“New insights in the formation of combined zeolitic/mesoporous materials by using a one-pot templating synthesis”. Vernimmen J, Meynen V, Herregods SJF, Mertens M, Lebedev OI, Van Tendeloo G, Cool P, European journal of inorganic chemistry , 4234 (2011). http://doi.org/10.1002/ejic.201100268
Abstract: Zeolitic growth is often absent or occurs in separate phases when synthetic strategies based on the combination of zeolite templates and mesopore templating agents are applied. In this work, zeolitic growth and mesopore formation have been investigated at different temperatures by applying a one-pot templating approach, based on a TS-1 zeolite synthesis whereby part of the microtemplate (tetrapropylammonium hydroxide, TPAOH) is replaced by a mesotemplate (hexadecyltrimethylammonium bromide, CTMABr). Moreover, the synthesis duration and the molar ratio of the microtemplate/mesotemplate have also been studied. The different syntheses clearly show the inherent competitive mechanism between zeolitic growth and mesopore formation. These insights have led to the conclusion that by following a one-pot templating strategy with standard, nonexotic commercial templates, i.e. CTMABr and TPAOH, it is not possible to develop a true hierarchical mesoporous zeolite, meaning a mesoporous siliceous material with highly crystalline zeolitic walls. The resultant materials are instead combined zeolitic/mesoporous composite structures with, however, highly tuneable and controllable porosity characteristics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.444
Times cited: 7
DOI: 10.1002/ejic.201100268
|
|
|
“Unprecedented shape selectivity in hydrogenation of triacylglycerol molecules with Pt/ZSM-5 zeolite”. Philippaerts A, Paulussen S, Breesch A, Turner S, Lebedev OI, Van Tendeloo G, Sels B, Jacobs P, Angewandte Chemie: international edition in English 50, 3947 (2011). http://doi.org/10.1002/anie.201007513
Abstract: Well tuned: ZSM-5 with platinum nanoparticles preferably hydrogenates trans fatty acids over cis isomers in model triacylglycerols for geometric reasons. The central fatty acid chain reacts faster, pointing to pore mouth adsorption in a tuning fork conformation (see picture). This conformation induces stepwise hydrogenation, resulting in fast removal of the unstable central triene, while formation of saturated chains is limited.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 31
DOI: 10.1002/anie.201007513
|
|
|
“Tailored vapor-phase growth of CuxO-TiO2(x=1,2) nanomaterials decorated with Au particles”. Barreca D, Carraro G, Gasparotto A, Maccato C, Lebedev OI, Parfenova A, Turner S, Tondello E, Van Tendeloo G, Langmuir: the ACS journal of surfaces and colloids 27, 6409 (2011). http://doi.org/10.1021/la200698t
Abstract: We report on the fabrication of CuxOTiO2 (x = 1, 2) nanomaterials by an unprecedented vapor-phase approach. The adopted strategy involves the growth of porous CuxO matrices by means of chemical vapor deposition (CVD), followed by the controlled dispersion of TiO2 nanoparticles. The syntheses are performed on Si(100) substrates at temperatures of 400550 °C under wet oxygen atmospheres, adopting Cu(hfa)2·TMEDA (hfa =1,1,1,5,5,5-hexafluoro-2,4-pentanedionate; TMEDA = N,N,N′,N′-tetramethylethylenediamine) and Ti(O-iPr)2(dpm)2 (O-iPr = isopropoxy; dpm = 2,2,6,6-tetramethyl-3,5-heptanedionate) as copper and titanium precursors, respectively. Subsequently, finely dispersed gold nanoparticles are introduced in the as-prepared systems via radio frequency (RF)-sputtering under mild conditions. The synthesis process results in the formation of systems with chemical composition and nano-organization strongly dependent on the nature of the initial CuxO matrix and on the deposited TiO2 amount. The decoration with low-size gold clusters paves the way to the engineering of hierarchically organized nanomaterials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.833
Times cited: 36
DOI: 10.1021/la200698t
|
|
|
“Resistive switching at manganite/manganite interfaces”. Kalkert C, Krisponeit J-O, Esseling M, Lebedev OI, Moshnyaga V, Damaschke B, Van Tendeloo G, Samwer K, Applied physics letters 99, 132512 (2011). http://doi.org/10.1063/1.3643425
Abstract: We report bipolar resistive switching between the interfaces of manganite nanocolumns. La0.7Sr0.3MnO3 films were prepared on Al2O3 substrates, where the films grow in nanocolumns from the substrate to the surface. Conductive atomic force microscopy directly detects that the resistive switching is located at the boundaries of the grains. Furthermore, mesoscopic transport measurements reveal a tunnel magnetoresistance. In combination with the resistive switching, this leads to a total of four different resistive states.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 10
DOI: 10.1063/1.3643425
|
|
|
“In situ HREM irradiation study of point-defect clustering in MBE-grown strained Si1-xGex/(001)Si structures”. Fedina L, Lebedev OI, Van Tendeloo G, van Landuyt J, Mironov OA, Parker EHC, Physical review : B : condensed matter and materials physics 61, 10336 (2000). http://doi.org/10.1103/PhysRevB.61.10336
