Abstract: This study demonstrates that the mechanism responsible for the transformation of glass into a degradation layer is pH-dependent. In acid conditions, the transformed glass is homogeneous and brittle. In mild alkaline conditions, transformed glass is heterogeneous due to the presence of lamellae composed of silica nanoparticles and the occurrence of Ca-rich inclusions. The fundamental difference between acid and alkaline conditions cannot be explained by the currently accepted degradation mechanism based on ion exchange. To explain this critical observation, we propose a refined degradation mechanism based on existing knowledge that involves several inwardly moving reaction fronts. The fronts responsible for the transformation of the silicate network into amorphous silica are also responsible for the morphology of the transformed glass. We have identified the feedback mechanism that explains the formation of lamellae in alkaline conditions.

Abstract: We present a decision-support system that guides heritage guardians in selecting mitigation actions to improve the indoor air quality and thus the preservation conditions of indoor collections in heritage buildings. This contribution shows that it is feasible to build a decision support system dedicated to preventive conservation when the following barriers are overcome: 1) simultaneous measurement of a wide range of environmental parameters in order to detect a larger number of undesired situations; 2) development of an algorithm to perform reproducible indoor air quality assessments; and 3) transformation of the air quality assessment into a graph that can be read intuitively without causing a wide variation of interpretations among stakeholders. An important aspect of the decision support system is that it reduces several sources of uncertainty that hamper reliable indoor air quality assessments. The possibilities of such a system are illustrated with a measurement campaign in a church where a heating system has been installed and used for the first time.

Abstract: Climate change will affect the preservation conditions of our cultural heritage. Therefore, well-considered mitigation actions should be implemented to safeguard our heritage for future generations. Environmental monitoring is essential to follow up the change in preservation conditions and to evaluate the effectiveness of performed mitigation actions. To support heritage guardians in the processing and evaluation of monitored data, an indoor air quality (IAQ) index for heritage applications is introduced. The index is calculated for each measured point in time and is visualized in a user-friendly and intuitive way. The current paper describes the backbone of the IAQ-calculating algorithm. The algorithm is subsequently applied on a case study in which a mitigation action is implemented in a church.

Abstract: It is commonly known that the conservation state of works of arts exhibited inside museums is strongly influenced by the indoor environmental quality (IEQ). Heritage institutions traditionally record and evaluate their IEQ by monitoring temperature, relative humidity, and -more rarely-light. However, smart use of technology enables monitoring other parameters that give a more complete insight in environmental air aggressiveness. One of this parameters is particulate matter (PM) and especially its concentration, size distribution and chemical composition. In this work, we present a selection of data sets which were obtained in a measuring campaign performed in the War Heritage Institute in Brussels, Belgium. A continuous monitoring of PM concentration with a light scattering based particle counter was performed. In addition the daily mass concentration and size distribution of airborne PM was monitored by means of Harvard impactors. The chemical composition of sampled PM was inferred from the results of XRF and IC analysis. The insights from these datasets are combined with the results of traditional environmental monitoring (temperature, relative humidity and light intensity), and assessed against the recommended guidelines for conservation environments. By using an integrated approach based on the calculation of an IEQ-index, we present a straightforward methodology to evaluate and visualize the IEQ including also continuous PM monitoring. It is clear from the results of this study how including PM in IEQ analysis allows to identify potential risks for museum collections that remain invisible when only traditional parameters are considered.

Abstract: This work reports the first systematic chemical characterization of Portuguese 18th century glassware. 28 selected glass fragments, recovered from an archaeological excavation carried out in the site where King D. João V of Portugal established an important glass manufacture, Real Fábrica de Vidros de Coina (Coina Royal Glass Factory), were studied. This factory operated from 1719 until 1747, the year in which the factory was transferred to Marinha Grande. The fragments were analysed by micro-energy dispersive X-ray fluorescence (micro-EDXRF), using a portable spectrometer ArtTAX, and scanning electron microscopy (SEM-EDX). The analytical data showed that a large variety of glass types was manufactured in that factory, namely soda-lime glass, mixed-alkali glass, high lime-low alkali glass, potash glass and lead glass. In general, the composition of the glass varies according to the function of the objects. It was demonstrated that micro-EDXRF can be an important tool to characterize museum glass objects when only in situ non-invasive analytical methods are allowed.

