“Direct observation of laser-induced crystallization of a-C : H films”. Nistor LC, van Landuyt J, Ralchenko VG, Kononenko TV, Obraztsova ED, Strelnitsky VE, Applied physics A : materials science &, processing 58, 137 (1994). http://doi.org/10.1007/BF00332170
Abstract: The post-growth modification of diamond-like amorphous hydrogenated carbon a-C:H films by laser treatment has been studied by transmission electron microscopy and Raman spectroscopy. a-C:H films grown on Si substrates by benzene decomposition in a rf glow discharge were irradiated with 15 ns pulses of a KrF-excimer laser with fluences in the ran e of E = 50-700 mJ/cm(2). At fluences below 100 mJ/cm(2) an increase in the number of graphitic clusters and in their ordering was evidenced from Raman spectra, while the film structure remained amorphous according to electron microscopy and electron diffraction observations. At higher fluences the appearance of diamond particles of 2-7 nm size, embedded into the lower crystallized graphitic matrix, was observed and simultaneously a progressive growth of graphite nanocrystals with dimensions from 2 nm to 4 nm was deduced from Raman measurements. The maximum thickness of the crystallized surface layer (approximate to 400 nm) and the degree of laser annealing are limited by the film ablation which starts at E > 250 mJ/cm(2). The laser-treated areas lose their chemical inertness. In particular, chemical etching in chromium acid becomes possible, which may be used for patterning the highly inert carbon films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 73
DOI: 10.1007/BF00332170
|
|
|
“Formation of diamond nanocrystals in laser-irradiated amorphous carbon films”. Nistor LC, van Landuyt J, Ralchenko VG, Kononenko TV, Obraztsova ED, Strelnitsky VE, International Conference on the New Diamond Science and Technology 4, 25 (1994)
Keywords: P3 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Films of filled single-wall carbon nanotubes as a new material for high-performance air-sustainable transparent conductive electrodes operating in a wide spectral range”. Tonkikh AA, Tsebro VI, Obraztsova EA, Rybkovskiy DV, Orekhov AS, Kondrashov II, Kauppinen EI, Chuvilin AL, Obraztsova ED, Nanoscale 11, 6755 (2019). http://doi.org/10.1039/C8NR10238D
Abstract: In this paper we show the advantages of transparent high conductive films based on filled single-wall carbon nanotubes. The nanotubes with internal channels filled with acceptor molecules (copper chloride or iodine) form networks demonstrating significantly improved characteristics. Due to the charge transfer between the nanotubes and filler, the doped-nanotube films exhibit a drop in electrical sheet resistance of an order of magnitude together with a noticeable increase of film transparency in the visible and near-infrared spectral range. The thermoelectric power measurements show a significant improvement of air-stability of the nanotube network in the course of the filling procedure. For the nanotube films with an initial transparency of 87% at 514 nm and electrical sheet resistance of 862 Ohm sq(-1) we observed an improvement of transparency up to 91% and a decrease of sheet resistance down to 98 Ohm sq(-1). The combination of the nanotube synthesis technique and molecules for encapsulation has been optimized for applications in optoelectronics.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 2
DOI: 10.1039/C8NR10238D
|
|