Abstract: We present a detailed analysis of the point-defect clustering in strained Si/Si(1-x)Ge(x)/(001)Si structures, including the interaction of the point defects with the strained interfaces and the sample surface during 400 kV electron irradiation at room temperature. Point-defect cluster formation is very sensitive to the type and magnitude of the strain in the Si and Si(1-x)Ge(x) layers. A small compressive strain (-0.3%) in the SiGe alloy causes an aggregation of vacancies in the form of metastable [110]-oriented chains. They are located on {113} planes and further recombine with interstitials. Tensile strain in the Si layer causes an aggregation of interstitial atoms in the forms of additional [110] rows which are inserted on {113} planes with [001]-split configurations. The chainlike configurations are characterized by a large outward lattice relaxation for interstitial rows (0.13 +/-0.01 nm) and a very small inward relaxation for vacancy chains (0.02+/-0.01 nm). A compressive strain higher than -0.5% strongly decreases point-defect generation inside the strained SiGe alloy due to the large positive value of the formation volume of a Frenkel pair. This leads to the suppression of point-defect clustering in a strained SiGe alloy so that SiGe relaxes via a diffusion of vacancies from the Si layer, giving rise to an intermixing at the Si/SiGe interface. In material with a 0.9% misfit a strongly increased flow of vacancies from the Si layer to the SiGe layer and an increased biaxial strain in SiGe bath promote the preferential aggregation of vacancies in the (001) plane, which relaxes to form intrinsic 60 degrees dislocation loops.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 27
DOI: 10.1103/PhysRevB.61.10336
|
|
|
“Direct imaging of loaded metal-organic framework materials (metal@MOF-5)”. Turner S, Lebedev OI, Schroeder F, Fischer RA, Van Tendeloo G, Chemistry of materials 20, 5622 (2008). http://doi.org/10.1021/cm801165s
Abstract: We illustrate the potential of advanced transmission electron microscopy for the characterization of a new class of soft porous materials: metal@Zn4O(bdc)3 (metal@MOF-5; bdc = 1,4-benzenedicarboxylate). By combining several electron microscopy techniques (transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), electron diffraction (ED), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), and electron tomography) and by carefully reducing the electron dose to avoid beam damage, it is possible to simultaneously characterize the MOF-5 framework material and the loaded metal nanoparticles. We also demonstrate that electron tomography can be used to accurately determine the position and distribution of the particles within the MOF-5 framework. To demonstrate the implementation of these microscopy techniques and what kind of results can be expected, measurements on gas-phase-loaded metal−organic framework materials Ru@MOF-5 and Pd@MOF-5 are presented.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 112
DOI: 10.1021/cm801165s
|
|
|
“New nano-architectures of mesoporous silica spheres analyzed by advanced electron microscopy”. Lebedev OI, Turner S, Liu S, Cool P, Van Tendeloo G, Nanoscale 4, 1722 (2012). http://doi.org/10.1039/c2nr11715k
Abstract: Using template-containing silica microspheres as a precursor, novel ordered mesoporous silica nanoparticles with a narrow pore size distribution and high crystallinity have been synthesized by various hydrothermal merging processes. Several architectures like chains, dumbbells, triangles, squares and flowers have been discovered. The linking mechanisms of these interacting silica spheres leading to the formation of ordered nano-structures are studied by HRTEM, HAADF-STEM and electron tomography and a plausible model is presented for several merging processes.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 7.367
Times cited: 5
DOI: 10.1039/c2nr11715k
|
|
|
“Pd-In2O3 interaction due to reduction in hydrogen: consequences for methanol steam reforming”. Lorenz H, Turner S, Lebedev OI, Van Tendeloo G, Klötzer B, Rameshan C, Pfaller K, Penner S, Applied catalysis : A : general 374, 180 (2010). http://doi.org/10.1016/j.apcata.2009.12.007
Abstract: Two different Pd/In2O3 samples including a thin film model catalyst with well-defined Pd particles grown on NaCl(0 0 1) supports and a powder catalyst prepared by an impregnation technique are examined by electron microscopy, X-ray diffraction and catalytic measurements in methanol steam reforming in order to correlate the formation of different oxide-supported bimetallic PdIn phases with catalytic activity and selectivity. A PdIn shell around the Pd particles is observed on the thin film catalyst after embedding the Pd particles in In2O3 at 300 K, likely because alloying to PdIn and oxidation to In2O3 are competing processes. Increased PdIn bimetallic formation is observed up to 573 K reduction temperature until at 623 K the film stability limit in hydrogen is reached. Oxidative treatments at 573 K lead to decomposition of PdIn and to the formation of an In2O3 shell covering the Pd particles, which irreversibly changes the activity and selectivity pattern to clean In2O3. PdIn and Pd2In3 phases are obtained on the powder catalyst after reduction at 573 K and 673 K, respectively. Only CO2-selective methanol steam reforming is observed in the reduction temperature range between 473 K and 573 K. After reduction at 673 K encapsulation of the bimetallic particles by crystalline In2O3 suppresses CO2 formation and only activity and selectivity of clean In2O3 are measured.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 55
DOI: 10.1016/j.apcata.2009.12.007
|
|
|
“Electron microscopy and X-ray structural investigations of incommensurate spin-ladder Sr4.1Ca4.7Bi0.3Cu17O29 single crystals”. Dluzewski P, Pietraszko A, Kozlowski M, Szczepanska A, Gorecka J, Baran M, Leonyuk L, Babonas GJ, Lebedev OI, Szymczak R, Acta physica Polonica: A: general physics, solid state physics, applied physics 98, 729 (2000)
