“TEM investigation of the role of the polycrystalline-silicon film/substrate interface in high quality radio frequency silicon substrates”. Ding L, Raskin J-P, Lumbeeck G, Schryvers D, Idrissi H, Materials Characterization 161, 110174 (2020). http://doi.org/10.1016/J.MATCHAR.2020.110174
Abstract: The microstructural characteristics of two polycrystalline silicon (poly-Si) films with different electrical properties produced by low-pressure chemical vapour deposition on top of high resistivity silicon substrates were investigated by advanced transmission electron microscopy (TEM), including high resolution aberration corrected TEM and automated crystallographic orientation mapping in TEM. The results reveal that the nature of the poly-Si film/Si substrate interface is the main factor controlling the electrical resistivity of the poly-Si films. The high resistivity and high electrical linearity of poly-Si films are strongly promoted by the Sigma 3 twin type character of the poly-Si/Si substrate interface, leading to the generation of a huge amount of extended defects including stacking faults, Sigma 3 twin boundaries as well as Sigma 9 grain boundaries at this interface. Furthermore, a high density of interfacial dislocations has been observed at numerous common and more exotic grain boundaries deviating from their standard crystallographic planes. In contrast, poly-Si film/Si substrate interfaces with random character do not favour the formation of such complex patterns of defects, leading to poor electrical resistivity of the poly-Si film. This finding opens windows for the development of high resistivity silicon substrates for Radio Frequency (RF) integrated circuits (ICs) applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.7
DOI: 10.1016/J.MATCHAR.2020.110174
|
|
|
“Enhancement of toughness of Al-to-steel Friction Melt Bonded welds via metallic interlayers”. Jimenez-Mena N, Jacques PJ, Ding L, Gauquelin N, Schryvers D, Idrissi H, Delannay F, Simar A, Materials science and engineering: part A: structural materials: properties, microstructure and processing 740-741, 274 (2019). http://doi.org/10.1016/j.msea.2018.10.101
Abstract: The toughness of Al-to-steel welds decreases with increasing thickness of the intermetallic (IM) layer formed at the interface. Co plating has been added as interlayer in Al-to-steel Friction Melt Bonded (FMB) welds to control the nature and thickness of the IM layer. In comparison to a weld without interlayer, Co plating brings about a reduction of the thickness of the IM layer by 70%. The critical energy release rate of the crack propagating in the weld is used as an indicator of toughness. It is evaluated via an adapted crack propagation test using an energy conservation criterion. For a weld without interlayer, critical energy release rate is found to increase when the thickness of the intermetallic layer decreases. When the intermetallic layer is thick, the crack propagates in a brittle manner through the intermetallic whereas, at low layer thickness, the crack deviates and partially propagates through the Al plate, which causes an increase of toughness. The use of a Co interlayer brings about an increase of toughness by causing full deviation of the crack towards the Al plate.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 4
DOI: 10.1016/j.msea.2018.10.101
|
|
|
“Dislocation structures and the role of grain boundaries in cyclically deformed Ni micropillars”. Samaee V, Sandfeld S, Idrissi H, Groten J, Pardoen T, Schwaiger R, Schryvers D, Materials Science And Engineering A-Structural Materials Properties Microstructure And Processing 769, 138295 (2020). http://doi.org/10.1016/j.msea.2019.138295
Abstract: Transmission electron microscopy and finite element-based dislocation simulations were combined to study the development of dislocation microstructures after cyclic deformation of single crystal and bicrystal Ni micropillars oriented for multi-slip. A direct correlation between large accumulation of plastic strain and the presence of dislocation cell walls in the single crystal micropillars was observed, while the presence of the grain boundary hampered the formation of wall-like structures in agreement with a smaller accumulated plastic strain. Automated crystallographic orientation and nanostrain mapping using transmission electron microscopy revealed the presence of lattice heterogeneities associated to the cell walls including long range elastic strain fields. By combining the nanostrain mapping with an inverse modelling approach, information about dislocation density, line orientation and Burgers vector direction was derived, which is not accessible otherwise in such dense dislocation structures. Simulations showed that the image forces associated with the grain boundary in this specific bicrystal configuration have only a minor influence on dislocation behavior. Thus, the reduced occurrence of “mature” cell walls in the bicrystal can be attributed to the available volume, which is too small to accommodate cell structures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.4
Times cited: 1
DOI: 10.1016/j.msea.2019.138295
|
|
|
“Damage mechanisms in selective laser melted AlSi10Mg under as built and different post-treatment conditions”. Zhao L, Macias JGS, Ding L, Idrissi H, Simar A, Microstructure And Processing 764, 138210 (2019). http://doi.org/10.1016/J.MSEA.2019.138210
