“Size-Induced Switching of Nanowire Growth Direction: a New Approach Toward Kinked Nanostructures”. Shen Y, Lebedev OI, Turner S, Van Tendeloo G, Song X, Yu X, Wang Q, Chen H, Dayeh SA, Wu T, Advanced functional materials 26, 3687 (2016). http://doi.org/10.1002/ADFM.201600142
Abstract: Exploring self-assembled nanostructures with controllable architectures has been a central theme in nanoscience and nanotechnology because of the tantalizing perspective of directly integrating such bottom-up nanostructures into functional devices. Here, the growth of kinked single-crystal In2O3 nanostructures consisting of a nanocone base and a nanowire tip with an epitaxial and defect-free transition is demonstrated for the first time. By tailoring the growth conditions, a reliable switching of the growth direction from [111] to [110] or [112] is observed when the Au catalyst nanoparticles at the apexes of the nanocones shrink below approximate to 100 nm. The natural formation of kinked nanoarchitectures at constant growth pressures is related to the size-dependent free energy that changes for different orientations of the nanowires. The results suggest that the mechanism of forming such kinked nanocone-nanowire nanostructures in well-controlled growth environment may be universal for a wide range of functional materials.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 2
DOI: 10.1002/ADFM.201600142
|
|
|
“Encapsulation of Noble Metal Nanoparticles through Seeded Emulsion Polymerization as Highly Stable Plasmonic Systems”. Scarabelli L, Schumacher M, Jimenez de Aberasturi D, Merkl J‐P, Henriksen‐Lacey M, Milagres de Oliveira T, Janschel M, Schmidtke C, Bals S, Weller H, Liz‐Marzán LM, Advanced functional materials 29, 1809071 (2019). http://doi.org/10.1002/adfm.201809071
Abstract: The implementation of plasmonic nanoparticles in vivo remains hindered by important limitations such as biocompatibility, solubility in biological fluids, and physiological stability. A general and versatile protocol is presented, based on seeded emulsion polymerization, for the controlled encapsulation of gold and silver nanoparticles. This procedure enables the encapsulation of single nanoparticles as well as nanoparticle clusters inside a protecting polymer shell. Specifically, the efficient coating of nanoparticles of both metals is demonstrated, with final dimensions ranging between 50 and 200 nm, i.e., sizes of interest for bio-applications. Such hybrid nanocomposites display extraordinary stability in high ionic strength and oxidizing environments, along with high cellular uptake, and low cytotoxicity. Overall, the prepared nanostructures are promising candidates for plasmonic applications under biologically relevant conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 19
DOI: 10.1002/adfm.201809071
|
|
|
“Self‐Assembly of Atomically Thin Chiral Copper Heterostructures Templated by Black Phosphorus”. Nerl HC, Pokle A, Jones L, Müller‐Caspary K, Bos KHW, Downing C, McCarthy EK, Gauquelin N, Ramasse QM, Lobato I, Daly D, Idrobo JC, Van Aert S, Van Tendeloo G, Sanvito S, Coleman JN, Cucinotta CS, Nicolosi V, Advanced functional materials 29, 1903120 (2019). http://doi.org/10.1002/adfm.201903120
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 1
DOI: 10.1002/adfm.201903120
|
|
|
“Thickness dependent properties in oxide heterostructures driven by structurally induced metal-oxygen hybridization variations”. Liao Z, Gauquelin N, Green RJ, Macke S, Gonnissen J, Thomas S, Zhong Z, Li L, Si L, Van Aert S, Hansmann P, Held K, Xia J, Verbeeck J, Van Tendeloo G, Sawatzky GA, Koster G, Huijben M, Rijnders G, Advanced functional materials 27, 1606717 (2017). http://doi.org/10.1002/ADFM.201606717
Abstract: Thickness-driven electronic phase transitions are broadly observed in different types of functional perovskite heterostructures. However, uncertainty remains whether these effects are solely due to spatial confinement, broken symmetry, or rather to a change of structure with varying film thickness. Here, this study presents direct evidence for the relaxation of oxygen-2p and Mn-3d orbital (p-d) hybridization coupled to the layer-dependent octahedral tilts within a La2/3Sr1/3MnO3 film driven by interfacial octahedral coupling. An enhanced Curie temperature is achieved by reducing the octahedral tilting via interface structure engineering. Atomically resolved lattice, electronic, and magnetic structures together with X-ray absorption spectroscopy demonstrate the central role of thickness-dependent p-d hybridization in the widely observed dimensionality effects present in correlated oxide heterostructures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 55
DOI: 10.1002/ADFM.201606717
|
|
|
“Nonlayered CdSe flakes homojunctions”. Jin B, Liang F, Hu Z-Y, Wei P, Liu K, Hu X, Van Tendeloo G, Lin Z, Li H, Zhou X, Xiong Q, Zhai T, Advanced Functional Materials 30, 1908902 (2020). http://doi.org/10.1002/ADFM.201908902
