Abstract: A new layered perovskite Sr2Al0.78Mn1.22O5.2 has been synthesized by solid state reaction in a sealed evacuated silica tube. The crystal structure has been determined using electron diffraction, high-resolution electron microscopy, and high-angle annular dark field imaging and refined from X-ray powder diffraction data (space group P4/mmm, a=3.89023(5) Å, c=7.8034(1) Å, RI=0.023, RP=0.015). The structure is characterized by an alternation of MnO2 and (Al0.78Mn0.22)O1.2 layers. Oxygen atoms and vacancies, as well as the Al and Mn atoms in the (Al0.78Mn0.22)O1.2 layers are disordered. The local atomic arrangement in these layers is suggested to consist of short fragments of brownmillerite-type tetrahedral chains of corner-sharing AlO4 tetrahedra interrupted by MnO6 octahedra, at which the chain fragments rotate over 90°. This results in an averaged tetragonal symmetry. This is confirmed by the valence state of Mn measured by EELS. The relationship between the Sr2Al0.78Mn1.22O5.2 tetragonal perovskite and the parent Sr2Al1.07Mn0.93O5 brownmillerite is discussed. Magnetic susceptibility measurements indicate spin glass behavior of Sr2Al0.78Mn1.22O5.2. The lack of long-range magnetic ordering contrasts with Mn-containing brownmillerites and is likely caused by the frustration of interlayer interactions due to presence of the Mn atoms in the (Al0.78Mn0.22)O1.2 layers.

Abstract: A new potassium palladate KPd2O3 was synthesized by the reaction of KO2 and PdO at elevated oxygen pressure. Its crystal structure was solved from powder X-ray diffraction data in the space group Rm (a = 6.0730(1) Å, c = 18.7770(7) Å, and Z = 6). KPd2O3 represents a new structure type, consisting of an alternating sequence of K+ and Pd2O3− layers with ordered Pd2+ and Pd4+ ions. The presence of palladium ions in di- and tetravalent low-spin states was confirmed by magnetic susceptibility measurements.

Abstract: A novel potassium-based fluoride-phosphate, KVPO4F, with a KTiOPO4 (KTP) type structure is synthesized and characterized. About 85% of potassium has been electrochemically extracted on oxidation producing a cathode material with attractive performance for Li-ion batteries. The material operates at the electrode potential near 4V vs Li/Li+ exhibiting a sloping voltage profile, extremely low polarization, small volume change of about 2% and excellent rate capability, maintaining more than 75% of the initial capacity at 40C discharge rate without significant fading.

Abstract: Highly homogeneous mullite-type solid solutions Bi2Fe4-xCrxO9 (x = 0.5, 1, 1.2) were synthesized using a soft chemistry technique followed by a solid-state reaction in Ar. The crystal structure of Bi2Fe3CrO9 was investigated using X-ray and neutron powder diffraction, transmission electron microscopy and Fe-57 Mossbauer spectroscopy (S.G. Pbam, a = 7.95579(9) angstrom , b = 8.39145(9) angstrom, c = 5.98242(7) angstrom, R-F(X-ray) = 0.022, R-F(neutron) = 0.057). The ab planes in the structure are tessellated with distorted pentagonal loops built up by three tetrahedrally coordinated Fe sites and two octahedrally coordinated Fe/Cr sites, linked together in the ab plane by corner-sharing forming a pentagonal Cairo lattice. Magnetic susceptibility measurements and powder neutron diffraction show that the compounds order antiferromagnetically (AFM) with the Neel temperatures decreasing upon increasing the Cr content from T-N similar to 250 K for x = 0 to T-N similar to 155 K for x = 1.2. The magnetic structure of Bi2Fe3CrO9 at T = 30 K is characterized by a propagation vector k = (1/2,1/2,1/2). The tetrahedrally coordinated Fe cations form singlet pairs within dimers of corner-sharing tetrahedra, but spins on the neighboring dimers are nearly orthogonal. The octahedrally coordinated (Fe, Cr) cations form antiferromagnetic up-up-down-down chains along c, while the spin arrangement in the ab plane is nearly orthogonal between nearest neighbors and collinear between second neighbors. The resulting magnetic structure is remarkably different from the one in pure Bi2Fe4O9 and features several types of spin correlations even on crystallographically equivalent exchange that may be caused by the simultaneous presence of Fe and Cr on the octahedral site.

Abstract: Knowledge on the mechanisms of oxygen reduction reaction (ORR) and descriptors linking the catalytic activity to the structural and electronic properties of transition metal oxides enable rational design of more efficient catalysts. In this work ORR electrocatalysis was studied on a set of single and complex Mn (III) oxides with a rotating disc electrode method and cyclic voltammetry. We discovered an exponential increase of the specific electrocatalytic activity with the potential of the surface Mn(IV)/Mn(III) red-ox couple, suggesting the latter as a new descriptor for the ORR electrocatalysis. The observed dependence is rationalized using a simple mean-field kinetic model considering availability of the Mn( III) centers and adsorbate-adsorbate interactions. We demonstrate an unprecedented activity of Mn2O3, ca. 40 times exceeding that of MnOOH and correlate the catalytic activity of Mn oxides to their crystal structure. (C) 2015 Elsevier Ltd. All rights reserved.