Abstract: Selective laser melting (SLM) manufactured AlSi10Mg alloys present a fine silicon-rich network and precipitates which grant high mechanical strength but low ductility. Post-treatments, aiming at eliminating inherent defects related to SLM such as residual stresses, porosity or inhomogeneity, result in significant changes in the microstructure and impact both the hardening and the damage mechanisms of the post-treated material. The present work is dedicated to the investigation of the fracture of SLM AlSi10Mg under as built and three post-treatment conditions, namely two stress relieve heat treatments and friction stir processing (FSP). It is found that the interconnected Si network fosters damage at low strain due to the brittleness of the Si phase. The onset of damage transfers load to the enclosed Al phase which then fractures quickly under high stress, thus leading to low material ductility. In contrast, when the Si network is globularized into Si particles, the ductility is highly increased even in the case where the porosity and inhomogeneity of the microstructure remain after the post-treatment. The ductility enhancement results from the delay in void nucleation on the Si particles as well as from the tolerance for void growth in the Al matrix.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 1
DOI: 10.1016/J.MSEA.2019.138210
|
|
|
““Branched&rdquo, structural transformation of the L12-Al3Zr phase manipulated by Cu substitution/segregation in the Al-Cu-Zr alloy system”. Ding L, Zhao M, Ehlers FJH, Jia Z, Zhang Z, Weng Y, Schryvers D, Liu Q, Idrissi H, Journal of materials science &, technology 185, 186 (2024). http://doi.org/10.1016/j.jmst.2023.11.015
Abstract: The effect of Cu on the evolution of the Al3Zr phase in an Al-Cu-Zr cast alloy during solution treatment at 500 °C has been thoroughly studied by combining atomic resolution high-angle annular dark-field scanning transmission electron microscopy, energy-dispersive X-ray spectroscopy and first-principles cal- culations. The heat treatment initially produces a pure L12-Al3Zr microstructure, allowing for about 13 % Cu to be incorporated in the dispersoid. Cu incorporation increases the energy barrier for anti-phase boundary (APB) activation, thus stabilizing the L12 structure. Additional heating leads to a Cu-induced “branched”path for the L12 structural transformation, with the latter process accelerated once the first APB has been created. Cu atoms may either (i) be repelled by the APBs, promoting the transformation to a Cu-poor D023 phase, or (ii) they may segregate at one Al-Zr layer adjacent to the APB, promoting a transformation to a new thermodynamically favored phase, Al4CuZr, formed when these segregation layers are periodically arranged. Theoretical studies suggest that the branching of the L12 transformation path is linked to the speed at which an APB is created, with Cu attraction triggered by a comparatively slow process. This unexpected transformation behavior of the L12-Al3Zr phase opens a new path to understanding, and potentially regulating the Al3Zr dispersoid evolution for high temperature applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 10.9
DOI: 10.1016/j.jmst.2023.11.015
|
|
|
“Influence of amorphous phase separation on the crystallization behavior of glass-ceramics in the BaO-TiO2-SiO2 system”. Boulay E, Ragoen C, Idrissi H, Schryvers D, Godet S, Journal of non-crystalline solids 384, 61 (2014). http://doi.org/10.1016/j.jnoncrysol.2013.06.023
Abstract: The possible role of a prior amorphous phase separation on the subsequent crystallization has been the topic of vigorous debates over the last decades and has not yet been clarified, especially regarding the role of the interfaces created by the phase separation. This study proposes to focus on the interplay between a prior amorphous phase separation and the crystallization of fresnoite in the BaO-TiO2-SiO2 system. The crystallization behavior of a non-stoichiometric composition inside the miscibility gap (called APS) is compared with the stoichiometric composition (called FRES) and a non-stoichiometric composition outside the miscibility gap (called NoAPS). The crystallization mechanisms are compared using differential thermal analysis (DTA) by calculating the Avrami parameters and the activation energies as a function of the particle size. The DTA study shows that the two non-stoichiometric compositions exhibit a pronounced surface crystallization behavior whereas FRES undergoes bulk nucleation. This is supported by a multi-scale microstructure characterization. Furthermore, this study demonstrates that the amorphous phase separation and the associated interfaces do not play any significant role in the nucleation step. Moreover, transmission electron microscope (TEM) and local orientation measurements show that the growth of the dendrites is not hindered by the SiO2-rich droplets. The final stage of crystallization of APS is tentatively explained by two composition effects that must be further investigated: the viscosity effect and the formation of a eutectic. (C) 2013 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.124
Times cited: 10
DOI: 10.1016/j.jnoncrysol.2013.06.023
|
|
|
“Study of the Q&prime, (Q)-phase precipitation in Al–Mg–Si–Cu alloys by quantification of atomic-resolution transmission electron microscopy images and atom probe tomography”. Ding L, Orekhov A, Weng Y, Jia Z, Idrissi H, Schryvers D, Muraishi S, Hao L, Liu Q, Journal of materials science 54, 7943 (2019). http://doi.org/10.1007/s10853-019-03427-6
