Abstract: This study demonstrates that the mechanism responsible for the transformation of glass into a degradation layer is pH-dependent. In acid conditions, the transformed glass is homogeneous and brittle. In mild alkaline conditions, transformed glass is heterogeneous due to the presence of lamellae composed of silica nanoparticles and the occurrence of Ca-rich inclusions. The fundamental difference between acid and alkaline conditions cannot be explained by the currently accepted degradation mechanism based on ion exchange. To explain this critical observation, we propose a refined degradation mechanism based on existing knowledge that involves several inwardly moving reaction fronts. The fronts responsible for the transformation of the silicate network into amorphous silica are also responsible for the morphology of the transformed glass. We have identified the feedback mechanism that explains the formation of lamellae in alkaline conditions.

Abstract: One of the most striking but unexplained phenomena in the natural degradation of glass is the transformation of an almost colorless, transparent and homogeneous glass into a colored, opaque and heterogeneous degradation layer. In many cases, the degradation layer consists of numerous lamellae with a thickness between 0.1 and 10 pm. However, both internal structure and formation proess of laminated degradation layers remain unclear. In this paper, a model is proposed where we assume that transformed (degraded) glass consists of a random packing of nano-sized silica particles while the lamellae are the result of different packing densities. The model is able to connect the texture of numerous lamellae observed by several types of microscopic techniques with the structure at molecular level determined by means of chemical analysis. In addition, the model is able to explain numerous properties such as the parameters responsible for the contrast between lamellae. This contrast can be caused by differences in color, density, elemental composition, or surface roughness. (C) 2016 Elsevier B.V. All rights reserved.

Abstract: Environmental parameters such as temperature, relative humidity, visible light, UV radiation and pollution influence the deterioration rate of heritage items. To judge on the environmental appropriateness for heritage conservation, it is therefore important to monitor the environment. Often, an incomplete set of environmental parameters is measured, or sporadic or time-averaged measurements are performed. As a result, a wide range of undesirable situations and hazards remain unnoticed. This might lead to an underestimation of environmental dangers (i.e., inaccurate judgement) or to inappropriate mitigation measures (i.e., inaccurate decision making). We present an innovative and user-friendly monitoring device that simultaneously and continuously measures (1) environmental parameters and (2) material behavior. An extended combination of off-the-shelf sensors for temperature, relative humidity, air speed, CO2, NO2, O-3 and particulate matter are connected to a multipurpose datalogger. In-house developed sensors for the shrinkage and expansion behavior of wood, as well as sensors for metal corrosion rates are connected to the same datalogger. Such extended monitoring shows the identification of a wider range of undesirable situations, and it facilitates the search for correlations between such situations and the sources that cause them, i.e., the hazards.

Abstract: Heritage-related guidelines and standards recommend stable climatic conditions, since these contribute to the extension of heritage collections life. As a result, numerous museums and other heritage institutions implement (expensive) mitigation measures to achieve stable conditions. Nevertheless, temperature and relative humidity fluctuations are often still observed. This contribution demonstrates that the analysis of temperature and humidity peaks and drops helps to identify hazards which cause fluctuations in different frequency ranges. This hazard identification provides information on the type of mitigation actions that are required in the near future and in which order they need to be implemented. The approach is illustrated with a case study. A 22 month monitoring campaign was performed in a chapel in the center of Antwerp (Belgium) where the climatic conditions are controlled with a heating, ventilation and air conditioning (HVAC) system. Low-, mid- and high-frequency fluctuations were separated and discussed for their hazards.

Abstract: It is commonly known that the conservation state of works of arts exhibited inside museums is strongly influenced by the indoor environmental quality (IEQ). Heritage institutions traditionally record and evaluate their IEQ by monitoring temperature, relative humidity, and -more rarely-light. However, smart use of technology enables monitoring other parameters that give a more complete insight in environmental air aggressiveness. One of this parameters is particulate matter (PM) and especially its concentration, size distribution and chemical composition. In this work, we present a selection of data sets which were obtained in a measuring campaign performed in the War Heritage Institute in Brussels, Belgium. A continuous monitoring of PM concentration with a light scattering based particle counter was performed. In addition the daily mass concentration and size distribution of airborne PM was monitored by means of Harvard impactors. The chemical composition of sampled PM was inferred from the results of XRF and IC analysis. The insights from these datasets are combined with the results of traditional environmental monitoring (temperature, relative humidity and light intensity), and assessed against the recommended guidelines for conservation environments. By using an integrated approach based on the calculation of an IEQ-index, we present a straightforward methodology to evaluate and visualize the IEQ including also continuous PM monitoring. It is clear from the results of this study how including PM in IEQ analysis allows to identify potential risks for museum collections that remain invisible when only traditional parameters are considered.

Abstract: There is a long tradition in evaluating industrial atmospheres by measuring the corrosion rate of exposed metal coupons. The heritage community also uses this method, but the interpretation of the corrosion rate often lacks clarity due to the low corrosivity in indoor museum environments. This investigation explores the possibilities and drawbacks of different silver corrosion rate assessments. The corrosion rate is determined by three approaches: (1) chemical characterization of metal coupons using analytical techniques such as electrochemical measurements, SEM-EDX, XRD, and µ-Raman spectroscopy, (2) continuous corrosion monitoring methods based on electrical resistivity loss of a corroding nm-sized metal wire and weight gain of a corroding silver coated quartz crystal, and (3) characterization of the visual degradation of the metal coupons. This study confirms that subtle differences in corrosivity between locations inside a museum can be determined on condition that the same corrosion rate assessment is used. However, the impact of the coupon orientation with respect to the prevailing direction of air circulation can be substantially larger than the impact of the coupon location.

