“Nanoscale investigation by TEM and STEM-EELS of the laser induced yellowing”. Godet M, Vergès-Belmin V, Gauquelin N, Saheb M, Monnier J, Leroy E, Bourgon J, Verbeeck J, Andraud C, Micron 115, 25 (2018). http://doi.org/10.1016/j.micron.2018.08.006
Abstract: Nd-YAG QS laser cleaning of soiled stone at 1064 nm can sometimes result in a more yellow appearance compared to other cleaning techniques. Especially in France, this yellowing effect is still considered as a major aesthetic issue by the architects and conservators. One explanation states that the yellowing is linked to the formation of iron-rich nanophase(s) through the laser beam interaction with black crusts that would re-deposit on the cleaned substrate after irradiation. To characterize these nanophases, a model crust containing hematite was elaborated and laser irradiated using a Nd-YAG QS laser. The color of the sample shifted instantaneously from red to a bright yellow and numerous particles were ablated in a visible smoke. Transmission electron microscopy (TEM) was used to examine the morphology and the crystallinity of the neo-formed compounds, both on the surface of the samples and in the ablated materials. In addition, an investigation of the chemical and structural properties of the nanophases was conducted by X-ray dispersive energy (EDX) and electron energy loss (EELS) spectroscopies. It was found that both the surface of the sample and the ablated materials are covered by crystallized nano-spheres and nano-residues, all containing iron and oxygen, sometimes along with calcium and sulfur. In particular an interfacial area containing the four elements was evidenced between some nanostructures and the substrate. Magnetite Fe3O4 was also identified at the nanoscale. This study demonstrates that the laser yellowing of a model crust is linked to the presence of iron-rich nanophases including CaxFeySzOδ nanostructures and magnetite Fe3O4 at the surface after irradiation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.98
Times cited: 9
DOI: 10.1016/j.micron.2018.08.006
|
|
|
“EM characterization of precipitates in as-cast and annealed Ni45.5Ti45.5Nb9 shape memory alloys”. Shi H, Frenzel J, Schryvers D, Materials science forum 738/739, 113 (2013). http://doi.org/10.4028/www.scientific.net/MSF.738-739.113
Abstract: Nb-rich precipitates in the matrix of as-cast and annealed Ni45.5Ti45.5Nb9 alloys are investigated by scanning and scanning transmission electron microscopy, including slice-and-view and geometric phase analysis (GPA). The Nb-rich bcc nano-precipitates in the as-cast alloy have a 10% lattice parameter difference with the B2 matrix and reveal compensating interface dislocations. The 3D reconstruction of the configuration of small Nb-rich precipitates in the annealed alloy reveals a wall-like distribution of precipitates, which may increase the thermal hysteresis of the material.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.4028/www.scientific.net/MSF.738-739.113
|
|
|
“Electron microscopy study of Nb-rich nanoprecipitates in NiTiNb and their influence on the martensitic transformation”. Shi H, Pourbabak S, Van Humbeeck J, Schryvers D, Scripta materialia 67, 939 (2012). http://doi.org/10.1016/j.scriptamat.2012.08.020
Abstract: Nb-rich nanoprecipitates in the matrix of an annealed commercial NiTiNb alloy are investigated by scanning and transmission electron microscopy, including slice-and-view and chemical analysis. The precipitates have a diameter of around 100 nm, are faceted and have a cube-on-cube relation with the B2 matrix. In situ TEM cooling shows that the martensitic transformation is hampered by the presence of these precipitates. The latter could explain the increase in hysteresis when compared with the binary system.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 29
DOI: 10.1016/j.scriptamat.2012.08.020
|
|
|
“Site occupation of Nb atoms in ternary Ni-Ti-Nb shape memory alloys”. Shi H, Frenzel J, Martinez GT, Van Rompaey S, Bakulin A, Kulkova A, Van Aert S, Schryvers D, Acta materialia 74, 85 (2014). http://doi.org/10.1016/j.actamat.2014.03.062
Abstract: Nb occupancy in the austenite B2-NiTi matrix and Ti2Ni phase in NiTiNb shape memory alloys was investigated by aberration-corrected scanning transmission electron microscopy and precession electron diffraction. In both cases, Nb atoms were found to prefer to occupy the Ti rather than Ni sites. A projector augmented wave method within density functional theory was used to calculate the atomic and electronic structures of the austenitic B2-NiTi matrix phase and the Ti2Ni precipitates both with and without addition of Nb. The obtained formation energies and analysis of structural and electronic characteristics explain the preference for Ti sites for Nb over Ni sites.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 21
DOI: 10.1016/j.actamat.2014.03.062
|
|
|
“Two-in-one solution using insect wings to produce graphene-graphite films for efficient electrocatalysis”. Li H, Zhang L, Li L, Wu C, Huo Y, Chen Y, Liu X, Ke X, Luo J, Van Tendeloo G, Nano Research 12, 33 (2019). http://doi.org/10.1007/S12274-018-2172-Z