Abstract: The precipitation mechanism of the Q phase in Al-Mg-Si-Cu alloys has long been the subject of ambiguity and debate since its metastable phase (Q 0) has the same crystal structure and similar lattice parameters as its equilibrium counterparts. In the present work, the evolution of the Q 0 (Q) phase during aging is studied by combination of quantitative atomic-resolution scanning transmission electron microscopy and atom probe tomography. It was found that the transformation from the Q 0 to the Q phase involves changes of the occupancy of Al atoms in atomic columns of the Q 0 (Q) phase. The Al atoms incorporated in the Cu, Si and Mg columns are gradually released into the Al matrix, while mixing between Cu and Si atoms occurs in the Si columns. This transformation process is mainly attributed to the low lattice misfit of the equilibrium Q phase. Besides, the formation of various compositions of the Q phase is due to the different occupancy in the atomic columns of the Q phase. The occupancy changes in the columns of the Q phase are kinetically controlled and are strongly influenced by the alloy composition and aging temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.599
Times cited: 1
DOI: 10.1007/s10853-019-03427-6
|
|
|
“In Situ Quantitative Tensile Testing of Antigorite in a Transmission Electron Microscope”. Idrissi H, Samaee V, Lumbeeck G, Werf T, Pardoen T, Schryvers D, Cordier P, Journal Of Geophysical Research-Solid Earth 125 (2020). http://doi.org/10.1029/2019JB018383
Abstract: The determination of the mechanical properties of serpentinites is essential toward the understanding of the mechanics of faulting and subduction. Here we present the first in situ tensile tests on antigorite in a transmission electron microscope. A push‐to‐pull deformation device is used to perform quantitative tensile tests, during which force and displacement are measured, while the evolving microstructure is imaged with the microscope. The experiments have been performed at room temperature on 2 × 1 × 0.2 μm3 beams prepared by focused ion beam. The specimens are not single crystals despite their small sizes. Orientation mapping indicated that several grains were well oriented for plastic slip. However, no dislocation activity has been observed even though the engineering tensile stress went up to 700 MPa. We show also that antigorite does not exhibit a purely elastic‐brittle behavior since, despite the presence of defects, the specimens accumulate permanent deformation and did not fail within the elastic regime. Instead, we observe that strain localizes at grain boundaries. All observations concur to show that under these experimental conditions, grain boundary sliding is the dominant deformation mechanism. This study sheds a new light on the mechanical properties of antigorite and calls for further studies on the structure and properties of grain boundaries in antigorite and more generally in phyllosilicates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.9
DOI: 10.1029/2019JB018383
|
|
|
“Effect of hydriding induced defects on the small-scale plasticity mechanisms in nanocrystalline palladium thin films”. Lumbeeck G, Idrissi H, Amin-Ahmadi B, Favache A, Delmelle R, Samaee V, Proost J, Pardoen T, Schryvers D, Journal Of Applied Physics 124, 225105 (2018). http://doi.org/10.1063/1.5055274
Abstract: Nanoindentation tests performed on nanocrystalline palladium films subjected to hydriding/dehydriding cycles demonstrate a significant softening when compared to the as-received material. The origin of this softening is unraveled by combining in situ TEM nanomechanical testing with automated crystal orientation mapping in TEM and high resolution TEM. The softening is attributed to the presence of a high density of stacking faults and of Shockley partial dislocations after hydrogen loading. The hydrogen induced defects affect the elementary plasticity mechanisms and the mechanical response by acting as preferential sites for twinning/detwinning during deformation. These results are analyzed and compared to previous experimental and simulation works in the literature. This study provides new insights into the effect of hydrogen on the atomistic deformation and cracking mechanisms as well as on the mechanical properties of nanocrystalline thin films and membranes.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 2.068
Times cited: 2
DOI: 10.1063/1.5055274
|
|
|
“Atomic-scale investigation of the heterogeneous precipitation in the E (Al₁₈Mg₃Cr₂) dispersoid of 7075 aluminum alloy”. Ding L, Zhao L, Weng Y, Schryvers D, Liu Q, Idrissi H, Journal Of Alloys And Compounds 851, 156890 (2021). http://doi.org/10.1016/J.JALLCOM.2020.156890
Abstract: The heterogeneous precipitation of the eta (MgZn2) phase on the E (Al18Mg3Cr2) dispersoids of the 7075 aluminum alloy was systematically investigated by atomic resolution high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and energy dispersive X-ray spectrometry (EDX). It is found that coarse B particles are heterogeneously precipitated at the E particle interface after water quenching and isothermal aging at 120 degrees C. The incoherent E/Al interface is responsible for the high tendency of heterogeneous precipitation of the B phase. Two different orientation relationships (ORs) between the eta, E and Al matrix are identified: OR1 [2 (11) over bar0](eta)[011](E)//[(1) over bar 12](Al), (01 (1) over bar0)(eta)//(13 (3) over bar)(E)//(201)(Al), OR2 [(1) over bar 12](E)//[0001](eta)//[011](Al), (01 (1) over bar0 )(eta)//(220)(E)//(34 (4) over bar)(Al). The eta phase is preferential to nucleate along the {111}(E) or the {220}(E) planes, depending on its OR. The heterogeneous nucleation of B phase on the E particle could stabilize the E/Al interface by introducing a coherent E/eta interface, which increases the drive force of heterogeneous precipitation. The reorientation of eta phase and mutual diffusion of solute atoms could assist the coherency of the E/eta interface. The present results suggest that increasing the coherency of the E/Al interface is a promising method to suppress the heterogeneous precipitation of the eta phase. (C) 2020 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
