“Rational synthesis of a nanocrystalline calcium phosphate cement exhibiting rapid conversion to hydroxyapatite”. Neira IS, Kolen'ko YV, Lebedev OI, Van Tendeloo G, Gupta HS, Matsushita N, Yoshimura M, Guitian F, Materials science and engineering: part C: biomimetic materials 29, 2124 (2009). http://doi.org/10.1016/j.msec.2009.04.011
Abstract: The rational synthesis, comprehensive characterization, and mechanical and micromechanical properties of a calcium phosphate cement are presented. Hydroxyapatite cement biomaterial was synthesized from reactive sub-micrometer-sized dicalcium phosphate dihydrate and tetracalcium phosphate via a dissolution-precipitation reaction using water as the liquid phase. As a result nanostructured, Ca-deficient and carbonated B-type hydroxyapatite is formed. The cement shows good processibility, sets in 22 ± 2 min and entirely transforms to the end product after 6 h of setting reaction, one of the highest conversion rates among previously reported for calcium phosphate cements based on dicalcium and tetracalcium phosphates. The combination of all elucidated physical-chemical traits leads to an essential bioactivity and biocompatibility of the cement, as revealed by in vitro acellular simulated body fluid and cell culture studies. The compressive strength of the produced cement biomaterial was established to be 25 ± 3 MPa. Furthermore, nanoindentation tests were performed directly on the cement to probe its local elasticity and plasticity at sub-micrometer/micrometer level. The measured elastic modulus and hardness were established to be Es = 23 ± 3.5 and H = 0.7 ± 0.2 GPa, respectively. These values are in close agreement with those reported in literature for trabecular and cortical bones, reflecting good elastic and plastic coherence between synthesized cement biomaterial and human bones.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.164
Times cited: 18
DOI: 10.1016/j.msec.2009.04.011
|
“Strong attachment of circadian pacemaker neurons on modified ultrananocrystalline diamond surfaces”. Voss A, Wei HY, Zhang Y, Turner S, Ceccone G, Reithmaier JP, Stengl M, Popov C, Materials science and engineering: part C: biomimetic materials 64, 278 (2016). http://doi.org/10.1016/j.msec.2016.03.092
Abstract: Diamond is a promising material for a number of bio-applications, including the fabrication of platforms for attachment and investigation of neurons and of neuroprostheses, such as retinal implants. In the current work ultrananocrystalline diamond (UNCD) films were deposited by microwave plasma chemical vapor deposition, modified by UV/O-3 treatment or NH3 plasma, and comprehensively characterized with respect to their bulk and surface properties, such as crystallinity, topography, composition and chemical bonding nature. The interactions of insect circadian pacemaker neurons with UNCD surfaces with H-, O- and NH2-terminations were investigated with respect to cell density and viability. The fast and strong attachment achieved without application of adhesion proteins allowed for advantageous modification of dispersion protocols for the preparation of primary cell cultures. Centrifugation steps, which are employed for pelletizing dispersed cells to separate them from dispersing enzymes, easily damage neurons. Now centrifugation can be avoided since dispersed neurons quickly and strongly attach to the UNCD surfaces. Enzyme solutions can be easily washed off without losing many of the dispersed cells. No adverse effects on the cell viability and physiological responses were observed as revealed by calcium imaging. Furthermore, the enhanced attachment of the neurons, especially on the modified UNCD surfaces, was especially advantageous for the immunocytochemical procedures with the cell cultures. The cell losses during washing steps were significantly reduced by one order of magnitude in comparison to controls. In addition, the integration of a titanium grid structure under the UNCD films allowed for individual assignment of physiologically characterized neurons to immunocytochemically stained cells. Thus, employing UNCD surfaces free of foreign proteins improves cell culture protocols and immunocytochemistry with cultured cells. The fast and strong attachment of neurons was attributed to a favorable combination of topography, surface chemistry and wettability. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.164
