“Critical influence of alumina content on the low temperature degradation of 2-3 mol% yttria-stabilized TZP for dental restorations”. Zhang F, Vanmeensel K, Inokoshi M, Batuk M, Hadermann J, Van Meerbeek B, Naert I, Vleugels J, Journal of the European Ceramic Society 35, 741 (2015). http://doi.org/10.1016/j.jeurceramsoc.2014.09.018
Abstract: The influence of 0.25, 2 and 5 wt.% alumina addition on the mechanical properties and low temperature degradation (LTD) of 3, 2.5 and 2 mol% yttria-stabilized TZP ceramics was investigated. The amount of alumina addition was observed to have a crucial impact on the degradation of Y-TZP ceramics. Independent on the yttria stabilizer content, 0.25 wt.% alumina had a higher degradation retarding effect to Y-TZP ceramics than 2 and 5 wt.% of alumina addition, which had a comparable effect. The apparent activation energy for the degradation process was increased by adding alumina, but it was the same for 0.255 wt.% alumina doped 3Y-TZP ceramics. For Y-TZPs containing a small amount of alumina addition, only the segregated Al3+ at the grain boundaries of the zirconia grains was effective to retard the degradation of Y-TZPs. The secondary phase Al2O3 grains increased the degradation kinetics, which might be attributed to the residual stresses.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 37
DOI: 10.1016/j.jeurceramsoc.2014.09.018
|
|
|
“3Y-TZP ceramics with improved hydrothermal degradation resistance and fracture toughness”. Zhang F, Vanmeensel K, Inokoshi M, Batuk M, Hadermann J, Van Meerbeek B, Naert I, Vleugels J, Journal of the European Ceramic Society 34, 2453 (2014). http://doi.org/10.1016/j.jeurceramsoc.2014.02.026
Abstract: Different factors such as the way of incorporating the Y2O3 stabilizer, alumina addition and sintering temperature were assessed with the goal to improve the low temperature degradation (LTD) resistance of 3Y-TZP without compromising on the mechanical properties. The degradation of hydrothermally treated specimens was studied by X-ray diffraction, micro-Raman spectroscopy and scanning electron microscopy. Decreasing the sintering temperature decreased the LTD susceptibility of 3Y-TZPs but did not allow to obtain a LTD resistant 3Y-TZP with optimized mechanical properties. Alumina addition along with the use of Y2O3 stabilizer coated starting powder allowed to combine both an excellent toughness and LTD resistance, as compared to alumina-free and stabilizer co-precipitated powder based equivalents. Transmission electron microscopy revealed that the improved LTD resistance could be attributed to the segregation of Al3+ at the grain boundary and the heterogeneously distributed Y3+ stabilizer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 48
DOI: 10.1016/j.jeurceramsoc.2014.02.026
|
|
|
“Phase assembly and microstructure of CeO2-doped ZrO2 ceramics prepared by spark plasma sintering”. Xu T, Wang P, Fang P, Kan Y, Chen L, Vleugels J, Van der Biest O, van Landuyt J, Journal of the European Ceramic Society 25, 3437 (2005). http://doi.org/10.1016/j.jeurceramsoc.2004.09.004
Abstract: CeO2-doped ZrO2, (8 mol%) starting powder was sintered by means of spark plasma sintering (SPS) at 1300 degrees C without holding time. The stability of the tetragonal ZrO2 phase in the Ce-ZrO2 ceramic sintered under strongly reducing conditions was investigated. The SPS sample consisted of monoclinic and tetragonal ZrO2 phase, with a volume ratio of two to one, as well as a trace amount of a Zr-Ce-O cubic solid solution phase. In contrast, the same powder sintered by hot-pressing in nitrogen at 1300 and 1500 degrees C for 1h showed no tetragonal ZrO2. Microstructural observation of the SPS ceramic by SEM and TEM revealed grains with and without twins. The reason for the appearance of the tetragonal phase in the SPS sample sintered under strongly reducing conditions is discussed. (c) 2004 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 13
DOI: 10.1016/j.jeurceramsoc.2004.09.004
|
|
|
“Magnetic field oriented tetragonal zirconia with anisotropic toughness”. Zhang L, Vleugels J, Darchuk L, van der Biest O, Journal of the European Ceramic Society 31, 1405 (2011). http://doi.org/10.1016/J.JEURCERAMSOC.2011.02.002
Abstract: (0 0 1)-oriented 3 mol% yttria stabilized tetragonal zirconia (3Y-TZP) has been developed by reactive synthesis of undoped pure monoclinic zirconia and co-precipitated 8 mol% yttria-stabilized zirconia (8Y-ZrO2). The dispersed pure monoclinic ZrO2 powder, having magnetic anisotropy, was first aligned in a strong magnetic field and co-sintered in a randomly distributed cubic 8Y-ZrO2 fine matrix powder. The reactive sintering resulted in a 3Y-TZP ceramic with a (0 0 1) orientation. The (0 0 1)-oriented 3Y-TZP showed a substantial toughness anisotropy, i.e. the toughness along the [0 0 1] direction is 54% higher than that of its perpendicular direction. Moreover, the toughness along the [0 0 1] direction is 49% higher than that of a non-textured isotropic reactively synthesized 3Y-TZP and 110% higher than that of an isotropic co-precipitated powder based 3Y-TZP. The substantially enhanced toughness was interpreted in terms of the tetragonal to monoclinic martensitic phase transformability.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.JEURCERAMSOC.2011.02.002
|
|
|
“HREM of ceramic high Tc superconductors”. Van Tendeloo G, Krekels T, Journal of the European Ceramic Society 16, 367 (1996). http://doi.org/10.1016/0955-2219(95)00193-X
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.947
Times cited: 1
DOI: 10.1016/0955-2219(95)00193-X
|
|