Abstract: Rh-structured catalysts for the catalytic partial oxidation of CH4 to syngas were prepared by electrosynthesis of Rh-containing hydrotalcite-type (HT) compounds on FeCrAlloy foams followed by calcination at 900 degrees C. During the calcination the simultaneous decomposition of the layered HT structure and formation of the protective FeCrAlloy outer shell in alumina occurred. Here, we studied the role of the coating-metallic support interaction in the properties of the catalysts after calcination, H-2 reduction, and catalytic tests, by a combination of electron (FEG-SEM/EDS) and synchrotron X-ray (XRF/XRPD and XRF/XANES) microscopic techniques. The characterization of crystalline phases in the metallic support and coating and distribution of Rh active species was carried out on several samples prepared by modifying the Rh content in the electrolytic solution (Rh/Mg/Al = 11.0/70.0/19.0, 5.0/70.0/25.0, 0/70.0/30.0 atomic ratio). A sample was also prepared with no aluminum in the electrolytic solution (Rh/Mg/Al = 13.6/86.4/0.0 atomic ratio) and calcined at 550 and 900 degrees C. The interaction between the elements of the metallic support and the catalytic coating increased the film adhesion during the thermal treatment and catalytic tests and modified the catalyst crystalline phases. A chemical reaction between Al corning from the foam and Mg in the coating occurred during calcination at high temperature leading to the formation of spinel phases in which rhodium is solved, together with some Rh2O3 and Rh. The metallic support was oxidized forming the corundum scale and chromium oxides, moreover t-Al2O3 was identified. For the Rh11.0Mg70.0Al19.0 catalyst the inclusion of Rh in the spinel phase decreased its reducibility in the H-2 pretreatment. The reduction continued during catalytic tests by feeding diluted CH4/O-2/He gas mixtures, evidenced by the catalyst activation. While under concentrated gas mixtures the deactivation occurred, probably by oxidation.

Abstract: Synchrotron radiation (SR)-based X-ray methods are powerful analytical tools for several purposes. They are widely used to probe the degradation mechanisms of inorganic artists' pigments in paintings, including chrome yellows (PbCr1-xSxO4; 0 <= x <= 0.8), a class of compounds often found in Van Gogh masterpieces. However, the high intensity and brightness of SR beams raise important issues regarding the potential damage inflicted on the analyzed samples. A thorough knowledge of the SR X-ray sensitivity of each class of pigment in the painting matrix is therefore required to find analytical strategies that seek to minimize the damage for preserving the integrity of the analyzed samples and to avoid data misinterpretation. Here, we employ a combination of Cr K-edge X-ray absorption near-edge structure spectroscopy, Cr-K-beta X-ray emission spectroscopy, and X-ray diffraction to monitor and quantify the effects of SR X-rays on the stability of chrome yellows and related Cr compounds and to define mitigation strategies. We found that the SR X-ray beam exposure induces changes in the oxidation state and local coordination environment of Cr ions and leads to a loss of the compound's crystalline structure. The extent of X-ray damage depends on some intrinsic properties of the samples (chemical composition of the pigment and the presence/absence and nature of the binder). It can be minimized by optimizing the overall fluence/dose released to the samples and by working in vacuum and under cryogenic conditions.

Abstract: The degradation of cadmium sulfide (CdS)-based oil paints is a phenomenon potentially threatening the iconic painting The Scream (ca. 1910) by Edvard Munch (Munch Museum, Oslo) that is still poorly understood. Here, we provide evidence for the presence of cadmium sulfate and sulfites as alteration products of the original CdS-based paint and explore the external circumstances and internal factors causing this transformation. Macroscale in situ noninvasive spectroscopy studies of the painting in combination with synchrotron-radiation x-ray microspectroscopy investigations of a microsample and artificially aged mock-ups show that moisture and mobile chlorine compounds are key factors for promoting the oxidation of CdS, while light (photodegradation) plays a less important role. Furthermore, under exposure to humidity, parallel/secondary reactions involving dissolution, migration through the paint, and recrystallization of water-soluble phases of the paint are associated with the formation of cadmium sulfates.

