Abstract: Twenty-seven glass fragments containing dark coloured grisaille paint layers of different qualities were collected from ten windows of the cathedral St. Michael & St. Gudule in Brussels (Belgium). The windows were made by J.-B. Capronnier (18141891) and cover the period between 1843 and 1878. The samples were cross-sectioned and examined in an electron microscope. Grisaille paint layers are not homogeneous and therefore, it is not meaningful to characterize them in terms of their average composition. Instead, parameters such as granularity, the number of residual gas bubbles per running millimetre of paint, the type of pigments, and the thickness of the paint layer were used to characterize them. The microscopic morphology allows a classification of the grisaille paint layers in four groups, every group associated with a quality level. Moreover, the main causes of the accelerated degradation of some of these paint layers could be explained. The classification made it possible to distinguish two periods in the work of Capronnier: (1) the early period (18431848) is characterized by the presence of either single granular paint layers or of double-layered systems consisting of a granular paint layer on top of a well-melted paint layer. The granular grisaille paint layers tend to pulverize; (2) the later period (18481878) is characterized by the presence of only well-vitrified paint layers. No sign of deterioration was found on the well-vitrified paint layers.

Abstract: Heritage-related guidelines and standards recommend stable climatic conditions, since these contribute to the extension of heritage collections life. As a result, numerous museums and other heritage institutions implement (expensive) mitigation measures to achieve stable conditions. Nevertheless, temperature and relative humidity fluctuations are often still observed. This contribution demonstrates that the analysis of temperature and humidity peaks and drops helps to identify hazards which cause fluctuations in different frequency ranges. This hazard identification provides information on the type of mitigation actions that are required in the near future and in which order they need to be implemented. The approach is illustrated with a case study. A 22 month monitoring campaign was performed in a chapel in the center of Antwerp (Belgium) where the climatic conditions are controlled with a heating, ventilation and air conditioning (HVAC) system. Low-, mid- and high-frequency fluctuations were separated and discussed for their hazards.

Abstract: Porous limestone and mortar are able to absorb large quantities of water. This phenomenon will accelerate the deterioration of the material. In such cases, the material might be treated with a hydrophobic product, which creates a superficial layer that hampers the penetration of water. In order to decide if such a treatment should be applied or not, the water absorbing behaviour of the material should be measured. With the same measuring technique the efficiency of the hydrophobic barrier can be evaluated. Moreover, it allows the monitoring of such barriers as a function of time. At the same time, the water absorption of porous stone material is an indication of the degree of deterioration and its sensitivity to future deterioration. Up to now, two different measuring techniques exist, but one can only be used in laboratory and the other, which can be operated in laboratory as well as in situ, is not always reliable for in situ analyses. This article proposes an alternative method: the contact sponge method. This recently developed method was tested on non-treated porous stone materials in a laboratory environment in order to evaluate its performance in comparison with the two existing methods.

Abstract: One of the most striking but unexplained phenomena in the natural degradation of glass is the transformation of an almost colorless, transparent and homogeneous glass into a colored, opaque and heterogeneous degradation layer. In many cases, the degradation layer consists of numerous lamellae with a thickness between 0.1 and 10 pm. However, both internal structure and formation proess of laminated degradation layers remain unclear. In this paper, a model is proposed where we assume that transformed (degraded) glass consists of a random packing of nano-sized silica particles while the lamellae are the result of different packing densities. The model is able to connect the texture of numerous lamellae observed by several types of microscopic techniques with the structure at molecular level determined by means of chemical analysis. In addition, the model is able to explain numerous properties such as the parameters responsible for the contrast between lamellae. This contrast can be caused by differences in color, density, elemental composition, or surface roughness. (C) 2016 Elsevier B.V. All rights reserved.