Times cited: 7
DOI: 10.1016/j.msec.2016.03.092
|
“Applications of advanced transmission electron microscopic techniques to Ni-Ti based shape memory materials”. Schryvers D, Potapov P, Santamarta R, Tirry W, Materials science and engineering: part A: structural materials: properties, microstructure and processing 378, 11 (2004). http://doi.org/10.1016/j.msea.2003.10.325
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 6
DOI: 10.1016/j.msea.2003.10.325
|
“Au particles supported on (110) anatase-TiO2”. Giorgio S, Henry CR, Pauwels B, Van Tendeloo G, Microstructure And Processing 297, 197 (2001). http://doi.org/10.1016/S0921-5093(00)01261-2
Abstract: Au particles were prepared by evaporation in ultra high vacuum at high temperature, on the surfaces of TiO2 micro-spheres with the anatase structure. The morphology and the structural deformation in Au deposits were studied by high resolution transmission electron microscopy and image simulations by the multislice technique. The particles were polyhedral, limited by (100) and (111) faces. Patches with a hexagonal lattice were found around the particles, which was interpreted as thin Au islands on the surface. In these islands the Au lattice was deformed and perfectly accommodated to the (110) surface of TiO2. (C) 2001 Elsevier Science B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 40
DOI: 10.1016/S0921-5093(00)01261-2
|
“Effect of annealing on cold-rolled Ni-Ti alloys”. Srivastava AK, Yang Z, Schryvers D, van Hurnbeeck J, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 594 (2008). http://doi.org/10.1016/j.msea.2006.12.216
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 8
DOI: 10.1016/j.msea.2006.12.216
|
“Electron energy-loss spectroscopy study of NiTi shape memory alloys”. Yang ZQ, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 214 (2008). http://doi.org/10.1016/j.msea.2006.12.227
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 7
DOI: 10.1016/j.msea.2006.12.227
|
“Hardening in relation with microstructure evolution of high purity \alpha-titanium deformed under monotonic and cyclic simple shear loadings at room temperature”. Bouvier S, Benmhenni N, Tirry W, Gregory F, Nixon ME, Cazacu O, Rabet L, Materials science and engineering: part A: structural materials: properties, microstructure and processing 535, 12 (2012). http://doi.org/10.1016/j.msea.2011.12.033
Abstract: The aim of this paper is to gain understanding of the quasi-static, large strain deformation behavior at room-temperature of high-purity alpha-Ti with an initial split-basal texture. Simple shear tests were conducted along different directions in order to quantify the material's anisotropy and hardening evolution for different strain paths such as monotonic, Bauschinger, and cyclic loadings. The stress-strain curves indicate that the material displays strong anisotropy in the flow behavior. In order to capture the link between microstructure evolution (occurrence of twinning, grain size evolution, etc.) and the macroscopic response, a thoroughly detailed multi-scale characterization using scanning electron microscope (SEM) observations and electron backscattered diffraction (EBSD) analysis was also conducted. Specifically, EBSD analyses indicate that the twin activity and grain fragmentation are responsible for the observed difference between the macroscopic hardening rates corresponding to different directions and loading paths. (C) 2011 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 22
DOI: 10.1016/j.msea.2011.12.033
|
“High resolution TEM study of Ni4Ti3 precipitates in austenitic Ni51Ti49”. Tirry W, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 378, 157 (2004). http://doi.org/10.1016/j.msea.2003.10.336
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 19
DOI: 10.1016/j.msea.2003.10.336
|
“Importance of twinning in static and dynamic compression of a Ti-6Al-4V titanium alloy with an equiaxed microstructure”. Coghe F, Tirry W, Rabet L, Schryvers D, Van Houtte P, Materials science and engineering: part A: structural materials: properties, microstructure and processing 537, 1 (2012). http://doi.org/10.1016/j.msea.2011.12.047
