Abstract: 'Natural' platelets are planar defects in {001} planes found in natural type-IaA/B diamonds. 'Man-made' platelets are platelets formed in the laboratory by annealing type-IaA diamonds at temperatures over 2500 degrees C. Careful study shows that the infrared (IR) spectra of the 'man-made' platelets are different from the IR spectra of 'natural' platelets. High-temperature (T greater than or equal to 2000 degrees C) annealing of platelets containing type-IaA/B diamonds modifies the IR absorption spectrum owing to the 'natural' platelets and makes it similar to the IR spectrum of the 'man-made' platelets. It is suggested that such high-temperature annealing changes the structure of the 'natural' platelets. The changes are too subtle to be detected by electron microscopy techniques. Topographic electron-energy-loss spectroscopy shows that platelets contain nitrogen at an average density of 0.7 atoms per a(0)(2); however, high-temperature annealing does not seem to affect the concentration of the nitrogen in the platelets.

Abstract: La1-xCaxMnO3-delta (LCMO) thin films are grown by pulsed laser deposition on a (100) SrTiO3 substrate at temperatures between 530 degrees C and 890 degrees C. The magnetotransport properties show a high negative magnetoresistance and a shift of the maximum of the R(T) curve as function of temperature. The Curie temperature changes with deposition temperature and film quality in the range of 100-220K. The film quality is characterised by X-ray diffraction and transmission electron microscopy (TEM); film and target compositions were verified by atomic emission spectroscopy. The local structure of the film depends on the growth conditions and substrate temperature. TEM reveals a slight distortion of the film leading to a breakdown of the symmetry from orthorhombic to monoclinic. At the highest growth temperatures, a well defined interface is observed within the LCMO film, parallel to the substrate surface; this interface divides the film into two lamellae with a different microstructure. The lamella close to the substrate is perfectly coherent with the substrate, suggesting that it is strained as a result of the lattice parameter mismatch; the upper lamella shows a typical domain structure with unusual translation interfaces characterised by a displacement vector of the type 1/2[010](m) and 1/2[001](m) when referred ten the monoclinic lattice.

Abstract: The crystal structure of BiSr8-xCa3+xO22 has been determined by single-crystal X-ray diffraction. This phase is the same as Bi9Sr11Ca5Oy that was previously studied by several authors as a secondary phase in the Bi-Sr-Ca-Cu-O system and coexists in thermodynamic equilibrium with the superconductors Bi2Sr2CuO6 and Bi2Sr2CaCu2O8 It crystallizes in the monoclinic space group P2(1)/c, with cell parameters a 11.037(3) Angstrom, b = 5.971(2) Angstrom, c = 19.703(7) Angstrom, beta = 101.46(3)degrees Z = 2. The structure was solved by direct methods and full-matrix least-squares refinement. It is built up by perovskite-related blocks of composition [Sr8-xBi2Ca3+xO16] that intergrow with double rows [Bi4O6] running along b. The perovskite blocks are formed by groups of five octahedra that are shifted from each other 3/2 root 2a(p) along [110](p) (a(p) being the parameter of the cubic perovskite subcell) in a zigzag configuration and are aligned with this direction parallel to the one forming an angle of 25" with the c axis. In turn, the perovskite blocks [Sr8-xBi2Ca3+xO16] are shifted from each other 1/2 of both a(p) and root 2a(p) along [100](p) and [110](p), respectively. In the double rows, two trivalent bismuth atoms are placed, forming dimeric anion complexes [Bi2O6].(6-).6- The oxygen atoms around bismuth in these dimers are placed in the vertexes of a distorted trigonal bipyramid, with one vacant position that would be occupied by the lone pairs characteristic for the electronic configuration of Bi(III). The B sites in the perovskite blocks are occupied by pentavalent bismuth atoms and calcium atoms; the remaining Sr and Ca ions occupy the A sites of the perovskite blocks with coordination numbers with oxygen ranging from 10 to 12. The mean valence for Bi is +3.67 [33.3% of Bi(V) and 66.7% of Bi(III)]. The oxygen vacancies are located in the boundaries between domains having the two possible configurations of the perovskite subcell as in the anionic superconductor Bi3BaO5.5. The oxidation of Bi6Sr8-xCa3+xO22 at 650 degrees C allows the complete filling of the oxygen vacancies to form the double perovskite (Sr2-xCax)Bi1.4Ca0.6O6 that shows 92.5% of bismuth in +5 oxidation state. The experimental high-resolution electon microscopy image and the electron diffraction pattern of powder samples along the [010]* zone axis are in good agreement with those calculated from the structural model obtained by single-crystal X-ray diffraction. The material is almost free of defects and the occurrence of planar defects is very exceptional.

Abstract: The optical and electrical properties and pi ase composition of magnetron sputtered antimony-doped SnOx thin films are investigated before and after laser thermotreatment The temperature dependencies on mobility and concentration of free charges are measured by Van der Pauw method. The gas sensitivity of SnOx has been measured before and after laser thermotreatment.

Abstract: The split diffuse maxima around the {110} and {100} positions in the diffraction pattern of short-range-ordered Cu1-xPdx alloys (x=0.10...0.60) are attributed to small atomic clusters, being part of the underlying fee lattice. By analyzing the reciprocal space geometry, our cluster method identifies two prominent cluster types: the tetrahedron of nearest neighbors and a linear three-points cluster along the [110] directions. Since both cluster types contain different information on the same nearest-neighbor correlations, local anisotropy has to be assumed. It is shown that the three interatomic pair interactions within these basic clusters are sufficient to generate the spot splitting in the diffraction pattern. A ground-state analysis with these interactions reproduces the results of the anisotropic next-nearest-neighbor Ising model.

Abstract: This HREM investigation focuses on the influence of point defects on the final epitaxial relation and atomic interface configuration in a CoSi2/Si(1 0 0) heterostructure. A two-step SPE-MBE grown CoSi2/Si(1 0 0) system is used and, by altering the number of deposited Co monolayers in the template layer, the point defect behavior is studied. We propose a film growth model in which the knowledge about the reconstructed (2 x 1) : Si(1 0 0) surface, the point defect behavior in the presence of an interface, especially a silicide interface, the migration of point defects through a lattice by formation of [1 0 0]-split interstitial (dumbbell) atomic configurations, and a new type of extended defect configurations in diamond type materials will all amalgamate. (C) 1998 Published by Elsevier Science B.V. All rights reserved.