Abstract: The precipitation of Rh/Mg/Al and Rh/Al hydroxides on the surface of FeCrAlloy foams by a base electrogeneration method was investigated to improve the properties of the deposited film (homogeneity and composition) and therefore the performances of the structured catalysts, obtained by calcination, in the Catalytic Partial Oxidation of CH4 to syngas. The work focussed on decreasing current gradients within open-cell foam cylinders by increasing the number of electrical contacts from 1 to 3 points to promote a more homogeneous precipitation of the hydroxides. Electrochemical and catalytic tests as well as SEM/EDS and mu-XRFIXRD analyses allowed to correlate the effect of the number of electrical contact points with materials properties. Lastly, syntheses were performed on Pt plates to study the effect of the electrical behaviour and shape of the support on the composition of the film. A more homogeneous coating of the foam surface was achieved by adopting a configuration with 3 contact points since the reduction of nitrates and water molecules that generates the basic media in the vicinity of the support was enhanced. Layer thicknesses up to 5-15 mu m were deposited; however, the sequential precipitation of a film with composition closer to the expected one and a layer enriched in Al and Rh (outer layer) was not avoided. The improvement in the coating gave rise to enhanced performances for a sample prepared at -1.1 V for 3000 s. Contrarily, the low adherence of the outer layer in a sample prepared at -1.2 V for 2000 s during both calcination and catalytic tests may be responsible of the unexpected decrease in catalytic performances. The same sequential precipitation was observed by performing the syntheses on Pt plates, showing that the electrical nature the support did not play a key role on this phenomenon. (C) 2014 Elsevier B.V. All rights reserved.

Abstract: The speed and effectiveness of a conservation treatment used for stained glass windows have been investigated. Dark-coloured Mn-rich stains can be found in the alteration layer of ancient glass artefacts and cause the surface to turn brown/black: this phenomenon is known as Mn-browning or Mn-staining. While in glass manganese is present in the +II or +III oxidation states, in the Mn-rich bodies, manganese is in a higher oxidation state (+IV). In restoration practice, mildly reducing solutions are employed to eliminate the dark colour and restore the clear appearance of the glass. In this paper the effectiveness and side effects of the use of hydroxylamine hydrochloride for this purpose are assessed. Archaeological fragments of stained glass windows, dated to the 14th century and originating from Sidney Sussex College, Cambridge (UK), were examined by means of synchrotron radiation (SR) based microscopic X-ray Absorption Near-Edge Spectroscopy (μ-XANES) and microscopic X-Ray Fluorescence (μ-XRF) and with high resolution computed absorption tomography (μ-CT) before, during and after the treatment. The monitoring of the glass fragments during the treatment allows us to better understand the manner in which the process unfolds and its kinetics. The results obtained reveal that the hydroxylamine hydrochloride treatment is effective, but also that it has a number of unwanted side effects. These findings are useful for optimizing the time and other modalities of the Mn-reducing treatment as well as minimizing its unwanted results.

Abstract: This study demonstrates that the mechanism responsible for the transformation of glass into a degradation layer is pH-dependent. In acid conditions, the transformed glass is homogeneous and brittle. In mild alkaline conditions, transformed glass is heterogeneous due to the presence of lamellae composed of silica nanoparticles and the occurrence of Ca-rich inclusions. The fundamental difference between acid and alkaline conditions cannot be explained by the currently accepted degradation mechanism based on ion exchange. To explain this critical observation, we propose a refined degradation mechanism based on existing knowledge that involves several inwardly moving reaction fronts. The fronts responsible for the transformation of the silicate network into amorphous silica are also responsible for the morphology of the transformed glass. We have identified the feedback mechanism that explains the formation of lamellae in alkaline conditions.

Abstract: We studied the Fe K-edge X-ray absorption near edge (XANES) spectra of several Roman black glass fragments in order to determine the Fe3+/ΣFe ratio of these materials. The selected archaeological glass samples cover the period 1st5th century AD in nine different sites of the North Western provinces of the Roman Empire. The fragments belong to two different compositional groups demonstrating a diachronic evolution: early Roman HMG (High Magnesia Glass) and Roman Imperial LMG (Low Magnesia Glass). The first group contains natural Fe levels (below 2 wt% as Fe2O3), while the LMG has concentrations above 5 wt%. This difference is also reflected by Fe3+/ΣFe values. Low iron glass was produced under strongly reducing conditions in order to obtain the black colour, with average Fe3+/ΣFe values ≈ 0.17. LMG glass is somewhat more oxidised (Fe3+/ΣFe ≈ 0.40.5). While HMG glass required active control of the furnace environment, LMG was made under ambient atmosphere and its higher oxidation degree is mainly determined by the chemistry of the raw glass.