Abstract: It is generally believed that β00 precipitates, rather than β0 precipitates, are the major strengthening precipitates in
aged Al–Mg–Si alloys. The reason for this difference is not well understood. To clarify this, two samples of the
same Al–Mg–Si alloy but with different aging states were prepared. The under-aged sample only contains nanoprecipitates
of the β00 type, while the peak-aged one contains nearly equal volumes of β00 and β0 precipitates. We
have, for the first time, separated the strengthening effect of the contribution from βʺ and βʹ precipitates,
respectively, by an indirect approach based on high-precision measurements of volume fractions, number densities,
sizes, proportions of the precipitates, their lattice strains, the composition and grain size of the matrix. The
β0 precipitates, which take 45.6% of the total precipitate volume in the peak-aged sample, contribute to the entire
precipitation strengthening by only 31.6%. The main reason why they are less useful compared to β00 precipitates
has been found to be associated with their smaller lattice strains relative to the matrix, which is 0.99% versus
2.10% (for β00 ).

Abstract: The effect of Cu on the evolution of the Al3Zr phase in an Al-Cu-Zr cast alloy during solution treatment at 500 °C has been thoroughly studied by combining atomic resolution high-angle annular dark-field scanning transmission electron microscopy, energy-dispersive X-ray spectroscopy and first-principles cal- culations. The heat treatment initially produces a pure L12-Al3Zr microstructure, allowing for about 13 % Cu to be incorporated in the dispersoid. Cu incorporation increases the energy barrier for anti-phase boundary (APB) activation, thus stabilizing the L12 structure. Additional heating leads to a Cu-induced “branched”path for the L12 structural transformation, with the latter process accelerated once the first APB has been created. Cu atoms may either (i) be repelled by the APBs, promoting the transformation to a Cu-poor D023 phase, or (ii) they may segregate at one Al-Zr layer adjacent to the APB, promoting a transformation to a new thermodynamically favored phase, Al4CuZr, formed when these segregation layers are periodically arranged. Theoretical studies suggest that the branching of the L12 transformation path is linked to the speed at which an APB is created, with Cu attraction triggered by a comparatively slow process. This unexpected transformation behavior of the L12-Al3Zr phase opens a new path to understanding, and potentially regulating the Al3Zr dispersoid evolution for high temperature applications.

Abstract: Computer simulations are performed for an argon inductively coupled plasma (ICP) with a capacitive radio-frequency bias power, to investigate the bias effect on the discharge mode transition and on the plasma characteristics at various ICP currents, bias voltages, and bias frequencies. When the bias frequency is fixed at 13.56 MHz and the ICP current is low, e.g., 6A, the spatiotemporal averaged plasma density increases monotonically with bias voltage, and the bias effect is already prominent at a bias voltage of 90 V. The maximum of the ionization rate moves toward the bottom electrode, which indicates clearly the discharge mode transition in inductive/capacitive discharges. At higher ICP currents, i.e., 11 and 13 A, the plasma density decreases first and then increases with bias voltage, due to the competing mechanisms between the ion acceleration power dissipation and the capacitive power deposition. At 11 A, the bias effect is still important, but it is noticeable only at higher bias voltages. At 13 A, the ionization rate is characterized by a maximum at the reactor center near the dielectric window at all selected bias voltages, which indicates that the ICP power, instead of the bias power, plays a dominant role under this condition, and no mode transition is observed. Indeed, the ratio of the bias power to the total power is lower than 0.4 over a wide range of bias voltages, i.e., 0300V. Besides the effect of ICP current, also the effect of various bias frequencies is investigated. It is found that the modulation of the bias power to the spatiotemporal distributions of the ionization rate at 2MHz is strikingly different from the behavior observed at higher bias frequencies. Furthermore, the minimum of the plasma density appears at different bias voltages, i.e., 120V at 2MHz and 90V at 27.12 MHz.

