“Non-invasive and non-destructive examination of artistic pigments, paints, and paintings by means of X-Ray methods”. Janssens K, van der Snickt G, Vanmeert F, Legrand S, Nuyts G, Alfeld M, Monico L, Anaf W, de Nolf W, Vermeulen M, Verbeeck J, De Wael K, Topics in Current Chemistry 374, 81 (2016). http://doi.org/10.1007/S41061-016-0079-2
Abstract: Recent studies are concisely reviewed, in which X-ray beams of (sub)micrometre to millimetre dimensions have been used for non-destructive analysis and characterization of pigments, minute paint samples, and/or entire paintings from the seventeenth to the early twentieth century painters. The overview presented encompasses the use of laboratory and synchrotron radiation-based instrumentation and deals with the use of several variants of X-ray fluorescence (XRF) as a method of elemental analysis and imaging, as well as with the combined use of X-ray diffraction (XRD) and X-ray absorption spectroscopy (XAS). Microscopic XRF is a variant of the method that is well suited to visualize the elemental distribution of key elements, mostly metals, present in paint multi-layers, on the length scale from 1 to 100 μm inside micro-samples taken from paintings. In the context of the characterization of artists pigments subjected to natural degradation, the use of methods limited to elemental analysis or imaging usually is not sufficient to elucidate the chemical transformations that have taken place. However, at synchrotron facilities, combinations of μ-XRF with related methods such as μ-XAS and μ-XRD have proven themselves to be very suitable for such studies. Their use is often combined with microscopic Fourier transform infra-red spectroscopy and/or Raman microscopy since these methods deliver complementary information of high molecular specificity at more or less the same length scale as the X-ray microprobe techniques. Since microscopic investigation of a relatively limited number of minute paint samples, taken from a given work of art, may not yield representative information about the entire artefact, several methods for macroscopic, non-invasive imaging have recently been developed. Those based on XRF scanning and full-field hyperspectral imaging appear very promising; some recent published results are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 4.033
Times cited: 50
DOI: 10.1007/S41061-016-0079-2
|
“Superconductivity in the quantum-size regime”. Shanenko AA, Croitoru MD, Peeters FM, , 79 (2008)
Abstract: Recent technological advances resulted in high-quality superconducting metallic nanofilms and nanowires. The physical properties of such nanostructures are governed by the size-quantization of the transverse electron spectrum. This has a substantial impact on the basic superconducting characteristics, e.g., the order parameter, the critical temperature and the critical magnetic field. In the present paper we give an overview of our theoretical results on this subject. Based on a numerical self-consistent solution of the Bogoliubov-de Gennes equations, we investigate how the superconducting properties are modified in the quantum-size regime.
Keywords: P1 Proceeding; Condensed Matter Theory (CMT); Electron microscopy for materials research (EMAT)
|
“Inelastic electron-vortex-beam scattering”. Van Boxem R, Partoens B, Verbeeck J, Physical review : A : atomic, molecular and optical physics 91, 032703 (2015). http://doi.org/10.1103/PhysRevA.91.032703
Abstract: Recent theoretical and experimental developments in the field of electron-vortex-beam physics have raised questions about what exactly this novelty in the field of electron microscopy (and other fields, such as particle physics) really provides. An important part of the answer to these questions lies in scattering theory. The present investigation explores various aspects of inelastic quantum scattering theory for cylindrically symmetric beams with orbital angular momentum. The model system of Coulomb scattering on a hydrogen atom provides the setting to address various open questions: How is momentum transferred? Do vortex beams selectively excite atoms, and how can one employ vortex beams to detect magnetic transitions? The analytical approach presented here provides answers to these questions. OAM transfer is possible, but not through selective excitation; rather, by pre- and postselection one can filter out the relevant contributions to a specific signal.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 2.925
Times cited: 31
DOI: 10.1103/PhysRevA.91.032703
|
“On the nucleation mechanism of {112} <, 111 >, mechanical twins in as-quenched beta metastable Ti-12 wt.% Mo alloy”. Marteleur M, Idrissi H, Amin-Ahmadi B, Prima F, Schryvers D, Jacques PJ, Materialia 7, Unsp 100418 (2019). http://doi.org/10.1016/J.MTLA.2019.100418
Abstract: Recently developed beta-metastable Ti grades take advantage of the simultaneous activation of TRIP and TWIP effects for enhancing their work hardening rate. However, the role of each plasticity mechanism on the macroscopic mechanical response is still unclear. In this work, the nucleation mechanism of the first activated plasticity mechanism, namely {112} < 111 > twinning, was investigated. Firstly, post-mortem TEM analysis showed that twins nucleate on pre-existing microstructural defects such as thermal jogs with the zonal dislocation mechanism. The precipitation of the omega phase on twin boundaries has been observed, as well as the emission of numerous dislocations from super-jogs present in these twin boundaries. It is also shown that {112} < 111 > twins act as effective dislocation sources for the subsequent plasticity mechanisms such as beta -> alpha '' martensitic transformation and {332} < 111 > twinning. Secondly, in situ TEM tensile testing of the investigated Ti grade highlighted the primary role of the initial defect configuration present in the microstructure. It is shown that twins cannot nucleate without the presence of specific defects allowing the triggering of the dislocation decomposition needed for the twinning mechanism highlighted in investigated bulk samples.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.MTLA.2019.100418