DOI: 10.1016/J.JALLCOM.2020.156890
|
|
|
“Advanced TEM investigation of the plasticity mechanisms in nanocrystalline freestanding palladium films with nanoscale twins”. Wang B, Idrissi H, Galceran M, Colla MS, Turner S, Hui S, Raskin JP, Pardoen T, Godet S, Schryvers D, International journal of plasticity 37, 140 (2012). http://doi.org/10.1016/j.ijplas.2012.04.003
Abstract: Nanocrystalline palladium thin films deposited by electron-beam evaporation and deformed by on-chip tensile testing reveal a surprisingly large strain hardening capacity when considering the small similar to 25 nm grain size. The as-grown films contain several coherent single and multifold twin boundaries. The coherency of the twin boundaries considerably decreases with deformation due to dislocation/twin boundary interactions. These reactions are described based on a detailed analysis of the number and the type of dislocations located at the twin boundaries using high-resolution TEM, including aberration corrected microscopy. Sessile Frank dislocations were observed at the twin/matrix interfaces, explaining the loss of the TB coherency due to the Burgers vector pointing out of the twinning plane. Grain boundary mediated processes were excluded as a mechanism dominating the plastic deformation based on the investigation of the grain size distribution as well as the crystallographic texture using Automated Crystallographic Orientation Indexation TEM. Other factors influencing the plastic deformation such as impurities and the presence of a native passivation oxide layer at the surface of the films were investigated using analytical TEM. The twin boundaries observed in the present work partly explain the high strain hardening capacity by providing both increasing resistance to dislocation motion with deformation and a source for dislocation multiplication. (C) 2012 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.702
Times cited: 44
DOI: 10.1016/j.ijplas.2012.04.003
|
|
|
“Single layer graphene controlled surface and bulk indentation plasticity in copper”. Bahrami F, Hammad M, Fivel M, Huet B, D'Haese C, Ding L, Nysten B, Idrissi H, Raskin JP, Pardoen T, International Journal Of Plasticity 138, 102936 (2021). http://doi.org/10.1016/J.IJPLAS.2021.102936
Abstract: The impact of graphene reinforcement on the mechanical properties of metals has been a subject of intense investigation over the last decade in surface applications to mitigate the impact of tribological loadings or for strengthening purposes when dispersed into a bulk material. Here, the effect on the plastic indentation response of a single graphene layer grown on copper is analyzed for two configurations: one with graphene at the surface, the other with graphene sandwiched under a 100 nm thick copper cap layer. Nanoindentation under both displacement and load control conditions show both earlier and shorter pop-in excursions compared to systems without graphene. Atomic force microscopy reveals much smoother pile-ups with no slip traces in the presence of a surface graphene layer. The configuration with the intercalated graphene layer appears as an ideal elementary system to address bulk hardening mechanisms by indentation testing. Transmission electron microscopy (TEM) cross-sections below indents show more diffuse and homogeneous dislocation activity in the presence of graphene. 3D dislocation dynamics simulations allow unraveling of the origin of these 3D complex phenomena and prove that the collective dislocation mechanisms are dominantly controlled by the strong back stress caused by the graphene barrier. These results provide a quantitative understanding of the impact of graphene on dislocation mechanisms for both surface and bulk applications, but with an impact that is not as large as anticipated from other studies or general literature claims.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.702
DOI: 10.1016/J.IJPLAS.2021.102936
|
|
|
“Effect of structural defects on the hydriding kinetics of nanocrystalline Pd thin films”. Delmelle R, Amin-Ahmadi B, Sinnaeve M, Idrissi H, Pardoen T, Schryvers D, Proost J, International journal of hydrogen energy 40, 7335 (2015). http://doi.org/10.1016/j.ijhydene.2015.04.017
Abstract: While the microstructure of a metal is well-known to affect its equilibrium hydrogen uptake and therefore the hydriding thermodynamics, microstructural effects on the hydriding kinetics are much less documented. Moreover, for thin film systems, such microstructural effects are difficult to separate from the internal stress effect, since most defects generate internal stresses. Such a decoupling has been achieved in this paper for nanocrystalline Pd thin film model systems through the use of a high-resolution, in-situ curvature measurement set-up during Pd deposition, annealing and hydriding. This set-up allowed producing Pd thin films with similar internal stress levels but significantly different microstructures. This was evidenced from detailed defect statistics obtained by transmission electron microscopy, which showed that the densities of grain boundaries, dislocations and twin boundaries have all been lowered by annealing. The same set-up was then used to study the hydriding equilibrium and kinetic behaviour of the resulting films at room temperature. A full quantitative analysis of their hydriding cycles showed that the rate constants of both the adsorption- and absorption-limited kinetic regimes were strongly affected by microstructure. Defect engineering was thereby shown to increase the rate constants for hydrogen adsorption and absorption in Pd by a factor 40 and 30, respectively. Copyright (C) 2015, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.582
Times cited: 13