Abstract: La3.2Ba0.8Mn3O10, a representative of the rare n = 3 members of the Ruddlesden-Popper manganites A(n+1)Mn(n)O(3n+1), was synthesized in an evacuated sealed silica tube. Its crystal structure was refined from a combination of powder X-ray diffraction (PXD) and precession electron diffraction (PED) data, with the rotations of the MnO6 octahedra described within the symmetry-adapted mode approach (space group Cccm, a = 29.068(1) angstrom, b = 5.5504(5) angstrom, c = 5.5412(5) angstrom; PXD RF = 0.053, RP = 0.026; PED RF = 0.248). The perovskite block in La3.2Ba0.8Mn3O10 features an octahedral tilting distortion with out-of-phase rotations of the Mn06 octahedra according to the (Phi,Phi,0)(Phi,Phi,0) mode, observed for the first time in the n = 3 Ruddlesden-Popper structures. The Mn06 octahedra demonstrate a noticeable deformation with the elongation of two apical Mn-O bonds due to the Jahn-Teller effect in the Mn3+ cations. The relationships between the octahedral tilting distortion, the ionic radii of the cations at the A- and B-positions, and the mismatch between the perovslcite and rock-salt blocks of the Ruddlesden-Popper structure are discussed. At low temperatures, La3.2Ba0.8Mn3O10 reveals a sizable remnant magnetization of about 1.3 mu(B)/Mn at 2K, and shows signatures of spin freezing below 150 K.

Abstract: New strontium titanyl phosphate Sr2TiO(PO4)2 (1) was synthesized and characterized by X-ray powder diffraction, electron diffraction, high-resolution electron microscopy, and band structure calculations. Titanyl phosphate 1 is isostructural with vanadyl phosphate Sr2VO(PO4)2 and has a layered structure. The titanium atoms are shifted from the centers of the TiO6 octahedra and form short (1.74 Å) titanyl bonds. The structure of 1 is an unusual example of the disordered orientation of the chains formed by TiO6 octahedra in complex titanium phosphates.

Abstract: Oxygen deficient perovskites Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75, were prepared by using the citrate route at 1373-1573 K for 48 h. The cubic Pm-3m perovskite structure for x=0.5 was confirmed by electron diffraction study and refined using neutron powder diffraction (NPD) data. For x=0.75, the superstructure corresponding to a=root 2 x a(per), b=2 x a(per), c=root 2 x a(per) (a(0)b(-)b(-) tilt system, space group Imma) was revealed by electron diffraction. The solid solution Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= x <= 0.6 and compound Ca0.75Y0.25Mn0.85Co0.15O2.92 were prepared in air at 1573 K for 48 h. The crystal structure of Ca0.75Y0.25Mn0.85Co0.15O2.92 was refined using NPD data (S.G. Pnma, a=5.36595(4), b=7.5091(6), c=5.2992(4) angstrom, R-p=0.057, R-wp=0.056, chi(2)=4.26). High-temperature thermal expansion properties of the prepared compounds were studied in air using both dilatometry and high-temperature X-ray powder diffraction data (HTXRPD). They expanding non-linearly at 298-1073 K due to the loss of oxygen at high temperatures. Calculated average thermal expansion coefficients (TECs) for Sr0.75Y0.25Co1-xMnxO3-y, x=0.5, 0.75 and Ca0.75Y0.25Mn0.85Co0.15O2.92(1) are 15.5, 15.1, and 13.8 ppm K-1, respectively. Anisotropy of the thermal expansion along different unit cell axes was observed for Sr0.15Ca0.6Y0.25Co0.25Mn0.75O3-y, and Ca0.75Y0.25Mn0.85Co0.15O2.92. Conductivity of Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75 increases with the temperature reaching 110 S/cm for x=0.5 and 44 S/cm for x=0.75 at 1173 K. Samples of Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= y <= 0.6 were found to be n-type conductors at room temperature with the similar temperature dependence of the conductivity and demonstrated the increase of the sigma value from similar to 1 to similar to 50 S/cm as the temperature increases from 300 to 1173 K. Their conductivity is described in terms of the small polaron charge transport with the activation energy (E-p) increasing from 340 to 430 meV with an increase of the calcium content from x=0 to x=0.6. (C) 2012 Elsevier Inc. All rights reserved.