Abstract: Transmission electron microscopy and X-ray diffraction proved chain/ladder incommensurate single crystal structure of investigated samples. The incommensurate ratio was determined from the X-ray and electron diffraction being equal to 0.704. Diffuse scattering intensities localised on the planes perpendicular to the c*-axis and passing through the spots originating from the periodicity of chain sublattice were detected. High-angle grain boundary or twinning formed by rotation of 33.3 degrees around [100] direction was observed. High-resolution electron microscopy images revealed the stacking faults in ac planes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.469
|
|
|
“Multi-step loading of titania on mesoporous silica: influence of the morphology and the porosity on the catalytic degradation of aqueous pollutants and VOC's”. de Witte K, Meynen V, Mertens M, Lebedev OI, Van Tendeloo G, Sepúlveda-Escribano A, Rodríguez-Reinoso F, Vansant EF, Cool P, Applied catalysis : B : environmental 84, 125 (2008). http://doi.org/10.1016/j.apcatb.2008.03.015
Abstract: Titania nanoparticles have been deposited on inert porous silica supports with high specific surface area. These materials have potential applications in paint and textile industry as the titania particles selectively deposited on the inner surface of the silica supports act as a photocatalyst. The inert external surface is necessary to avoid photodegradation of the textile material or the paint components. The photocatalytic activity of the catalysts has been evaluated with two catalytic setups. One setup in aqueous phase, for the degradation of dyes such as rhodamine-6G, is commonly used. The second setup is a continuous flow gaseous phase setup which was used for the mineralization of ethanol as a representative volatile organic compound (VOC). The influence of the porosity and the morphology of the silica supports on the photocatalytic activity are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 9.446
Times cited: 24
DOI: 10.1016/j.apcatb.2008.03.015
|
|
|
“Structure and microstructure of epitaxial SrnFenO3n-1 films”. Lebedev OI, Verbeeck J, Van Tendeloo G, Hayashi N, Terashima T, Takano M, Philosophical magazine 84, 3825 (2004). http://doi.org/10.1080/14786430412331313187
Abstract: Thin films of SrFeO3-x (0 less than or equal to x less than or equal to 0.5) (SFO) grown on a (LaAlO3)(0.3) (SrAl0.5Ta0.5O3)(0.7) (LSAT) substrate by Pulsed laser deposition have been structurally investigated by electron diffraction and high resolution transmission electron microscopy for different post-deposition oxygen treatments. During the deposition and post-growth oxidation, the oxygen-reduced SFO films accept extra oxygen along the tetrahedral layers to minimize the elastic strain energy. The oxidation process stops at a concentration SFO2.875 and/or SFO2.75 because a zero misfit with the LSAT substrate is reached. A possible growth mechanism and phase transition mechanism are suggested. The non-oxidized films exhibit twin boundaries having a local perovskite-type structure with a nominal composition close to SFO3.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.505
Times cited: 4
DOI: 10.1080/14786430412331313187
|
|
|
“Au@MOF-5 and Au/Mox@MOF-5 (M = Zn, Ti, x = 1, 2) : preparation and microstructural characterisation”. Müller M, Turner S, Lebedev OI, Wang Y, Van Tendeloo G, Fischer RA, European journal of inorganic chemistry , 1876 (2011). http://doi.org/10.1002/ejic.201001297
Abstract: The Zn-carboxylate-based porous coordination polymer MOF-5 [Zn4O(bdc)3] and the metal oxide loaded materials ZnO@MOF-5 and TiO2@MOF-5 were loaded in a second step with the precursor [ClAuCO] to yield intermediate materials denoted as [ClAuCO]@MOF-5, [ClAuCO]/ZnO@MOF-5 and [ClAuCO]/TiO2@MOF-5. These composites were decomposed to Au@MOF-5, Au/ZnO@MOF-5 and Au/TiO2@MOF-5 under hydrogen at 100 °C. The nanoparticle-loaded hybrid materials were characterised by powder X-ray diffraction (PXRD), IR spectroscopy, X-ray photoelectron spectroscopy (XPS) and N2 sorption measurements, which reveal an intact MOF-5 structure that maintains a high specific surface area. For Au@MOF-5, crystalline Au nanoparticles were distributed over the MOF matrix in a homogeneous fashion with a size of ca. 13 nm, evidenced by high resolution transmission electron microscopy. In the case of Au/ZnO@MOF-5, the Au and metal oxide particles of a few nm in size were coexistent in a given volume of the MOF-5 matrix and were not separated in different crystalline MOF particles. For the TiO2 loaded materials the oxide is preferentially located near the outer surface of the MOF particles, leading to an increase of larger exterior Au particles in comparison to very small interior Au particles as observed for the other materials. Au@MOF-5, Au/ZnO@MOF-5 and Au/TiO2@MOF-5 were tested in liquid-phase oxidation of alcohols. Preliminary results show a high activity for the Au loaded materials in this reaction. This observation is attributed to the microstructure of the composites with very small Au particles distributed homogeneously over the MOF matrix.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
Times cited: 75
DOI: 10.1002/ejic.201001297
|
|
|
“Metal to insulator transition in the n-type hollandite vanadate Pb1.6V8O16”. Maignan A, Lebedev OI, Van Tendeloo G, Martin C, Hebert S, Physical review : B : condensed matter and materials physics 82, 035122 (2010). http://doi.org/10.1103/PhysRevB.82.035122