Abstract: Whereas deformation twinning is known to be an important deformation mechanism for hexagonal materials like magnesium and pure titanium, so far almost no literature exists on the twinning behaviour of the Ti-6Al-4V alloy. In this work it was shown that the activation of twinning as a deformation mechanism could have a pronounced effect on the mechanical behaviour of the Ti-6Al-4V alloy. This effect is even more pronounced under dynamic loading conditions. Transmission electron microscopy showed that only the {1 0 1 2}{1 0 1 1} tensile twin system was activated under certain loading conditions. Light-optical microscopy and electron backscatter diffraction data were afterwards used to experimentally determine the twin fractions. The importance of twinning for the texture evolution was also studied. It was shown that even small twin fractions can lead to distinct texture features, especially due to the discrete reorientation of the c-axes. The experimental results were compared to simulated results that were obtained with a viscoplastic self-consistent crystal plasticity code, after experimental validation that twinning can be reliably modelled as a unidirectional slip system. Although good agreement was obtained for the experimental and simulated stress-strain curves, the simulated results concerning twinning correlated well only on a qualitative basis as the simulated twin fractions were systematically higher than the experimental fractions. This seems to strengthen the hypothesis made by other research groups that complete grains might reorient by twinning. (C) 2011 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 35
DOI: 10.1016/j.msea.2011.12.047
|
“In situ transmission electron microscopy of stress-induced martensite with focus on martensite twinning”. Tirry W, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 420 (2008). http://doi.org/10.1016/j.msea.2006.12.214
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 22
DOI: 10.1016/j.msea.2006.12.214
|
“Martensitic transformations and microstructures in splat-cooled Ni-Al”. Schryvers D, Holland-Moritz D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 273/275, 697 (1999). http://doi.org/10.1016/S0921-5093(99)00399-8
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 6
DOI: 10.1016/S0921-5093(99)00399-8
|
“Measuring strain fields and concentration gradients around Ni4Ti3 precipitates”. Schryvers D, Tirry W, Yang ZQ;, Materials science and engineering A: structural materials properties microstructure and processing 438, 485 (2006). http://doi.org/10.1016/j.msea.2006.02.166
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 35
DOI: 10.1016/j.msea.2006.02.166
|
“A multi-scale characterization of deformation twins in Ti6Al4V sheet material deformed by simple shear”. Tirry W, Coghe F, Bouvier S, Gasperini M, Rabet L, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 527, 4136 (2010). http://doi.org/10.1016/j.msea.2010.03.039
Abstract: Ti6Al4V sheet material is subjected to simple shear deformation with strain ratio's of 10%, 30% and 50%. Optical microscopy, transmission electron microscopy and electron backscatter diffraction techniques are applied to study the presence and morphology of deformation twins. Only the View the MathML source type of twins seems to be present with a volume fraction below 1%. These View the MathML source twins show a high density of basal stacking faults of the ABABACAC type identified using atomic resolution transmission electron microscopy. A resolved shear stress analysis shows that twins most often occur on those planes with the highest resolved shear stresses, but that the starting texture is not beneficial for the occurrence of twins. It is further suggested that a transitory strain hardening regime observed around 530 MPa might be related with the onset of twinning.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 20
DOI: 10.1016/j.msea.2010.03.039
|
“New (3(3)under-bar) long-period microtwin variant in the martensitic phase of the PtTi alloy”. Rotaru G-M, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 437 (2008). http://doi.org/10.1016/j.msea.2006.12.201
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 3
DOI: 10.1016/j.msea.2006.12.201
|
“Quantitative determination of the crystal structure of Ni4Ti3 precipitates”. Tirry W, Schryvers D, Jorissen K, Lamoen D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 438, 517 (2006). http://doi.org/10.1016/j.msea.2006.02.063
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 7
DOI: 10.1016/j.msea.2006.02.063
|