|
“Mixed layers in copper based superconducting materials”. Hervieu, Van Tendeloo G, Michel, Pelloquin, Raveau, Microscopy, microanalysis, microstructures 7, 107 (1996). http://doi.org/10.1051/mmm:1996109
Abstract: Recently discovered series of high Tc superconductors, characterized by the existence of two types of cations within the same layer, are presented. The first family concerns the mercury based cuprates, Hg(1-x)M(x)A(2)Ca(m-1)Cu(m)O(2m+2+delta), with A = Ba and/or Sr, which exhibit structures closely related to that of the thallium cuprates TlBa2Cam-1CumO2m+3. They differ from the thallium cuprates by a high oxygen deficiency at the level of the mercury layer. It is shown that cations such as M = Cu, Pb, Tl, Bi, Ce, Pr, Cr, V, Mo, W, Ti, Sr, Ca,... can partially substitute for mercury ions, stabilizing the structures. The cationic composition of the layer depends indeed on the nature of the M cation but also on that of the alkaline earth A. For given A and M cations, the a: value remains unchanged even when the number of copper layers varies. M and Hg cations are either statistically distributed over the same site or ordered. Different types of ordering have been detected. Another way of generating mixed layers is to shear periodically the structure, leading to the formation of the so called ''collapsed phase''. In the collapsed bismuth cuprates, bismuth and copper segments, a few octahedra long, alternate in strongly waving layers. In the collapsed oxycarbonates, carbonate groups and M cations are ordered within the intermediate layer so that they can be simply described from a partial and ordered substitution of carbon for Hg,TI, Bi and other M cations building the intermediate layer. The oxycarbonitrates (Y1-xCax)(n)Ba2nCu3n-1(C,N)O3O7n-3 can also be described as an ordered substitution of carbon for copper in the 123 matrix. The different families of superconducting materials which are generated by such mechanisms are described as well as the way the different species are distributed within the mixed layers. Their influence on the physical properties are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1051/mmm:1996109
|
“Surface processes during purification of InP quantum dots”. Mordvinova N, Emelin P, Vinokurov A, Dorofeev S, Abakumov A, Kuznetsova T, Beilstein journal of nanotechnology 5, 1220 (2014). http://doi.org/10.3762/bjnano.5.135
Abstract: Recently, a new simple and fast method for the synthesis of InP quantum dots by using phosphine as phosphorous precursor and myristic acid as surface stabilizer was reported. Purification after synthesis is necessary to obtain samples with good optical properties. Two methods of purification were compared and the surface processes which occur during purification were studied. Traditional precipitation with acetone is accompanied by a small increase in photoluminescence. It occurs that during the purification the hydrolysis of the indium precursor takes place, which leads to a better surface passivation. The electrophoretic purification technique does not increase luminescence efficiency but yields very pure quantum dots in only a few minutes. Additionally, the formation of In(OH)(3) during the low temperature synthesis was explained. Purification of quantum dots is a very significant part of post-synthetical treatment that determines the properties of the material. But this subject is not sufficiently discussed in the literature. The paper is devoted to the processes that occur at the surface of quantum dots during purification. A new method of purification, electrophoresis, is investigated and described in particular.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.127
Times cited: 5
DOI: 10.3762/bjnano.5.135
|
“Synthesis and properties of charge-ordered thallium halide perovskites, CsTl0.5+Tl0.53+X3 (X = F or Cl) : theoretical precursors for superconductivity?”. Retuerto M, Emge T, Hadermann J, Stephens PW, Li MR, Yin ZP, Croft M, Ignatov A, Zhang SJ, Yuan Z, Jin C, Simonson JW, Aronson MC, Pan A, Basov DN, Kotliar G, Greenblatt M;, Chemistry of materials 25, 4071 (2013). http://doi.org/10.1021/cm402423x