Abstract: The transport and magnetic measurements of polycrystalline Pb1.6V8O16 hollandite reveal a concomitant metal to insulator and antiferromagnetic transition at TMI≈140 K. A clear localization is found below TMI, evidenced by a rapid increase in the absolute value of the negative Seebeck coefficient. The structural study by x-ray and transmission electron microscopy confirms the hollandite structure and shows that no structural transition occurs at TMI, ruling out a possible charge orbital ordering. The negative Seebeck coefficient observed from 50 K up to 900 K, with values reaching S=−38 μV K−1 at 900 K, is explained by the electron doping of ∼1.4e− in the V empty t2g orbitals responsible for the bad metal resistivity (ρ900 K∼2 mΩ cm). As this S value is close to that obtained by considering only the spin and orbital degeneracies, it is expected that |S| for such vanadates will not be sensitive at high temperature to the t2g band filling
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 10
DOI: 10.1103/PhysRevB.82.035122
|
|
|
“Defect structure of ferromagnetic superconducting RuSr2GdCu2O8”. Lebedev OI, Van Tendeloo G, Attfield JP, McLaughlin AC, Physical review : B : condensed matter and materials physics 73 (2006). http://doi.org/10.1103/PhysRevB.73.224524
Abstract: The structure and defect structure of superconducting ferromagnetic bulk RuSr2GdCu2O8 has been investigated using high-resolution transmission electron microscopy and high-resolution scanning transmission microscopy. Two distinct, but closely related structures, due to ordering of rotated RuO6 octahedra and due to Cu substitution in the Ru-O layer, have been revealed. The structure of Ru1-xSr2GdCu2+xO8-delta can be described as a periodic alteration along the c axis of CuO4 planes and RuO6 octahedra. The unit-cell parameters of this phase are root 2a(p) x root 2a(p) x 2c. The possible influence of this phase and defect structure on the sensitivity of the superconductivity and magnetic properties is discussed. Local defects such as 90 S domain boundaries, (130) antiphase boundaries, and the associated dislocations are analyzed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 11
DOI: 10.1103/PhysRevB.73.224524
|
|
|
“Au@ZIFs: stabilization and encapsulation of cavity-size matching gold clusters inside functionalized Zeolite Imidazolate Frameworks, ZIFs”. Esken D, Turner S, Lebedev OI, Van Tendeloo G, Fischer RA, Chemistry of materials 22, 6393 (2010). http://doi.org/10.1021/cm102529c
Abstract: The selective formation and stabilization of very small, naked metal particles inside the cavities of metal organic frameworks (MOFs) and the simultaneous realization of an even distribution of the particles throughout the crystalline MOF host matrix over a wide range of metal loading are challenging goals. MOFs reveal high specific surface areas, tunable pore sizes, and organic linkers, which are able to interact with guests. The chemically very robust zeolite imidazolate frameworks (ZIFs) are a subclass of MOFs. We chose the microporous sodalite-like ZIF-8 (Zn(MelM)(2); IM = imidazolate) and ZIF-90 (Zn(ICA)(2); ICA = imidazolate-2-carboxyaldehyde) as host matrices to influence the dispersion of imbedded gold nanoparticles (Au NPs). The metal loading was achieved via gas phase infiltration of [Au(CO)Cl] followed by a thermal hydrogenation step to form the Au NPs. Low-dose high-resolution transmission electron microscopy ((HR)TEM) and electron tomography reveal a homogeneous distribution of Au NPs throughout the ZIF matrix. The functional groups of ZIF-90 direct the anchoring of intermediate Au species and stabilize drastically smaller and quite monodisperse Au NPs in contrast to the parent not functionalized ZIF-8. The particles can be very small, match the cavity size and approach defined molecular clusters of magic numbers, i.e., Au(55), independently from the level of loading. Post-synthetic oxidation of the aldehyde groups to yield alkyl esters by the adjacent, catalytically active metal NPs is presented as a new concept of encapsulating nanoparticles inside MOFs and allows multiple steps of metal loadings without decomposition of the MOF.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 194
DOI: 10.1021/cm102529c
|
|
|
“Rational synthesis of a nanocrystalline calcium phosphate cement exhibiting rapid conversion to hydroxyapatite”. Neira IS, Kolen'ko YV, Lebedev OI, Van Tendeloo G, Gupta HS, Matsushita N, Yoshimura M, Guitian F, Materials science and engineering: part C: biomimetic materials 29, 2124 (2009). http://doi.org/10.1016/j.msec.2009.04.011
Abstract: The rational synthesis, comprehensive characterization, and mechanical and micromechanical properties of a calcium phosphate cement are presented. Hydroxyapatite cement biomaterial was synthesized from reactive sub-micrometer-sized dicalcium phosphate dihydrate and tetracalcium phosphate via a dissolution-precipitation reaction using water as the liquid phase. As a result nanostructured, Ca-deficient and carbonated B-type hydroxyapatite is formed. The cement shows good processibility, sets in 22 ± 2 min and entirely transforms to the end product after 6 h of setting reaction, one of the highest conversion rates among previously reported for calcium phosphate cements based on dicalcium and tetracalcium phosphates. The combination of all elucidated physical-chemical traits leads to an essential bioactivity and biocompatibility of the cement, as revealed by in vitro acellular simulated body fluid and cell culture studies. The compressive strength of the produced cement biomaterial was established to be 25 ± 3 MPa. Furthermore, nanoindentation tests were performed directly on the cement to probe its local elasticity and plasticity at sub-micrometer/micrometer level. The measured elastic modulus and hardness were established to be Es = 23 ± 3.5 and H = 0.7 ± 0.2 GPa, respectively. These values are in close agreement with those reported in literature for trabecular and cortical bones, reflecting good elastic and plastic coherence between synthesized cement biomaterial and human bones.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.164
