocol is presented, based on seeded emulsion polymerization, for the controlled encapsulation of gold and silver nanoparticles. This procedure enables the encapsulation of single nanoparticles as well as nanoparticle clusters inside a protecting polymer shell. Specifically, the efficient coating of nanoparticles of both metals is demonstrated, with final dimensions ranging between 50 and 200 nm, i.e., sizes of interest for bio-applications. Such hybrid nanocomposites display extraordinary stability in high ionic strength and oxidizing environments, along with high cellular uptake, and low cytotoxicity. Overall, the prepared nanostructures are promising candidates for plasmonic applications under biologically relevant conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 19
DOI: 10.1002/adfm.201809071
|
|
|
“Decoupling the shape parameter to assess gold nanorod uptake by mammalian cells”. Kinnear C, Rodriguez-Lorenzo L, Clift MJD, Goris B, Bals S, Rothen B, Fink AS, Nanoscale 8, 16416 (2016). http://doi.org/10.1039/C6NR03543D
Abstract: The impact of nanoparticles (NPs) upon biological systems can be fundamentally associated with their physicochemical parameters. A further often-stated tenet is the importance of NP shape on rates of endocytosis. However, given the convoluted parameters concerning the NP-cell interaction, it is experimentally challenging to attribute any findings to shape alone. Herein we demonstrate that shape, below a certain limit, which is specific to nanomedicine, is not important for the endocytosis of spherocylinders by either epithelial or macrophage cells in vitro. Through a systematic approach, we reshaped a single batch of gold nanorods into different aspect ratios resulting in near-spheres and studied their cytotoxicity, (pro-)inflammatory status, and endocytosis/exocytosis. It was found that on a length scale of ~10-90 nm and at aspect ratios less than 5, NP shape has little impact upon their entry into either macrophages or epithelial cells. Conversely, nanorods with an aspect ratio above 5 were preferentially endocytosed by epithelial cells, whereas there was a lack of shape dependent uptake following exposure to macrophages in vitro. These findings have implications both in the understanding of nanoparticle reshaping mechanisms, as well as in the future rational design of nanomaterials for biomedical applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 23
DOI: 10.1039/C6NR03543D
|
|
|
“Single layer graphene controlled surface and bulk indentation plasticity in copper”. Bahrami F, Hammad M, Fivel M, Huet B, D'Haese C, Ding L, Nysten B, Idrissi H, Raskin JP, Pardoen T, International Journal Of Plasticity 138, 102936 (2021). http://doi.org/10.1016/J.IJPLAS.2021.102936
Abstract: The impact of graphene reinforcement on the mechanical properties of metals has been a subject of intense investigation over the last decade in surface applications to mitigate the impact of tribological loadings or for strengthening purposes when dispersed into a bulk material. Here, the effect on the plastic indentation response of a single graphene layer grown on copper is analyzed for two configurations: one with graphene at the surface, the other with graphene sandwiched under a 100 nm thick copper cap layer. Nanoindentation under both displacement and load control conditions show both earlier and shorter pop-in excursions compared to systems without graphene. Atomic force microscopy reveals much smoother pile-ups with no slip traces in the presence of a surface graphene layer. The configuration with the intercalated graphene layer appears as an ideal elementary system to address bulk hardening mechanisms by indentation testing. Transmission electron microscopy (TEM) cross-sections below indents show more diffuse and homogeneous dislocation activity in the presence of graphene. 3D dislocation dynamics simulations allow unraveling of the origin of these 3D complex phenomena and prove that the collective dislocation mechanisms are dominantly controlled by the strong back stress caused by the graphene barrier. These results provide a quantitative understanding of the impact of graphene on dislocation mechanisms for both surface and bulk applications, but with an impact that is not as large as anticipated from other studies or general literature claims.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.702
DOI: 10.1016/J.IJPLAS.2021.102936
|
|
|
“Advanced electron microscopy for advanced materials”. Van Tendeloo G, Bals S, Van Aert S, Verbeeck J, van Dyck D, Advanced materials 24, 5655 (2012). http://doi.org/10.1002/adma.201202107
Abstract: The idea of this Review is to introduce newly developed possibilities of advanced electron microscopy to the materials science community. Over the last decade, electron microscopy has evolved into a full analytical tool, able to provide atomic scale information on the position, nature, and even the valency atoms. This information is classically obtained in two dimensions (2D), but can now also be obtained in 3D. We show examples of applications in the field of nanoparticles and interfaces.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 19.791
Times cited: 107
DOI: 10.1002/adma.201202107
|
|
|
“Effect of cation dopant radius on the hydrothermal stability of tetragonal zirconia: Grain boundary segregation and oxygen vacancy annihilation”. Zhang F, Batuk M, Hadermann J, Manfredi G, Mariën A, Vanmeensel K, Inokoshi M, Van Meerbeek B, Naert I, Vleugels J, Acta materialia 106, 48 (2016). http://doi.org/10.1016/j.actamat.2015.12.051
Abstract: The hydrothermal aging stability of 3Y-TZP-xM2O3 (M = La, Nd, Sc) was investigated as a function of 0.02–5 mol% M2O3 dopant content and correlated to the overall phase content, t-ZrO2 lattice parameters, grain size distribution, grain boundary chemistry and ionic conductivity.