Abstract: Recently, CsTlCl3 and CsTlF3 perovskites were theoretically predicted to be potential superconductors if they were optimally doped. The syntheses of these two compounds together with a complete characterization of the samples are reported. CsTlCl3 was obtained as orange crystals in two different polymorphs: a tetragonal phase (I4/m) and a cubic phase (Fm (3) over barm). CsTlF3 was formed as a light brown powder, and also as a double cubic perovskite (Fm (3) over barm). In all three CsTlX3 phases, Tl+ and Tl3+ were located in two different crystallographic positions that accommodate their different bond lengths. In CsTlCl3, some Tl vacancies were found in the Tl+ position. The charge ordering between Tl+ and Tl3+ was confirmed by X-ray absorption and Raman spectroscopy. The Raman spectroscopy of CsTlCl3 at high pressure (58 GPa) did not indicate any phase transition to a possible single Tl2+ state. However, the highly insulating material became less resistive with an increasing high pressure, while it underwent a change in its optical properties, from transparent to deeply opaque red, indicative of a decrease in the magnitude of the band gap. The theoretical design and experimental validation of the existence of CsTlF3 and CsTlCl3 cubic perovskites are the necessary first steps in confirming the theoretical prediction of superconductivity in these materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 28
DOI: 10.1021/cm402423x
|
“Locating light and heavy atomic column positions with picometer precision using ISTEM”. van den Bos KHW, Krause FF, Béché, A, Verbeeck J, Rosenauer A, Van Aert S, Ultramicroscopy 172, 75 (2016). http://doi.org/10.1016/j.ultramic.2016.10.003
Abstract: Recently, imaging scanning transmission electron microscopy (ISTEM) has been proposed as a promising new technique combining the advantages of conventional TEM (CTEM) and STEM [1]. The ability to visualize light and heavy elements together makes it a particularly interesting new, spatially incoherent imaging mode. Here, we evaluate this technique in term of precision with which atomic column locations can be measured. By using statistical parameter estimation theory, we will show that these locations can be accurately measured with a precision in the picometer range. Furthermore, a quantitative comparison is made with HAADF STEM imaging to investigate the advantages of ISTEM.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 8
DOI: 10.1016/j.ultramic.2016.10.003
|
“The maximum a posteriori probability rule for atom column detection from HAADF STEM images”. Fatermans J, Van Aert S, den Dekker AJ, Ultramicroscopy 201, 81 (2019). http://doi.org/10.1016/j.ultramic.2019.02.003
Abstract: Recently, the maximum a posteriori (MAP) probability rule has been proposed as an objective and quantitative method to detect atom columns and even single atoms from high-resolution high-angle annular dark-field (HAADF) scanning transmission electron microscopy (STEM) images. The method combines statistical parameter estimation and model-order selection using a Bayesian framework and has been shown to be especially useful for the analysis of the structure of beam-sensitive nanomaterials. In order to avoid beam damage, images of such materials are usually acquired using a limited incoming electron dose resulting in a low contrast-to-noise ratio (CNR) which makes visual inspection unreliable. This creates a need for an objective and quantitative approach. The present paper describes the methodology of the MAP probability rule, gives its step-by-step derivation and discusses its algorithmic implementation for atom column detection. In addition, simulation results are presented showing that the performance of the MAP probability rule to detect the correct number of atomic columns from HAADF STEM images is superior to that of other model-order selection criteria, including the Akaike Information Criterion (AIC) and the Bayesian Information Criterion (BIC). Moreover, the MAP probability rule is used as a tool to evaluate the relation between STEM image quality measures and atom detectability resulting in the introduction of the so-called integrated CNR (ICNR) as a new image quality measure that better correlates with atom detectability than conventional measures such as signal-to-noise ratio (SNR) and CNR.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 1
DOI: 10.1016/j.ultramic.2019.02.003
|
“Physical properties of epitaxial SrMnO2.5−δFγoxyfluoride films”. Wang J, Shin Y, Gauquelin N, Yang Y, Lee C, Jannis D, Verbeeck J, Rondinelli JM, May SJ, Journal of physics : condensed matter 31, 365602 (2019). http://doi.org/10.1088/1361-648X/ab2414
Abstract: Recently, topotactic fluorination has become an alternative way of doping epitaxial perovskite oxides through anion substitution to engineer their electronic properties instead of the more commonly used cation substitution. In this work, epitaxial oxyfluoride SrMnO2.5−δ F γ films were synthesized via topotactic fluorination of SrMnO2.5 films using polytetrafluoroethylene as the fluorine source. Oxidized SrMnO3 films were also prepared for comparison with the fluorinated samples. The F content, probed by x-ray photoemission spectroscopy, was systematically controlled by adjusting fluorination conditions. Electronic transport measurements reveal that increased F content (up to γ = 0.14) systematically increases the electrical resistivity, despite the nominal electron-doping induced by F substitution for O in these films. In contrast, oxidized SrMnO3 exhibits a decreased resistivity and conduction activation energy. A blue-shift of optical absorption features occurs with increasing F content. Density functional theory calculations indicate that F acts as a scattering center for electronic transport, controls the observed weak ferromagnetic behavior of the films, and reduces the inter-band optical transitions in the manganite films. These results stand in contrast to bulk electron-doped La1−x Ce x MnO3, illustrating how aliovalent anionic substitutions can yield physical behavior distinct from A-site substituted perovskites with the same nominal B-site oxidation states.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.649