Abstract: Natural organisms contain rich elements and naturally optimized smart structures, both of which have inspired various innovative concepts and designs in human society. In particular, several natural organisms have been used as element sources to synthesize low-cost and environmentally friendly electrocatalysts for the oxygen reduction reaction (ORR) in fuel cells and metal-air batteries, which are clean energy devices. However, to date, no naturally optimized smart structures have been employed in the synthesis of ORR catalysts, including graphene-based materials. Here, we demonstrate a novel strategy to synthesize graphene-graphite films (GGFs) by heating butterfly wings coated with FeCl3 in N-2, in which the full power of natural organisms is utilized. The wings work not only as an element source for GGF generation but also as a porous supporting structure for effective nitrogen doping, two-dimensional spreading, and double-face exposure of the GGFs. These GGFs exhibit a half-wave potential of 0.942 V and a H2O2 yield of < 0.07% for ORR electrocatalysis; these values are comparable to those for the best commercial Pt/C and all previously reported ORR catalysts in alkaline media. This two-in-one strategy is also successful with cicada and dragonfly wings, indicating that it is a universal, green, and cost-effective method for developing high-performance graphene-based materials.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.354
Times cited: 7
DOI: 10.1007/S12274-018-2172-Z
|
|
|
“Oxidation and degradation of native wheat starch by acidic bromate in water at room temperature”. Komulainen S, Verlackt C, Pursiainen J, Lajunen M, Carbohydrate Polymers 93, 73 (2013). http://doi.org/10.1016/j.carbpol.2012.06.001
Abstract: Native wheat starch was oxidized by benign acidic bromate in water at room temperature. HPLC-ELSD study indicated that starch degraded in the course of oxidation but it still had a polymeric structure characterized by H-1, C-13, HSQC and HMBC NMR measurements. Products were generally water-soluble fragments but the use of a short reaction time and dilute reaction mixture yielded water-insoluble products. Titration of the products showed, that the increase of the starch content and reaction time increased the content of carbonyl and carboxyl groups in the range of 0.5-2.5% and 1.7-17.2%, respectively, in the product fragments. A mechanism for the oxidation reaction was proposed. (C) 2012 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 4.811
Times cited: 32
DOI: 10.1016/j.carbpol.2012.06.001
|
|
|
“p -CoO x / n -SnO 2 nanostructures: New highly selective materials for H 2 S detection”. Rumyantseva MN, Vladimirova SA, Vorobyeva NA, Giebelhaus I, Mathur S, Chizhov AS, Khmelevsky NO, Aksenenko AY, Kozlovsky VF, Karakulina OM, Hadermann J, Abakumov AM, Gaskov AM, Sensors and actuators : B : chemical (2017). http://doi.org/10.1016/j.snb.2017.08.096
Abstract: Nanostructures p-CoOx/n-SnO2 based on tin oxide nanowires have been prepared by two step CVD technique and characterized in detail by XRD, XRF, XPS, HAADF-STEM imaging and EDX-STEM mapping. Depending on the temperature of decomposition of cobalt complex during the second step of CVD synthesis of nanostructures cobalt oxide forms a coating and/or isolated nanoparticles on SnO2 nanowire surface. It was found that cobalt presents in +2 and +3 oxidation states. The measurements of gas sensor properties have been carried out during exposure to CO (14 ppm), NH3 (21 ppm), and H2S (2 ppm) in dry air. The opposite trends were observed in the effect of cobalt oxide on the SnO2 gas sensitivity when detecting CO or NH3 in comparison to H2S. The decrease of sensor signal toward CO and NH3 was attributed to high catalytic activity of Co3O4 in oxidation of these gases. Contrary, the significant increase of sensor signal in the presence of H2S was attributed to the formation of metallic cobalt sulfide and removal of the barrier between p-CoOx and n-SnO2. This effect provides an excellent selectivity of p-CoOx/n-SnO2 nanostructures in H2S detection.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.401
Times cited: 13
DOI: 10.1016/j.snb.2017.08.096
|
|
|
“Correlation between the nanocrystalline Sm(Fe,Mo)12 and its out of equilibrium phase Sm(Fe,Mo)10”. Khazzan S, Bessais L, Van Tendeloo G, Mliki N, Journal of magnetism and magnetic materials 363, 125 (2014). http://doi.org/10.1016/j.jmmm.2014.03.030
Abstract: Nanostructured Sm-Fe-Mo semi-hard magnetic material exhibiting enhanced magnetic properties can be produced by ball milling followed by recrystallization. Milled samples were annealed for 30 min in a vacuum at different temperatures (T-A) between 700 and 1190 degrees C. The effects of heat treatment and Mo content on structural and magnetic property changes have been investigated by means of X-ray diffraction using the Rietvekl method, transmission electron microscopy and magnetic measurements. For samples annealed at T-A > 900 degrees C the tetragonal ThMn12-type structure is identified, while for 700 < T-A < 900 degrees C a new out of equilibrium P6/mmm type structure was found as the major phase. This novel nanocrystalline phase has never been synthesized before. The correspondent stoichiometry is determined on the basis of the vacancy model. The Rietveld analysis gives a stoichiometry ratio equal to 1:10, for the out of equilibrium hexagonal phase, which is described with three crystallographic transition metal sites: 3g is fully occupied, 61 occupation is limited to hexagons surrounding the Fe dumbbell pairs 2e. We have performed a magnetic and structural study of nanocrystalline metastable P6/mrnm Sm(Fe1-xMo)(10), correlated with structural transformation towards its equilibrium derivative 14/mrnm Sm(Fe1-xMo)(12). A maximum of the coercive field H-C (H-C > 5 kOe) has been observed for the new hexagonal P6/rnmm phase suggesting that nanocrystalline Sm(Fe,Mo)(10), is a semi hard material, and is potential candidate for magnetic recording. (C) 2014 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.63
Times cited: 6
DOI: 10.1016/j.jmmm.2014.03.030
|
|
|
“One-Step Microheterogeneous Formation of Rutile@Anatase Core–Shell Nanostructured Microspheres Discovered by Precise Phase Mapping”. Tarasov A, Hu Z-Y, Meledina M, Trusov G, Goodilin E, Van Tendeloo G, Dobrovolsky Y, The journal of physical chemistry: C : nanomaterials and interfaces 121, 4443 (2017). http://doi.org/10.1021/acs.jpcc.6b12991
