“In-situ chromium and vanadium recovery of landfilled ferrochromium and stainless steel slags”. Spooren J, Kim E, Horckmans L, Broos K, Nielsen P, Quaghebeur M, Chemical engineering journal 303, 359 (2016). http://doi.org/10.1016/J.CEJ.2016.05.128
Abstract: A novel heap leaching method was investigated for selective removal of chromium (Cr) and-vanadium (V) from ferrochromium (FeCr) and stainless steel (SS) slags. In particular, alkaline oxidative heap leaching was simulated on lab-scale by batch and column leaching tests. The results show a selective leaching of Cr (11-19%) and V (7.0-7.5%) after 64 days of column leaching, with a very low dissolution (<2.2% (FeCr slag) and <0.15% (SS slag)) of matrix elements (e.g. Al, Fe, Si, Mg, Ca), when NaOCl is applied as oxidation agent and NaOH as alkaline agent. Furthermore, the used leaching liquor is reactive for a longer period of time, indicating that circulation of leaching liquor could be possible. Finally, the experimental results were fed into a first-order model which predicts that Cr will continue to leach from the tested slags for 4-5 years at a chosen infiltration rate of 73,000 l/(y m(2)). (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Sustainable Energy, Air and Water Technology (DuEL)
DOI: 10.1016/J.CEJ.2016.05.128
|
“New method for selective Cr recovery from stainless steel slag by NaOCl assisted alkaline leaching and consecutive BaCrO4 precipitation”. Kim E, Spooren J, Broos K, Nielsen P, Horckmans L, Vrancken KC, Quaghebeur M, Chemical engineering journal 295, 542 (2016). http://doi.org/10.1016/J.CEJ.2016.03.073
Abstract: A new hydrometallurgical method was investigated for selective leaching of chromium from stainless steel slag (SS slag) consisting of temperature controlled extraction with NaOH in the presence of NaOCl, followed by water leaching. After parameter optimization of the NaOCl-NaOH extraction step, a selective Cr leaching of 68% was reached, while dissolution of matrix materials was low (Al 0.3%, Ca 2.0%, Si 0.4%). The optimum conditions for the investigated system are: 105 degrees C, 6 h, SS slag particle size <63 mu m, mass ratio of NaOH to SS slag 0.13, and 3.3 mmol NaOCl to 1 g SS slag. The described oxidative alkaline leaching process by hypochlorite enables selective recovery of Cr at a significantly lower temperature and required amount of alkaline agent than molten salt or alkaline roasting processes. BaCrO4 was precipitated to purify and concentrate Cr from the leachate in which also minor amounts of Mn and V were present. This method allowed for a 99.9% Cr recovery rate. The obtained leaching residue shows no alterations of the SS slag's mineralogy with respect to untreated material. Therefore, a known carbonation treatment of the slag can be applied to prepare novel construction materials with a lowered Cr content. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Sustainable Energy, Air and Water Technology (DuEL)
DOI: 10.1016/J.CEJ.2016.03.073
|
“Valorization of stainless steel slag by selective chromium recovery and subsequent carbonation of the matrix material”. Kim E, Spooren J, Broos K, Nielsen P, Horckmans L, Geurts R, Vrancken KC, Quaghebeur M, Journal of cleaner production 117, 221 (2016). http://doi.org/10.1016/J.JCLEPRO.2016.01.032
Abstract: This study focuses on the recycling of stainless steel (SS) slags containing about 1.2 wt% of chromium (Cr). The selective recovery of Cr from SS slag by a hydrometallurgical method (alkaline pressure leaching) was investigated. Leaching experiments were carried out based on 2(4-1) factorial design of experiment (DOE) with the following parameters: NaOH concentration, temperature, leaching time, and mechanical activation (MA). Results show that temperature and MA are the most influencing factors for an enhanced Cr leaching. The maximum Cr leaching was 46% at 1 M NaOH, 240 degrees C, 6 h, MA 30 min, while the matrix material was dissolved only to a limited extent (Al 2.88%, Si 0.12%, Ca 0.05%). After Cr leaching followed by alkali washing, a carbonation treatment is proposed to stabilize the remaining Cr in the matrix material and make the subsequent recycling of the matrix material as a construction material possible. (C) 2016 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Sustainable Energy, Air and Water Technology (DuEL)
DOI: 10.1016/J.JCLEPRO.2016.01.032
|