Times cited: 5
DOI: 10.1088/1361-648X/ab2414
|
“A method to determine the local surface profile from reconstructed exit waves”. Wang A, Chen FR, Van Aert S, van Dyck D, Ultramicroscopy 111, 1352 (2011). http://doi.org/10.1016/j.ultramic.2011.04.005
Abstract: Reconstructed exit waves are useful to quantify unknown structure parameters such as the position and composition of the atom columns at atomic scale. Existing techniques provide a complex wave in a flat plane which is close to the plane where the electrons leave the atom columns. However, due to local deviation in the flatness of the exit surface, there will be an offset between the plane of reconstruction and the actual exit of a specific atom column. Using the channelling theory, it has been shown that this defocus offset can in principle be determined atom column-by-atom column. As such, the surface roughness could be quantified at atomic scale. However, the outcome strongly depends on the initial plane of reconstruction especially in a crystalline structure. If this plane is further away from the true exit, the waves of the atom columns become delocalized and interfere mutually which strongly complicates the interpretation of the exit wave in terms of the local structure. In this paper, we will study the delocalization with defocus using the channelling theory in a more systematic way.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 3
DOI: 10.1016/j.ultramic.2011.04.005
|
“Tomographic spectroscopic imaging, an experimental proof of concept”. van den Broek W, Verbeeck J, Schryvers D, de Backer S, Scheunders P, Ultramicroscopy 109, 296 (2009). http://doi.org/10.1016/j.ultramic.2008.11.022
Abstract: Recording the electron energy loss spectroscopy data cube with a series of energy filtered images is a dose inefficient process because the energy slit blocks most of the electrons. When recording the data cube by scanning an electron probe over the sample, perfect dose efficiency is attained; but due to the low current in nanoprobes, this often is slower, with a smaller field of view. In W. Van den Broek et al. [Ultramicroscopy, 106 (2006) 269], we proposed a new method to record the data cube, which is more dose efficient than an energy filtered series. It produces a set of projections of the data cube and then tomographically reconstructs it. In this article, we demonstrate these projections in practice, we present a simple geometrical model that allows for quantification of the projection angles and we present the first successful experimental reconstruction, all on a standard post-column instrument.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 1
DOI: 10.1016/j.ultramic.2008.11.022
|
“Catalytic upcycling of PVC waste-derived phthalate esters into safe, hydrogenated plasticizers”. Windels S, Diefenhardt T, Jain N, Marquez C, Bals S, Schlummer M, De Vos DE, Green chemistry : cutting-edge research for a greener sustainable future 24, 754 (2022). http://doi.org/10.1039/D1GC03864H
Abstract: Recycling of end-of-life polyvinyl chloride (PVC) calls for solutions to deal with the vast amounts of harmful phthalate plasticizers that have historically been incorporated in PVC. Here, we report on the upcycling of such waste-extracted phthalate esters into analogues of the much safer diisononyl 1,2-cyclohexanedicarboxylate plasticizer (DINCH), via a catalytic one-pot (trans)esterification-hydrogenation process. For most of the virgin phthalates, Ru/Al2O3 is a highly effective hydrogenation catalyst, yielding >99% ring-hydrogenated products under mild reaction conditions (0.1 mol% Ru, 80 degrees C, 50 bar H-2). However, applying this reaction to PVC-extracted phthalates proved problematic, (1) as benzyl phthalates are hydrogenolyzed to benzoic acids that inhibit the Ru-catalyst, and (2) because impurities in the plasticizer extract (PVC, sulfur) further retard the hydrogenation. These complications were solved by coupling the hydrogenation to an in situ (trans)esterification with a higher alcohol, and by pretreating the extract with an activated carbon adsorbent. In this way, a real phthalate extract obtained from post-consumer PVC waste was eventually completely (>99%) hydrogenated to phthalate-free, cycloaliphatic plasticizers.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.8
Times cited: 8
DOI: 10.1039/D1GC03864H
|
“Edge stabilization in reduced-dimensional perovskites”. Quan LN, Ma D, Zhao Y, Voznyy O, Yuan H, Bladt E, Pan J, de Arquer FPG, Sabatini R, Piontkowski Z, Emwas A-H, Todorovic P, Quintero-Bermudez R, Walters G, Fan JZ, Liu M, Tan H, Saidaminov M I, Gao L, Li Y, Anjum DH, Wei N, Tang J, McCamant DW, Roeffaers MBJ, Bals S, Hofkens J, Bakr OM, Lu Z-H, Sargent EH, Nature Communications 11, 170 (2020). http://doi.org/10.1038/S41467-019-13944-2
Abstract: Reduced-dimensional perovskites are attractive light-emitting materials due to their efficient luminescence, color purity, tunable bandgap, and structural diversity. A major limitation in perovskite light-emitting diodes is their limited operational stability. Here we demonstrate that rapid photodegradation arises from edge-initiated photooxidation, wherein oxidative attack is powered by photogenerated and electrically-injected carriers that diffuse to the nanoplatelet edges and produce superoxide. We report an edge-stabilization strategy wherein phosphine oxides passivate unsaturated lead sites during perovskite crystallization. With this approach, we synthesize reduced-dimensional perovskites that exhibit 97 +/- 3% photoluminescence quantum yields and stabilities that exceed 300 h upon continuous illumination in an air ambient. We achieve green-emitting devices with a peak external quantum efficiency (EQE) of 14% at 1000 cd m(-2); their maximum luminance is 4.5 x 10(4) cd m(-2) (corresponding to an EQE of 5%); and, at 4000 cd m(-2), they achieve an operational half-lifetime of 3.5 h.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.6