Abstract: Nanostructured core−shell microspheres with a rough rutile core and a thin anatase shell are synthesized via a one-step heterogeneous templated hydrolysis process of TiCl4 vapor on the aerosol water−air interface. The rutile-in-anatase core−shell structure has been evidenced by different electron microscopy techniques, including electron energy-loss spectroscopy and 3D electron tomography. A new mechanism for the formation of a crystalline rutile core inside the anatase shell is proposed based on a statistical evaluation of a large number of electron microscopy data. We found that the control over the TiCl4 vapor pressure, the ratio between TiCl4 and H2O aerosol, and the reaction conditions plays a crucial role in the formation of the core−shell morphology and increases the yield of nanostructured microspheres.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 4
DOI: 10.1021/acs.jpcc.6b12991
|
|
|
“One-pot synthesis of carbon-coated nanostructured iron oxide on few-layer graphene for lithium-ion batteries”. Sun Z, Madej E, Wiktor, Sinev I, Fischer RA, Van Tendeloo G, Muhler M, Schuhmann W, Ventosa E, Chemistry: a European journal 21, 16154 (2015). http://doi.org/10.1002/chem.201501935
Abstract: Nanostructure engineering has been demonstrated to improve the electrochemical performance of iron oxide based electrodes in Li-ion batteries (LIBs). However, the synthesis of advanced functional materials often requires multiple steps. Herein, we present a facile one-pot synthesis of carbon-coated nanostructured iron oxide on few-layer graphene through high-pressure pyrolysis of ferrocene in the presence of pristine graphene. The ferrocene precursor supplies both iron and carbon to form the carbon-coated iron oxide, while the graphene acts as a high-surface-area anchor to achieve small metal oxide nanoparticles. When evaluated as a negative-electrode material for LIBs, our composite showed improved electrochemical performance compared to commercial iron oxide nanopowders, especially at fast charge/discharge rates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 8
DOI: 10.1002/chem.201501935
|
|
|
“Observation of nanostripes and -clusters in (Nd, EuGd)Ba2Cu3Ox superconductors”. Koblischka MR, Winter M, Das P, Koblischka-Veneva A, Muralidhar M, Wolf T, Babu NH, Turner S, Van Tendeloo G, Hartmann U, Physica: C : superconductivity 469, 168 (2009). http://doi.org/10.1016/j.physc.2009.01.007
Abstract: Nanostripes are observed in melt-textured and single-crystalline samples of the ternary light rare earth (LRE)-compound (Nd0.33Eu0.33Gd0.33)Ba2Cu3Ox (NEG) by means of atomic force microscopy, scanning tunnelling microscopy at ambient conditions, combined with transmission electron microscopy and electron backscatter diffraction. This enables the observation of several important features: The nanostripes are formed by chains of nanoclusters, representing the LRE/Ba substitution. The dimensions of the nanostripes are similar for both types of NEG samples. The periodicity of the nanostripes is found to range between 40 and 60 nm; the shape of the nanoclusters is elliptic with a major axis length between 300 and 500 nm and a minor axis length of about 30150 nm. The stripes are filling effectively the space in between the twin boundaries. Concerning the flux pinning, the nanoclusters are the important pinning sites, not the nanostripes themselves.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.404
Times cited: 6
DOI: 10.1016/j.physc.2009.01.007
|
|
|
Friedrich T (2023) Quantifying atomic structures using neural networks from 4D scanning transmission electron microscopy (STEM) datasets. 127 p
Abstract: Nanoscience and nanotechnologies are of immense importance across many fields of science and for numerous practical applications. In this context, scanning transmission electron microscopy (STEM) and 4D-STEM are among the most powerful characterization methods at the atomic scale. Annular dark-field (ADF)-STEM can be used to quantify atomic structures in 3D by counting atoms based on a single projection image. In 4D-STEM a full diffraction pattern is recorded at each scan step, which enables more dose efficient imaging and the utilization of various advanced imaging modalities, which can however be complex and slow. Both, STEM and 4D-STEM suffer from noise and distortions. In the first section of this work the most important of these distortions are discussed and it is shown how image restoration with a dedicated convolutional neural network (CNN) can be beneficial for atomic structure quantifications in ADF-STEM. In the second part, a new 4D-STEM imaging method real-time-integrated-centre-of-mass (riCOM) is introduced, which is a very dose-efficient and fast algorithm that enables unprecedented live-imaging capabilities for 4D-STEM. It is based on the integrated centre-of-mass approach, but is reformulated with variable integration ranges and optional filters, which allows for a tunable contrast transfer function. This enables the imaging of light and heavy elements simultaneously at very low doses. In the third part another new 4D-STEM method, coined AIRPI (AI-assisted rapid phase imaging) is introduced, which uses a CNN to retrieve a patch of the specimen's phase image for each scan position, based on the diffraction patterns in the probe's immediate surroundings. This allows also live imaging in principle and surpasses comparable state-of-the-art algorithms in terms of resolution also at low doses. Different atomic columns can be reliably distinguished over a wide range of atomic numbers, enabling a very good image interpretability. Further, AIRPI can recover low frequency image components, which preserves thickness information. This is a unique and important feature which could make quantitative 4D-STEM feasible.