Abstract: Chemical transformations in paintings often induce discolorations, disturbing the appearance of the image. For an appropriate conservation of such valuable and irreplaceable heritage objects, it is important to have a good know-how on the degradation processes of the (historical) materials: which pigments have been discolored, what are the responsible processes, and which (environmental) conditions have the highest impact on the pigment degradation and should be mitigated. Pigment degradation is already widely studied, either by analyzing historical samples or by accelerated weathering experiments on dummies. However, in historic samples several processes may have taken place, increasing the complexity of the current state, while aging experiments are time-consuming due to the often extended aging period. An alternative method is proposed for a fast monitoring of degradation processes of semiconductor pigments, using an electrochemical setup mimicking the real environment and allowing the identification of harmful environmental parameters for each pigment. Examples are given for the pigments cadmium yellow (CdS) and vermilion (α-HgS).

Abstract: A set of ca. 500 window glass fragments originating from different historical sites in Belgium and covering the period 12(th)- 18(th) century was analyzed by rneans of electron probe microanalysis. Most samples are archaeological finds deriving from non-figurative windows in secular buildings. However. the analyzed set also contains glass sampled from still existing non-figurative windows in secular buildings and stained-glass windows in religious buildings. A sudden compositional change at the end of the 14(th) century can be noticed among the series of glass compositions that were obtained. These changes could be related to the use of different glassmaker recipes and to the introduction of new raw materials for glass making. (c) 2007 Elsevier B.V All rights reserved.

Abstract: Twenty-seven glass fragments containing dark coloured grisaille paint layers of different qualities were collected from ten windows of the cathedral St. Michael & St. Gudule in Brussels (Belgium). The windows were made by J.-B. Capronnier (18141891) and cover the period between 1843 and 1878. The samples were cross-sectioned and examined in an electron microscope. Grisaille paint layers are not homogeneous and therefore, it is not meaningful to characterize them in terms of their average composition. Instead, parameters such as granularity, the number of residual gas bubbles per running millimetre of paint, the type of pigments, and the thickness of the paint layer were used to characterize them. The microscopic morphology allows a classification of the grisaille paint layers in four groups, every group associated with a quality level. Moreover, the main causes of the accelerated degradation of some of these paint layers could be explained. The classification made it possible to distinguish two periods in the work of Capronnier: (1) the early period (18431848) is characterized by the presence of either single granular paint layers or of double-layered systems consisting of a granular paint layer on top of a well-melted paint layer. The granular grisaille paint layers tend to pulverize; (2) the later period (18481878) is characterized by the presence of only well-vitrified paint layers. No sign of deterioration was found on the well-vitrified paint layers.

Abstract: In this study, the results of analysing of a series of 16th-19th century painted enamel objects of the Limoges School currently in collections in three Dutch and Flemish museums by means of portable and micro x-ray fluorescence analysis (PXRF and µ-XRF) and electron probe micro analysis (EPMA) are presented. The aim of the investigation was the authentication of specific pieces. Therefore, the glass compositions as well as the (glass) colouring agents used by the Limoges' artists were studied as a function of the age of the objects. Due to the evolution of these properties, it is possible to approximately date these objects based on their chemical composition. The complete émail peint collection of the Museum Boijmans-Van Beuningen (Rotterdam, The Netherlands), consisting of 20 émail peint plaques, was analysed with µ-XRF. Quantitative information was obtained by EPMA analysis of 15 enamel fragments of objects from museum and private collections in the Low Countries. PXRF analyses were performed on the painted enamel collection of the Antwerp Vleeshuis Museum (13 objects) and the Mayer van den Bergh Museum (4 objects) and on a set of 18 plaques that were donated to the Boijmans-Van Beuningen Museum by a private collector. The results obtained by means of EPMA, µ-XRF and PXRF proved to be useful in the discrimination of 16th century painted enamel objects from those of the19th century. From a total of 70 objects examined, 2 objects (OM964A and OM993) featured a chemical signature that deviated from the published literature composition and pigment use consistent with its presumed period of manufacture.

Abstract: In this article, results using confocal µ-Raman to analyse the cross-section of paint samples are presented. Results obtained with light microscopy, scanning electron microscopy (SEM) combined with an energy dispersive X-ray analysis (EDX) and micro-X-ray fluorescence (µ-XRF) are mentioned and compared to the ones obtained with confocal (MRS). In some cases, pigment identification was possible only by combining analytical results from different techniques. The samples were drawn from five paintings belonging to the Academy of Fine Arts of Antwerp, which are part of a collection of 34 paintings made by students from the Academy between 1819 and 1920. Since, on the one hand, the painting techniques and materials, especially pigments, used in this period are still not completely known, and on the other hand, this collection constitutes a very important and reliable resource of information, these paintings were chosen for a systematic investigation. They represent the evolution of painting in Belgium over approximately a century.