Times cited: 147
DOI: 10.1038/S41467-019-13944-2
|
“Restructuring of titanium oxide overlayers over nickel nanoparticles during catalysis”. Monai M, Jenkinson K, Melcherts AEM, Louwen JN, Irmak EA, Van Aert S, Altantzis T, Vogt C, van der Stam W, Duchon T, Smid B, Groeneveld E, Berben P, Bals S, Weckhuysen BM, Science 380, 644 (2023). http://doi.org/10.1126/SCIENCE.ADF6984
Abstract: Reducible supports can affect the performance of metal catalysts by the formation of suboxide overlayers upon reduction, a process referred to as the strong metal-support interaction (SMSI). A combination of operando electron microscopy and vibrational spectroscopy revealed that thin TiOx overlayers formed on nickel/titanium dioxide catalysts during 400 degrees C reduction were completely removed under carbon dioxide hydrogenation conditions. Conversely, after 600 degrees C reduction, exposure to carbon dioxide hydrogenation reaction conditions led to only partial reexposure of nickel, forming interfacial sites in contact with TiOx and favoring carbon-carbon coupling by providing a carbon species reservoir. Our findings challenge the conventional understanding of SMSIs and call for more-detailed operando investigations of nanocatalysts at the single-particle level to revisit static models of structure-activity relationships.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 56.9
Times cited: 29
DOI: 10.1126/SCIENCE.ADF6984
|
“Mn(I) in an extended oxide : the synthesis and characterization of La1-xCaxMnO2+\delta (0.6\leq x\leq1)”. Dixon E, Hadermann J, Ramos S, Goodwin AL, Hayward MA, Journal of the American Chemical Society 133, 18397 (2011). http://doi.org/10.1021/ja207616c
Abstract: Reduction of La1xCaxMnO3 (0.6 ≤ x ≤ 1) perovskite phases with sodium hydride yields materials of composition La1xCaxMnO2+δ. The calcium-rich phases (x = 0.9, 1) adopt (La0.9Ca0.1)0.5Mn0.5O disordered rocksalt structures. However local structure analysis using reverse Monte Carlo refinement of models against pair distribution functions obtained from neutron total scattering data reveals lanthanum-rich La1xCaxMnO2+δ (x = 0.6, 0.67, 0.7) phases adopt disordered structures consisting of an intergrowth of sheets of MnO6 octahedra and sheets of MnO4 tetrahedra. X-ray absorption data confirm the presence of Mn(I) centers in La1xCaxMnO2+δ phases with x < 1. Low-temperature neutron diffraction data reveal La1xCaxMnO2+δ (x = 0.6, 0.67, 0.7) phases become antiferromagnetically ordered at low temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 33
DOI: 10.1021/ja207616c
|
“A New Method for Quantitative XEDS Tomography of Complex Heteronanostructures”. Zanaga D, Altantzis T, Polavarapu L, Liz-Marzán LM, Freitag B, Bals S, Particle and particle systems characterization 33, 396 (2016). http://doi.org/10.1002/ppsc.201600021
Abstract: Reliable quantification of 3D results obtained by X-ray Energy Dispersive Spectroscopy (XEDS) tomography is currently hampered by the presence of shadowing effects and poor spatial resolution. Here, we present a method that overcomes these problems by synergistically combining quantified XEDS data and High Angle Annular Dark Field – Scanning Transmission Electron Microscopy (HAADF-STEM) tomography. As a proof of principle, the approach is applied to characterize a complex Au/Ag nanorattle obtained through a galvanic replacement reaction. However, the technique we propose here is widely applicable to a broad range of nanostructures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.474
Times cited: 29
DOI: 10.1002/ppsc.201600021
|
“Unexpected optical response of single ZnO nanowires probed using controllable electrical contacts”. Zeng YI, Menghini M, Li DY, Lin SS, Ye ZZ, Hadermann J, Moorkens T, Seo JW, Locquet J-P, van Haesendonck C, Physical chemistry, chemical physics 13, 6931 (2011). http://doi.org/10.1039/c1cp00012h
Abstract: Relying on combined electron-beam lithography and lift-off methods Au/Ti bilayer electrical contacts were attached to individual ZnO nanowires (NWs) that were grown by a vapor phase deposition method. Reliable Schottky-type as well as ohmic contacts were obtained depending on whether or not an ion milling process was used. The response of the ZnO NWs to ultraviolet light was found to be sensitive to the type of contacts. The intrinsic electronic properties of the ZnO NWs were studied in a field-effect transistor configuration. The transfer characteristics, including gate threshold voltage, hysteresis and operational mode, were demonstrated to unexpectedly respond to visible light. The origin of this effect could be accounted for by the presence of point defects in the ZnO NWs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.123
Times cited: 7
DOI: 10.1039/c1cp00012h
|
“Atomic and electronic structure of a multidomain GeTe crystal”. Frolov AS, Sanchez-Barriga J, Callaert C, Hadermann J, Fedorov A V, Usachov DY, Chaika AN, Walls BC, Zhussupbekov K, Shvets I V, Muntwiler M, Amati M, Gregoratti L, Varykhalov AY, Rader O, Yashina L V, Acs Nano 14, 16576 (2020). http://doi.org/10.1021/ACSNANO.0C05851