Abstract: 2D homojunctions have stimulated extensive attention because of their perfect thermal and lattice matches, as well as their tunable band structures in 2D morphology, which provide fascinating opportunities for novel electronics and optoelectronics. Recently, 2D nonlayered materials have attracted the attention of researchers owing to their superior functional applications and diverse portfolio of the 2D family. Therefore, 2D nonlayered homojunctions would open the door to a rich spectrum of exotic 2D materials. However, they are not investigated due to their extremely difficult synthesis methods. Herein, nonlayered CdSe flakes homojunctions are obtained via self-limited growth with InCl3 as a passivation agent. Interestingly, two pieces of vertical wurtzite-zinc blende (WZ-ZB) homojunctions epitaxially integrate into WZ/ZB lateral junctions. These homojunctions show a divergent second-harmonic generation intensity, strongly correlated to the multiple twinned ZB phase, as identified by aberration-corrected scanning transmission electron microscopy and theoretical calculations. Impressively, the photodetector based on this WZ/ZB CdSe homojunction shows excellent performances, integrating a high photoswitching ratio (3.4 x 10(5)) and photoresponsivity (3.7 x 10(3) A W-1), suggesting promising potential for applications in electronics and optoelectronics.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19
Times cited: 8
DOI: 10.1002/ADFM.201908902
|
|
|
“Tailoring vanadium dioxide film orientation using nanosheets : a combined microscopy, diffraction, transport, and soft X-ray in transmission study”. Tran Phong Le P, Hofhuis K, Rana A, Huijben M, Hilgenkamp H, Rijnders GAJHM, ten Elshof JE, Koster G, Gauquelin N, Lumbeeck G, Schuessler-Langeheine C, Popescu H, Fortuna F, Smit S, Verbeek XH, Araizi-Kanoutas G, Mishra S, Vaskivskyi I, Duerr HA, Golden MS, Advanced Functional Materials 30, 1900028 (2020). http://doi.org/10.1002/ADFM.201900028
Abstract: Vanadium dioxide (VO2) is a much-discussed material for oxide electronics and neuromorphic computing applications. Here, heteroepitaxy of VO2 is realized on top of oxide nanosheets that cover either the amorphous silicon dioxide surfaces of Si substrates or X-ray transparent silicon nitride membranes. The out-of-plane orientation of the VO2 thin films is controlled at will between (011)(M1)/(110)(R) and (-402)(M1)/(002)(R) by coating the bulk substrates with Ti0.87O2 and NbWO6 nanosheets, respectively, prior to VO2 growth. Temperature-dependent X-ray diffraction and automated crystal orientation mapping in microprobe transmission electron microscope mode (ACOM-TEM) characterize the high phase purity, the crystallographic and orientational properties of the VO2 films. Transport measurements and soft X-ray absorption in transmission are used to probe the VO2 metal-insulator transition, showing results of a quality equal to those from epitaxial films on bulk single-crystal substrates. Successful local manipulation of two different VO2 orientations on a single substrate is demonstrated using VO2 grown on lithographically patterned lines of Ti0.87O2 and NbWO6 nanosheets investigated by electron backscatter diffraction. Finally, the excellent suitability of these nanosheet-templated VO2 films for advanced lensless imaging of the metal-insulator transition using coherent soft X-rays is discussed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19
Times cited: 1
DOI: 10.1002/ADFM.201900028
|
|
|
“Circumventing Wear and Tear of Adaptive Porous Materials”. Canossa S, Ji Z, Wuttke S, Advanced Functional Materials , 1908547 (2020). http://doi.org/10.1002/adfm.201908547
Abstract: The assessment of the architectural stability of molecular porous materials is not yet a common practice, but critical to their understanding and development. The conformational adaptation of porous materials to guest binding and other chemical dynamics poses a risk of architectural damage, leading to performance deterioration during their prolonged usage. The deformation of the framework backbone and the disconnection of building units are driven by chemical, mechanical, and thermal perturbations, and can be quantitatively described by the term connection completeness. Analytical means that can be used to measure this parameter are presented in order to provide a standard, practical protocol for evaluating architectural damage made to framework materials. Preventive and remedial strategies are proposed for enhancing the architectural integrity of frameworks without compromising their functional mechanisms, paving the way to the design of robust yet adaptive materials. In this way, the discussion on architectural stability is initiated, and readers are encouraged to carefully characterize molecular porous materials for a better understanding of their structure-property relationship.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19
DOI: 10.1002/adfm.201908547
|
|
|
“Pore Chemistry of Metal–Organic Frameworks”. Ji Z, Wang H, Canossa S, Wuttke S, Yaghi OM, Advanced Functional Materials 30, 2000238 (2020). http://doi.org/10.1002/adfm.202000238
Abstract: The pores in metal–organic frameworks (MOFs) can be functionalized by placing chemical entities along the backbone and within the backbone. This chemistry is enabled by the architectural, thermal, and chemical robustness of the frameworks and the ability to characterize them by many diffraction and spectroscopic techniques. The pore chemistry of MOFs is articulated in terms of site isolation, coupling, and cooperation and relate that to their functions in guest recognition, catalysis, ion and electron transport, energy transfer, pore‐dynamic modulation, and interface construction. It is envisioned that the ultimate control of pore chemistry requires arranging functionalities into defined sequences and developing techniques for reading and writing such sequences within the pores.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19