“Structural aspects of AuCu I or AuCu II and a cuboidal black configuration of f.c.c. disordered phase in AuCu-Pt and AuCu-Ag pseudobinary alloys”. Udoh K-I, El- Araby AM, Tanaka Y, Hisatsune K, Yasuda K, Van Tendeloo G, van Landuyt J, Materials science and engineering: part A: structural materials: properties, microstructure and processing 203, 154 (1995). http://doi.org/10.1016/0921-5093(95)09850-X
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.567
Times cited: 15
DOI: 10.1016/0921-5093(95)09850-X
|
“Structure of multi-grain spherical particles in an amorphous Ti50Ni25Cu25 melt-spun ribbon”. Santamarta R, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 378, 143 (2004). http://doi.org/10.1016/j.msea.2003.11.060
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 5
DOI: 10.1016/j.msea.2003.11.060
|
“Clustering behavior during natural aging and artificial aging in Al-Mg-Si alloys with different Ag and Cu addition”. Weng Y, Jia Z, Ding L, Muraishi S, Liu Q, Microstructure And Processing 732, 273 (2018). http://doi.org/10.1016/J.MSEA.2018.07.018
Abstract: The effect of Ag and Cu addition on clustering behavior of Al-Mg-Si alloys during natural aging (NA) and artificial aging (AA) was investigated by hardness measurement, tensile test and atom probe tomography analysis. The results show that both Ag and Cu atoms could enter clusters and GP-zones, change the Mg/Si ratio and increase their volume fractions. Compared with the Al base alloy, the clusters in the Ag/Cu-added alloys more easily transform to beta" phases for size and compositional similarity, and the strengthening ability of these particles is enhanced by the increased volume fraction and shear modulus. In NA condition, Cu is greater in improving the volume fraction of clusters than Ag and thus produces higher T4 temper hardness. In AA condition, in contrary, Ag is more effective in facilitating the formation and growth of particles than Cu due to the stronger Ag-Mg interaction and the high diffusivity of Ag atoms in Al matrix, leading to highest hardening response. Compared to the Cu-added alloy, the Ag-added alloy shows higher precipitation kinetics during AA treatment and maintains a lower T4 temper hardness.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 11
DOI: 10.1016/J.MSEA.2018.07.018
|
“Enhancement of toughness of Al-to-steel Friction Melt Bonded welds via metallic interlayers”. Jimenez-Mena N, Jacques PJ, Ding L, Gauquelin N, Schryvers D, Idrissi H, Delannay F, Simar A, Materials science and engineering: part A: structural materials: properties, microstructure and processing 740-741, 274 (2019). http://doi.org/10.1016/j.msea.2018.10.101
Abstract: The toughness of Al-to-steel welds decreases with increasing thickness of the intermetallic (IM) layer formed at the interface. Co plating has been added as interlayer in Al-to-steel Friction Melt Bonded (FMB) welds to control the nature and thickness of the IM layer. In comparison to a weld without interlayer, Co plating brings about a reduction of the thickness of the IM layer by 70%. The critical energy release rate of the crack propagating in the weld is used as an indicator of toughness. It is evaluated via an adapted crack propagation test using an energy conservation criterion. For a weld without interlayer, critical energy release rate is found to increase when the thickness of the intermetallic layer decreases. When the intermetallic layer is thick, the crack propagates in a brittle manner through the intermetallic whereas, at low layer thickness, the crack deviates and partially propagates through the Al plate, which causes an increase of toughness. The use of a Co interlayer brings about an increase of toughness by causing full deviation of the crack towards the Al plate.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 4
DOI: 10.1016/j.msea.2018.10.101
|
“Dislocation structures and the role of grain boundaries in cyclically deformed Ni micropillars”. Samaee V, Sandfeld S, Idrissi H, Groten J, Pardoen T, Schwaiger R, Schryvers D, Materials Science And Engineering A-Structural Materials Properties Microstructure And Processing 769, 138295 (2020). http://doi.org/10.1016/j.msea.2019.138295