Abstract: Renewed interest in the ferroelectric semi-conductor germanium telluride was recently triggered by the direct observation of a giant Rashba effect and a 30-year-old dream about a functional spin field-effect transistor. In this respect, all-electrical control of the spin texture in this material in combination with ferroelectric properties at the nanoscale would create advanced functionalities in spintronics and data information processing. Here, we investigate the atomic and electronic properties of GeTe bulk single crystals and their (111) surfaces. We succeeded in growing crystals possessing solely inversion domains of similar to 10 nm thickness parallel to each other. Using HAADF-TEM we observe two types of domain boundaries, one of them being similar in structure to the van der Waals gap in layered materials. This structure is responsible for the formation of surface domains with preferential Te-termination (similar to 68%) as we determined using photoelectron diffraction and XPS. The lateral dimensions of the surface domains are in the range of similar to 10-100 nm, and both Ge- and Te-terminations reveal no reconstruction. Using spin-ARPES we establish an intrinsic quantitative relationship between the spin polarization of pure bulk states and the relative contribution of different terminations, a result that is consistent with a reversal of the spin texture of the bulk Rashba bands for opposite configurations of the ferroelectric polarization within individual nanodomains. Our findings are important for potential applications of ferroelectric Rashba semiconductors in nonvolatile spintronic devices with advanced memory and computing capabilities at the nanoscale.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 17.1
DOI: 10.1021/ACSNANO.0C05851
|
“Charge order, frustration relief, and spin-orbit coupling in U3O8”. Saniz R, Baldinozzi G, Arts I, Lamoen D, Leinders G, Verwerft M, Physical review materials 7, 054410 (2023). http://doi.org/10.1103/PhysRevMaterials.7.054410
Abstract: Research efforts on the description of the low-temperature magnetic order and electronic properties of U3O8 have been inconclusive so far. Reinterpreting neutron scattering results, we use group representation theory to show that the ground state presents collinear out-of-plane magnetic moments, with antiferromagnetic coupling both in-layer and between layers. Charge order relieves the initial geometric frustration, generating a slightly distorted honeycomb sublattice with Néel-type order. The precise knowledge of the characteristics of this magnetic ground state is then used to explain the fine features of the band gap. In this system, spin-orbit coupling (SOC) is of critical importance, as it strongly affects the electronic structure, narrowing the gap by ∼38%, compared to calculations neglecting SOC. The predicted electronic structure actually explains the salient features of recent optical absorption measurements, further demonstrating the excellent agreement between the calculated ground state properties and experiment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.4
DOI: 10.1103/PhysRevMaterials.7.054410
|
“Nonvolatile resistive switching in Pt/LaAlO3/SrTiO3 heterostructures”. Wu S, Luo X, Turner S, Peng H, Lin W, Ding J, David A, Wang B, Van Tendeloo G, Wang J, Wu T;, Physical review X 3, 041027 (2013). http://doi.org/10.1103/PhysRevX.3.041027
Abstract: Resistive switching heterojunctions, which are promising for nonvolatile memory applications, usually share a capacitorlike metal-oxide-metal configuration. Here, we report on the nonvolatile resistive switching in Pt/LaAlO3/SrTiO3 heterostructures, where the conducting layer near the LaAlO3/SrTiO3 interface serves as the unconventional bottom electrode although both oxides are band insulators. Interestingly, the switching between low-resistance and high-resistance states is accompanied by reversible transitions between tunneling and Ohmic characteristics in the current transport perpendicular to the planes of the heterojunctions. We propose that the observed resistive switching is likely caused by the electric-field-induced drift of charged oxygen vacancies across the LaAlO3/SrTiO3 interface and the creation of defect-induced gap states within the ultrathin LaAlO3 layer. These metal-oxide-oxide heterojunctions with atomically smooth interfaces and defect-controlled transport provide a platform for the development of nonvolatile oxide nanoelectronics that integrate logic and memory devices.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.789
Times cited: 77
DOI: 10.1103/PhysRevX.3.041027
|
“Defects in high-dose oxygen implanted silicon : a TEM study”. Deveirman A, van Landuyt J, Vanhellemont J, Maes HE, Yallup K, Vacuum: the international journal and abstracting service for vacuum science and technology
T2 –, 1ST SIOMX WORKSHOP ( SEPARATION BY IMPLANTATION OF OXYGEN ) ( SWI-88 ), NOV 07-08, 1988, UNIV SURREY, GUILDFORD, ENGLAND 42, 367 (1991). http://doi.org/10.1016/0042-207X(91)90055-N
Abstract: Results are discussed of a transmission electron microscopy study of high-dose oxygen implanted silicon. In addition to the general high temperature (> 1200-degrees-C) annealing treatments also annealings at 'low' temperatures (1000-1100-degrees-C) were performed in order to slow down the precipitate and defect reactions. The observed dissolution of the oxide precipitates during prolonged high temperature annealing is explained by critical radius considerations. Threading dislocations are the remaining lattice defects in the silicon overlayer and cannot be removed by further annealing. Low temperature annealing results in the formation and subsequent unfaulting of extrinsic stacking fault loops below the buried oxide layer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.858