DOI: 10.1002/adfm.202000238
|
|
|
“Excellent excitonic photovoltaic effect in 2D CsPbBr₃/CdS heterostructures”. Jin B, Zuo N, Hu Z-Y, Cui W, Wang R, Van Tendeloo G, Zhou X, Zhai T, Advanced Functional Materials , 2006166 (2020). http://doi.org/10.1002/ADFM.202006166
Abstract: P-n photovoltaic junctions are essential building blocks for optoelectronic devices for energy conversion. However, this photovoltaic efficiency has almost reached its theoretical limit. Here, a brand-new excitonic photovoltaic effect in 2D CsPbBr3/CdS heterostructures is revealed. These heterostructures, synthesized by epitaxial growth, display a clean interface and a strong interlayer coupling. The excitonic photovoltaic effect is a function of both the built-in equilibrium electrical potential energy and the chemical potential energy, which is generated by the significant concentration gradient of electrons and holes at the heterojunction interface. Excitingly, this novel photovoltaic effect results in a large open-circuit voltage of 0.76 V and a high power conversion efficiency of 17.5%. In addition, high photodetection performance, including a high photoswitch ratio (I-light/I-dark) of 10(5)and a fast response rate of 23 mu s are obtained. These findings provide a new platform for photovoltaic applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19
Times cited: 1
DOI: 10.1002/ADFM.202006166
|
|
|
“Functionalization chemistry of porous materials”. Canossa S, Wuttke S, Advanced Functional Materials 30, 2003875 (2020). http://doi.org/10.1002/ADFM.202003875
Keywords: Editorial; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19
Times cited: 1
DOI: 10.1002/ADFM.202003875
|
|
|
“Intracellular fate of hydrophobic nanocrystal self-assemblies in tumor cells”. Nicolas-Boluda A, Yang Z, Dobryden I, Carn F, Winckelmans N, Pechoux C, Bonville P, Bals S, Claesson PM, Gazeau F, Pileni MP, Advanced Functional Materials 30, 2004274 (2020). http://doi.org/10.1002/ADFM.202004274
Abstract: Control of interactions between nanomaterials and cells remains a biomedical challenge. A strategy is proposed to modulate the intralysosomal distribution of nanoparticles through the design of 3D suprastructures built by hydrophilic nanocrystals (NCs) coated with alkyl chains. The intracellular fate of two water-dispersible architectures of self-assembled hydrophobic magnetic NCs: hollow deformable shells (colloidosomes) or solid fcc particles (supraballs) is compared. These two self-assemblies display increased cellular uptake by tumor cells compared to dispersions of the water-soluble NC building blocks. Moreover, the self-assembly structures increase the NCs density in lysosomes and close to the lysosome membrane. Importantly, the structural organization of NCs in colloidosomes and supraballs are maintained in lysosomes up to 8 days after internalization, whereas initially dispersed hydrophilic NCs are randomly aggregated. Supraballs and colloidosomes are differently sensed by cells due to their different architectures and mechanical properties. Flexible and soft colloidosomes deform and spread along the biological membranes. In contrast, the more rigid supraballs remain spherical. By subjecting the internalized suprastructures to a magnetic field, they both align and form long chains. Overall, it is highlighted that the mechanical and topological properties of the self-assemblies direct their intracellular fate allowing the control intralysosomal density, ordering, and localization of NCs.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19
Times cited: 11
DOI: 10.1002/ADFM.202004274
|
|
|
“Phase-transformation-induced giant deformation in thermoelectric Ag₂Se semiconductor”. Liang Q, Yang D, Xia F, Bai H, Peng H, Yu R, Yan Y, He D, Cao S, Van Tendeloo G, Li G, Zhang Q, Tang X, Wu J, Advanced Functional Materials , 2106938 (2021). http://doi.org/10.1002/ADFM.202106938
Abstract: In most semiconducting metal chalcogenides, a large deformation is usually accompanied by a phase transformation, while the deformation mechanism remains largely unexplored. Herein, a phase-transformation-induced deformation in Ag2Se is investigated by in situ transmission electron microscopy, and a new ordered high-temperature phase (named as alpha '-Ag2Se) is identified. The Se-Se bonds are folded when the Ag+-ion vacancies are ordered and become stretched when these vacancies are disordered. Such a stretch/fold of the Se-Se bonds enables a fast and large deformation occurring during the phase transition. Meanwhile, the different Se-Se bonding states in alpha-, alpha '-, beta-Ag2Se phases lead to the formation of a large number of nanoslabs and the high concentration of dislocations at the interface, which flexibly accommodate the strain caused by the phase transformation. This study reveals the atomic mechanism of the deformation in Ag2Se inorganic semiconductors during the phase transition, which also provides inspiration for understanding the phase transition process in other functional materials.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
DOI: 10.1002/ADFM.202106938
|
|
|
“The role of SnF₂, additive on interface formation in all lead-free FASnI₃, perovskite solar cells”. Zillner J, Boyen H-G, Schulz P, Hanisch J, Gauquelin N, Verbeeck J, Kueffner J, Desta D, Eisele L, Ahlswede E, Powalla M, Advanced functional materials , 2109649 (2022). http://doi.org/10.1002/ADFM.202109649
