Abstract: The structural and transport properties of YBa2Cu3O7−x films grown by pulsed laser deposition with mixed 2.5 mol% Ba2YTaO6 (BYTO) and 2.5 mol% Ba2YNbO6 (BYNO) double-perovskite secondary phases are investigated in an extended film growth rate, R = 0.02–1.8 nm s−1. The effect of R on the film microstructure analyzed by TEM techniques shows an evolution from sparse and straight to denser, thinner and splayed continuous columns, with mixed BYNO + BYTO (BYNTO) composition, as R increases from 0.02 nm s−1 to 1.2 nm s−1. This microstructure results in very efficient flux pinning at 77 K, leading to a remarkable improvement in the critical current density (J c) behaviour, with the maximum pinning force density F p(Max) = 13.5 GN m−3 and the irreversibility field in excess of 11 T. In this range, the magnetic field values at which the F p is maximized varies from 1 T to 5 T, being related to the BYNTO columnar density. The film deposited when R = 0.3 nm s−1 exhibits the best performances over the whole temperature and magnetic field ranges, achieving F p(Max) = 900 GN m−3 at 10 K and 12 T. At higher rates, R > 1.2 nm s−1, BYNTO columns show a meandering nature and are prone to form short nanorods. In addition, in the YBCO film matrix a more disordered structure with a high density of short stacking faults is observed. From the analysis of the F p(H, T) curves it emerges that in films deposited at the high R limit, the vortex pinning is no longer dominated by BYNTO columnar defects, but by a new mechanism showing the typical temperature scaling law. Even though this microstructure produces a limited improvement at 77 K, it exhibits a strong J c improvement at lower temperature with F p = 700 GN m−3 at 10 K, 12 T and 900 GN m−3 at 4.2 K, 18 T.

Abstract: When strained in tension, high-manganese austenitic twinning induced plasticity (TWIP) steels achieve very high strength and elongation before necking. The main hypotheses available in the literature about the origin of their excellent work hardening include deformation twinning and dynamic strain ageing. In order to provide some answers, various experiments at different scales were conducted on FeMnC steels and the Fe28 wt%Mn3.5 wt%Al2.8 wt%Si alloy. At a macroscopic scale, tensile tests were performed on all the studied grades. It was shown that, though the FeMnAlSi based alloy retains very high elongation, the FeMnC steels properties are even more extraordinary. Tensile tests at different strain rates with the help of digital image correlation were also performed on the Fe20 wt%Mn1.2 wt%C steel to study the PLC effect occurring in this type of steel. It is suggested that supplementary hardening could come from reorientation of MnC pairs in the cores of the dislocations. At a microscopic scale, the Fe20 wt%Mn1.2 wt%C TWIP steel and the FeMnAlSi grade were thoroughly investigated by means of in situ TEM analysis. In the FeMnC steel, the formed twins could also lead to a composite effect, since they contain plenty of sessile dislocations. In the FeMnAlSi alloy, mechanical twins are thicker and contain fewer defects, leading to a lower work hardening than the other grade.

Abstract: This paper aims to give an overview of the technique of energy-filtered transmission electron microscopy (EFTEM). It explains the basic principles of the technique and points to the relevant literature for more detailed issues. Experimental examples are given to show the power of EFTEM to study the chemical composition of nanoscale samples in materials science. Advanced EFTEM applications like imaging spectroscopy and EFTEM tomography are briefly discussed. (C) 2004 Elsevier B.V. All rights reserved.

Abstract: A LuFe2O4+delta sample, previously characterized by X-ray synchrotron and neutron diffraction, has been studied by electron microscopy techniques, in order to get a precise description of its micro- and nanostructures at room temperature. The X-ray synchrotron data vs. temperature show that the monoclinic distortion is associated with the charge ordering; this distortion results in elongated twinning domains, which enhance the complexity of the microstructural state at room temperature. The structural modulation associated with oxygen excess is observed in large domains inside a non modulated matrix, in contrast with the modulations associated with the charge ordering of the Fe2+ and Fe3+ species, which are mostly short-range. The investigation of the nature and density of defects in the sample shows that they are nano-scaled, preserving the regularity of the layer stacking mode, and limited to the formation of one- or two-units large stacking faults, associated with gliding mechanisms. Based on these observations, an original description of the LuFe2O4 ferrite structure, through puckered [LuO4](infinity) sandwiching [Fe-2](infinity) layers, is proposed. (C) 2013 Elsevier Masson SAS. All rights reserved.

Abstract: The Fe2(Sr2 − xAx)FeO6.5 − ä/2 systems have been investigated, by doping the iron rich 2201-type parent structure with Ba2+, La3+ and 5d10 post-transition cations. The syntheses have been carried out up to the limit of the 2201-type solid solutions, in order to test the role of the double iron layer Fe2O2.5 − ä/2. The localisation of the charge carriers in these compounds is consistent with their strong antiferro-magnetism. The investigation was then carried out in the transition part of the diagram up to the formation of stable phases. The study of structural mechanisms was carried using high resolution electron microscopy (transmission and scanning transmission), electron diffraction and energy dispersive spectroscopy. Different non-stoichiometry mechanisms are observed, depending on the electronic structure and chemical properties of the doping elements. The specific behavior of the modulated double iron layer is discussed.

Abstract: The influence of the amount of catalyst and the reaction time on the quantity and quality of catalytically grown single wall carbon nanotubes (SWNT) was investigated. The aim was to optimize some of the SWNT growth parameters using TEM and HRTEM. The thickness of catalyst layer influences the synthesis of the nanotube because the gas composition can differ between top and bottom. Microscopic investigation of the grown SWNT samples showed that the thicker the catalyst layer the lower relative nanotube content, so the deeper parts of the catalyst layer are less effective: The optimum time for the reaction was found to be 10 minutes. This may be understood assuming that nanotube growth needs an initial incubation time while the activity of the catalyst decreases steadily until the nariotube growth stops.

Abstract: Oxygen-deficient complex cobalt oxides BaCo1 − xYxO3 − y, = 0.15, 0.25 and 0.33, with a cubic perovskite structure have been synthesized in air at 1100 °C using a citrate route. Cation composition of the compounds was confirmed by energy-dispersed X-ray (EDX) microanalysis while oxygen content was determined by iodometric titration. An electron diffraction (ED) study of the x = 0.25 and 0.33 compositions show the presence of a diffuse intensity, indicating possible short-range ordering of the B cations. It was found that the treatment of BaCo0.75Y0.25O2.55 in a humid atmosphere leads to the absorption of water vapour at the first stage. Oxygen permeation studies of the ceramic membranes of BaCo0.75Y0.25O2.55 and BaCo0.67Y0.33O2.55 with variable thickness showed high oxygen fluxes of 0.170.32 µmol/cm2/s at 950 °C.