Keywords: Doctoral thesis; Electron microscopy for materials research (EMAT)
|
|
|
“Biocompatible Zr-based nanoscale MOFs coated with modified poly(epsilon-caprolactone) as anticancer drug carriers”. Filippousi M, Turner S, Leus K, Siafaka PI, Tseligka ED, Vandichel M, Nanaki SG, Vizirianakis IS, Bikiaris DN, Van Der Voort P, Van Tendeloo G, International journal of pharmaceutics 509, 208 (2016). http://doi.org/10.1016/j.ijpharm.2016.05.048
Abstract: Nanoscale Zr-based metal organic frameworks (MOFs) UiO-66 and UiO-67 were studied as potential anticancer drug delivery vehicles. Two model drugs were used, hydrophobic paclitaxel and hydrophilic cisplatin, and were adsorbed onto/into the nano MOFs (NMOFs). The drug loaded MOFs were further encapsulated inside a modified poly(epsilon-caprolactone) with d-alpha-tocopheryl polyethylene glycol succinate polymeric matrix, in the form of microparticles, in order to prepare sustained release formulations and to reduce the drug toxicity. The drugs physical state and release rate was studied at 37 degrees C using Simulated Body Fluid. It was found that the drug release depends on the interaction between the MOFs and the drugs while the controlled release rates can be attributed to the microencapsulated formulations. The in vitro antitumor activity was assessed using HSC-3 (human oral squamous carcinoma; head and neck) and U-87 MG (human glioblastoma grade IV; astrocytoma) cancer cells. Cytotoxicity studies for both cell lines showed that the polymer coated, drug loaded MOFs exhibited better anticancer activity compared to free paclitaxel and cisplatin solutions at different concentrations.
Keywords: A1 Journal article; Pharmacology. Therapy; Electron microscopy for materials research (EMAT)
Impact Factor: 3.649
Times cited: 37
DOI: 10.1016/j.ijpharm.2016.05.048
|
|
|
“Anatase TiO2nanoparticle coating on porous COK-12 platelets as highly active and reusable photocatalysts”. Wee LH, Meledina M, Turner S, Custers K, Kerkhofs S, Sree SP, Gobechiya E, Kirschhock CEA, Van Tendeloo G, Martens JA, RSC advances 6, 46678 (2016). http://doi.org/10.1039/C6RA06141A
Abstract: Nanoscale TiO2 photocatalysts are widely used for biomedical applications, self-cleaning processes and wastewater treatments. The impregnation/deposition of TiO2 nanoparticles is indispensable for facile handling and separation as well as the improvement of their photocatalytic performance. In the present study, ordered mesoporous COK-12 silica thin platelets with a high-aspect-ratio and rough surfaces are demonstrated as a potential nanoporous support for homogeneous TiO2 nanoparticle coatings with high loading up to 16.7 wt%. The photocatalytic composite of COK-12 platelets and TiO2 nanoparticles is characterized in detail by HRSEM, SAXS, XRD, N2 physisorption analysis, solid-state UV-vis spectroscopy, HAADF-STEM, EDX analysis, and electron tomography. HAADF-STEM-EDX and electron tomography studies reveal a homogeneous dispersion of nanosized TiO2 nanoparticles over COK-12 platelets. The final composite material with anatase TiO2 nanoparticles that demonstrate a blueshifted semiconductor band gap energy of 3.2 eV coated on a highly porous COK-12 support shows exceptional photocatalytic catalytic activity for photodegradation of organic dyes (rhodamine 6G and methylene blue) and an organic pollutant (1-adamantanol) under UV light radiation, outperforming the commercial P25 TiO2 (Degussa) catalyst.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 6
DOI: 10.1039/C6RA06141A
|
|
|
“Strain Anisotropy and Magnetic Domains in Embedded Nanomagnets”. Nord M, Semisalova A, Kákay A, Hlawacek G, MacLaren I, Liersch V, Volkov OM, Makarov D, Paterson GW, Potzger K, Lindner J, Fassbender J, McGrouther D, Bali R, Small , 1904738 (2019). http://doi.org/10.1002/smll.201904738
Abstract: Nanoscale modifications of strain and magnetic anisotropy can open pathways to engineering magnetic domains for device applications. A periodic magnetic domain structure can be stabilized in sub‐200 nm wide linear as well as curved magnets, embedded within a flat non‐ferromagnetic thin film. The nanomagnets are produced within a non‐ferromagnetic B2‐ordered Fe60Al40 thin film, where local irradiation by a focused ion beam causes the formation of disordered and strongly ferromagnetic regions of A2 Fe60Al40. An anisotropic lattice relaxation is observed, such that the in‐plane lattice parameter is larger when measured parallel to the magnet short‐axis as compared to its length. This in‐plane structural anisotropy manifests a magnetic anisotropy contribution, generating an easy‐axis parallel to the short axis. The competing effect of the strain and shape anisotropies stabilizes a periodic domain pattern in linear as well as spiral nanomagnets, providing a versatile and geometrically controllable path to engineering the strain and thereby the magnetic anisotropy at the nanoscale.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 2
DOI: 10.1002/smll.201904738
|
|
|
“Effects of Nanostructure and Coating on the Mechanics of Carbon Nanotube Arrays”. Poelma RH, Fan X, Hu Z-Y, Van Tendeloo G, van Zeijl HW, Zhang GQ, Advanced functional materials 26, 1233 (2016). http://doi.org/10.1002/adfm.201503673
Abstract: Nanoscale materials are one of the few engineering materials that can be grown from the bottom up in a controlled manner. Here, the effects of nanostructure and nanoscale conformal coating on the mechanical behavior of vertically aligned carbon nanotube (CNT) arrays through experiments and simulation are systematically investigated. A modeling approach is developed and used to quantify the compressive strength and modulus of the CNT array under large deformation. The model accounts for the porous