Times cited: 18
DOI: 10.1016/j.msec.2009.04.011
|
|
|
“Fluorine doped Fe2O3 nanostructures by a one-pot plasma-assisted strategy”. Carraro G, Gasparotto A, Maccato C, Bontempi E, Lebedev OI, Turner S, Sada C, Depero LE, Van Tendeloo G, Barreca D, RSC advances 3, 23762 (2013). http://doi.org/10.1039/c3ra43775b
Abstract: The present work reports on the synthesis of fluorine doped Fe2O3 nanomaterials by a single-step plasma enhanced-chemical vapor deposition (PE-CVD) strategy. In particular, Fe(hfa)2TMEDA (hfa = 1,1,1,5,5,5-hexafluoro-2,4-pentanedionate; TMEDA = N,N,N′,N′-tetramethylethylenediamine) was used as molecular source for both Fe and F in Ar/O2 plasmas. The structure, morphology and chemical composition of the synthesized nanosystems were thoroughly analyzed by two-dimensional X-ray diffraction (XRD2), field emission-scanning electron microscopy (FE-SEM), X-ray photoelectron spectroscopy (XPS), secondary ion mass spectrometry (SIMS) and transmission electron microscopy (TEM). A suitable choice of processing parameters enabled the selective formation of α-Fe2O3 nanomaterials, characterized by an homogeneous F doping, even at 100 °C. Interestingly, a simultaneous control of the system nanoscale organization and fluorine content could be achieved by varying the sole growth temperature. The tailored properties of the resulting materials can be favourably exploited for several technological applications, ranging from photocatalysis, to photoelectrochemical cells and gas sensing.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.108
Times cited: 23
DOI: 10.1039/c3ra43775b
|
|
|
“Rational design of Ag/TiO2 nanosystems by a combined RF-sputtering/sol-gel approach”. Armelao L, Barreca D, Bottaro G, Gasparotto A, Maccato C, Tondello E, Lebedev OI, Turner S, Van Tendeloo G, Štangar UL, ChemPhysChem : a European journal of chemical physics and physical chemistry 10, 3249 (2009). http://doi.org/10.1002/cphc.200900571
Abstract: The present work is devoted to the preparation of Ag/TiO2 nanosystems by an original synthetic strategy, based on the radio-frequency (RF) sputtering of silver particles on titania-based xerogels prepared by the sol-gel (SG) route. This approach takes advantage of the synergy between the microporous xerogel structure and the infiltration power characterizing RF-sputtering, whose combination enables the obtainment of a tailored dispersion of Ag-containing particles into the titania matrix. In addition, the systems chemico-physical features can be tuned further through proper ex situ thermal treatments in air at 400 and 600 °C. The synthesized composites are extensively characterized by the joint use of complementary techniques, that is, X-ray photoelectron and X-ray excited Auger electron spectroscopies (XPS, XE-AES), secondary ion mass spectrometry (SIMS), glancing incidence X-ray diffraction (GIXRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), electron diffraction (ED), high-angle annular dark field scanning TEM (HAADF-STEM), energy-filtered TEM (EF-TEM) and optical absorption spectroscopy. Finally, the photocatalytic performances of selected samples in the decomposition of the azo-dye Plasmocorinth B are preliminarily investigated. The obtained results highlight the possibility of tailoring the system characteristics over a broad range, directly influencing their eventual functional properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 56
DOI: 10.1002/cphc.200900571
|
|
|
“The superconducting bismuth-based mixed oxides”. Antipov EV, Khasanova NR, Pshirkov JS, Putilin SN, Bougerol C, Lebedev OI, Van Tendeloo G, Baranov AN, Park YW, Current applied physics
T2 –, QTSM and QFS 02 Symposium, MAY 08-10, 2002, SEOUL, SOUTH KOREA 2, 425 (2002). http://doi.org/10.1016/S1567-1739(02)00105-0
Abstract: The present paper describes the synthesis, characterization of mixed-valence bismuthates with three- or two-dimensional perovskite-like structures and structural criteria that influence superconductivity in these compounds. Single-phase samples of Sr1-xKxBiO3 were prepared for the broad range of K-content: 0.25 less than or equal to x less than or equal to 0.65. For these bismuthates the symmetry of the structure changes from monoclinic to orthorhombic and finally to tetragonal upon increasing the K-content thus resulting in the decrease of the Bi-O distances and reduction of the network distortions. Superconductivity with maximum T-c = 12 K exists in the narrow range (x approximate to 0.5-0.6) within the stability field of the tetragonal phase (0.33 less than or equal to x less than or equal to 0.65), when the three-dimensional octahedral framework has close to the ideal perovskite structure arrangement. The layered type (Ba,K)(3)Bi2O7 and (Ba,K)(2)BiO4 bismuthates belonging to the A(n+1)B(n)O(3n+1) homologous series were investigated. Buckling of the (BiO2) layers in the structure of the n = 2 member occurs due to the ordering of alkaline- and alkaline-earth cations between two independent positions. The formation of the one-layer bismuthate was revealed by Electron Microscopy and XRPD studies. Both types of compounds are considered to be possible candidates for new superconducting materials among bismuthates. (C) 2002 Published by Elsevier Science B.V.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.971