The increased aging stability with increasing Sc2O3 content and the optimum content of 0.4–0.6 mol% Nd2O3 or 0.2–0.4 mol% La2O3, resulting in the highest aging resistance, could be directly related to the constituent phases and the lattice parameters of the remaining tetragonal zirconia.
At low M2O3 dopant contents ≤0.4 mol%, the different aging behavior of tetragonal zirconia was attributed to the defect structure of the zirconia grain boundary which was influenced by the dopant cation radius. It was observed that the grain boundary ionic resistivity and the aging resistance followed the same trend: La3+ > Nd3+ > Al3+ > Sc3+, proving that hydrothermal aging is driven by the diffusion of water-derived mobile species through the oxygen vacancies. Accordingly, we elucidated the underlying mechanism by which a larger trivalent cation segregating at the zirconia grain boundary resulted in a higher aging resistance.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 37
DOI: 10.1016/j.actamat.2015.12.051
|
|
|
“Attracting shallow donors : hydrogen passivation in (Al,Ga,In)-doped ZnO”. Matsubara M, Amini MN, Saniz R, Lamoen D, Partoens B, Physical review : B : condensed matter and materials physics 86, 165207 (2012). http://doi.org/10.1103/PhysRevB.86.165207
Abstract: The hydrogen interstitial and the substitutional AlZn, GaZn, and InZn are all shallow donors in ZnO and lead to n-type conductivity. Although shallow donors are expected to repel each other, we show by first-principles calculations that in ZnO these shallow donor impurities attract and form a complex, leading to a donor level deep in the band gap. This puts a limit on the n-type conductivity of (Al,Ga,In)-doped ZnO in the presence of hydrogen.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 7
DOI: 10.1103/PhysRevB.86.165207
|
|
|
“Exploring the role of graphene oxide as a co-catalyst in the CZTS photocathodes for improved photoelectrochemical properties”. Vishwakarma M, Batra Y, Hadermann J, Singh A, Ghosh A, Mehta BR, ACS applied energy materials 5, 7538 (2022). http://doi.org/10.1021/ACSAEM.2C01011
Abstract: The hydrogen evolution properties of CZTS heterostructure photocathodes are reported with graphene oxide (GO) as a co-catalyst layer coated by a drop-cast method and an Al2O3 protection layer fabricated using atomic layer deposition. In the CZTS absorber, a minor deviation from stoichiometry across the cross section of the thin film results in nanoscale growth of spurious phases, but the kesterite phase remains the dominant phase. We have investigated the band alignment parameters such as the band gap, work function, and Fermi level position that are crucial for making kesterite-based heterostructure devices. The photocurrent density in the photocathode CZTS/CdS/ZnO is found to be improved to -4.71 mAmiddotcm(-2) at -0.40 V-RHE, which is 3 times that of the pure CZTS. This enhanced photoresponse can be attributed to faster carrier separation at p-n junction regions driven by upward band bending at CZTS grain boundaries and the ZnO layer. GO as a co-catalyst over the heterostructure photocathode significantly improves the photocurrent density to -6.14 mAmiddotcm(-2) at -0.40 V-RHE by effective charge migration in the CZTS/CdS/ZnO/GO configuration, but the onset potential shifts only after application of the Al2O3 protection layer. Significant photocurrents of -29 mAmiddotcm(-2) at -0.40 V-RHE and -8 mAmiddotcm(-2) at 0 V-RHE are observed, with an onset potential of 0.7 V-RHE in CZTS/CdS/ZnO/GO/Al2O3. The heterostructure configuration and the GO co-catalyst reduce the charge-transfer resistance, while the Al2O3 top layer provides a stable photocurrent for a prolonged time (similar to 16 h). The GO co-catalyst increases the flat band potential from 0.26 to 0.46 V-RHE in CZTS/CdS/ZnO/GO, which supports the bias-induced band bending at the electrolyte-electrode interface.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.4
DOI: 10.1021/ACSAEM.2C01011
|
|
|
“Controlled precipitation in a new Al-Mg-Sc alloy for enhanced corrosion behavior while maintaining the mechanical performance”. Krishnamurthy SC, Arseenko M, Kashiwar A, Dufour P, Marchal Y, Delahaye J, Idrissi H, Pardoen T, Mertens A, Simar A, Materials characterization 200, 112886 (2023). http://doi.org/10.1016/J.MATCHAR.2023.112886