nanostructure, which contains multiple CNTs with random waviness, van der Waals interactions, fracture strain, contacts, and frictional forces. CNT array micropillars are grown and their porous nanostructure is controlled by the infi ltration and deposition of thin conformal coatings using chemical vapor deposition. Flat-punch nanoindentation experiments reveal signifi cant changes in material properties as a function of coating thickness. The simulations explain the experimental results and show the novel failure transition regime that changes from collective CNT buckling toward structural collapse due to fracture. The compressive strength and the elastic
modulus increase exponentially as a function of the coating thickness and demonstrate a unique dependency on the CNT waviness. More interestingly, a design rule is identifi ed that predicts the optimum coating thickness for porous materials.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 17
DOI: 10.1002/adfm.201503673
|
|
|
“Local environment of Fe dopants in nanoscale Fe : CeO2-x oxygen storage material”. Meledina M, Turner S, Galvita VV, Poelman H, Marin GB, Van Tendeloo G, Nanoscale 7, 3196 (2015). http://doi.org/10.1039/c4nr06060a
Abstract: Nanoscale Fe : CeO2-x oxygen storage material for the process of chemical looping has been investigated by advanced transmission electron microscopy and electron energy-loss spectroscopy before and after a model looping procedure, consisting of redox cycles at heightened temperature. Separately, the activity of the nanomaterial has been tested in a toluene total oxidation reaction. The results show that the material consists of ceria nanoparticles, doped with single Fe atoms and small FeOx clusters. The iron ion is partially present as Fe3+ in a solid solution within the ceria lattice. Furthermore, enrichment of reduced Fe2+ species is observed in nanovoids present in the ceria nanoparticles, as well as at the ceria surface. After chemical looping, agglomeration occurs and reduced nanoclusters appear at ceria grain boundaries formed by sintering. These clusters originate from surface Fe2+ aggregation, and from bulk Fe3+, which “leaks out” in reduced state after cycling to a slightly more agglomerated form. The activity of Fe : CeO2 during the toluene total oxidation part of the chemical looping cycle is ensured by the dopant Fe in the Fe1-xCexO2 solid solution, and by surface Fe species. These measurements on a model Fe : CeO2-x oxygen storage material give a unique insight into the behavior of dopants within a nanosized ceria host, and allow to interpret a plethora of (doped) cerium oxide-based reactions.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 17
DOI: 10.1039/c4nr06060a
|
|
|
“Measuring the corrugation amplitude of suspended and supported graphene”. Kirilenko DA, Dideykin AT, Van Tendeloo G, Physical review : B : condensed matter and materials physics 84, 235417 (2011). http://doi.org/10.1103/PhysRevB.84.235417
Abstract: Nanoscale corrugation is a fundamental property of graphene arising from its low-dimensional nature. It places a fundamental limit to the conductivity of graphene and influences its properties. However the degree of the influence of the corrugation has not been well established because of the little knowledge about its spectrum in suspended graphene. We present a transmission electron microscopy technique that enables us to measure the average corrugation height and length. We applied the technique also to measure the temperature dependence of the corrugation. The difference in corrugation between suspended and supported graphene has been illustrated.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 31
DOI: 10.1103/PhysRevB.84.235417
|
|
|
“Tailoring Cu+ for Ga3+ cation exchange in Cu2-xS and CuInS2 nanocrystals by controlling the Ga precursor chemistry”. Hinterding SOM, Berends AC, Kurttepeli M, Moret M-E, Meeldijk JD, Bals S, van der Stam W, de Donega CM, ACS nano 13, 12880 (2019). http://doi.org/10.1021/ACSNANO.9B05337
Abstract: Nanoscale cation exchange (CE) has resulted in colloidal nanomaterials that are unattainable by direct synthesis methods. Aliovalent CE is complex and synthetically challenging because the exchange of an unequal number of host and guest cations is required to maintain charge balance. An approach to control aliovalent CE reactions is the use of a single reactant to both supply the guest cation and extract the host cation. Here, we study the application of GaCl3-L complexes [L = trioctylphosphine (TOP), triphenylphosphite (TPP), diphenylphosphine (DPP)] as reactants in the exchange of Cu+ for Ga3+ in Cu2-xS nanocrystals. We find that noncomplexed GaCl3 etches the nanocrystals by S2- extraction, whereas GaCl3-TOP is unreactive. Successful exchange of Cu+ for Ga3+ is only possible when GaCl3 is complexed with either TPP or DPP. This is attributed to the pivotal role of the Cu2-xS-GaCl3-L activated complex that forms at the surface of the nanocrystal at the onset of the CE reaction, which must be such that simultaneous Ga3+ insertion and Cu+ extraction can occur. This requisite is only met if GaCl3 is bound to a phosphine ligand, with a moderate bond strength, to allow facile dissociation of the complex at the nanocrystal surface. The general validity of this mechanism is demonstrated by using GaCl3-DPP to convert CuInS2 into (Cu,Ga,In)S-2 nanocrystals, which increases the photoluminescence quantum yield 10 -fold, while blue -shifting the photoluminescence into the NIR biological window. This highlights the general applicability of the mechanistic insights provided by our work.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 27
DOI: 10.1021/ACSNANO.9B05337
|
|
|
“Nanorattles with tailored electric field enhancement”. Schnepf MJ, Mayer M, Kuttner C, Tebbe M, Wolf D, Dulle M, Altantzis T, Formanek P, Förster S, Bals S, König TAF, Fery A, Nanoscale 9, 9376 (2017). http://doi.org/10.1039/C7NR02952G
Abstract: Nanorattles are metallic core–shell particles with core and shell separated by a dielectric spacer. These
nanorattles have been identified as a promising class of nanoparticles, due to their extraordinary high
electric-field enhancement inside the cavity. Limiting factors are reproducibility and loss of axial symmetry