Abstract: Tin-based perovskites are promising alternative absorber materials for leadfree perovskite solar cells but need strategies to avoid fast tin (Sn) oxidation. Generally, this reaction can be slowed down by the addition of tin fluoride (SnF2) to the perovskite precursor solution, which also improves the perovskite layer morphology. Here, this work analyzes the spatial distribution of the additive within formamidinium tin triiodide (FASnI(3)) films deposited on top of poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) hole transporting layers. Employing time-of-flight secondary ion mass spectrometry and a combination of hard and soft X-ray photoelectron spectroscopy, it is found that Sn F2 preferably accumulates at the PEDOT:PSS/perovskite interface, accompanied by the formation of an ultrathin SnS interlayer with an effective thickness of approximate to 1.2 nm.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19
Times cited: 22
DOI: 10.1002/ADFM.202109649
|
|
|
“Effect of interface evolution on thermal conductivity of vacuum hot pressed SiC/Al composites”. Chen Z, Tan Z, Ji G, Schryvers D, Ouyang Q, Li Z, Advanced engineering materials 17, 1076 (2015). http://doi.org/10.1002/adem.201400412
Abstract: The SiC/Al composites have been fabricated by a vacuum hot pressing (VHP) process in order to study the effect of interface evolution on the global thermal conductivity (TC). By optimizing the VHP parameters of sintering temperature and time, the three different kinds of SiC/Al interface configurations, that is, non-bonded, diffusion-bonded, and reaction-bonded interfaces, are formed and identified by measurement of relative density, X-ray diffraction, scanning and (high-resolution) transmission electron microscopy. The VHPed composite sintered at 655 °C for 60 min is fully dense and presents a tightly-adhered and clean SiC/Al interface at the nanoscale, the ideal diffusion-bonded interface being the most favorable for minimizing interfacial thermal resistance, which in turn results in the highest TC of around 270 W/mK.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.319
Times cited: 9
DOI: 10.1002/adem.201400412
|
|
|
“Intrinsic thermal instability of methylammonium lead trihalide perovskite”. Conings B, Drijkoningen J, Gauquelin N, Babayigit A, D'Haen J, D'Olieslaeger L, Ethirajan A, Verbeeck J, Manca J, Mosconi E, Angelis FD, Boyen HG;, Laser physics review 5, 1500477 (2015). http://doi.org/10.1002/aenm.201500477
Abstract: Organolead halide perovskites currently are the new front-runners as light absorbers in hybrid solar cells, as they combine efficiencies passing already 20% with deposition temperatures below 100 °C and cheap solution-based fabrication routes. Long-term stability remains a major obstacle for application on an industrial scale. Here, it is demonstrated that significant decomposition effects already occur during annealing of a methylammonium lead triiode perovskite at 85 °C even in inert atmosphere thus violating international standards. The observed behavior supports the view of currently used perovskite materials as soft matter systems with low formation energies, thus representing a major bottleneck for their application, especially in countries with high average temperatures. This result can trigger a broader search for new perovskite families with improved thermal stability.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.721
Times cited: 1691
DOI: 10.1002/aenm.201500477
|
|
|
“Shelf life degradation of bulk heterojunction solar cells : intrinsic evolution of charge transfer complex”. Guerrero A, Heidari H, Ripolles TS, Kovalenko A, Pfannmöller M, Bals S, Kauffmann L-D, Bisquert J, Garcia-Belmonte G, Laser physics review 5, 1401997 (2015). http://doi.org/10.1002/aenm.201401997
Abstract: Achievement of long-term stability of organic photovoltaics is currently one of the major topics for this technology to reach maturity. Most of the techniques used to reveal degradation pathways are destructive and/or do not allow for real-time measurements in operating devices. Here, three different, nondestructive techniques able to provide real-time information, namely, film absorbance, capacitance-voltage (C-V), and impedance spectroscopy (IS), are combined over a period of 1 year using non-accelerated intrinsic degradation conditions. It is discerned between chemical modifications in the active layer, physical processes taking place in the bulk of the blend from those at the active layer/contact interfaces. In particular, it is observed that during the ageing experiment, the main source for device performance degradation is the formation of donor-acceptor charge-transfer complex (P3HT(center dot+)-PCBM center dot-) that acts as an exciton quencher. Generation of these radical species diminishes photocurrent and reduces open-circuit voltage by the creation of electronic defect states. Conclusions extracted from absorption, C-V, and IS measurements will be further supported by a range of other techniques such as atomic force microscopy, X-ray diffraction, and dark-field imaging of scanning transmission electron microscopy on ultrathin cross-sections.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.721
Times cited: 30
DOI: 10.1002/aenm.201401997
|
|
|