Abstract: The hot working of 5xxx series alloys with Mg ≥3.5 wt% is a concern due to the precipitation of β (Al3Mg2) phase at grain boundaries favoring Inter Granular Corrosion (IGC). The mechanical and corrosion properties of a new 5028-H116 Al-Mg-Sc alloy under various β precipitates distribution is analyzed by imposing different cooling rates from the hot forming temperature (i.e. 325 °C). The mechanical properties are maintained regardless of the heat treatment. However, the different nucleation sites and volume fractions of β precipitates for different cooling rates critically affect IGC. Controlled furnace cooling after the 325 °C heat treatment is ideal in 5028-H116 alloy to reduce susceptibility to IGC after sensitization.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.7
DOI: 10.1016/J.MATCHAR.2023.112886
|
|
|
“Homojunction of oxygen and titanium vacancies and its interfacial n-p effect”. Wu S-M, Liu X-L, Lian X-L, Tian G, Janiak C, Zhang Y-X, Lu Y, Yu H-Z, Hu J, Wei H, Zhao H, Chang G-G, Van Tendeloo G, Wang L-Y, Yang X-Y, Su B-L, Advanced materials 30, 1802173 (2018). http://doi.org/10.1002/ADMA.201802173
Abstract: The homojunction of oxygen/metal vacancies and its interfacial n-p effect on the physiochemical properties are rarely reported. Interfacial n-p homojunctions of TiO2 are fabricated by directly decorating interfacial p-type titanium-defected TiO2 around n-type oxygen-defected TiO2 nanocrystals in amorphous-anatase homogeneous nanostructures. Experimental measurements and theoretical calculations on the cell lattice parameters show that the homojunction of oxygen and titanium vacancies changes the charge density of TiO2; a strong EPR signal caused by oxygen vacancies and an unreported strong titanium vacancies signal of 2D H-1 TQ-SQ MAS NMR are present. Amorphous-anatase TiO2 shows significant performance regarding the photogeneration current, photocatalysis, and energy storage, owing to interfacial n-type to p-type conductivity with high charge mobility and less structural confinement of amorphous clusters. A new homojunction of oxygen and titanium vacancies concept, characteristics, and mechanism are proposed at an atomic-/nanoscale to clarify the generation of oxygen vacancies and titanium vacancies as well as the interface electron transfer.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 39
DOI: 10.1002/ADMA.201802173
|
|
|
“Sub-nanometer free electrons with topological charge”. Schattschneider P, Stöger-Pollach M, Löffler S, Steiger-Thirsfeld A, Hell J, Verbeeck J, Ultramicroscopy 115, 21 (2012). http://doi.org/10.1016/j.ultramic.2012.01.010
Abstract: The holographic mask technique is used to create freely moving electrons with quantized angular momentum. With electron optical elements they can be focused to vortices with diameters below the nanometer range. The understanding of these vortex beams is important for many applications. Here, we produce electron vortex beams and compare them to a theory of electrons with topological charge. The experimental results show excellent agreement with simulations. As an immediate application, fundamental experimental parameters like spherical aberration and partial coherence are determined. (C) 2012 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 24
DOI: 10.1016/j.ultramic.2012.01.010
|
|
|
“Gas-phase loading of [Zn4O(btb)2] (MOF-177) with organometallic CVD-precursors: inclusion compounds of the type [LnM]a@MOF-177 and the formation of Cu and Pd nanoparticles inside MOF-177”. Müller M, Lebedev OI, Fischer RA, Journal of materials chemistry 18, 5274 (2008). http://doi.org/10.1039/b810989c
Abstract: The highly porous and desolvated (activated) coordination polymer [Zn4O(btb)2] (btb = benzene-1,3,5-tribenzoate; MOF-177) was loaded with the organometallic compounds [Cp2Fe], [Cp*2Zn], [Cu(OCHMeCH2NMe2)2], [CpCuL] (L = PMe3, CNtBu) and [CpPd(3-C3H5)] via solvent-free adsorption from the gas-phase. The inclusion compounds of the type [LnM]a@MOF-177, where [LnM] indicates the respective compound and the parameter a denotes the number of molecules per formula unit of the MOF-177, were characterised by elemental analysis, FT-IR, solid-state NMR spectroscopy and by powder X-ray diffraction (PXRD). Remarkably high effective loadings of up to 11 molecules [Cp2Fe] and 10 molecules [CpPd(3-C3H5)] per cavity were determined. The analytical data prove that the host lattice and the guest molecules interact only by weak van-der-Waals forces without any significant change of the framework or the chemical nature of the included molecules. Cu nanoparticles showing the typical surface plasmon resonance at 580 nm and Pd nanoparticles of about 2.6 nm in size were formed inside the cavities of MOF-177 by the thermally activated hydrogenolysis of the inclusion compounds [CpCuCNtBu]2@MOF-177 and by photolysis of [CpPd(3-C3H5)]10@MOF-177 in an inert atmosphere (Ar). PXRD, FT-IR and NMR studies revealed that the MOF-177 matrix remained unchanged during the decomposition process of the precursors. N2 adsorption studies of the obtained materials Cu@MOF-177 (e.g. 10.6 wt.% Cu, 2309 m2 g-1) and Pd@MOF-177 (e.g. 32.5 wt.%, 1063 m2 g-1) reveal high remaining specific surface areas (Langmuir model).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 65