Abstract: Transmission electron microscopy and finite element-based dislocation simulations were combined to study the development of dislocation microstructures after cyclic deformation of single crystal and bicrystal Ni micropillars oriented for multi-slip. A direct correlation between large accumulation of plastic strain and the presence of dislocation cell walls in the single crystal micropillars was observed, while the presence of the grain boundary hampered the formation of wall-like structures in agreement with a smaller accumulated plastic strain. Automated crystallographic orientation and nanostrain mapping using transmission electron microscopy revealed the presence of lattice heterogeneities associated to the cell walls including long range elastic strain fields. By combining the nanostrain mapping with an inverse modelling approach, information about dislocation density, line orientation and Burgers vector direction was derived, which is not accessible otherwise in such dense dislocation structures. Simulations showed that the image forces associated with the grain boundary in this specific bicrystal configuration have only a minor influence on dislocation behavior. Thus, the reduced occurrence of “mature” cell walls in the bicrystal can be attributed to the available volume, which is too small to accommodate cell structures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.4
Times cited: 1
DOI: 10.1016/j.msea.2019.138295
|
“Damage mechanisms in selective laser melted AlSi10Mg under as built and different post-treatment conditions”. Zhao L, Macias JGS, Ding L, Idrissi H, Simar A, Microstructure And Processing 764, 138210 (2019). http://doi.org/10.1016/J.MSEA.2019.138210
Abstract: Selective laser melting (SLM) manufactured AlSi10Mg alloys present a fine silicon-rich network and precipitates which grant high mechanical strength but low ductility. Post-treatments, aiming at eliminating inherent defects related to SLM such as residual stresses, porosity or inhomogeneity, result in significant changes in the microstructure and impact both the hardening and the damage mechanisms of the post-treated material. The present work is dedicated to the investigation of the fracture of SLM AlSi10Mg under as built and three post-treatment conditions, namely two stress relieve heat treatments and friction stir processing (FSP). It is found that the interconnected Si network fosters damage at low strain due to the brittleness of the Si phase. The onset of damage transfers load to the enclosed Al phase which then fractures quickly under high stress, thus leading to low material ductility. In contrast, when the Si network is globularized into Si particles, the ductility is highly increased even in the case where the porosity and inhomogeneity of the microstructure remain after the post-treatment. The ductility enhancement results from the delay in void nucleation on the Si particles as well as from the tolerance for void growth in the Al matrix.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 1
DOI: 10.1016/J.MSEA.2019.138210
|
“Quantified contribution of β&Prime, and β&prime, precipitates to the strengthening of an aged Al–Mg–Si alloy”. Yang M, Chen H, Orekhov A, Lu Q, Lan X, Li K, Zhang S, Song M, Kong Y, Schryvers D, Du Y, Materials Science And Engineering A-Structural Materials Properties Microstructure And Processing 774, 138776 (2020). http://doi.org/10.1016/j.msea.2019.138776
Abstract: It is generally believed that β00 precipitates, rather than β0 precipitates, are the major strengthening precipitates in
aged Al–Mg–Si alloys. The reason for this difference is not well understood. To clarify this, two samples of the
same Al–Mg–Si alloy but with different aging states were prepared. The under-aged sample only contains nanoprecipitates
of the β00 type, while the peak-aged one contains nearly equal volumes of β00 and β0 precipitates. We
have, for the first time, separated the strengthening effect of the contribution from βʺ and βʹ precipitates,
respectively, by an indirect approach based on high-precision measurements of volume fractions, number densities,
sizes, proportions of the precipitates, their lattice strains, the composition and grain size of the matrix. The
β0 precipitates, which take 45.6% of the total precipitate volume in the peak-aged sample, contribute to the entire
precipitation strengthening by only 31.6%. The main reason why they are less useful compared to β00 precipitates
has been found to be associated with their smaller lattice strains relative to the matrix, which is 0.99% versus
2.10% (for β00 ).