DOI: 10.1016/j.ijhydene.2015.04.017
|
|
|
“Dislocations and plasticity of experimentally deformed coesite”. Idrissi H, Cordier P, Jacob D, Walte N, European journal of mineralogy 20, 665 (2008). http://doi.org/10.1127/0935-1221/2008/0020-1849
Abstract: Dislocation microstructures have been characterized by transmission electron microscopy in polycrystalline coesite deformed experimentally at 4 GPa, 1200 degrees C. Burgers vectors have been determined by large-angle convergent-beam electron diffraction. Sample orientation was assisted by precession electron diffraction to overcome difficulties arising from pseudo-hexagonal symmetry. The results are explained by using a pseudo-hexagonal setting. We found that most dislocations observed are of the 1/3 < 2 (1) over bar(1) over bar0 > type. No clear glide plane was identified, suggesting that climb is activated under these conditions. This conclusion is supported by the observation of numerous subgrain boundaries. We have also observed some [00011 dislocations. Finally, the C12/cl space group to which coesite belongs being centred, an additional slip system is observed: 1/6[(1) over bar2 (1) over bar3](01 (1) over bar1) (1/2[(1) over bar 10](110) in the monoclinic setting).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.362
Times cited: 5
DOI: 10.1127/0935-1221/2008/0020-1849
|
|
|
“Effect of microstructure and internal stress on hydrogen absorption into Ni thin film electrodes during alkaline water electrolysis”. Delvaux A, Lumbeeck G, Idrissi H, Proost J, Electrochimica Acta 340, 135970 (2020). http://doi.org/10.1016/J.ELECTACTA.2020.135970
Abstract: Efforts to improve the cell efficiency of hydrogen production by water electrolysis continue to address the electrochemical kinetics of the oxygen and hydrogen evolution reactions in detail. The objective of this work is to study a parasitic reaction occurring during the hydrogen evolution reaction (HER), namely the absorption of hydrogen atoms into the bulk electrode. Effects of the electrode microstructure and internal stress on this reaction have been addressed as well in this paper. Ni thin film samples were deposited on a Si substrate by sputter deposition with different deposition pressures, resulting in different microstructures and varying levels of internal stress. These microstructures were first analyzed in detail by Transmission Electron Microscopy (TEM). Cathodic chrono-amperometric measurements and cyclic voltammetries have then been performed in a homemade electrochemical cell. These tests were coupled to a multi-beam optical sensor (MOS) in order to obtain in-situ curvature measurements during hydrogen absorption. Indeed, since hydrogen absorption in the thin film geometry results in a constrained volume expansion, internal stress generation during HER can be monitored by means of curvature measurements. Our results show that different levels of internal stress, grain size and twin boundary density can be obtained by varying the deposition parameters. From an electrochemical point of view, this paper highlights the fact that the electrochemical surface mechanisms during HER are the same for all the electrodes, regardless of their microstructure. However it is shown that the absolute amount of hydrogen being absorbed into the Ni thin films increases when the grain size is reduced, due to a higher grain boundaries density which are favourite absorption sites for hydrogen. At the same time, it was concluded that H-2 evolution is favoured at electrodes having a more compressive (i.e. a less tensile) internal stress. Finally, the subtle effect of microstructure on the hydrogen absorption rate will be discussed as well. (C) 2020 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.6
Times cited: 2
DOI: 10.1016/J.ELECTACTA.2020.135970
|
|
|
“On amorphization as a deformation mechanism under high stresses”. Idrissi H, Carrez P, Cordier P, Current opinion in solid state and materials science 26, 100976 (2022). http://doi.org/10.1016/J.COSSMS.2021.100976
Abstract: In this paper we review the work related to amorphization under mechanical stress. Beyond pressure, we highlight the role of deviatoric or shear stresses. We show that the most recent works make amorphization appear as a deformation mechanism in its own right, in particular under extreme conditions (shocks, deformations under high stresses, high strain-rates).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11
DOI: 10.1016/J.COSSMS.2021.100976
|
|
|
“A versatile lab-on-chip test platform to characterize elementary deformation mechanisms and electromechanical couplings in nanoscopic objects”. Pardoen T, Colla M-S, Idrissi H, Amin-Ahmadi B, Wang B, Schryvers D, Bhaskar UK, Raskin J-P, Comptes rendus : physique 17, 485 (2016). http://doi.org/10.1016/j.crhy.2015.11.005
Abstract: A nanomechanical on-chip test platform has recently been developed to deform under a variety of loading conditions freestanding thin films, ribbons and nanowires involving submicron dimensions. The lab-on-chip involves thousands of elementary test structures from which the elastic modulus, strength, strain hardening, fracture, creep properties can be extracted. The technique is amenable to in situ transmission electron microscopy (TEM) investigations to unravel the fundamental underlying deformation and fracture mechanisms that often lead to size-dependent effects in small-scale samples. The method allows addressing electrical and magnetic couplings as well in order to evaluate the impact of large mechanical stress levels on different solid-state physics phenomena. We had the chance to present this technique in details to Jacques Friedel in 2012 who, unsurprisingly, made a series of critical and very relevant suggestions. In the spirit of his legacy, the paper will address both mechanics of materials related phenomena and couplings with solids state physics issues.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.048