DOI: 10.1039/b810989c
|
|
|
“Reducing electron beam damage through alternative STEM scanning strategies, Part I: Experimental findings”. Velazco A, Béché, A, Jannis D, Verbeeck J, Ultramicroscopy 232, 113398 (2022). http://doi.org/10.1016/j.ultramic.2021.113398
Abstract: The highly energetic electrons in a transmission electron microscope (TEM) can alter or even completely destroy the structure of samples before sufficient information can be obtained. This is especially problematic in the case of zeolites, organic and biological materials. As this effect depends on both the electron beam and the sample and can involve multiple damage pathways, its study remained difficult and is plagued with irreproducibility issues, circumstantial evidence, rumors, and a general lack of solid data. Here we take on the experimental challenge to investigate the role of the STEM scan pattern on the damage behavior of a commercially available zeolite sample with the clear aim to make our observations as reproducible as possible. We make use of a freely programmable scan engine that gives full control over the tempospatial distribution of the electron probe on the sample and we use its flexibility to obtain multiple repeated experiments under identical conditions comparing the difference in beam damage between a conventional raster scan pattern and a newly proposed interleaved scan pattern that provides exactly the same dose and dose rate and visits exactly the same scan points. We observe a significant difference in beam damage for both patterns with up to 11 % reduction in damage (measured from mass loss). These observations demonstrate without doubt that electron dose, dose rate and acceleration voltage are not the only parameters affecting beam damage in (S)TEM experiments and invite the community to rethink beam damage as an unavoidable consequence of applied electron dose.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.2
Times cited: 18
DOI: 10.1016/j.ultramic.2021.113398
|
|
|
“Atomic scale real-space mapping of holes in YBa2Cu3O6+δ”. N Gauquelin D G Hawthorn G A Sawatzky R X Liang D A Bonn W N Hardy &, GA Botton, Nature Communications 5, 4275 (2014). http://doi.org/10.1038/ncomms5275
Abstract: The high-temperature superconductor YBa2Cu3O6+δ consists of two main structural units—a bilayer of CuO2 planes that are central to superconductivity and a CuO2+δ chain layer. Although the functional role of the planes and chains has long been established, most probes integrate over both, which makes it difficult to distinguish the contribution of each. Here we use electron energy loss spectroscopy to directly resolve the plane and chain contributions to the electronic structure in YBa2Cu3O6 and YBa2Cu3O7. We directly probe the charge transfer of holes from the chains to the planes as a function of oxygen content, and show that the change in orbital occupation of Cu is large in the chain layer but modest in CuO2 planes, with holes in the planes doped primarily into the O 2p states. These results provide direct insight into the local electronic structure and charge transfers in this important high-temperature superconductor.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Times cited: 22
DOI: 10.1038/ncomms5275
|
|
|
“Dislocation-mediated relaxation in nanograined columnar palladium films revealed by on-chip time-resolved HRTEM testing”. Colla M-S, Amin-Ahmadi B, Idrissi H, Malet L, Godet S, Raskin J-P, Schryvers D, Pardoen T, Nature communications 6, 5922 (2015). http://doi.org/10.1038/ncomms6922