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.4
DOI: 10.1016/j.msea.2019.138776
|
“Community structure and feeding preference of nematodes associated with methane seepage at the Darwin mud volcano (Gulf of Cádiz)”. Pape E, Bezerra TN, Vanneste H, Heeschen K, Moodley L, Leroux F, van Breugel P, Vanreusel A, Marine ecology progress series 438, 71 (2011). http://doi.org/10.3354/meps09278
Abstract: We sampled the Darwin mud volcano (MV) for meiofaunal community and trophic structure in relation to pore-water geochemistry along a 10 m transect from a seep site on the rim of the crater towards the MV slope. Pore-water profiles indicated considerable variation in upward methane (CH4) flow among sediment cores taken along the transect, with highest flux in the seep sediment core, gradually decreasing along the transect, to no CH4 flux in the core taken at a 5 m distance. Low sulphate concentrations and high levels of total alkalinity and sulphide (H2S) suggested that anaerobic oxidation of methane (AOM) occurred close to the sediment surface in the seep sediment core. High H2S levels had a genus- and species-specific impact on meiofaunal densities. Nematode genus composition varied gradually between sediment cores, with the genus Sabatieria dominating almost all sediment cores. However, genus diversity increased with increasing distance from the seep site. These limited data suggest that the community structure of seep meiofauna is highly dependent on local (a)biotic habitat characteristics, and a typical seep meiofaunal community cannot be delineated. Stable isotope values suggested the nematode diet up to 10 m from the seep site included thiotrophic carbon. The thicker hemipelagic sediment layer (photosynthetic carbon), the increased trophic diversity, and the heavier nematode δ13C farther from the seep site suggest a decrease in thiotrophy and an increase in photosynthetic carbon in the nematode diet.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.292
Times cited: 18
DOI: 10.3354/meps09278
|
“An electron microscopic study of highly oriented undoped and FeCl3-doped poly (p-phenylenevinylene)”. Zhang XB, Van Tendeloo G, van Landuyt J, van Dyck D, Briers J, Bao Y, Geise HJ, Macromolecules 29, 1554 (1996). http://doi.org/10.1021/ma9513067
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 5.8
Times cited: 10
DOI: 10.1021/ma9513067
|
“Glycogen as a biodegradable construction nanomaterial for in vivo use”. Filippov SK, Sedlacek O, Bogomolova A, Vetrik M, Jirak D, Kovar J, Kucka J, Bals S, Turner S, Stepanek P, Hruby M;, Macromolecular bioscience 12, 1731 (2012). http://doi.org/10.1002/mabi.201200294
Abstract: It is demonstrated that glycogen as a biodegradable and inexpensive material coming from renewable resources can be used as a carrier for the construction of in vivo imaging nanoagents. The model system considered is composed of glycogen modified with gadolinium and fluorescent labels. Systematic studies of properties of these nanocarriers by a variety of physical methods and results of in vivo tests of biodegradability are reported. This represents, to the authors' best knowledge, the first such use of glycogen.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.238
Times cited: 22
DOI: 10.1002/mabi.201200294
|
“Highly Efficient Hyperbranched CNT Surfactants: Influence of Molar Mass and Functionalization”. Bertels E, Bruyninckx K, Kurttepeli, Smet M, Bals S, Goderis B, Langmuir: the ACS journal of surfaces and colloids 30, 12200 (2014). http://doi.org/10.1021/la503032g
Abstract: End-group-functionalized hyperbranched polymers were synthesized to act as a carbon nanotube (CNT) surfactant in aqueous solutions. Variation of the percentage of triphenylmethyl (trityl) functionalization and of the molar mass of the hyperbranched polyglycerol (PG) core resulted in the highest measured surfactant efficiency for a 5000 g/mol PG with 5.6% of the available hydroxyl end-groups replaced by trityl functions, as shown by UV-vis measurements. Semiempirical model calculations suggest an even higher efficiency for PG5000 with 2.5% functionalization and maximal molecule specific efficiency in general at low degrees of functionalization. Addition of trityl groups increases the surfactant-nanotube interactions in comparison to unfunctionalized PG because of pi-pi stacking interactions. However, at higher functionalization degrees mutual interactions between trityl groups come into play, decreasing the surfactant efficiency, while lack of water solubility becomes an issue at very high functionalization degrees. Low molar mass surfactants are less efficient compared to higher molar mass species most likely because the higher bulkiness of the latter allows for a better CNT separation and stabilization. The most efficient surfactant studied allowed dispersing 2.85 mg of CNT in 20 mL with as little as 1 mg of surfactant. These dispersions, remaining stable for at least 2 months, were mainly composed of individual CNTs as revealed by electron microscopy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.833