owing to the movable metal core; movement of the core results in fluctuation of the nanocavity dimensions
and commensurate variations in enhancement factor. We present a novel synthetic approach for
the robust fixation of the central gold rod within a well-defined box, which results in an axisymmetric
nanorattle. We determine the structure of the resulting axisymmetric nanorattles by advanced transmission
electron microscopy (TEM) and small-angle X-ray scattering (SAXS). Optical absorption and scattering
cross-sections obtained from UV-vis-NIR spectroscopy quantitatively agree with finite-difference
time-domain (FDTD) simulations based on the structural model derived from SAXS. The predictions of
high and homogenous field enhancement are evidenced by scanning TEM electron energy loss spectroscopy
(STEM-EELS) measurement on single-particle level. Thus, comprehensive understanding of
structural and optical properties is achieved for this class of nanoparticles, paving the way for photonic
applications where a defined and robust unit cell is crucial.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 69
DOI: 10.1039/C7NR02952G
|
|
|
“Y2O3 inclusions in YBa2Cu3O7-\delta thin films”. Verbist K, Vasiliev AL, Van Tendeloo G, Applied physics letters 66, 1424 (1995). http://doi.org/10.1063/1.113266
Abstract: Nanoprecipitates in YBa2Cu3O7‐δ(YBCO) thin films have been identified by high resolution electron microscopy (HREM) as Y2O3 inclusions; they correspond to two different types of epitaxial relationships namely [001] or [110] parallel to the YBCOc‐axis. The [001] precipitates are situated near the YBCO surface, in the bulk and on the YBCO film/substrate interface. The [110] precipitates have only been observed at the surface. Literature data have been reinterpreted.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.302
Times cited: 28
DOI: 10.1063/1.113266
|
|
|
“Electrodeposition of Highly Porous Pt Nanoparticles Studied by Quantitative 3D Electron Tomography: Influence of Growth Mechanisms and Potential Cycling on the Active Surface Area”. Ustarroz J, Geboes B, Vanrompay H, Sentosun K, Bals S, Breugelmans T, Hubin A, ACS applied materials and interfaces 9, 16168 (2017). http://doi.org/10.1021/acsami.7b01619
Abstract: Nanoporous Pt nanoparticles (NPs) are promising fuel cell catalysts due to their large surface area and increased electrocatalytic activity towards the oxygen reduction reaction (ORR). Herein, we report on the infuence of the growth mechanisms on the surface properties of electrodeposited Pt dendritic NPs with large surface areas. The electrochemically active surface was studied by hydrogen underpotential deposition (HUPD) and compared for the rst time to high angle annular dark eld scanning transmission electron microscopy (HAADF-STEM) quantitative 3D electron tomography of individual nanoparticles. Large nucleation overpotential leads to a large surface coverage of Pt roughened spheroids, which provide large roughness factor (Rf ) but low mass-specic electrochemically active surface area (EASA). Lowering the nucleation overpotential leads to highly porous Pt NPs with pores protruding to the center of the structure. At the expense of smaller Rf , the obtained EASA values of these structures are in the range of these of large surface area supported fuel cell catalysts. The active surface area of the Pt dendritic NPs was measured by electron tomography and it was found that the potential cycling in the H adsorption/desorption and Pt oxidation/reduction region, which is generally performed to determine the EASA, leads to a signicant reduction of that surface area due to a partial collapse of their dendritic and porous morphology. Interestingly, the extrapolation of the microscopic tomography results to macroscopic electrochemical parameters indicated that the surface properties measured by H UPD are comparable to the values measured on individual NPs by electron tomography after the degradation caused by the H UPD measurement. These results highlight that the combination of electrochemical and quantitative 3D surface analysis techniques is essential to provide insights into the surface properties, the electrochemical stability and, hence, the applicability of these materials. Moreover, it indicates that care must be taken with widely used electrochemical methods of surface area determination, especially in the case of large surface area and possibly unstable nanostructures, since the measured surface can be strongly aected by the measurement itself.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 7.504
Times cited: 24
DOI: 10.1021/acsami.7b01619
|
|
|
“Electrochemical behavior of electrodeposited nanoporous Pt catalysts for the oxygen reduction reaction”. Geboes B, Ustarroz J, Sentosun K, Vanrompay H, Hubin A, Bals S, Breugelmans T, ACS catalysis 6, 5856 (2016). http://doi.org/10.1021/acscatal.6b00668
Abstract: Nanoporous Pt based nanoparticles (NP's) are promising fuel cell catalysts due to their high surface area and increased electrocatalytic activity toward the ORR In this work a direct double-pulse electrodeposition procedure at room temperature is applied to obtain dendritic Pt structures (89 nm diameter) with a high level of porosity (ca. 25%) and nanopores of 2 nm protruding until the center of the NP's. The particle morphology is characterized using aberration corrected high angle annular dark field scanning transmission electron microscopy (HAADF-STEM) and electron tomography (ET) combined with field emission scanning electron microscopy (FESEM) and macroscopic electrochemical measurements to assess their activity and stability toward the ORR. Macroscopic determination of the active surface area through hydrogen UPD measurements in combination with FESEM and ET showed that a considerable amount of the active sites inside the pores of the low overpotential NP's were accessible to oxygen species. As a result of this accessibility, up to a 9-fold enhancement of the Pt mass corrected ORR activity at 0.85 V vs RHE was observed at the highly porous structures. After successive potential cycling upward to 1.5 V vs RHE in a deaerated HClO4 solution a negative shift of 71 mV in half-wave potential occurred. This decrease in ORR activity could be correlated to the partial collapse of the nanopores, visible in both the EASA values and 3D ET reconstructions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 10.614