Abstract: The high-rate sensitivity of nanostructured metallic materials demonstrated in the recent literature is related to the predominance of thermally activated deformation mechanisms favoured by a large density of internal interfaces. Here we report time-resolved high-resolution electron transmission microscopy creep tests on thin nanograined films using on-chip nanomechanical testing. Tests are performed on palladium, which exhibited unexpectedly large creep rates at room temperature. Despite the small 30-nm grain size, relaxation is found to be mediated by dislocation mechanisms. The dislocations interact with the growth nanotwins present in the grains, leading to a loss of coherency of twin boundaries. The density of stored dislocations first increases with applied deformation, and then decreases with time to drive additional deformation while no grain boundary mechanism is observed. This fast relaxation constitutes a key issue in the development of various micro- and nanotechnologies such as palladium membranes for hydrogen applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 34
DOI: 10.1038/ncomms6922
|
|
|
“A 2a2a3c superstructure in hexagonal Ni1-xS : a study by means of electron-diffraction and HRTEM”. Lioutas CB, Manolikas C, Van Tendeloo G, van Landuyt J, Journal of crystal growth 126, 457 (1993). http://doi.org/10.1016/0022-0248(93)90051-W
Abstract: The high temperature phase of Ni1-xS has the NiAs-type structure. The coexistence of two superstructures, ''3a3a3c'' and ''2a2a3c'' with the basic phase is confirmed by means of electron diffraction. The 2a2a3c superstructure is studied by means of electron diffraction and high resolution electron microscopy. A structure model is proposed based on the periodic insertion of stacking faults in the NiAs-type basic structure and the ordering of vacancies in alternate metal-atom layers. Microtwinning in very narrow slabs is found to be a main feature of the 2a2a3c regions and two defect models are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.698
Times cited: 4
DOI: 10.1016/0022-0248(93)90051-W
|
|
|
“Atomic-scale investigation of the heterogeneous precipitation in the E (Al₁₈Mg₃Cr₂) dispersoid of 7075 aluminum alloy”. Ding L, Zhao L, Weng Y, Schryvers D, Liu Q, Idrissi H, Journal Of Alloys And Compounds 851, 156890 (2021). http://doi.org/10.1016/J.JALLCOM.2020.156890
Abstract: The heterogeneous precipitation of the eta (MgZn2) phase on the E (Al18Mg3Cr2) dispersoids of the 7075 aluminum alloy was systematically investigated by atomic resolution high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and energy dispersive X-ray spectrometry (EDX). It is found that coarse B particles are heterogeneously precipitated at the E particle interface after water quenching and isothermal aging at 120 degrees C. The incoherent E/Al interface is responsible for the high tendency of heterogeneous precipitation of the B phase. Two different orientation relationships (ORs) between the eta, E and Al matrix are identified: OR1 [2 (11) over bar0](eta)[011](E)//[(1) over bar 12](Al), (01 (1) over bar0)(eta)//(13 (3) over bar)(E)//(201)(Al), OR2 [(1) over bar 12](E)//[0001](eta)//[011](Al), (01 (1) over bar0 )(eta)//(220)(E)//(34 (4) over bar)(Al). The eta phase is preferential to nucleate along the {111}(E) or the {220}(E) planes, depending on its OR. The heterogeneous nucleation of B phase on the E particle could stabilize the E/Al interface by introducing a coherent E/eta interface, which increases the drive force of heterogeneous precipitation. The reorientation of eta phase and mutual diffusion of solute atoms could assist the coherency of the E/eta interface. The present results suggest that increasing the coherency of the E/Al interface is a promising method to suppress the heterogeneous precipitation of the eta phase. (C) 2020 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
DOI: 10.1016/J.JALLCOM.2020.156890
|
|
|
“Role of graphene inter layer on the formation of the MoS2 –, CZTS interface during growth”. Vishwakarma M, Thota N, Karakulina O, Hadermann J, Mehta BR, (icc-2017) (2018). http://doi.org/10.1063/1.5033000
Abstract: The growth of MoS2 layer near the Mo/CZTS interface during sulphurization process can have an impact on back contact cell parameters (series resistance and fill factor) depending upon the thickness or quality of MoS2. This study reports the dependence of the thickness of interfacial MoS2 layer on the growth of graphene at the interface between molybdenum back contact and deposited CZTS layer. The graphene layer reduces the accumulation of Zn/ZnS, Sn/SnO2 and formation of pores near the MoS2-CZTS interface. The use of graphene as interface layer can be potentially useful for improving the quality of Mo/MoS2/CZTS interface.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1063/1.5033000
|
|
|