Times cited: 4
DOI: 10.1016/0042-207X(91)90055-N
|
“Point defect reactions in silicon studied in situ by high flux electron irradiation in high voltage transmission electron microscope”. Vanhellemont J, Romano Rodriguez A, Fedina L, van Landuyt J, Aseev A, Materials science and technology 11, 1194 (1995). http://doi.org/10.1179/mst.1995.11.11.1194
Abstract: Results are presented of in situ studies of 1 MeV electron irradiation induced (113) defect generation in silicon containing different types and concentrations of extrinsic point defects. A semiquantitative model is developed describing the influence of interfaces and stress fields and of extrinsic point defects on the (113) defect generation in silicon during irradiation. The theoretical results obtained are correlated with experimental data obtained on silicon uniformly doped with boron and phosphorus and with observations obtained by irradiating cross-sectional samples of wafers with highly doped surface layers. It is shown that in situ irradiation in a high voltage election microscope is a powerful tool for studying local point defect reactions in silicon. (C) 1995 The Institute of Materials.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 0.995
Times cited: 7
DOI: 10.1179/mst.1995.11.11.1194
|
“Optical spectroscopy of oxygen precipitates in heavily doped p-type silicon”. Simoen E, Loo R, Claeys C, de Gryse O, Clauws P, van Landuyt J, Lebedev O, Journal of physics : condensed matter
T2 –, Conference on Extended Defects in Semiconductors (EDS 2002), JUN 01-06, 2002, BOLOGNA, ITALY 14, 13185 (2002). http://doi.org/10.1088/0953-8984/14/48/367
Abstract: Results are presented on the photoluminescence (PL) characterization of heavily doped p(+) Czochralski silicon, which has been subjected to a two-step, oxygen precipitation heat treatment. It will be shown that the presence of oxygen precipitates gives rise to the D1, D2 and D5 lines, where the energy of the D1 line shifts to lower values for a stronger degree of precipitation. The occurrence of these PL features is also a function of the boron concentration in the p(+) material. The PL results are compared with Fourier transform infrared absorption data and with transmission electron microscope, results. From this, it is concluded that PL has a good potential for use in the assessment of oxygen precipitation in heavily doped silicon.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.649
Times cited: 3
DOI: 10.1088/0953-8984/14/48/367
|
“Evidence for another low-temperature phase transition in tetragonal Pb(ZrxTi1-x)O3 (x=0.515,0.520)”. Mishra RSK, Pandey D, Lemmens H, Van Tendeloo G, Physical review : B : condensed matter and materials physics 64, 054104 (2001). http://doi.org/10.1103/PhysRevB.64.054101
Abstract: Results of dielectric and resonance frequency (f(r)) measurements below room temperature are presented for Pb(ZrxTi1-x)O-3, x = 0.515 and 0.520. It is shown that the temperature coefficient of f(r) changes sign from negative to positive around 210 and 265 K for x = 0.520 and 200 and 260 K for x = 0.515. Anomalies in the real part of the dielectric constant (epsilon') are observed around the same temperatures at which the temperature coefficient of f(r) changes sign because of the electrostrictive coupling between the elastic and dielectric responses. Low-temperature powder x-ray-diffraction (XRD) data, however, reveal only one transition from the tetragonal to monoclinic phase similar to that reported by Noheda et al. [Phys. Rev. B, 61, 8687 (2000)]. Electron-diffraction data, on the other hand, reveal yet another structural transition at lower temperatures corresponding to the second anomaly in the epsilon' vs T and f(r) vs T curves. This second transition is shown to be a cell-doubling transition not observed by Noheda et al. in their XRD studies. The observation of superlattice reflections raises doubts about the correctness of the Cm space group proposed by Noheda et al. for the monoclinic phase of Pb(ZrxTi(1-x))O-3 below the second transition temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
DOI: 10.1103/PhysRevB.64.054101
|
“Measurement of local crystal lattice strain variations in dealloyed nanoporous gold”. Mahr C, Müller-Caspary K, Graf M, Lackmann A, Grieb T, Schowalter M, Krause FF, Mehrtens T, Wittstock A, Weissmueller J, Rosenauer A, Materials research letters 6, 84 (2018). http://doi.org/10.1080/21663831.2017.1396263
Abstract: Reversible macroscopic length changes in nanoporous structures can be achieved by applying electric potentials or by exposing them to different gases or liquids. Thus, these materials are interesting candidates for applications as sensors or actuators. Macroscopic length changes originate from microscopic changes of crystal lattice parameters. In this report, we show spatially resolved measurements of crystal lattice strain in dealloyed nanoporous gold. The results confirm theory by indicating a compression of the lattice along the axis of cylindrically shaped ligaments and an expansion in radial direction. Furthermore, we show that curved npAu surfaces show inward relaxation of the surface layer. [GRAPHICS] .
