Abstract: The relationships between incommensurability, charge ordering and magnetotransport properties in Nd0.5Ca0.5Mn1-xCrxO3 manganites have been studied by electron diffraction and lattice imaging versus temperature with 0.02 less than or equal to x less than or equal to 0.07. All compositions show an incommensurate superstructure over the whole temperature domain, despite the fact that they are ferromagnetic and conductive below 140 K, The q-vector (1/2 – delta)a* decreases with increasing temperature for all compositions x. For a given temperature q also decreases with x. Lattice images obtained at low temperature give a clear view of the characteristics of the incommensurate structure. They also provide a better understanding of the charge ordering process. The low-temperature form of the Cr-doped manganites is not a perfectly doubled cell [[2a(p)root 2 x 2a(p) x a(p)root 2]], but defects inducing a tripled cell occur pseudo-periodically. (C) 2000 Elsevier Science B.V. All rights reserved.

Abstract: Despite the general belief that hydrogen-bonded ferro- and antiferroelectrics undergo a pure order/disorder transition at the structural instability, new NMR data and a new theoretical concept yield convincing evidence that a pronounced displacive component is present in these systems, which modifies substantially the temperature dependencies of the tunnel and lattice mode frequencies. The experiments and their interpretation are presented. (C) 1999 Elsevier Science Ltd. All rights reserved.

Abstract: A two-step process for the formation of sensitivity centers different from earlier described two-step processes was found for sulfur sensitized emulsions. After deposition of sulfur in the first step, it was found that the second step does not consist of rearrangement of sulfur over the surface, but of the supply of silver interstitial ions towards the deposited sulfur clusters. The two processes could be separated by adsorbing and desorbing TAI (4-hydroxy-1, 3,3a, 7-tetraazaindene) at/from the silver halide surface. When 1.5 mmol TAI/mol Ag is added before the sulfur reaction, the silver interstitials are immobilized but sulfur still can be deposited at the same level. By lowering the pH to 2.50 after this sulfur reaction, TAI is desorbed from the surface and the released interstitials then cause a restoration of the properties of a sulfur system without TAI. These effects could be demonstrated via diffuse reflectance spectroscopy (DRS), sensitometry and dielectric loss measurements. We could also confirm the isolation of silver sulfide clusters by TAI from other chemicals in the solution, by adsorption of TAI on the clusters.

Abstract: Multishell tabular grains have a higher speed than pure AgBr tabular grains. Usually the shells differ in size and iodide content, but also the precipitation method for the iodide containing shells has an influence on the iodide incorporation. A TEM investigation was performed to determine the defect structure of multishell AgBr (111) tabular crystals containing a shell with a low iodide concentration and one with a high iodide concentration. The twins that induce tabular growth and stacking fault contrast in the region of the iodide shells have been observed, similar to previously studied AgBr/Ag(Br,I) coreshell crystals. Moreover in some of the crystals dislocations have been observed, sometimes even an entire network. The number of dislocations formed varies for the different methods of iodide addition. Also variations in average thickness between the different iodide addition methods have been observed. A higher number of dislocations and thicker crystals point towards a higher local concentration of iodide. These observations allow deciding which iodide incorporation method is most useful for a preferred dislocation pattern.