Times cited: 15
DOI: 10.1021/la503032g
|
“Immersion calorimetry as a tool to evaluate the catalytic performance of titanosilicate materials in the epoxidation of cyclohexene”. Vernimmen J, Guidotti M, Silvestre-Albero J, Jardim EO, Mertens M, Lebedev OI, Van Tendeloo G, Psaro R, Rodríguez-Reinoso F, Meynen V, Cool P, Langmuir: the ACS journal of surfaces and colloids 27, 3618 (2011). http://doi.org/10.1021/la104808v
Abstract: Different types of titanosilicates are synthesized, structurally characterized, and subsequently catalytically tested in the liquid-phase epoxidation of cyclohexene. The performance of three types of combined zeolitic/mesoporous materials is compared with that of widely studied Ti-grafted-MCM-41 molecular sieve and the TS-1 microporous titanosilicate. The catalytic test results are correlated with the structural characteristics of the different catalysts. Moreover, for the first time, immersion calorimetry with the same substrate molecule as in the catalytic test reaction is applied as an extra means to interpret the catalytic results. A good correlation between catalytic performance and immersion calorimetry results is found. This work points out that the combination of catalytic testing and immersion calorimetry can lead to important insights into the influence of the materials structural characteristics on catalysis. Moreover, the potential of using immersion calorimetry as a screening tool for catalysts in epoxidation reactions is shown.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.833
Times cited: 19
DOI: 10.1021/la104808v
|
“Structural characterization of colloidal Ag2Se nanocrystals”. Buschmann V, Van Tendeloo G, Langmuir 14, 1528 (1998). http://doi.org/10.1021/la9713210
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.833
Times cited: 15
DOI: 10.1021/la9713210
|
“Tailored vapor-phase growth of CuxO-TiO2(x=1,2) nanomaterials decorated with Au particles”. Barreca D, Carraro G, Gasparotto A, Maccato C, Lebedev OI, Parfenova A, Turner S, Tondello E, Van Tendeloo G, Langmuir: the ACS journal of surfaces and colloids 27, 6409 (2011). http://doi.org/10.1021/la200698t
Abstract: We report on the fabrication of CuxOTiO2 (x = 1, 2) nanomaterials by an unprecedented vapor-phase approach. The adopted strategy involves the growth of porous CuxO matrices by means of chemical vapor deposition (CVD), followed by the controlled dispersion of TiO2 nanoparticles. The syntheses are performed on Si(100) substrates at temperatures of 400550 °C under wet oxygen atmospheres, adopting Cu(hfa)2·TMEDA (hfa =1,1,1,5,5,5-hexafluoro-2,4-pentanedionate; TMEDA = N,N,N′,N′-tetramethylethylenediamine) and Ti(O-iPr)2(dpm)2 (O-iPr = isopropoxy; dpm = 2,2,6,6-tetramethyl-3,5-heptanedionate) as copper and titanium precursors, respectively. Subsequently, finely dispersed gold nanoparticles are introduced in the as-prepared systems via radio frequency (RF)-sputtering under mild conditions. The synthesis process results in the formation of systems with chemical composition and nano-organization strongly dependent on the nature of the initial CuxO matrix and on the deposited TiO2 amount. The decoration with low-size gold clusters paves the way to the engineering of hierarchically organized nanomaterials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.833
Times cited: 36
DOI: 10.1021/la200698t
|
“A framework to account for sedimentation and diffusion in particle-cell interactions”. Cui J, Faria M, Bjornmalm M, Ju Y, Suma T, Gunawan ST, Richardson JJ, Heidar H, Bals S, Crampin EJ, Caruso F, Langmuir: the ACS journal of surfaces and colloids 32, 12394 (2016). http://doi.org/10.1021/ACS.LANGMUIR.6B01634
Abstract: In vitro experiments provide a solid basis for understanding the interactions between particles and biological systems. An important confounding variable for these studies is the difference between the amount of particles administered and that which reaches the surface of cells. Here, we engineer a hydrogel-based nanoparticle system and combine in situ characterization techniques, 3D-printed cell cultures, and computational modeling to evaluate and study particle cell interactions of advanced particle systems. The framework presented demonstrates how sedimentation and diffusion can explain differences in particle cell association, and provides a means to account for these effects. Finally, using in silico modeling, we predict the proportion of particles that reaches the cell surface using common experimental conditions for a wide range of inorganic and organic micro- and nanoparticles. This work can assist in the understanding and control of sedimentation and diffusion when investigating cellular interactions of engineered particles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.833
Times cited: 40
DOI: 10.1021/ACS.LANGMUIR.6B01634
|