“Square-centimeter-sized high-efficiency polymer solar cells : how the processing atmosphere and film quality influence performance at large scale”. Ben Dkhil S, Pfannmöller M, Bals S, Koganezawa T, Yoshimoto N, Hannani D, Gaceur M, Videlot-Ackermann C, Margeat O, Ackermann J, Laser physics review 6, 1600290 (2016). http://doi.org/10.1002/aenm.201600290
Abstract: Organic solar cells based on two benzodithiophene-based polymers (PTB7 and PTB7-Th) processed at square centimeter-size under inert atmosphere and ambient air, respectively, are investigated. It is demonstrated that the performance of solar cells processed under inert atmosphere is not limited by the upscaling of photoactive layer and the interfacial layers. Thorough morphological and electrical characterizations of optimized layers and corresponding devices reveal that performance losses due to area enlargement are only caused by the sheet resistance of the transparent electrode reducing the effi ciency from 9.3% of 7.8% for PTB7-Th in the condition that both photoactive layer and the interfacial layers are of high layer quality. Air processing of photoactive layer and the interfacial layers into centimeter-sized solar cells lead to additional, but only slight, losses (< 10%) in all photovoltaic parameters, which can be addressed to changes in the electronic properties of both active layer and ZnO layers rather than changes in layer morphology. The demonstrated compatibility of polymer solar cells using solution-processed photoactive layer and interfacial layers with large area indicates that the introduction of a standard active area of 1 cm(2) for measuring effi ciency of organic record solar cells is feasible. However electric standards for indium tin oxides (ITO) or alternative transparent electrodes need to be developed so that performance of new photovoltaic materials can be compared at square centimeter-size.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.721
Times cited: 6
DOI: 10.1002/aenm.201600290
|
|
|
“Toward high-temperature stability of PTB7-based bulk heterojunction solar cells : impact of fullerene size and solvent additive”. Ben Dkhil S, Pfannmöller M, Saba MI, Gaceur M, Heidari H, Videlot-Ackermann C, Margeat O, Guerrero A, Bisquert J, Garcia-Belmonte G, Mattoni A, Bals S, Ackermann J, Laser physics review 7, 1601486 (2017). http://doi.org/10.1002/AENM.201601486
Abstract: The use of fullerene as acceptor limits the thermal stability of organic solar cells at high temperatures as their diffusion inside the donor leads to phase separation via Ostwald ripening. Here it is reported that fullerene diffusion is fully suppressed at temperatures up to 140 degrees C in bulk heterojunctions based on the benzodithiophene-based polymer (the poly[[4,8-bis[(2-ethylhexyl)oxy]benzo[1,2-b: 4,5-b']dithiophene-2,6-diyl][3-fluoro-2-[(2-ethylhexyl) carbonyl]thieno[3,4-b]thiophenediyl]], (PTB7) in combination with the fullerene derivative [6,6]-phenyl-C71-butyric acid methyl ester (PC70BM). The blend stability is found independently of the presence of diiodooctane (DIO) used to optimize nanostructuration and in contrast to PTB7 blends using the smaller fullerene derivative PC70BM. The unprecedented thermal stability of PTB7: PC70BM layers is addressed to local minima in the mixing enthalpy of the blend forming stable phases that inhibit fullerene diffusion. Importantly, although the nanoscale morphology of DIO processed blends is thermally stable, corresponding devices show strong performance losses under thermal stress. Only by the use of a high temperature annealing step removing residual DIO from the device, remarkably stable high efficiency solar cells with performance losses less than 10% after a continuous annealing at 140 degrees C over 3 days are obtained. These results pave the way toward high temperature stable polymer solar cells using fullerene acceptors.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.721
Times cited: 27
DOI: 10.1002/AENM.201601486
|
|
|
“The role of the electrode surface in Na-Air batteries : insights in electrochemical product formation and chemical growth of NaO2”. Lutz L, Corte DAD, Chen Y, Batuk D, Johnson LR, Abakumov A, Yate L, Azaceta E, Bruce PG, Tarascon J-M, Grimaud A, Advanced energy materials 8, 1701581 (2018). http://doi.org/10.1002/AENM.201701581
Abstract: The Na-air battery, because of its high energy density and low charging overpotential, is a promising candidate for low-cost energy storage, hence leading to intensive research. However, to achieve such a battery, the role of the positive electrode material in the discharge process must be understood. This issue is herein addressed by exploring the electrochemical reduction of oxygen, as well as the chemical formation and precipitation of NaO2 using different electrodes. Whereas a minor influence of the electrode surface is demonstrated on the electrochemical formation of NaO2, a strong dependence of the subsequent chemical precipitation of NaO2 is identified. In the origin, this effect stems from the surface energy and O-2/O-2(-) affinity of the electrode. The strong interaction of Au with O-2/O-2(-) increases the nucleation rate and leads to an altered growth process when compared to C surfaces. Consequently, thin (3 mu m) flakes of NaO2 are found on Au, whereas on C large cubes (10 mu m) of NaO2 are formed. This has significant impact on the cell performance and leads to four times higher capacity when C electrodes with low surface energy and O-2/O-2(-) affinity are used. It is hoped that these findings will enable the design of new positive electrode materials with optimized surfaces.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.721