Abstract: There is a long tradition in evaluating industrial atmospheres by measuring the corrosion rate of exposed metal coupons. The heritage community also uses this method, but the interpretation of the corrosion rate often lacks clarity due to the low corrosivity in indoor museum environments. This investigation explores the possibilities and drawbacks of different silver corrosion rate assessments. The corrosion rate is determined by three approaches: (1) chemical characterization of metal coupons using analytical techniques such as electrochemical measurements, SEM-EDX, XRD, and µ-Raman spectroscopy, (2) continuous corrosion monitoring methods based on electrical resistivity loss of a corroding nm-sized metal wire and weight gain of a corroding silver coated quartz crystal, and (3) characterization of the visual degradation of the metal coupons. This study confirms that subtle differences in corrosivity between locations inside a museum can be determined on condition that the same corrosion rate assessment is used. However, the impact of the coupon orientation with respect to the prevailing direction of air circulation can be substantially larger than the impact of the coupon location.

Abstract: One of the most striking but unexplained phenomena in the natural degradation of glass is the transformation of an almost colorless, transparent and homogeneous glass into a colored, opaque and heterogeneous degradation layer. In many cases, the degradation layer consists of numerous lamellae with a thickness between 0.1 and 10 pm. However, both internal structure and formation proess of laminated degradation layers remain unclear. In this paper, a model is proposed where we assume that transformed (degraded) glass consists of a random packing of nano-sized silica particles while the lamellae are the result of different packing densities. The model is able to connect the texture of numerous lamellae observed by several types of microscopic techniques with the structure at molecular level determined by means of chemical analysis. In addition, the model is able to explain numerous properties such as the parameters responsible for the contrast between lamellae. This contrast can be caused by differences in color, density, elemental composition, or surface roughness. (C) 2016 Elsevier B.V. All rights reserved.

Abstract: Several artists pigments are semiconductors. Some of these materials appear stable over time, whereas others already show remarkable signs of degradation after limited time periods. The (in)stability of these pigments can be understood using a thermodynamic approach. For several pigment-related materials, the thermodynamic oxidation and reduction potential (ϕox and ϕred) were determined and evaluated considering the absolute energy positions of the valence and conduction band edges and the water redox potentials. The positions of ϕox and ϕred can be used in a fast screening of the stability of semiconductor pigments towards photoinduced corrosion in an aqueous/humid environment. This theoretical approach corresponds well with experimental data on pigment permanence and degradation phenomena found in literature.

Abstract: Chemical transformations in paintings often induce discolorations, disturbing the appearance of the image. For an appropriate conservation of such valuable and irreplaceable heritage objects, it is important to have a good know-how on the degradation processes of the (historical) materials: which pigments have been discolored, what are the responsible processes, and which (environmental) conditions have the highest impact on the pigment degradation and should be mitigated. Pigment degradation is already widely studied, either by analyzing historical samples or by accelerated weathering experiments on dummies. However, in historic samples several processes may have taken place, increasing the complexity of the current state, while aging experiments are time-consuming due to the often extended aging period. An alternative method is proposed for a fast monitoring of degradation processes of semiconductor pigments, using an electrochemical setup mimicking the real environment and allowing the identification of harmful environmental parameters for each pigment. Examples are given for the pigments cadmium yellow (CdS) and vermilion (α-HgS).

Abstract: X-ray radiographic images of paintings often show little or no contrast. In order to increase the contrast in radiographic images we measured the X-ray spectrum of a low power X-ray tube, after passing through the painting, with a high energy-resolution SDD detector. To obtain images, the detector is collimated with a 400 mu m diameter pinhole and the painting was moved through the beam in the x and y-direction using a dwell time of a few seconds per pixel. The data obtained consists of a data cube of, typically, 200 x 200 pixels and a 512-channel X-ray spectrum for each pixel, spanning the energy range from 0 to 40 keV. Having the absorbance spectrum available for each pixel, we are able, a posteriori, to produce images by edge subtraction for any given element. In this way high contrast, element-specific, images can be obtained. Because of the high energy-resolution a much simpler edge subtraction algorithm can be applied. We also used principal-component imaging to obtain, in a more automated way, images with high contrast. Some of these images can easily be attributed to specific elements. It turns out that preprocessing of the spectral data is crucial for the success of the multivariate image processing.

