Abstract: We studied the morphology of ramps in REBa2CU3O7 (REBCO) epitaxial films on SrTiO3 substrates, fabricated by RF magnetron sputter deposition and pulsed laser deposition (PLD), by scanning probe microscopy (SPM) and high resolution electron microscopy (HREM). The ramps were fabricated by Ar ion beam etching using masks of standard photoresist and TIN. AFM-studies on ramps in sputter deposited films show a strong dependence, i.e. formation of facets and ridges, on the angle of incidence of the ion beam with respect to the substrate surface as well as the rotation angle with respect to the crystal axes of the substrate. Ramps in pulsed laser deposited films did not show this dependence, Furthermore, we studied the effect of an anneal step prior to the deposition of barrier layers (i.e. PrBa2CU3O7, SrTiO3, CeO2) on the ramp. First results show a recrystallization of the ramp surface, resulting in terraces and a non-homogeneous growth of the barrier material on top of it. The thickness variations, for thin layers of barrier material, con even become much larger than expected from the amount of deposited material and are dependent on the deposition and anneal conditions. HREM studies show a well defined interface between barrier layer and electrodes. The angle of the ramp depends on the etch rate of the mask and REBCO, and on the angle of incidence of the ion beam. TiN has a much lower etch rate compared to photoresist, resulting in an angle of the ramp comparable to the angle of incidence, resulting in a low etching rate on the ramp. These results will lead to improved electrical characteristics of ramp-type junctions.

Abstract: Recent developments in the field of TEM characterisation of Si device materials are discussed and illustrated by a few case studies of material in different stages of various kinds of processing. Important challenges are the ever decreasing defect densities and device feature sizes. Defect delineation techniques using large area inspection tools yielding accurate coordinates of the defects to be studied have therefore become an essential part of the TEM analysis procedure. The possibility to transfer these defect coordinates without loss of accuracy to tools for local TEM specimen preparation is also a conditio sine qua non for a successful analysis. Insitu TEM remains important as dynamic processes can be observed and analysed under well defined experimental conditions. As case studies illustrating new developments, results are presented on defects in as-grown Ct silicon, on in-situ studies in processed silicon, on problem sites in advanced integrated circuit structures and on assessment of localised strain fields in the nm size scale.