Times cited: 7
DOI: 10.1016/j.crhy.2015.11.005
|
|
|
“Fostering crack deviation via local internal stresses in Al/NiTi composites and its correlation with fracture toughness”. Zhao L, Ding L, Soete J, Idrissi H, Kerckhofs G, Simar A, Composites: part A: applied science and manufacturing 126, 105617 (2019). http://doi.org/10.1016/J.COMPOSITESA.2019.105617
Abstract: In the framework of metal matrix composites, a research gap exists regarding tailoring damage mechanisms. The present work aims at developing an Al/NiTi composite incorporating internal stresses in the vicinity of reinforcements. The composite is manufactured by friction stir processing which allows a homogenous NiTi distribution and a good Al/NiTi interface bonding. The internal stresses are introduced via shape memory effect of the embedded NiTi particles. The induced internal strain field is confirmed by digital image correlation and the corresponding stress field is evaluated by finite element simulation. It is found that the damage mechanism is modified in the presence of internal stresses. The consequent enhancement of fracture toughness arises by the fact that the internal stresses foster discrete damages shifted from the fracture ligament line. These damages release the stress concentration at the main crack tip and lead to a deviated crack path when coalescing to accommodate fracture propagation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.075
DOI: 10.1016/J.COMPOSITESA.2019.105617
|
|
|
“Tailoring Mechanical Properties of a-C:H:Cr Coatings”. Bagherpour A, Baral P, Colla M-S, Orekhov A, Idrissi H, Haye E, Pardoen T, Lucas S, Coatings 13, 2084 (2023). http://doi.org/10.3390/coatings13122084
Abstract: The development of coatings with tunable performances is critical to meet a wide range of technological applications each one with different requirements. Using the plasma-enhanced chemical vapor deposition (PECVD) process, scientists can create hydrogenated amorphous carbon coatings doped with metal (a-C:H:Me) with a broad range of mechanical properties, varying from those resembling polymers to ones resembling diamond. These diverse properties, without clear relations between the different families, make the material selection and optimization difficult but also very rich. An innovative approach is proposed here based on projected performance indices related to fracture energy, strength, and stiffness in order to classify and optimize a-C:H:Me coatings. Four different a-C:H:Cr coatings deposited by PECVD with Ar/C2H2 discharge under different bias voltage and pressures are investigated. A path is found to produce coatings with a selective critical energy release rate between 5–125 J/m2 without compromising yield strength (1.6–2.7 GPa) and elastic limit (≈0.05). Finally, fine-tuned coatings are categorized to meet desired applications under different testing conditions.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
DOI: 10.3390/coatings13122084
|
|
|
“On the Origin of Damped Electrochemical Oscillations at Silicon Anodes (Revisited)”. Proost J, Blaffart F, Turner S, Idrissi H, ChemPhysChem : a European journal of chemical physics and physical chemistry 15, 3116 (2014). http://doi.org/10.1002/cphc.201402207
Abstract: Electrochemical oscillations accompanying the formation of anodic silica have been shown in the past to be correlated with rather abrupt changes in the mechanical stress state of the silica film, commonly associated with some kind of fracture or porosification of the oxide. To advance the understanding on the origin of such oscillations in fluoride-free electrolytes, we have revisited a seminal experiment reported by Lehmann almost two decades ago. We thereby demonstrate that the oscillations are not stress-induced, and do not originate from a morphological transformation of the oxide in the course of anodisation. Alternatively, the mechanical features accompanying the oscillations can be explained by a partial relaxation of the field-induced electrostrictive stress. Furthermore, our observations suggest that the oscillation mechanism more likely results from a periodic depolarisation of the anodic silica.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.075
Times cited: 5
DOI: 10.1002/cphc.201402207
|
|
|
“Critical assessments and thermodynamic modeling of BaO-SiO2 and SiO2-TiO2 systems and their extensions into liquid immiscibility in the BaO-SiO2-TiO2 system”. Boulay E, Nakano J, Turner S, Idrissi H, Schryvers D, Godet S, Calphad computer coupling of phase diagrams and thermochemistry 47, 68 (2014). http://doi.org/10.1016/j.calphad.2014.06.004
Abstract: This study discusses rational reproduction of liquid immiscibility in the BaO-SiO2-TiO2 system. While a ternary assessment requires sub-binary descriptions in the same thermodynamic model, the related sub-binary systems BaO-SiO2, BaO-TiO2 and SiO2-TiO2 liquid and solid phases have been evaluated using different thermodynamic models in the literature. In this study, BaO-SiO2 and SiO2-TiO2 were assessed using the Ionic Two Sublattice model (I2SL) based on experimental data from the literature. BaO-TiO2 was already assessed using this model. Binary descriptions developed were then used for the assessment of liquid immiscibility in the BaO-SiO2-TiO2 system. Ternary interaction parameters were found necessary for rational reproduction of the new ternary experimental data gathered in the present work. The model parameters for each system were evaluated using a CAPLHAD approach. A set of parameters is proposed. They show good agreement between the calculated and experimental equilibrium liquidus, liquid immiscibility and thermochemical properties in the BaO-SiO2-TiO2 system. (C) 2014 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.6