Times cited: 13
DOI: 10.1002/AENM.201701581
|
|
|
“Carbon Incorporation and Anion Dynamics as Synergistic Drivers for Ultrafast Diffusion in Superionic LiCB11H12 and NaCB11H12”. Dimitrievska M, Shea P, Kweon KE, Bercx M, Varley JB, Tang WS, Skripov AV, Stavila V, Udovic TJ, Wood BC, Advanced energy materials 8, 1703422 (2018). http://doi.org/10.1002/AENM.201703422
Abstract: The disordered phases of LiCB11H12 and NaCB11H12 possess superb superionic conductivities that make them suitable as solid electrolytes. In these materials, cation diffusion correlates with high orientational mobilities of the CB11H12- anions; however, the precise relationship has yet to be demonstrated. In this work, ab initio molecular dynamics and quasielastic neutron scattering are combined to probe anion reorientations and their mechanistic connection to cation mobility over a range of timescales and temperatures. It is found that anions do not rotate freely, but rather transition rapidly between orientations defined by the cation sublattice symmetry. The symmetry-breaking carbon atom in CB11H12- also plays a critical role by perturbing the energy landscape along the instantaneous orientation of the anion dipole, which couples fluctuations in the cation probability density directly to the anion motion. Anion reorientation rates exceed 3 x 10(10) s(-1), suggesting the underlying energy landscape fluctuates dynamically on diffusion-relevant timescales. Furthermore, carbon is found to modify the orientational preferences of the anions and aid rotational mobility, creating additional symmetry incompatibilities that inhibit ordering. The results suggest that synergy between the anion reorientational dynamics and the carbon-modified cation-anion interaction accounts for the higher ionic conductivity in CB11H12- salts compared with B12H122-.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.721
Times cited: 20
DOI: 10.1002/AENM.201703422
|
|
|
“Hybrid YBa2Cu3O7 superconducting-ferromagnetic nanocomposite thin films prepared from colloidal chemical solutions”. Bartolome E, Cayado P, Solano E, Mocuta C, Ricart S, Mundet B, Coll M, Gazquez J, Meledin A, Van Tendeloo G, Valvidares SM, Herrero-Martin J, Gargiani P, Pellegrin E, Magen C, Puig T, Obradors X, Advanced Electronic Materials 3, 1700037 (2017). http://doi.org/10.1002/AELM.201700037
Abstract: High T-c superconductor-ferromagnetic heterostructures constitute an appealing playground to study the interplay between flux vortices and magnetic moments. Here, the capability of a solution-derived route to grow hybrid YBa2Cu3O7-ferromagnetic nanocomposite epitaxial thin films from preformed spinel ferrite (MFe2O4, M = Mn, Co) nanoparticles (NPs) is explored. The characterization, performed using a combination of structural and magnetic techniques, reveals the complexity of the resulting nanocomposites. Results show that during the YBCO growth process, most of the NPs evolve to ferromagnetic double-perovskite (DP) phases (YBaCu2-x-yFexCoyO5/YBaCoFeO5), while a residual fraction of preformed ferrite NPs may remain in the YBCO matrix. Magnetometry cycles reflect the presence of ferromagnetic structures associated to the DPs embedded in the superconducting films. In addition, a superparamagnetic signal that may be associated with a diluted system of ferromagnetic clusters around complex defects has been detected, as previously observed in standard YBCO films and nanocomposites. The hybrid nanocomposites described in this work will allow studying several fundamental issues like the nucleation of superconductivity and the mechanisms of magnetic vortex pinning in superconducting/ferromagnetic heterostructures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.193
Times cited: 7
DOI: 10.1002/AELM.201700037
|
|
|
“Resistive switching in Ag₂Te semiconductor modulated by Ag+-ion diffusion and phase transition”. Guo A, Bai H, Liang Q, Feng L, Su X, Van Tendeloo G, Wu J, Advanced Electronic Materials , 2200850 (2022). http://doi.org/10.1002/AELM.202200850
Abstract: Memristors are considered to be the fourth circuit element and have great potential in areas like logic operations, information storage, and neuromorphic computing. The functional material in a memristor, which has a nonlinear resistance, is the key component to be developed. Herein, resistive switching is demonstrated and the structural evolutions in Ag2Te are examined under an external electric field. It is shown that the electroresistance effect is originating from an electronically triggered phase transition together with directional Ag+-ion diffusion. Using in situ transmission electron microscopy, the phase transition from the monoclinic alpha-Ag2Te into the face-centered cubic beta-Ag2Te, accompanied by a change in resistance, is directly observed. Diffusion of Ag+-ions modulates the localized density of Ag+-ion vacancies, leading to a change in electrical conductivity and influences the threshold voltage to trigger the phase transition. During the electric field-driven phase transition, the spontaneous and localized multiple polarizations from the low-symmetry alpha-Ag2Te (referring to an antiferroelectric structure) are vanishing in the cubic beta-Ag2Te (referring to a paraelectric structure). The abrupt resistance change of thin Ag2Te caused by the phase transition and modulated by the applied electric field demonstrates its great potential as functional material in volatile memory and memristors with a low-energy consumption.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.2