“Electron microscopy and X-ray study of the growth of FeCr2S4 spinel single crystals by chemical vapour transport”. Volkov VV, van Heurck C, van Landuyt J, Amelinckx S, Zhukov EG, Polulyak ES, Novotortsev VM, Crystal research and technology 28, 1051 (1993). http://doi.org/10.1002/crat.2170280804
Abstract: The growth features of FeCr2S4 spinel single crystals prepared by chemical vapour transport were studied by means of scanning electron microscopy, transmission electron microscopy, high resolution electron microscopy, electron diffraction and X-ray analysis. Our results indicate that the epitaxial growth of the new phases FeCr7S12 and FeCr8S12, both based on the NiAs structure, can essentially inhibit the growth of large FeCr2S4 spinel single crystals in the octahedral habit. The new phases are fully characterised and the effects of defect ordering in these new phases are also reported.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.935
Times cited: 1
DOI: 10.1002/crat.2170280804
|
|
|
“Magnetotransport across the metal-graphene hybrid interface and its modulation by gate voltage”. Chen J-J, Ke X, Van Tendeloo G, Meng J, Zhou Y-B, Liao Z-M, Yu D-P, Nanoscale 7, 5516 (2015). http://doi.org/10.1039/c5nr00223k
Abstract: The graphene-metal contact is very important for optimizing the performance of graphene based electronic devices. However, it is difficult to probe the properties of the graphene/metal interface directly via transport measurements in traditional graphene lateral devices, because the dominated transport channel is graphene, not the interface. Here, we employ the Au/graphene/Au vertical and lateral hybrid structure to unveil the metal-graphene interface properties, where the transport is dominated by the charge carriers across the interface. The magnetoresistance (MR) of Au/monolayer graphene/Au and Au/stacked two-layered graphene/Au devices is measured and modulated by gate voltage, demonstrating that the interface is a device. The gate-tunable MR is identified from the graphene lying on the SiO2 substrate and underneath the top metal electrode. Our unique structures couple the in-plane and out-of-plane transport and display linear MR with small amplitude oscillations at low temperatures. Under a magnetic field, the electronic coupling between the graphene edge states and the electrode leads to the appearance of quantum oscillations. Our results not only provide a new pathway to explore the intrinsic transport mechanism at the graphene/metal interface but also open up new vistas of magnetoelectronics.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 3
DOI: 10.1039/c5nr00223k
|
|
|
“Globular structure of M2 high speed steel by thermomechanical treatment in the semisolid state”. Amin-Ahmadi B, Aashuri H, Steel research international 81, 381 (2010). http://doi.org/10.1002/srin.201000014
Abstract: The globular structure of M2 high speed steel in the rolled – annealed and as cast conditions was investigated in the semisolid state. Metallographic observations resulted in globular austenite particles that were surrounded by a liquid phase. Dissolution of various carbides in the austenite phase at semisolid temperatures led to grain boundary liquation and formation of near-spherical solid grains in a liquid matrix. Therefore, at the semisolid state, the solid particles were free from carbides. MC- type and M6C- type eutectic carbides re- precipitated at the grain boundaries during cooling of the samples from the semisolid temperature. The variation of shape factor versus holding time and holding temperature was examined. A transition value for shape factor changes in high speed steels was achieved. The growth rate constants of the Ostwald ripening and the coalescence mechanisms were calculated by using the experimentally determined rate constant. It was observed that less liquid droplets were enclosed inside the solid particles compared with non-ferrous alloys. Besides, it has been shown that at high solid fraction, the Ostwald ripening mechanism plays a prominent role in the coarsening phenomenon in comparison with the coalescence mechanism. Grains can rotate and arrange low misorientation with each other at high liquid contents, therefore low energetic grain boundaries form between these grains. These grain boundaries play an important role in the coalescence mechanism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.235
Times cited: 1
DOI: 10.1002/srin.201000014
|
|
|