Times cited: 9
DOI: 10.1016/j.calphad.2014.06.004
|
|
|
“High resolution transmission electron microscopy characterization of fcc ->, 9R transformation in nanocrystalline palladium films due to hydriding”. Amin-Ahmadi B, Idrissi H, Delmelle R, Pardoen T, Proost J, Schryvers D, Applied physics letters 102, 071911 (2013). http://doi.org/10.1063/1.4793512
Abstract: Sputtered nanocrystalline palladium thin films with nanoscale growth twins have been subjected to hydriding cycles. The evolution of the twin boundaries has been investigated using high resolution transmission electron microscopy. Surprisingly, the Sigma 3{112} incoherent twin boundaries dissociate after hydriding into two phase boundaries bounding a 9R phase. This phase which corresponds to single stacking faults located every three {111} planes in the fcc Pd structure was not expected because of the high stacking fault energy of Pd. This observation is connected to the influence of the Hydrogen on the stacking fault energy of palladium and the high compressive stresses building up during hydriding. (C) 2013 American Institute of Physics. [http://dx.doi.org/10.1063/1.4793512]
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 14
DOI: 10.1063/1.4793512
|
|
|
“Plasticity mechanisms in ultrafine grained freestanding aluminum thin films revealed by in-situ transmission electron microscopy nanomechanical testing”. Idrissi H, Kobler A, Amin-Ahmadi B, Coulombier M, Galceran M, Raskin J-P, Godet S, Kuebel C, Pardoen T, Schryvers D, Applied physics letters 104, 101903 (2014). http://doi.org/10.1063/1.4868124
Abstract: In-situ bright field transmission electron microscopy (TEM) nanomechanical tensile testing and in-situ automated crystallographic orientation mapping in TEM were combined to unravel the elementary mechanisms controlling the plasticity of ultrafine grained Aluminum freestanding thin films. The characterizations demonstrate that deformation proceeds with a transition from grain rotation to intragranular dislocation glide and starvation plasticity mechanism at about 1% deformation. The grain rotation is not affected by the character of the grain boundaries. No grain growth or twinning is detected. (C) 2014 AIP Publishing LLC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 24
DOI: 10.1063/1.4868124
|
|
|
“Synergistic effects altering reaction pathways : the case of glucose hydrogenation over Fe-Ni catalysts”. Fu Y, Ding L, Singleton ML, Idrissi H, Hermans S, Applied Catalysis B-Environmental 288, 119997 (2021). http://doi.org/10.1016/J.APCATB.2021.119997
Abstract: Carbon black (CB) supported Ni, Fe, or Fe-Ni alloy catalysts were synthesized by sol-gel to elucidate the reaction pathways over each catalyst, as well as synergistic effects in glucose to sorbitol hydrogenation. The bimetallic materials presented small and alloyed nanoparticles that were richer in reduced metallic sites at the surface than their monometallic counterparts. Glucose isomerization to fructose was favoured over Fe/CB, while glucose hydrogenation to sorbitol is the dominating pathway over Ni/CB catalyst. By contrast, sorbitol production was promoted and undesired isomerization was suppressed when Fe and Ni formed a nanoalloy. In addition, the alloy catalyst presented better stability than the corresponding monometallic catalyst. A comparison with a mechanical mixture of Fe/CB and Ni/CB monometallic catalysts demonstrated the synergy at the nanoscale in the alloy. By comparing different Fe:Ni ratios, the 1:1 formulation was identified as the best compromise to achieve a high activity while maintaining high sorbitol selectivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.446
DOI: 10.1016/J.APCATB.2021.119997
|
|
|
“Thin films of the spin ice compound Ho2Ti2O7”. Leusink DP, Coneri F, Hoek M, Turner S, Idrissi H, Van Tendeloo G, Hilgenkamp H, APL materials 2, 032101 (2014). http://doi.org/10.1063/1.4867222
Abstract: The pyrochlore compounds Ho2Ti2O7 and Dy2Ti2O7 show an exotic form of magnetism called the spin ice state, resulting from the interplay between geometrical frustration and ferromagnetic coupling. A fascinating feature of this state is the appearance of magnetic monopoles as emergent excitations above the degenerate ground state. Over the past years, strong effort has been devoted to the investigation of these monopoles and other properties of the spin ice state in bulk crystals. Here, we report the fabrication of Ho2Ti2O7 thin films using pulsed laser deposition on yttria-stabilized ZrO2 substrates. We investigated the structural properties of these films by X-ray diffraction, scanning transmission electron microscopy, and atomic force microscopy, and the magnetic properties by vibrating sample magnetometry at 2 K. The films not only show a high crystalline quality, but also exhibit the hallmarks of a spin ice: a pronounced magnetic anisotropy and an intermediate plateau in the magnetization along the [111] crystal direction.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.335
Times cited: 18
DOI: 10.1063/1.4867222
|
|
|
“Ultrahigh strain hardening in thin palladium films with nanoscale twins”. Idrissi H, Wang B, Colla MS, Raskin JP, Schryvers D, Pardoen T, Advanced materials 23, 2119 (2011). http://doi.org/10.1002/adma.201004160