Times cited: 2
DOI: 10.1016/S1567-1739(02)00105-0
|
|
|
“The superconducting bismuth-based mixed oxides”. Antipov EV, Khasanova NR, Pshirkov JS, Putilin SN, Bougerof C, Lebedev OI, Van Tendeloo G, Baranov A, Park YW, Journal of low temperature physics
T2 –, International Conference on Physics and Chemistry of Molecular and Oxide, Superconductors (MOS2002), AUG 13-18, 2002, HSINCHU, TAIWAN 131, 575 (2003). http://doi.org/10.1023/A:1022923924607
Abstract: The present paper describes the synthesis, characterization of mixed-valence bismuthates with 3- or 2-dimensional perovskite-like structures and structural criteria that influence superconductivity in these compounds. Single-phase samples of Sr1-xKxBiO3 were prepared for the broad range of K-content: 0.25 less than or equal to x less than or equal to 0.65. For these bismuthates the symmetry of the structure changes from monoclinic to orthorhombic and finally to tetragonal upon increasing the K-content thus resulting in the decrease of the Bi-O distances and reduction of the network distortions. Superconductivity with maximum T-c = 12K exists in the narrow range (x approximate to 0.5 – 0.6) within the stability field of the tetragonal phase (0.33 less than or equal to x less than or equal to 0.65), when the 3-dimensional octahedral framework has close to the ideal perovskite structure arrangement. At the same time compositions with close to optimal Bi-valence (x = 0.33 and 0.43) do not show any sign of superconductivity, probably, due to structural distortions. The layered type (BaK)(3)Bi2O7 and (Ba,K)(2)BiO4 bismuthates belonging to the A(n+1)B(n)O(3n+1) homologous series were investigated Buckling of the (BiO2) layers in the structure of the n = 2 member was revealed The formation of the n=1 bismuthate was found by Electron Microscopy and X-ray powder diffraction studies. Both types of compounds are considered to be possible candidates for new superconducting materials among bismuthates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.3
Times cited: 3
DOI: 10.1023/A:1022923924607
|
|
|
“One-step synthesis of shelled PbS nanoparticles in a layered double hydroxide matrix”. Lukashin AV, Eliseev AA, Zhuravleva NG, Vertegel AA, Tretyakov YD, Lebedev OI, Van Tendeloo G, Mendeleev communications , 174 (2004). http://doi.org/10.1070/MC2004v014n04ABEH001973
Abstract: The one-step preparation of capped PbS nanoparticles in an inorganic matrix via UV-induced decomposition of lead thiosulfate complexes intercalated into a hydrotalcite-type layered double hydroxide is reported.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.741
Times cited: 9
DOI: 10.1070/MC2004v014n04ABEH001973
|
|
|
“Crosshatching on La0.5Ca0.5MnO3 ultrathin films epitaxially grown on SrTiO3(100)”. Wang Z-H, Lebedev OI, Van Tendeloo G, Cristiani G, Habermeier H-U, Physical review : B : condensed matter and materials physics 77, 1 (2008). http://doi.org/10.1103/PhysRevB.77.115330
Abstract: The morphological evolution in La(0.5)Ca(0.5)MnO(3)/SrTiO(3)(100) ultrathin films has been revealed by atomic force microscopy. It was found that ordered linear defects, which are in 1-2 unit cells high and oriented along the cubic [110] and [100] directions, first appear on the smooth surface of films with a thickness of 10 nm. As the epitaxial growth proceeds, these lines on surface develop into a crosshatch pattern for films with a thickness of 25 nm. Using the results of transmission electron microscopy and electrical measurements, we discuss the interplay between the surface pattern formation, the internal dislocation structure, and the variations in the electrical properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 8
DOI: 10.1103/PhysRevB.77.115330
|
|
|
“Negative magnetoresistance in a V3+/V4+ mixed valent vanadate”. Maignan A, Lebedev OI, Van Tendeloo G, Martin C, Hébert S, Applied physics letters 96, 232502 (2010). http://doi.org/10.1063/1.3446892
Abstract: The magnetotransport and magnetic properties of the PbV6O11 vanadate, crystallizing in the P63mc space group, reveal the existence of a negative magnetoresistance related to its ferromagnetic state (TC ∼ 90 K). The maximum effect is observed at 20 K reaching −30% in 9 T. The structural study of this ceramic reveals a V/Pb ratio smaller than expected from the formula. This is explained by the presence of numerous stacking faults observed by high resolution transmission electron microscopy. The existence of these planar defects acting as resistive barriers along the c axis could be responsible for tunneling magnetoresistance.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
DOI: 10.1063/1.3446892
|
|
|
“Interfacial spin glass state and exchange bias in manganite bilayers with competing magnetic orders”. Ding JF, Lebedev OI, Turner S, Tian YF, Hu WJ, Seo JW, Panagopoulos C, Prellier W, Van Tendeloo G, Wu T, Physical review : B : condensed matter and materials physics 87, 054428 (2013). http://doi.org/10.1103/PhysRevB.87.054428