DOI: 10.1002/AELM.202200850
|
|
|
“Synthesis and characterisation of lanthanide-based dioxide”. Esquivel MR, Zelaya E, Advances in applied ceramics 110, 219 (2011). http://doi.org/10.1179/1743676110Y.0000000021
Abstract: In the present work, the microstructure and structure of La(0.25)Ce(0.52)Nd(0.17)Pr(0.06)(OH)(3) and La(0.25)Ce(0.52)Nd(0.17)Pr(0.06)O(2) is obtained from transmission electron microscopy and X-ray diffraction measurements. Space group P6(3)/m is assigned to the structure of La(0.25)Ce(0.52)Nd(0.17)Pr(0.06)(OH)(3). Lanthanides are assigned to Wyckoff positions 2c. Cell parameters are a=6.375(5) angstrom and c=3.753(5) angstrom. The thermal decomposition of this compound was studied by differential scanning calorimetry. The process is exothermal with an enthalpy change Delta H degrees value of -254 +/- 10 kJ mol(-1). The decomposition kinetics is complex and two global processes with E(a) values of 98 +/- 4 and 61 +/- 2 kJ mol 21 were observed. The product is a lanthanide dioxide. Space group Fm3m is assigned to the La(0.25)Ce(0.52)Nd(0.17)Pr(0.06)O(2). Lanthanides are distributed in Wyckoff positions 4a. The cell parameter is a=5.479(5) angstrom. Nanopores in the oxide surface are obtained using this method and characterised by STEM measurements.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.325
Times cited: 3
DOI: 10.1179/1743676110Y.0000000021
|
|
|
“Electron microscopy and X-ray structural investigations of incommensurate spin-ladder Sr4.1Ca4.7Bi0.3Cu17O29 single crystals”. Dluzewski P, Pietraszko A, Kozlowski M, Szczepanska A, Gorecka J, Baran M, Leonyuk L, Babonas GJ, Lebedev OI, Szymczak R, Acta physica Polonica: A: general physics, solid state physics, applied physics 98, 729 (2000)
Abstract: Transmission electron microscopy and X-ray diffraction proved chain/ladder incommensurate single crystal structure of investigated samples. The incommensurate ratio was determined from the X-ray and electron diffraction being equal to 0.704. Diffuse scattering intensities localised on the planes perpendicular to the c*-axis and passing through the spots originating from the periodicity of chain sublattice were detected. High-angle grain boundary or twinning formed by rotation of 33.3 degrees around [100] direction was observed. High-resolution electron microscopy images revealed the stacking faults in ac planes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.469
|
|
|
“Structural analysis of CuInSe2, CuInTe2 and CuInSeTe by electron microscopy and X-ray techniques”. Leon M, Merino JM, Van Tendeloo G, Acta Microscopica 18, 128 (2009)
Abstract: A structural research of semiconductor compounds for photovoltaic applications CuInSe(2), CuInTe(2) and CuInSeTe, has been done by x-ray diffraction using the Rietveld analysis of experimental diagrams. Besides, in the CuInSeTe compound the electron diffraction and high resolution microscopy techniques have been used. All the studied compounds were polycrystals with chalcopyrite tetragonal structure, I. 42d. A model for the atomic occupancy in each compound has been proposed, and the results have been compared analyzing the Se-Te substitution effect.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.07
|
|
|
“The effect of microstructure and film composition on the mechanical properties of linear antenna CVD diamond thin films”. Mary Joy R, Pobedinskas P, Baule N, Bai S, Jannis D, Gauquelin N, Pinault-Thaury M-A, Jomard F, Sankaran KJ, Rouzbahani R, Lloret F, Desta D, D’Haen J, Verbeeck J, Becker MF, Haenen K, Acta materialia 264, 119548 (2024). http://doi.org/10.1016/j.actamat.2023.119548
Abstract: This study reports the impact of film microstructure and composition on the Young’s modulus and residual stress in nanocrystalline diamond (NCD) thin films ( thick) grown on silicon substrates using a linear antenna microwave plasma-enhanced chemical vapor deposition (CVD) system. Combining laser acoustic wave spectroscopy to determine the elastic properties with simple wafer curvature measurements, a straightforward method to determine the intrinsic stress in NCD films is presented. Two deposition parameters are varied: (1) the substrate temperature from 400 °C to 900 °C, and (2) the [P]/[C] ratio from 0 ppm to 8090 ppm in the H2/CH4/CO2/PH3 diamond CVD plasma. The introduction of PH3 induces a transition in the morphology of the diamond film, shifting from NCD with larger grains to ultra-NCD with a smaller grain size, concurrently resulting in a decrease in Young’s modulus. Results show that the highest Young’s modulus of (113050) GPa for the undoped NCD deposited at 800 °C is comparable to single crystal diamond, indicating that NCD with excellent mechanical properties is achievable with our process for thin diamond films. Based on the film stress results, we propose the origins of tensile intrinsic stress in the diamond films. In NCD, the tensile intrinsic stress is attributed to larger grain size, while in ultra-NCD films the tensile intrinsic stress is due to grain boundaries and impurities.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.4
DOI: 10.1016/j.actamat.2023.119548
|
|
|
“Characterization of NbC and (Nb, Ti)N nanoprecipitates in TRIP assisted multiphase steels”. Tirumalasetty GK, van Huis MA, Fang CM, Xu Q, Tichelaar FD, Hanlon DN, Sietsma J, Zandbergen HW, Acta materialia 59, 7406 (2011). http://doi.org/10.1016/j.actamat.2011.08.012