Abstract: A two-dimensional hybrid Monte Carlofluid model, incorporating a full-wave solution of Maxwell's equations, is employed to describe the behavior of high frequency (HF) and very high frequency capacitively coupled plasmas (CCPs), operating both at single frequency (SF) and dual frequency (DF) in a CF4/O2 gas mixture. First, the authors investigate the plasma composition, and the simulations reveal that besides CF4 and O2, also COF2, CF3, and CO2 are important neutral species, and CF+3 and F− are the most important positive and negative ions. Second, by comparing the results of the model with and without taking into account the electromagnetic effects for a SF CCP, it is clear that the electromagnetic effects are important, both at 27 and 60 MHz, because they affect the absolute values of the calculation results and also (to some extent) the spatial profiles, which accordingly affects the uniformity in plasma processing. In order to improve the plasma radial uniformity, which is important for the etch process, a low frequency (LF) source is added to the discharge. Therefore, in the major part of the paper, the plasma uniformity is investigated for both SF and DF CCPs, operating at a HF of 27 and 60 MHz and a LF of 2 MHz. For this purpose, the authors measure the etch rates as a function of position on the wafer in a wide range of LF powers, and the authors compare them with the calculated fluxes toward the wafer of the plasma species playing a role in the etch process, to explain the trends in the measured etch rate profiles. It is found that at a HF of 60 MHz, the uniformity of the etch rate is effectively improved by adding a LF power of 2 MHz and 300 W, while its absolute value increases by about 50%, thus a high etch rate with a uniform distribution is observed under this condition.

Abstract: In this work, we have studied the TMA/H(2)O (TMA Al(CH(3))(3)) atomic layer deposition (ALD) of Al(2)O(3) on hydroxyl (OH) and thiol (SH) terminated semiconductor substrates. Total reflection x-ray fluorescence reveals a complex growth-per-cycle evolution during the early ALD reaction cycles. OH and SH terminated surfaces demonstrate growth inhibition from the second reaction cycle on. Theoretical calculations, based on density functional theory, are performed on cluster models to investigate the first TMA/H(2)O reaction cycle. Based on the theoretical results, we discuss possible mechanisms for the growth inhibition from the second reaction cycle on. In addition, our calculations show that AlCH(3) groups are hydrolyzed by a H(2)O molecule adsorbed on a neighboring Al atom, independent of the type of backbonds (Si-O, Ge-O, or Ge-S) of AlCH(3). The coordination of Al remains four-fold after the first TMA/H(2)O reaction cycle. (C) 2012 American Vacuum Society. [DOI: 10.1116/1.3664090]

Abstract: Atomic layer deposition (ALD) is a vapor phase technique that is able to deposit uniform, conformal thin films with an excellent thickness control at the atomic scale. 18 nm thick Al2O3 and TiO2 coatings were deposited conformaly and pinhole-free onto micrometer-sized Cu powder, using trimethylaluminum and tetrakis(dimethylamido)titanium(IV), respectively, as a precursor and de-ionized water as a reactant. The capability of the ALD coating to protect the Cu powder against corrosion was investigated. Therefore, the stability of the coatings was studied in solutions with different pH in the range of 0–14, and in situ raman spectroscopy was used to detect the emergence of corrosion products of Cu as an indication that the protective coating starts to fail. Both ALD coatings provide good protection at standard pH values in the range of 5–7. In general, the TiO2 coating shows a better barrier protection against corrosion than the Al2O3 coating. However, for the most extreme pH conditions, pH 0 and pH 14, the TiO2 coating starts also to degrade.

Abstract: Defects on hollow silica spheres synthesized in a tetraethylorthosilicate-octylamine-HCl-H2O system were recorded by scanning microscope. Based on the results, influences of synthesis composition on the formation of these defects are discussed. It is evidenced that products prepared with different octylamine-to-tetraethylorthosilicate ratios may have surface depressions, cracks and non-hollow microspheres. However, by changing water and acid additions, these defects could be reduced or eliminated. Generally, samples synthesized with a large octylamine addition commonly exhibit surface depressions. A small octylamine or a large water addition benefits the formation of solid silica microspheres among the product. Acid, although is not indispensable for the formation of hollow spheres, helps to eliminate or reduce depressions on the hollow shells. It is explained that the added acid gives rise to a relative localized fast hydrolysis versus condensation, facilitating an easy mobility of hydrolyzed silica species, and consequently the shell surface is smoothened.