“Giant Pd clusters observed by high resolution electron microscopy”. Volkov VV, Van Tendeloo G, Vargaftik MN, Stolyarov IP, Moiseev II, Mendeleev communications , 187 (1993)
Abstract: The giant cationic palladium clusters, approximate formula Pd561L60(OAc)180 (L = Dipy, Phen), were characterized by electron diffraction and high resolution microscopy to contain an FCC metal core, most of the larger Pd particles (8 nm) exhibiting multiple twinning, evidence for a distorted icosahedral structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.34
Times cited: 10
|
|
|
“Resolving the FCC/HCP interfaces of the \gamma'(Ag2Al) precipitate phase in aluminium”. Zhang Z, Rosalie JM, Medhekar NV, Bourgeois L, Acta materialia 174, 116 (2019). http://doi.org/10.1016/J.ACTAMAT.2019.04.058
Abstract: The gamma'(Ag2Al) phase in the Al-Ag alloy system has served as a textbook example for understanding phase transformations, precipitating hexagonal close-packed (HCP) crystals in the face-centred cubic (FCC) aluminium matrix. The gamma' precipitates display fully coherent interfaces at their broad facets and semicoherent interfaces at their edges. Shockley partial dislocations are expected to decorate the semicoherent interface due to the FCC-HCP structural transformation. Determining the exact locations and core structures of interfacial dislocations, however, remains challenging. In this study, we used aberration-corrected scanning transmission electron microscopy and atomistic simulations to re-visit this classical system. We characterised and explained the Ag segregation at coherent interfaces in the early stage of precipitation. For semicoherent interfaces, interfacial dislocations and reconstructions were revealed by bridging advanced microstructure characterisation and atomistic simulations. In particular, we discovered a new FCC/HCP interfacial structure that displays a unique combination of Shockley partial, Lomer-Cottrell and Hirth dislocations that evolve from the known interfacial structure purely composed by Shockley partial dislocations. Our findings show that the FCC-HCP transformation is more complex than hitherto considered, due to the interplay between structure and composition confined at interfaces. (C) 2019 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 3
DOI: 10.1016/J.ACTAMAT.2019.04.058
|
|
|
“Atomic-scale viscoplasticity mechanisms revealed in high ductility metallic glass films”. Idrissi H, Ghidelli M, Béché, A, Turner S, Gravier S, Blandin J-J, Raskin J-P, Schryvers D, Pardoen T, Scientific reports 9, 13426 (2019). http://doi.org/10.1038/s41598-019-49910-7
Abstract: The fundamental plasticity mechanisms in thin freestanding Zr65Ni35 metallic glass films are investigated in order to unravel the origin of an outstanding strength/ductility balance. The deformation process is homogenous until fracture with no evidence of catastrophic shear banding. The creep/relaxation behaviour of the films was characterized by on-chip tensile testing, revealing an activation volume in the range 100–200 Å3. Advanced high-resolution transmission electron microscopy imaging and spectroscopy exhibit a very fine glassy nanostructure with well-defined dense Ni-rich clusters embedded in Zr-rich clusters of lower atomic density and a ~2–3 nm characteristic length scale. Nanobeam electron diffraction analysis reveals that the accumulation of plastic deformation at roomtemperature
correlates with monotonously increasing disruption of the local atomic order. These results provide experimental evidences of the dynamics of shear transformation zones activation in metallic glasses. The impact of the nanoscale structural heterogeneities on the mechanical properties including the rate dependent behaviour is discussed, shedding new light on the governing plasticity mechanisms in metallic glasses with initially heterogeneous atomic arrangement.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.259
DOI: 10.1038/s41598-019-49910-7
|
|
|
“Interlayer structure in YBCO-coated conductors prepared by chemical solution deposition”. Molina L, Egoavil R, Turner S, Thersleff T, Verbeeck J, Holzapfel B, Eibl O, Van Tendeloo G, Superconductor science and technology 26, 075016 (2013). http://doi.org/10.1088/0953-2048/26/7/075016