Abstract: The magnetic properties of manganite bilayers composed of G-type antiferromagnetic (AFM) SrMnO3 and double-exchange ferromagnetic (FM) La0.7Sr0.3MnO3 are studied. A spin-glass state is observed as a result of competing magnetic orders and spin frustration at the La0.7Sr0.3MnO3/SrMnO3 interface. The dependence of the irreversible temperature on the cooling magnetic field follows the Almeida-Thouless line. Although an ideal G-type AFM SrMnO3 is featured with a compensated spin configuration, the bilayers exhibit exchange bias below the spin glass freezing temperature, which is much lower than the Néel temperature of SMO, indicating that the exchange bias is strongly correlated with the spin glass state. The results indicate that the spin frustration that originates from the competition between the AFM super-exchange and the FM double-exchange interactions can induce a strong magnetic anisotropy at the La0.7Sr0.3MnO3/SrMnO3 interface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 98
DOI: 10.1103/PhysRevB.87.054428
|
|
|
“Phase transition and magnetic anisotropy of (La,Sr)MnO3 thin films”. Wang Z-H, Kronmüller H, Lebedev OI, Gross GM, Razavi FS, Habermeier HU, Shen BG, Physical review : B : condensed matter and materials physics 65, 054411 (2002). http://doi.org/10.1103/PhysRevB.65.054411
Abstract: The magnetic proper-ties and their correlation with the microstructure and electrical transport are investigated in La0.88Sr0.1MnO3 films grown on (100)SrTiO3 Single crystal substrates with thickness ranging from 100 to 2500 Angstrom. The ultrathin film (t = 100 Angstrom) has a single ferromagnetic transition (FMT) at T-c of 250 K, whereas the thicker films exhibit two FMTs, with the main one at a lowered T-c of 200 K while the minor one around 300 K. Furthermore, a thickness dependent magnetic anisotropy has been found, strongly indicating the existence of strain effect, which is also revealed by the transmission electron microscopy study. The suppressed Jahn-Teller distortion (JTD) by the epitaxial strain, and the recovered JTD due to the strain relexation are suggested to explain the metallic behavior in thin films and the insulating behavior in the thick film (t = 2500 Angstrom), repectively.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 23
DOI: 10.1103/PhysRevB.65.054411
|
|
|
“Pd@MOF-5: limitations of gas-phase infiltration and solution impregnation of [Zn4O(bdc)3] (MOF-5) with metalorganic palladium precursors for loading with Pd nanoparticles”. Esken D, Zhang X, Lebedev OI, Schröder F, Fischer RA, Journal of materials chemistry 19, 1314 (2009). http://doi.org/10.1039/b815977g
Abstract: The limitations of the loading of the porous metalorganic framework [Zn4O(bdc)3] (bdc = benzene-1,4-dicarboxylate; MOF-5 or IRMOF-1) with Pd nanoparticles was investigated. First, the volatile organometallic precursor [Pd(5-C5H5)(3-C3H5)] was employed to get the inclusion compound [Pd(5-C5H5)(3-C3H5)]x@MOF-5 via gas-phase infiltration at 10-3 mbar. A loading of four molecules of [Pd(5-C5H5)(3-C3H5)] per formula unit of MOF-5 (x = 4) can be reached (35 wt.% Pd). Second, the metalorganic precursor [Pd(acac)2] (acac = 2,4-pentanedionate) was used and the inclusion materials [Pd(acac)2]x@MOF-5 of different Pd loadings were obtained by incipient wetness infiltration. However, the maximum loading was lower as compared with the former case with about two precursor molecules per formula unit of MOF-5. Both loading routes are suitable for the synthesis of Pd nanoparticles inside the porous host matrix. Homogeneously distributed nanoparticles with diameter of 2.4(±0.2) nm can be achieved by photolysis of the inclusion compounds [Pd(5-C5H5)(3-C3H5)]x@MOF-5 (x 4), while the hydrogenolysis of [Pd(acac)2]x@MOF-5 (x 2) leads to a mixture of small particles inside the network (< 3 nm) and large Pd agglomerates (40 nm) on the outer surface of the MOF-5 specimens. The pure Pdx@MOF-5 materials proved to be stable under hydrogen pressure (2 bar) at 150 °C over many hours. Neither hydrogenation of the bdc linkers nor particle growth was observed. The new composite materials were characterized by 1H/13C-MAS-NMR, powder XRD, ICP-AES, FT-IR, N2 sorption measurements and high resolution TEM. Raising the Pd loading of a representative sample Pd4@MOF-5 (35 wt.% Pd) by using [Pd(5-C5H5)(3-C3H5)] as precursor in a second cycle of gas-phase infiltration and photolysis was accompanied by the collapse of the long-range crystalline order of the MOF.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 100
DOI: 10.1039/b815977g
|
|
|
“Nanoscale ordering in oxygen deficient quintuple perovskite Sm2-\epsilonBa3+\epsilonFe5O15-\delta : implication for magnetism and oxygen stoichiometry”. Volkova NE, Lebedev OI, Gavrilova LY, Turner S, Gauquelin N, Seikh MM, Caignaert V, Cherepanov VA, Raveau B, Van Tendeloo G, Chemistry of materials 26, 6303 (2014). http://doi.org/10.1021/cm503276p
Abstract: The investigation of the system SmBaFe-O in air has allowed an oxygen deficient perovskite Sm2-epsilon Ba3+epsilon Fe5O15-delta (delta = 0.75, epsilon = 0.125) to be synthesized. In contrast to the XRPD pattern which gives a cubic symmetry (a(p) = 3.934 angstrom), the combined HREM/EELS study shows that this phase is nanoscale ordered with a quintuple tetragonal cell, a(p) X a(p) X 5(ap). The nanodomains exhibit a unique stacking sequence of the A-site cationic layers along the crystallographic c-axis, namely SmBaBa/SmBa/SmBaSm, and are chemically twinned in the three crystallographic directions. The nanoscale ordering of this perovskite explains its peculiar magnetic properties on the basis of antiferromagnetic interactions with spin blockade at the boundary between the nanodomains. The variation of electrical conductivity and oxygen content of this oxide versus temperature suggest potential SOFC applications. They may be related to the particular distribution of oxygen vacancies in the lattice and to the 3d(5)(L) under bar configuration of iron.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 16