Abstract: Pb2.85Ba2.15Fe4SnO13, a new n=5 member of the anion-deficient perovskite based AnBnO3n−2 (A=Pb, Ba, B=Fe, Sn) homologous series, was synthesized by the solid state method. The crystal structure of Pb2.85Ba2.15Fe4SnO13 was investigated using a combination of neutron powder diffraction, electron diffraction, high angle annular dark field scanning transmission electron microscopy and Mössbauer spectroscopy. It crystallizes in the Ammm space group with unit cell parameters a=5.7990(1) Å, b=4.04293(7) Å and c=26.9561(5) Å. The Pb2.85Ba2.15Fe4SnO13 structure consists of quasi two-dimensional perovskite blocks separated by 1/2[110](1̄01)p crystallographic shear (CS) planes. The corner-sharing FeO6 octahedra at the CS planes are transformed into edge-sharing FeO5 distorted tetragonal pyramids. The octahedral positions in the perovskite blocks between the CS planes are jointly taken up by Fe and Sn, with a preference of Sn towards the position at the center of the perovskite block. The chains of FeO5 pyramids and (Fe,Sn)O6 octahedra of the perovskite blocks delimit six-sided tunnels at the CS planes occupied by double chains of Pb atoms. The compound is antiferromagnetically ordered below TN=368±15 K.

Abstract: Pr2−xCexCuO4 (x = 0.05; 0.1; 0.15) samples were synthesized and systematically characterized towards application as a cathode material for solid oxide fuel cells (SOFCs). High-temperature electrical conductivity, thermal expansion, and electrocatalytic activity in the oxygen reduction reaction (ORR) were examined. The electrical conductivity of Pr2−xCexCuO4 oxides demonstrates semiconducting behavior up to 900 °C. Small Ce-doping (2.5 at%) allows an increase in electrical conductivity from 100 to 130 S cm−1 in air at 500–800 °C. DFT calculations revealed that the density of states directly below the Fermi level, comprised mainly of Cu 3d and O 2p states, is significantly affected by atoms in rare earth positions, which might give an indication of a correlation between calculated electronic structures and measured conducting properties. Ce-doping in Pr2−xCexCuO4 slightly increases TEC from 11.9 × 10−6 K−1 for x = 0 to 14.2 × 10−6 K−1 for x = 0.15. Substitution of 2.5% of Pr atoms in Pr2CuO4 by Ce is effective to enhance the electrochemical performance of the material as a SOFC cathode in the ORR (ASR of Pr1.95Ce0.05CuO4 electrode applied on Ce0.9Gd0.1O1.95 electrolyte is 0.39 Ω cm2 at 750 °C in air). The peak power density achieved for the electrolyte-supported fuel cell with the Pr1.95Ce0.05CuO4 cathode is 150 mW cm−2 at 800 °C

Abstract: Tetrahedral chain ordering in the Sr2MnGaO5 structure is studied using electron diffraction (ED) and high-resolution electron microscopy. The ED patterns show the presence of satellite reflections, which indicate a commensurately modulated structure with a = 5.4056(8) Angstrom b 16.171(3) Angstrom, c = 5.5592(7) Angstrom, q – 1/2c*, superspace group Immma(00gamma,)s00. The Superstructure arises due to ordering of the two types of symmetry related tetrahedral chains (L and R) according to a ... LRLR ... sequence, where L and R chains alternate along the c-axis within the same (GaO) layer. Numerous defects at different structural levels were observed, comprising interleaving L and R chains, violation of the ... LRLR ... chain sequence within one layer, different stacking modes of the ... LRLR ... ordered layers with subsequent alternation of blocks of different width along the h-axis of the brownmillerite subcell and island fragmentation of the modulated superstructure. By in situ heating ED experiments it is found that the long-range ordering of the tetrahedral chains is stable tip to 665degreesC and is completely suppressed at 905degreesC. (C) 2003 Elsevier Inc. All rights reserved.

Abstract: The crystal structure of a novel compound Pb13Mn9O25 has been determined through a direct space structure solution with a Monte-Carlo-based global optimization using precession electron diffraction data (a=14.177(3) Å, c=3.9320(7) Å, SG P4/m, RF=0.239) and compositional information obtained from energy dispersive X-ray analysis and electron energy loss spectroscopy. This allowed to obtain a reliable structural model even despite the simultaneous presence of both heavy (Pb) and light (O) scattering elements and to validate the accuracy of the electron diffraction-based structure refinement. This provides an important benchmark for further studies of complex structural problems with electron diffraction techniques. Pb13Mn9O25 has an anion- and cation-deficient perovskite-based structure with the A-positions filled by the Pb atoms and 9/13 of the B positions filled by the Mn atoms in an ordered manner. MnO6 octahedra and MnO5 tetragonal pyramids form a network by sharing common corners. Tunnels are formed in the network due to an ordered arrangement of vacancies at the B-sublattice. These tunnels provide sufficient space for localization of the lone 6s2 electron pairs of the Pb2+ cations, suggested as the driving force for the structural difference between Pb13Mn9O25 and the manganites of alkali-earth elements with similar compositions.