Times cited: 48
DOI: 10.1021/acscatal.6b00668
|
|
|
“Structural diversity in three-dimensional self-assembly of nanoplatelets by spherical confinement”. Wang D, Hermes M, Najmr S, Tasios N, Grau-Carbonell A, Liu Y, Bals S, Dijkstra M, Murray CB, van Blaaderen A, Nature communications 13, 6001 (2022). http://doi.org/10.1038/S41467-022-33616-Y
Abstract: Nanoplatelets offer many possibilities to construct advanced materials due to new properties associated with their (semi)two-dimensional shapes. However, precise control of both positional and orientational order of the nanoplatelets in three dimensions, which is required to achieve emerging and collective properties, is challenging to realize. Here, we combine experiments, advanced electron tomography and computer simulations to explore the structure of supraparticles self-assembled from nanoplatelets in slowly drying emulsion droplets. We demonstrate that the rich phase behaviour of nanoplatelets, and its sensitivity to subtle changes in shape and interaction potential can be used to guide the self-assembly into a wide range of different structures, offering precise control over both orientation and position order of the nanoplatelets. Our research is expected to shed light on the design of hierarchically structured metamaterials with distinct shape- and orientation- dependent properties. Nanoplatelets can be used as anisotropic building blocks for constructing novel optoelectronic materials. Here, Wang et al. show a route of assembling nanoplatelets with controllable positional and orientational order in three dimensions facilitated by the surface tension of drying emulsion droplets.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.6
Times cited: 7
DOI: 10.1038/S41467-022-33616-Y
|
|
|
“The optical nanosizer –, quantitative size and shape analysis of individual nanoparticles by high-throughput widefield extinction microscopy”. Payne LM, Albrecht W, Langbein W, Borri P, Nanoscale (2020). http://doi.org/10.1039/D0NR03504A
Abstract: Nanoparticles are widely utilised for a range of applications, from catalysis to medicine, requiring accurate knowledge of their size and shape. Current techniques for particle characterisation are either not very accurate or time consuming and expensive. Here we demonstrate a rapid and quantitative method for particle analysis based on measuring the polarisation-resolved optical extinction cross-section of hundreds of individual nanoparticles using wide-field microscopy, and determining the particle size and shape from the optical properties. We show measurements on three samples consisting of nominally spherical gold nanoparticles of 20 nm and 30 nm diameter, and gold nanorods of 30 nm length and 10 nm diameter. Nanoparticle sizes and shapes in three dimensions are deduced from the measured optical cross-sections at different wavelengths and light polarisation, by solving the inverse problem, using an ellipsoid model of the particle polarisability in the dipole limit. The sensitivity of the method depends on the experimental noise and the choice of wavelengths. We show an uncertainty down to about 1 nm in mean diameter, and 10% in aspect ratio when using two or three color channels, for a noise of about 50 nm<sup>2</sup>in the measured cross-section. The results are in good agreement with transmission electron microscopy, both 2D projection and tomography, of the same sample batches. Owing to its combination of experimental simplicity, ease of access to statistics over many particles, accuracy, and geometrical particle characterisation in 3D, this “optical nanosizer” method has the potential to become the technique of choice for quality control in next-generation particle manufacturing.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.7
DOI: 10.1039/D0NR03504A
|
|
|
“Quantifying Strain and Dislocation Density at Nanocube Interfaces after Assembly and Epitaxy”. Agrawal H, Patra BK, Altantzis T, De Backer A, Garnett EC, Acs Applied Materials &, Interfaces 12, 8788 (2020). http://doi.org/10.1021/acsami.9b17779
Abstract: Nanoparticle self-assembly and epitaxy are utilized extensively to make 1D and 2D structures with complex shapes. High-resolution transmission electron microscopy (HRTEM) has shown that single-crystalline interfaces can form, but little is known about the strain and dislocations at these interfaces. Such information is critically important for applications: drastically reducing
dislocation density was the key breakthrough enabling widespread implementation of light-emitting diodes, while strain engineering has been fundamental to modern high-performance transistors, solar cells, and thermoelectrics. In this work, the interfacial defect and strain formation after selfassembly and room temperature epitaxy of 7 nm Pd nanocubes capped with polyvinylpyrrolidone (PVP) is examined. It is observed that, during ligand removal, the cubes move over large distances on the substrate, leading to both spontaneous self-assembly and epitaxy to form single crystals. Subsequently, atomically resolved images are used to quantify the strain and dislocation density at the epitaxial interfaces between cubes with different lateral and angular misorientations. It is shown that dislocation- and strain-free interfaces form when the nanocubes align parallel to each other. Angular misalignment between adjacent cubes does not necessarily lead to grain boundaries but does cause dislocations, with higher densities associated with larger rotations.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 9.5
DOI: 10.1021/acsami.9b17779