Abstract: Nanocrystalline Pd thin films containing coherent growth twin boundaries are deformed using on-chip nanomechanical testing. A large work-hardening capacity is measured. The origin of the observed behavior is unraveled using transmission electron microscopy and shows specific dislocations and twin boundaries interactions. The results indicate the potential for large strength and ductility balance enhancement in Pd films, as needed in membranes for H technologies.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 57
DOI: 10.1002/adma.201004160
|
|
|
“High strength-ductility of thin nanocrystalline palladium films with nanoscale twins : on-chip testing and grain aggregate model”. Colla M-S, Wang B, Idrissi H, Schryvers D, Raskin J-P, Pardoen T, Acta materialia 60, 1795 (2012). http://doi.org/10.1016/j.actamat.2011.11.054
Abstract: The mechanical behaviour of thin nanocrystalline palladium films with an ∼30 nm in plane grain size has been characterized on chip under uniaxial tension. The films exhibit a large strain hardening capacity and a significant increase in the strength with decreasing thickness. Transmission electron microscopy has revealed the presence of a moderate density of growth nanotwins interacting with dislocations. A semi-analytical grain aggregate model is proposed to investigate the impact of different contributions to the flow behaviour, involving the effect of twins, of grain size and of the presence of a thin surface layer. This model provides guidelines to optimizing the strength/ductility ratio of the films.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 38
DOI: 10.1016/j.actamat.2011.11.054
|
|
|
“On the mechanism of twin formation in FeMnC TWIP steels”. Idrissi H, Renard K, Ryelandt L, Schryvers D, Jacques PJ, Acta materialia 58, 2464 (2010). http://doi.org/10.1016/j.actamat.2009.12.032
Abstract: Although it is well known that FeMnC TWIP steels exhibit high work-hardening rates, the elementary twinning mechanisms controlling the plastic deformation of these steels have still not been characterized. The aim of the present study is to analyse the extended defects related to the twinning occurrence using transmission electron microscopy. Based on these observations, the very early stage of twin nucleation can be attributed to the pole mechanism with deviation proposed by Cohen and Weertman or to the model of Miura, Takamura and Narita, while the twin growth is controlled by the pole mechanism proposed by Venables. High densities of sessile Frank dislocations are observed within the twins at the early stage of deformation, which can affect the growth and the stability of the twins, but also the strength of these twins and their interactions with the gliding dislocations present in the matrix. This experimental evidence is discussed and compared to recent results in order to relate the defects analysis to the macroscopic behaviour of this category of material.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 244
DOI: 10.1016/j.actamat.2009.12.032
|
|
|
“Dislocation/hydrogen interaction mechanisms in hydrided nanocrystalline palladium films”. Amin-Ahmadi B, Connétable D, Fivel M, Tanguy D, Delmelle R, Turner S, Malet L, Godet S, Pardoen T, Proost J, Schryvers D, Idrissi H, Acta materialia 111, 253 (2016). http://doi.org/10.1016/j.actamat.2016.03.054
Abstract: The nanoscale plasticity mechanisms activated during hydriding cycles in sputtered nanocrystalline Pd films have been investigated ex-situ using advanced transmission electron microscopy techniques. The internal stress developing within the films during hydriding has been monitored in-situ. Results showed that in Pd films hydrided to β-phase, local plasticity was mainly controlled by dislocation activity in spite of the small grain size. Changes of the grain size distribution and the crystallographic texture have not been observed. In contrast, significant microstructural changes were not observed in Pd films hydrided to α-phase. Moreover, the effect of hydrogen loading on the nature and density of dislocations has been investigated using aberration-corrected TEM. Surprisingly, a high density of shear type stacking faults has been observed after dehydriding, indicating a significant effect of hydrogen on the nucleation energy barriers of Shockley partial dislocations. Ab-initio calculations of the effect of hydrogen on the intrinsic stable and unstable stacking fault energies of palladium confirm the experimental observations.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 14
DOI: 10.1016/j.actamat.2016.03.054
|
|
|
“Dislocation and back stress dominated viscoplasticity in freestanding sub-micron Pd films”. Lemoine G, Delannay L, Idrissi H, Colla M-S, Pardoen T, Acta materialia 111, 10 (2016). http://doi.org/10.1016/j.actamat.2016.03.038
Abstract: A dislocation-based crystal plasticity model is developed in order to study the mechanical and creep/ relaxation behaviour of polycrystalline metallic thin films. The model accounts for the confinement of plasticity due to grain boundaries and for the anisotropy of individual grains, as well as for the significant viscoplastic effects associated to dislocation dominated thermally activated mechanisms. Numerical predictions are assessed based on experimental tensile test followed by relaxation on freestanding Pd films, based on an on-chip test technique. The dislocation-based mechanism assumption captures all the experimental trends, including the stress strain response, the relaxation behaviour and the dislocation density evolution, confirming the dominance of a dislocation driven deformation mechanism for the present Pd films with high defects density. The model has also been used to address some original experimental evidences involving back stresses, Bauschinger effect, backward creep and strain recovery. (C) 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 6
DOI: 10.1016/j.actamat.2016.03.038
|
|