Abstract: The speed and effectiveness of a conservation treatment used for stained glass windows have been investigated. Dark-coloured Mn-rich stains can be found in the alteration layer of ancient glass artefacts and cause the surface to turn brown/black: this phenomenon is known as Mn-browning or Mn-staining. While in glass manganese is present in the +II or +III oxidation states, in the Mn-rich bodies, manganese is in a higher oxidation state (+IV). In restoration practice, mildly reducing solutions are employed to eliminate the dark colour and restore the clear appearance of the glass. In this paper the effectiveness and side effects of the use of hydroxylamine hydrochloride for this purpose are assessed. Archaeological fragments of stained glass windows, dated to the 14th century and originating from Sidney Sussex College, Cambridge (UK), were examined by means of synchrotron radiation (SR) based microscopic X-ray Absorption Near-Edge Spectroscopy (μ-XANES) and microscopic X-Ray Fluorescence (μ-XRF) and with high resolution computed absorption tomography (μ-CT) before, during and after the treatment. The monitoring of the glass fragments during the treatment allows us to better understand the manner in which the process unfolds and its kinetics. The results obtained reveal that the hydroxylamine hydrochloride treatment is effective, but also that it has a number of unwanted side effects. These findings are useful for optimizing the time and other modalities of the Mn-reducing treatment as well as minimizing its unwanted results.

Abstract: During the study of a large number of archaeological glass fragments, manganese-rich inclusions in leached layers were observed in a limited number of cases. This phenomenon occurs only in black-coloured leached layers. Since the formation mechanism of such manganese-rich inclusions is still unclear, a combination of several analytical techniques was used in order to investigate this phenomenon and, more specifically, to obtain more information on (a) the composition and morphology of the inclusions, (b) the chemical state of Mn and (c) the 3D morphology of the inclusions. A mechanism that might explain the formation of these inclusions is proposed.

Abstract: The chemical composition of 11 glass panes originating from two 13th century non-figurative windows were analyzed by means of Scanning Electron MicroscopyEnergy Dispersive X-ray system (SEM-EDX). The windows were discovered in the back-wall of the triforium during the restoration of the choir of the cathedral St. Michael and St. Gudule in Brussels (Belgium). In order to determine if these windows were fabricated with glass of different origin or not, the compositional difference between the panes were compared with the variation in composition as a result of the following causes: (1) compositional fluctuation between panes cut from the same sheet of glass, (2) compositional fluctuation caused when panes are cut from different sheets that were made with the same batch, (3) compositional fluctuation caused when the glass is made from different batches at the same production center, and (4) compositional fluctuation as a result of glass produced at different fabrication centers.

Abstract: In this study, the results of analysing of a series of 16th-19th century painted enamel objects of the Limoges School currently in collections in three Dutch and Flemish museums by means of portable and micro x-ray fluorescence analysis (PXRF and µ-XRF) and electron probe micro analysis (EPMA) are presented. The aim of the investigation was the authentication of specific pieces. Therefore, the glass compositions as well as the (glass) colouring agents used by the Limoges' artists were studied as a function of the age of the objects. Due to the evolution of these properties, it is possible to approximately date these objects based on their chemical composition. The complete émail peint collection of the Museum Boijmans-Van Beuningen (Rotterdam, The Netherlands), consisting of 20 émail peint plaques, was analysed with µ-XRF. Quantitative information was obtained by EPMA analysis of 15 enamel fragments of objects from museum and private collections in the Low Countries. PXRF analyses were performed on the painted enamel collection of the Antwerp Vleeshuis Museum (13 objects) and the Mayer van den Bergh Museum (4 objects) and on a set of 18 plaques that were donated to the Boijmans-Van Beuningen Museum by a private collector. The results obtained by means of EPMA, µ-XRF and PXRF proved to be useful in the discrimination of 16th century painted enamel objects from those of the19th century. From a total of 70 objects examined, 2 objects (OM964A and OM993) featured a chemical signature that deviated from the published literature composition and pigment use consistent with its presumed period of manufacture.