|
|
|
“Stabilization effects in binary colloidal Cu and Ag nanoparticle electrodes under electrochemical CO₂, reduction conditions”. Wu L, Kolmeijer KE, Zhang Y, An H, Arnouts S, Bals S, Altantzis T, Hofmann JP, Costa Figueiredo M, Hensen EJM, Weckhuysen BM, van der Stam W, Nanoscale 13, 4835 (2021). http://doi.org/10.1039/D0NR09040A
Abstract: Nanoparticle modified electrodes constitute an attractive way to tailor-make efficient carbon dioxide (CO2) reduction catalysts. However, the restructuring and sintering processes of nanoparticles under electrochemical reaction conditions not only impedes the widespread application of nanoparticle catalysts, but also misleads the interpretation of the selectivity of the nanocatalysts. Here, we colloidally synthesized metallic copper (Cu) and silver (Ag) nanoparticles with a narrow size distribution (<10%) and utilized them in electrochemical CO2 reduction reactions. Monometallic Cu and Ag nanoparticle electrodes showed severe nanoparticle sintering already at low overpotential of -0.8 V vs. RHE, as evidenced by ex situ SEM investigations, and potential-dependent variations in product selectivity that resemble bulk Cu (14% for ethylene at -1.3 V vs. RHE) and Ag (69% for carbon monoxide at -1.0 V vs. RHE). However, by co-deposition of Cu and Ag nanoparticles, a nanoparticle stabilization effect was observed between Cu and Ag, and the sintering process was greatly suppressed at CO2 reducing potentials (-0.8 V vs. RHE). Furthermore, by varying the Cu/Ag nanoparticle ratio, the CO2 reduction reaction (CO2RR) selectivity towards methane (maximum of 20.6% for dense Cu-2.5-Ag-1 electrodes) and C-2 products (maximum of 15.7% for dense Cu-1-Ag-1 electrodes) can be tuned, which is attributed to a synergistic effect between neighbouring Ag and Cu nanoparticles. We attribute the stabilization of the nanoparticles to the positive enthalpies of Cu-Ag solid solutions, which prevents the dissolution-redeposition induced particle growth under CO2RR conditions. The observed nanoparticle stabilization effect enables the design and fabrication of active CO2 reduction nanocatalysts with high durability.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 7.367
Times cited: 24
DOI: 10.1039/D0NR09040A
|
|
|
“Advanced electron tomography of nanoparticle assemblies”. Altantzis T, Zanaga D, Bals S, Europhysics letters 119, 38001 (2017). http://doi.org/10.1209/0295-5075/119/38001
Abstract: Nanoparticle assemblies have attracted enormous scientific interest during the last
years, due to their unique properties compared to those of their building blocks. To understand
the origin of these properties and to establish the connection with their structure, a detailed and
quantitative structural characterization is essential. Transmission electron microscopy has been
widely used to investigate nano-assemblies. However, TEM images only correspond to a twodimensional
projection of a three-dimensional object. Therefore, in order to obtain the necessary
3D structural information electron tomography has to be applied. By means of advanced electron
tomography, both qualitative and quantitative information can be obtained, which can be used
for detailed theoretical studies.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.957
Times cited: 8
DOI: 10.1209/0295-5075/119/38001
|
|
|
“Quantitative 3D analysis of huge nanoparticle assemblies”. Zanaga D, Bleichrodt F, Altantzis T, Winckelmans N, Palenstijn WJ, Sijbers J, de Nijs B, van Huis MA, Sanchez-Iglesias A, Liz-Marzan LM, van Blaaderen A, Joost Batenburg K, Bals S, Van Tendeloo G, Nanoscale 8, 292 (2016). http://doi.org/10.1039/c5nr06962a
Abstract: Nanoparticle assemblies can be investigated in 3 dimensions using electron tomography. However, it is not straightforward to obtain quantitative information such as the number of particles or their relative position. This becomes particularly difficult when the number of particles increases. We propose a novel approach in which prior information on the shape of the individual particles is exploited. It improves the quality of the reconstruction of these complex assemblies significantly. Moreover, this quantitative Sparse Sphere Reconstruction approach yields directly the number of particles and their position as an output of the reconstruction technique, enabling a detailed 3D analysis of assemblies with as many as 10 000 particles. The approach can also be used to reconstruct objects based on a very limited number of projections, which opens up possibilities to investigate beam sensitive assemblies where previous reconstructions with the available electron tomography techniques failed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 7.367
Times cited: 34
DOI: 10.1039/c5nr06962a
|
|
|
“Band structure quantization in nanometer sized ZnO clusters”. Schouteden K, Zeng Y-J, Lauwaet K, Romero CP, Goris B, Bals S, Van Tendeloo G, Lievens P, Van Haesendonck C, Nanoscale 5, 3757 (2013). http://doi.org/10.1039/c3nr33989k
Abstract: Nanometer sized ZnO clusters are produced in the gas phase and subsequently deposited on clean Au(111) surfaces under ultra-high vacuum conditions. The zinc blende atomic structure of the approximately spherical ZnO clusters is resolved by high resolution scanning transmission electron microscopy. The large band gap and weak n-type conductivity of individual clusters are determined by scanning tunnelling microscopy and spectroscopy at cryogenic temperatures. The conduction band is found to exhibit clear quantization into discrete energy levels, which can be related to finite-size effects reflecting the zero-dimensional confinement. Our findings illustrate that gas phase cluster production may provide unique possibilities for the controlled fabrication of high purity quantum dots and heterostructures that can be size selected prior to deposition on the desired substrate under controlled ultra-high vacuum conditions.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 13
DOI: 10.1039/c3nr33989k
|
|