Abstract: In order to increase the understanding of the underlying processes in organic solvent nanofiltration (OSN), a study has been undertaken aimed at clarifying the solvent flux behaviour of ceramic nanofiltration and ultrafiltration membranes. Ceramic membranes were chosen for their non-swelling character. Pure water and a variation of 11 different organic solvents were measured on a series of different ceramic membranes with pore-size diameters ranging from 0.9 nm up to 100 nm. To avoid any historical effects, each flux measurement was carried out on a new membrane. The flux results were analysed in a phenomenological way, and a common very simple linear relationship was observed between the product of flux and viscosity of the solvent, and the total Hansen solubility parameter of the solvent. The linear relationship was found for all membranes, independent of the membrane pore size and the membrane material. The slope of the linear relationship was found to depend exponentially on the pore-size diameter and on the polarity of the membrane surface. This result emphasizes the importance of viscosity in the solvent transport, but also of the polarity difference between membrane surface and solvent. The very simple flux model deduced, allows a straightforward prediction of the flux of any solvent or solvent mixture, once the water flux of the membrane is known. At the high pore-size end, the phenomenological model naturally transforms into the viscous-flow or pore-flow behaviour as required. A tentative physical explanation of the model takes into account the presence and extension of a water layer adsorbed to the total pore surface of these membranes. This work also shows that the water flux of a hydrophilic membrane gives a good indication of its molecular weight cut-off (MWCO), and therefore of its separation performance in water. (C)0 2013 Elsevier B.V. All rights reserved.

Abstract: Capture and storage of CO2 (CCS) from fossil-fuel power plants is vital in order to counteract a pending anthropogenic global warming. High temperature oxygen transport perovskite membranes can fulfill an important role in the separation of oxygen from air needed in the oxy-fuel technologies for CCS. In this study we present the development, performance and stability of gastight, macrovoid-free and sulfur-free Ba0.5Sr0.5Co0.8Fe0.2O3 − δ (BSCF) mixed conductor capillary membranes prepared by phase-inversion spinning and sintering. A sulfur-free phase-inversion polymer was chosen in order to obtain a phase-pure BSCF crystal phase. Special attention was given to the polymer solution and ceramic spinning suspension in order to avoid macrovoids and achieve gastight membranes. The sulfur-free BSCF capillaries showed an average 4-point bending strength of 64 ± 8 MPa and a maximum oxygen flux of not, vert, similar5.3 Nml/(cm2 min) at 950 °C for an argon sweep flow rate of 125 Nml/min. The comparison of the performance of sulfur-free and sulfur-containing BSCF capillaries with similar dimensions revealed a profound impact of the sulfur contamination on both the oxygen flux and the activation energy of the overall oxygen transport mechanism. Both long-term oxygen permeation at different temperatures and post-operation analysis of a sulfur-free BSCF capillary were performed and discussed.

Abstract: Analysis of oxygen permeation fluxes through Ba0.5Sr0.5Co0.8Fe0.2O3−δ (BSCF) capillary membranes, fabricated via a phase-inversion spinning technique using polysulfone as binder, showed a significant limiting role of the surface-oxygen exchange kinetics. Within the studied temperature and oxygen partial pressure ranges, the activation of core and shell sides of the BSCF capillary with praseodymium oxide (PrOx) resulted in an increase in permeation rate of about 300%. At 11231223 K the activated BSCF membranes demonstrate almost 3-times lower activation energies for the overall oxygen transport (not, vert, similar35 kJ/mol) than the non-activated capillaries, indicating that the mechanism of oxygen transport through the activated capillaries becomes significantly controlled by bulk diffusion limitations, allowing further improvement of the overall performance by decreasing the wall thickness. XRD, EDS and EPMA studies revealed the formation of (Pr,Ba,Sr)(Co,Fe)O3−δ perovskite-type oxides on the surface of the PrOx-modified membranes, which may be responsible for the drastic increase in oxygen exchange rate. At T > 1123 K both non-activated and activated Ba0.5Sr0.5Co0.8Fe0.2O3−δ membranes demonstrate stable performance with time, while at 1073 K only a small initial decrease in permeation was observed.

Abstract: Sylgard®184/multiwalled carbon nanotube (MWNT) composites have been prepared by in situ polymerization using purified and functionalized multiwalled carbon nanotubes (f-MWNTs) as fillers. Surface modification of the MWNTs has been carried out by silanization with 7-octenyltrichlorosilane (7OTCS) and n-octyltrichlorosilane (nOTCS). The modification and dispersion of the carbon nanotubes in composites were characterized by X-ray photoelectron spectroscopy (XPS), transmission electron spectroscopy (TEM), and high-resolution transmission electron spectroscopy (HRTEM). Youngs modulus results were derived from indentation testing. It is shown that the terminal-vinyl group of 7OTCS molecules plays an essential role for both the dispersion of the f-MWNTs in the composite and its mechanical properties. At loading as low as 0.2 wt%, the Youngs modulus is shown to increase up to 50%. This is interpreted as resulting from a combination of the good compatibility in the forming silicone matrix of the MWNTs coated with a siloxane network, on the one hand, and the covalent links created between the terminal-vinyl groups and the host matrix in formation, on the other hand.