DOI: 10.1021/cm503276p
|
|
|
“Gas-phase loading of [Zn4O(btb)2] (MOF-177) with organometallic CVD-precursors: inclusion compounds of the type [LnM]a@MOF-177 and the formation of Cu and Pd nanoparticles inside MOF-177”. Müller M, Lebedev OI, Fischer RA, Journal of materials chemistry 18, 5274 (2008). http://doi.org/10.1039/b810989c
Abstract: The highly porous and desolvated (activated) coordination polymer [Zn4O(btb)2] (btb = benzene-1,3,5-tribenzoate; MOF-177) was loaded with the organometallic compounds [Cp2Fe], [Cp*2Zn], [Cu(OCHMeCH2NMe2)2], [CpCuL] (L = PMe3, CNtBu) and [CpPd(3-C3H5)] via solvent-free adsorption from the gas-phase. The inclusion compounds of the type [LnM]a@MOF-177, where [LnM] indicates the respective compound and the parameter a denotes the number of molecules per formula unit of the MOF-177, were characterised by elemental analysis, FT-IR, solid-state NMR spectroscopy and by powder X-ray diffraction (PXRD). Remarkably high effective loadings of up to 11 molecules [Cp2Fe] and 10 molecules [CpPd(3-C3H5)] per cavity were determined. The analytical data prove that the host lattice and the guest molecules interact only by weak van-der-Waals forces without any significant change of the framework or the chemical nature of the included molecules. Cu nanoparticles showing the typical surface plasmon resonance at 580 nm and Pd nanoparticles of about 2.6 nm in size were formed inside the cavities of MOF-177 by the thermally activated hydrogenolysis of the inclusion compounds [CpCuCNtBu]2@MOF-177 and by photolysis of [CpPd(3-C3H5)]10@MOF-177 in an inert atmosphere (Ar). PXRD, FT-IR and NMR studies revealed that the MOF-177 matrix remained unchanged during the decomposition process of the precursors. N2 adsorption studies of the obtained materials Cu@MOF-177 (e.g. 10.6 wt.% Cu, 2309 m2 g-1) and Pd@MOF-177 (e.g. 32.5 wt.%, 1063 m2 g-1) reveal high remaining specific surface areas (Langmuir model).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 65
DOI: 10.1039/b810989c
|
|
|
“Proximity induced metal-insulator transition in YBa2Cu3O7/La2/3Ca1/3MnO3 superlattices”. Holden T, Habermeier H-U, Cristiani G, Golnik A, Boris A, Pimenov A, Humlicek J, Lebedev OI, Van Tendeloo G, Keimer B, Bernhard C, Physical review : B : condensed matter and materials physics 69, 064505 (2004). http://doi.org/10.1103/PhysRevB.69.064505
Abstract: The far-infrared dielectric response of superlattices (SL) composed of superconducting YBa2Cu3O7 (YBCO) and ferromagnetic La0.67Ca0.33MnO3 (LCMO) has been investigated by ellipsometry. A drastic decrease of the free-carrier response is observed which involves an unusually large length scale of d(crit)approximate to20 nm in YBCO and d(crit)approximate to10 nm in LCMO. A corresponding suppression of metallicity is not observed in SL's where LCMO is replaced by the paramagnetic metal LaNiO3. Our data suggest that either a long-range charge transfer from the YBCO to the LCMO layers or alternatively a strong coupling of the charge carriers to the different and competitive kind of magnetic correlations in the LCMO and YBCO layers is at the heart of the observed metal-insulator transition. The low free-carrier response observed in the far-infrared dielectric response of the magnetic superconductor RuSr2GdCu2O8 is possibly related to this effect.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 101
DOI: 10.1103/PhysRevB.69.064505
|
|
|
“Selective anodes for seawater splitting via functionalization of manganese oxides by a plasma-assisted process”. Bigiani L, Barreca D, Gasparotto A, Andreu T, Verbeeck J, Sada C, Modin E, Lebedev OI, Morante JR, Maccato C, Applied Catalysis B-Environmental 284, 119684 (2021). http://doi.org/10.1016/J.APCATB.2020.119684
Abstract: The electrolysis of seawater, a significantly more abundant natural reservoir than freshwater, stands as a promising alternative for sustainable hydrogen production, provided that the competitive chloride electro-oxidation is minimized. Herein, we propose an original material combination to selectively trigger oxygen evolution from seawater at expenses of chlorine generation. The target systems, based on MnO2 or Mn2O3 decorated with Fe2O3 or Co3O4, are fabricated by plasma enhanced-chemical vapor deposition of manganese oxides, functionalization with Fe2O3 and Co3O4 by sputtering, and annealing in air/Ar to obtain Mn(IV)/Mn(III) oxides. Among the various options, MnO2 decorated with Co3O4 yields the best performances in alkaline seawater splitting, with an outstanding Tafel slope of approximate to 40 mV x dec(-1) and an overpotential of 450 mV, enabling to rule out chlorine evolution. These attractive performances, resulting from the synergistic contribution of catalytic and electronic effects, open the door to low-cost hydrogen generation from seawater under real-world conditions, paving the way to eventual large-scale applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.446
Times cited: 67
DOI: 10.1016/J.APCATB.2020.119684
|
|