Abstract: Oxygen deficient perovskites Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75, were prepared by using the citrate route at 1373-1573 K for 48 h. The cubic Pm-3m perovskite structure for x=0.5 was confirmed by electron diffraction study and refined using neutron powder diffraction (NPD) data. For x=0.75, the superstructure corresponding to a=root 2 x a(per), b=2 x a(per), c=root 2 x a(per) (a(0)b(-)b(-) tilt system, space group Imma) was revealed by electron diffraction. The solid solution Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= x <= 0.6 and compound Ca0.75Y0.25Mn0.85Co0.15O2.92 were prepared in air at 1573 K for 48 h. The crystal structure of Ca0.75Y0.25Mn0.85Co0.15O2.92 was refined using NPD data (S.G. Pnma, a=5.36595(4), b=7.5091(6), c=5.2992(4) angstrom, R-p=0.057, R-wp=0.056, chi(2)=4.26). High-temperature thermal expansion properties of the prepared compounds were studied in air using both dilatometry and high-temperature X-ray powder diffraction data (HTXRPD). They expanding non-linearly at 298-1073 K due to the loss of oxygen at high temperatures. Calculated average thermal expansion coefficients (TECs) for Sr0.75Y0.25Co1-xMnxO3-y, x=0.5, 0.75 and Ca0.75Y0.25Mn0.85Co0.15O2.92(1) are 15.5, 15.1, and 13.8 ppm K-1, respectively. Anisotropy of the thermal expansion along different unit cell axes was observed for Sr0.15Ca0.6Y0.25Co0.25Mn0.75O3-y, and Ca0.75Y0.25Mn0.85Co0.15O2.92. Conductivity of Sr0.75Y0.25Co1-xMnxO3-y, x=0.5 and 0.75 increases with the temperature reaching 110 S/cm for x=0.5 and 44 S/cm for x=0.75 at 1173 K. Samples of Sr0.75-xCaxY0.25Co0.25Mn0.75O3-y, 0.1 <= y <= 0.6 were found to be n-type conductors at room temperature with the similar temperature dependence of the conductivity and demonstrated the increase of the sigma value from similar to 1 to similar to 50 S/cm as the temperature increases from 300 to 1173 K. Their conductivity is described in terms of the small polaron charge transport with the activation energy (E-p) increasing from 340 to 430 meV with an increase of the calcium content from x=0 to x=0.6. (C) 2012 Elsevier Inc. All rights reserved.

Abstract: LiNaCo 0.5 Fe 0.5 PO 4 F fluoride-phosphate was synthesized via conventional solid-state and novel freeze-drying routes. The crystal structure was refined based on neutron powder diffraction (NPD) data and validated by electron diffraction (ED) and high-resolution transmission electron microscopy (HRTEM). The alkali ions are ordered in LiNaCo 0.5 Fe 0.5 PO 4 F and the transition metals jointly occupy the same crystallographic sites. The oxidation state and oxygen coordination environment of the Fe atoms were verified by 57 Fe Mössbauer spectroscopy. Electrochemical tests of the LiNaCo 0.5 Fe 0.5 PO 4 F cathode material demonstrated a reversible activity of the Fe 3+ /Fe 2+ redox couple at the electrode potential near 3.4 V and minor activity of the Co 3+ /Co 2+ redox couple over 5 V vs Li/Li + . The material exhibits a good capacity retention in the 2.4÷4.6 V vs Li/Li + potential range with the delivered discharge capacity of more than 82% (theo.) regarding Fe 3+ /Fe 2+ .

Abstract: Pb2Ba2BiFe4ScO13, a new n = 5 member of the oxygen-deficient perovskite-based A(n)B(n)O(3n-2) homologous series, was synthesized using a solid-state method. The crystal structure of Pb2Ba2BiFe4ScO13 was investigated by a combination of synchrotron X-ray powder diffraction, electron diffraction, high-angle annular dark-field scanning transmission electron microscopy and Mossbauer spectroscopy. At 900 K, it crystallizes in the Ammm space group with the unit cell parameters a = 5.8459(1) angstrom, b = 4.0426(1) angstrom, and c=27.3435(1) angstrom. In the Pb2Ba2BiFe4ScO13 structure, quasi-two-dimensional perovskite blocks are periodically interleaved with 1/2[1 1 0] ((1) over bar 0 1)(p) crystallographic shear (CS) planes. At the CS planes, the corner-sharing FeO6 octahedra are transformed into chains of edge-sharing FeO5 distorted tetragonal pyramids. B-positions of the perovskite blocks between the CS planes are jointly occupied by Fe3+ and Sc3+. The chains of the FeO5 pyramids and (Fe,Sc)O-6 octahedra delimit six-sided tunnels that are occupied by double columns of cations with a lone electron pair (Pb2+). The remaining A-cations (Bi3+, Ba2+) occupy positions in the perovskite block. According to the magnetic susceptibility measurements, Pb2Ba2BiFe4ScO13 is antiferromagnetically ordered below T-N approximate to 350 K. (C) 2013 Elsevier Ltd. All rights reserved.