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.773
Times cited: 4
DOI: 10.1080/21663831.2017.1396263
|
“Quantifying inflow and RANS turbulence model form uncertainties for wind engineering flows”. Gorle C, Garcia Sánchez C, Iaccarino G, Journal of wind engineering and industrial aerodynamics
T2 –, 6th International Symposium on Computational Wind Engineering (CWE), JUN 08-12, 2014, Hamburg, GERMANY 144, 202 (2015). http://doi.org/10.1016/j.jweia.2015.03.025
Abstract: Reynolds-averaged Navier-Stokes (RANS) simulations are often used in the wind engineering practice for the analysis of turbulent bluff body flows. An approach that allows identifying the uncertainty related to the use of reduced-order turbulence models in RANS simulations would significantly increase the confidence in the use of simulation results as a basis for design decisions. In the present study we apply a strategy that enables quantifying these uncertainties by introducing perturbations in the Reynolds stress tensor to simulations of the flow in downtown Oklahoma City. The method is combined with a framework to quantify uncertainties in the inflow wind direction and intensity, and the final result of the UQ approach is compared to field measurement data for the velocity at 13 locations in the downtown area. (C) 2015 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.049
Times cited: 22
DOI: 10.1016/j.jweia.2015.03.025
|
“Electrochemical stability of rhodium-platinum core-shell nanoparticles : an identical location scanning transmission electron microscopy study”. Vega-Paredes M, Aymerich-Armengol R, Arenas Esteban D, Marti-Sanchez S, Bals S, Scheu C, Manjon AG, ACS nano 17, 16943 (2023). http://doi.org/10.1021/ACSNANO.3C04039
Abstract: Rhodium-platinum core-shell nanoparticleson a carbonsupport (Rh@Pt/C NPs) are promising candidates as anode catalystsfor polymer electrolyte membrane fuel cells. However, their electrochemicalstability needs to be further explored for successful applicationin commercial fuel cells. Here we employ identical location scanningtransmission electron microscopy to track the morphological and compositionalchanges of Rh@Pt/C NPs during potential cycling (10 000 cycles,0.06-0.8 V-RHE, 0.5 H2SO4)down to the atomic level, which are then used for understanding thecurrent evolution occurring during the potential cycles. Our resultsreveal a high stability of the Rh@Pt/C system and point toward particledetachment from the carbon support as the main degradation mechanism.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 17.1
Times cited: 2
DOI: 10.1021/ACSNANO.3C04039
|
“Composite Supraparticles with Tunable Light Emission”. Montanarella F, Altantzis T, Zanaga D, Rabouw FT, Bals S, Baesjou P, Vanmaekelbergh D, van Blaaderen A, ACS nano 11, 9136 (2017). http://doi.org/10.1021/acsnano.7b03975
Abstract: Robust luminophores emitting light with broadly tunable colors are desirable in many applications such as light-emitting diode (LED)-based lighting, displays, integrated optoelectronics and biology. Nanocrystalline quantum dots with multicolor emission, from core- and shell-localized excitons, as well as solid layers of mixed quantum dots that emit different colors have been proposed. Here, we report on colloidal supraparticles that are composed of three types of Cd(Se,ZnS) core/(Cd,Zn)S shell nanocrystals with emission in the red, green, and blue. The emission of the supraparticles can be varied from pure to composite colors over the entire visible region and finetuned into variable shades of white light by mixing the nanocrystals in controlled proportions. Our approach results in supraparticles with sizes spanning the colloidal domain and beyond that combine versatility and processability with a broad, stable, and tunable emission, promising applications in lighting devices and biological research.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 36
DOI: 10.1021/acsnano.7b03975
|
“Quantifying a Heterogeneous Ru Catalyst on Carbon Black Using ADF STEM”. Varambhia AM, Jones L, De Backer A, Fauske VT, Van Aert S, Ozkaya D, Nellist PD, Particle and particle systems characterization 33, 438 (2016). http://doi.org/10.1002/ppsc.201600067
Abstract: Ru catalysts are part of a set of late transition metal nanocatalysts that have garnered much interest for catalytic applications such as ammonia synthesis and fuel cell production. Their performance varies greatly depending on their morphology and size, these catalysts are widely studied using electron microscopy. Using recent developments in Annular Dark Field (ADF) Scanning Transmission Electron Microscopy (STEM) quantification techniques, a rapid atom counting procedure was utilized to document the evolution of a heterogeneous Ru catalyst supported on carbon black. Areas of the catalyst were imaged for approximately 15 minutes using ADF STEM. When the Ru clusters were exposed to the electron beam, the clusters changed phase from amorphous to crystalline. To quantify the thickness of the crystalline clusters, two techniques were applied (simulation and statistical decomposition) and compared. These techniques show that stable face centredcubic crystal structures in the form of rafts, between 2 and 8 atoms thick, were formed after the initial wetting of the carbon support.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.474
Times cited: 4
DOI: 10.1002/ppsc.201600067
|