Abstract: Multiphase steels utilising composite strengthening may be further strengthened via grain refinement or precipitation by the addition of microalloying elements. In this study a Nb microalloyed steel comprising martensite, bainite and retained austenite has been studied. By means of transmission electron microscopy (TEM) we have investigated the size distribution and the structural properties of (Nb, Ti)N and NbC precipitates, their occurrence in the various steel phases, and their relationship with the Fe matrix. (Nb, Ti)N precipitates were found in ferrite, martensite, and bainite, while NbC precipitates were found only in ferrite. All NbC precipitates were found to be small (520 nm in size) and to have a face centred cubic (fcc) crystal structure with lattice parameter a = 4.36 ± 0.05 Å. In contrast, the (Nb, Ti)N precipitates were found to have a broader size range (5150 nm) and to have a fcc crystal structure with lattice parameter a = 8.09 ± 0.05 Å. While the NbC precipitates were found to be randomly oriented, the (Nb, Ti)N precipitates have a well-defined NishiyamaWasserman orientation relationship with the ferrite matrix. An analysis of the lattice mismatch suggests that the latter precipitates have a high potential for effective strengthening. Density functional theory calculations were performed for various stoichiometries of NbCx and NbxTiyNz phases and the comparison with experimental data indicates that both the carbides and nitrides are deficient in C and N content.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 58
DOI: 10.1016/j.actamat.2011.08.012
|
|
|
“Deformation-induced austenite grain rotation and transformation in TRIP-assisted steel”. Tirumalasetty GK, van Huis MA, Kwakernaak C, Sietsma J, Sloof WG, Zandbergen HW, Acta materialia 60, 1311 (2012). http://doi.org/10.1016/j.actamat.2011.11.026
Abstract: Uniaxial straining experiments were performed on a rolled and annealed Si-alloyed TRIP (transformation-induced plasticity) steel sheet in order to assess the role of its microstructure on the mechanical stability of austenite grains with respect to martensitic transformation. The transformation behavior of individual metastable austenite grains was studied both at the surface and inside the bulk of the material using electron back-scattered diffraction (EBSD) and X-ray diffraction (XRD) by deforming the samples to different strain levels up to about 20%. A comparison of the XRD and EBSD results revealed that the retained austenite grains at the surface have a stronger tendency to transform than the austenite grains in the bulk of the material. The deformation-induced changes of individual austenite grains before and after straining were monitored with EBSD. Three different types of austenite grains can be distinguished that have different transformation behaviors: austenite grains at the grain boundaries between ferrite grains, twinned austenite grains, and embedded austenite grains that are completely surrounded by a single ferrite grain. It was found that twinned austenite grains and the austenite grains present at the grain boundaries between larger ferrite grains typically transform first, i.e. are less stable, in contrast to austenite grains that are completely embedded in a larger ferrite grain. In the latter case, straining leads to rotations of the harder austenite grain within the softer ferrite matrix before the austenite transforms into martensite. The analysis suggests that austenite grain rotation behavior is also a significant factor contributing to enhancement of the ductility. (C) 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 80
DOI: 10.1016/j.actamat.2011.11.026
|
|
|
“Effect of nanoprecipitates on the transformation behavior and functional properties of a Ti50.8 at.% Ni alloy with micron-sized grains”. Wang X, Kustov S, Li K, Schryvers D, Verlinden B, Van Humbeeck J, Acta materialia 82, 224 (2015). http://doi.org/10.1016/j.actamat.2014.09.018
Abstract: In order to take advantage of both grain refinement and precipitation hardening effects, nanoscaled Ni4Ti3 precipitates are introduced in a Ti50.8 at.% Ni alloy with micron-sized grains (average grain size of 1.7 μm). Calorimetry, electrical resistance studies and thermomechanical tests were employed to study the transformation behavior and functional properties in relation to the obtained microstructure. A significant suppression of martensite transformation by the obtained microstructure is observed. The thermomechanical tests show that the advantageous properties of both grain refinement and precipitation hardening are combined in the developed materials, resulting in superior shape memory characteristics and stability of pseudoelasticity. It is concluded that introducing nanoscaled Ni4Ti3 precipitates into small grains is a new approach to improve the functional properties of NiTi shape memory alloys.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 51
DOI: 10.1016/j.actamat.2014.09.018
|
|
|
“Electron energy-loss spectroscopy and first-principles calculation studies on a Ni-Ti shape memory alloy”. Yang Z, Tirry W, Lamoen D, Kulkova S, Schryvers D, Acta materialia 56, 395 (2008). http://doi.org/10.1016/j.actamat.2007.10.001
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 20
DOI: 10.1016/j.actamat.2007.10.001
|
|