Abstract: The functionality of YBa2Cu3O7−δ (YBCO)-coated conductor technology depends on the reliability and microstructural properties of a given tape or wire architecture. Particularly, the interface to the metal tape is of interest since it determines the adhesion, mechanical stability of the film and thermal contact of the film to the substrate. A trifluoroacetate (TFA)metal organic deposition (MOD) prepared YBCO film deposited on a chemical solution-derived buffer layer architecture based on CeO2/La2Zr2O7 and grown on a flexible Ni5 at.%W substrate with a {100}⟨001⟩ biaxial texture was investigated. The YBCO film had a thickness was 440 nm and a jc of 1.02 MA cm−2 was determined at 77 K and zero external field. We present a sub-nanoscale analysis of a fully processed solution-derived YBCO-coated conductor by aberration-corrected scanning transmission electron microscopy (STEM) combined with electron energy-loss spectroscopy (EELS). For the first time, structural and chemical analysis of the valence has been carried out on the sub-nm scale. Intermixing of Ni, La, Ce, O and Ba takes place at these interfaces and gives rise to nanometer-sized interlayers which are a by-product of the sequential annealing process. Two distinct interfacial regions were analyzed in detail: (i) the YBCO/CeO2/La2Zr2O7 region (10 nm interlayer) and (ii) the La2Zr2O7/Ni5 at.%W substrate interface region (20 nm NiO). This is of particular significance for the functionality of these YBCO-coated conductor architectures grown by chemical solution deposition.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 11
DOI: 10.1088/0953-2048/26/7/075016
|
|
|
“In situ transmission electron microscopy study of Ni silicide phases formed on (001) Si active lines”. Teodorescu V, Nistor L, Bender H, Steegen A, Lauwers A, Maex K, van Landuyt J, Journal of applied physics 90, 167 (2001). http://doi.org/10.1063/1.1378812
Abstract: The formation of Ni silicides is studied by transmission electron microscopy during in situ heating experiments of 12 nm Ni layers on blanket silicon, or in patterned structures covered with a thin chemical oxide. It is shown that the first phase formed is the NiSi2 which grows epitaxially in pyramidal crystals. The formation of NiSi occurs quite abruptly around 400 degreesC when a monosilicide layer covers the disilicide grains and the silicon in between. The NiSi phase remains stable up to 800 degreesC, at which temperature the layer finally fully transforms to NiSi2. The monosilicide grains show different epitaxial relationships with the Si substrate. Ni2Si is never observed. (C) 2001 American Institute of Physics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 97
DOI: 10.1063/1.1378812
|
|
|
“C-H\cdots X (X = S, P) hydrogen bonding : the complexes of halothane with dimethyl sulfide and trimethylphosphine”. Michielsen B, Verlackt C, van der Veken BJ, Herrebout WA, Journal Of Molecular Structure 1023, 90 (2012). http://doi.org/10.1016/j.molstruc.2012.02.063
Abstract: The formation of CH⋯S and CH⋯P hydrogen bonded complexes of halothane, CHBrClCF3, with dimethyl sulfide(-d6) and trimethylphosphine(-d9) have been studied in solutions of liquid krypton using infrared and Raman spectroscopy. In the 1:1 complexes, the halothane CH stretching mode is found to be red-shifted by 43 cm−1 in the dimethyl sulfide complex, and by 63 cm−1 in the trimethylphosphine complex. The complexation enthalpies were derived and amount to −10.7(2) and −11.2(2) kJ mol−1 for the respective complexes. The experiments were supported by ab initio calculations and Monte Carlo simulations. The obtained data for the CH⋯S and CH⋯P hydrogen bonds is compared to that of corresponding CH⋯O and CH⋯N hydrogen bonds.
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 1.753
Times cited: 21
DOI: 10.1016/j.molstruc.2012.02.063
|
|
|
“Synthesis of a 3D network of Pt nanowires by atomic layer deposition on a carbonaceous template”. Deng S, Kurttepeli M, Deheryan S, Cott DJ, Vereecken PM, Martens JA, Bals S, Van Tendeloo G, Detavernier C, Nanoscale 6, 6939 (2014). http://doi.org/10.1039/c4nr00982g
Abstract: The formation of a 3D network composed of free standing and interconnected Pt nanowires is achieved by a two-step method, consisting of conformal deposition of Pt by atomic layer deposition (ALD) on a forest of carbon nanotubes and subsequent removal of the carbonaceous template. Detailed characterization of this novel 3D nanostructure was carried out by transmission electron microscopy (TEM) and electrochemical impedance spectroscopy (EIS). The characterization showed that this pure 3D nanostructure of platinum is self-supported and offers an enhancement of the electrochemically active surface area by a factor of 50.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 14
DOI: 10.1039/c4nr00982g
|
|