Carrasco, S.; Orcajo, G.; Martínez, F.; Imaz, I.; Kavak, S.; Arenas-Esteban, D.; Maspoch, D.; Bals, S.; Calleja, G.; Horcajada, P. |
|
| |
Title |
Hf/porphyrin-based metal-organic framework PCN-224 for CO2 cycloaddition with epoxides |
Type |
A1 Journal Article |
| |
Year  |
2023 |
Publication |
Materials Today Advances |
Abbreviated Journal |
|
|
| |
Volume |
19 |
Issue |
|
Pages |
100390 |
|
| |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
| |
Abstract |
Herein, we describe for the first time the synthesis of the highly porous Hf-tetracarboxylate porphyrin-based metal-organic framework (MOF) (Hf)PCN-224(M) (M = H2, Co2+). (Hf)PCN-224(H2) was easily and efficiently prepared following a simple microwave-assisted procedure with good yields (56–67%; space-time yields: 1100–1270 kg m−3·day−1), high crystallinity and phase purity by using trifluoromethanesulfonic acid and benzoic acid as modulators in less than 30 min. By simply introducing a preliminary step (10 min), 5,10,15,20-(tetra-4-carboxyphenyl)porphyrin linker (TCPP) was quantitatively metalated with Co2+ without additional purification and/or time consuming protection/deprotection steps to further obtain (Hf)PCN-224(Co). (Hf)PCN-224(Co) was then tested as catalyst in CO2 cycloaddition reaction with different epoxides to yield cyclic carbonates, showing the best catalytic performance described to date compared to other PCNs, under mild conditions (1 bar CO2, room temperature, 18–24 h). Twelve epoxides were tested, obtaining from moderate to excellent conversions (35–96%). Moreover, this reaction was gram scaled-up (x50) without significant loss of yield to cyclic carbonates. (Hf)PCN-224(Co) maintained its integrity and crystallinity even after 8 consecutive runs, and poisoning was efficiently reverted by a simple thermal treatment (175 °C, 6 h), fully recovering the initial catalytic activity. |
|
| |
Address |
|
|
| |
Corporate Author |
|
Thesis |
|
|
| |
Publisher |
|
Place of Publication |
|
Editor |
|
|
| |
Language |
|
Wos |
001025764000001 |
Publication Date |
2023-06-19 |
|
| |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
| |
Series Volume |
|
Series Issue |
|
Edition |
|
|
| |
ISSN |
2590-0498 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
| |
Impact Factor |
10 |
Times cited |
1 |
Open Access |
OpenAccess |
|
| |
Notes |
S.C. acknowledges the European Union's Horizon 2020 research and innovation programme under the Marie Skłodowska-Curie (MSCA-COFUND) grant agreement No 754382 (GOT Energy Talent). S.C. and P.H. acknowledge “Comunidad de Madrid” and European Regional Development Fund-FEDER 2014-2020-OE REACT-UE 1 for their financial support to VIRMOF-CM project associated to R&D projects in response to COVID-19. The authors acknowledge H2020-MSCA-ITN-2019 HeatNMof (ref. 860942), the M-ERA-NET C-MOF-cell (grant PCI2020-111998 funded by MCIN/AEI /10.13039/501100011033 and European Union NextGenerationEU/PRTR) project, and Retos Investigación MOFSEIDON (grant PID2019-104228RB-I00 funded by MCIN/AEI/10.13039/501100011033) project. This work has been also supported by the Regional Government of Madrid (Project ACES2030-CM, S2018/EMT-4319) and the Universidad Rey Juan Carlos IMPULSO Project (grant MATER M − 3000). S.K acknowledges the Flemish Fund for Scientific Research (FWO Vlaanderen) through a PhD research grant (1181122 N). |
Approved |
Most recent IF: 10; 2023 IF: NA |
|
| |
Call Number |
EMAT @ emat @c:irua:197198 |
Serial |
8800 |
|
| Permanent link to this record |
| |
|
| |
|
Author |
Arenas-Vivo, A.; Rojas, S.; Ocaña, I.; Torres, A.; Liras, M.; Salles, F.; Arenas-Esteban, D.; Bals, S.; Ávila, D.; Horcajada, P. |
|
| |
Title |
Ultrafast reproducible synthesis of a Ag-nanocluster@MOF composite and its superior visible-photocatalytic activity in batch and in continuous flow |
Type |
A1 Journal article |
| |
Year |
2021 |
Publication |
Journal Of Materials Chemistry A |
Abbreviated Journal |
J Mater Chem A |
|
| |
Volume |
9 |
Issue |
28 |
Pages |
15704-15713 |
|
| |
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
|
| |
Abstract |
The (photo)catalytic properties of metal–organic frameworks (MOFs) can be enhanced by post-synthetic inclusion of metallic species in their porosity. Due to their extraordinarily high surface area and well defined porous structure, MOFs can be used for the stabilization of metal nanoparticles with adjustable size within their porosity. Originally, we present here an optimized ultrafast photoreduction protocol for the<italic>in situ</italic>synthesis of tiny and monodisperse silver nanoclusters (AgNCs) homogeneously supported on a photoactive porous titanium carboxylate MIL-125-NH<sub>2</sub>MOF. The strong metal–framework interaction between –NH<sub>2</sub>and Ag atoms influences the AgNC growth, leading to the surfactant-free efficient catalyst AgNC@MIL-125-NH<sub>2</sub>with improved visible light absorption. The potential use of AgNC@MIL-125-NH<sub>2</sub>was further tested in challenging applications: (i) the photodegradation of the emerging organic contaminants (EOCs) methylene blue (MB-dye) and sulfamethazine (SMT-antibiotic) in water treatment, and (ii) the catalytic hydrogenation of<italic>p</italic>-nitroaniline (4-NA) to<italic>p</italic>-phenylenediamine (PPD) with industrial interest. It is noteworthy that compared with the pristine MIL-125-NH<sub>2</sub>, the composite presents an improved catalytic activity and stability, being able to photodegrade 92% of MB in 60 min and 96% of SMT in 30 min, and transform 100% of 4-NA to PPD in 30 min. Aside from these very good results, this study describes for the first time the use of a MOF in a visible light continuous flow reactor for wastewater treatment. With only 10 mg of AgNC@MIL-125-NH<sub>2</sub>, high SMT removal efficiency over 70% is maintained after >2 h under water flow conditions found in real wastewater treatment plants, signaling a future real application of MOFs in water remediation. |
|
| |
Address |
|
|
| |
Corporate Author |
|
Thesis |
|
|
| |
Publisher |
|
Place of Publication |
|
Editor |
|
|
| |
Language |
|
Wos |
000671839200001 |
Publication Date |
2021-06-21 |
|
| |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
| |
Series Volume |
|
Series Issue |
|
Edition |
|
|
| |
ISSN |
2050-7488 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
| |
Impact Factor |
8.867 |
Times cited |
18 |
Open Access |
OpenAccess |
|
| |
Notes |
Comunidad de Madrid, CAM PEJD-2016/IND-2828 Talento Modality 2, 2017-T2/IND-5149 ; Secretaría de Estado de Investigación, Desarrollo e Innovación, Raphuel project (ENE2016-79608-C2-1-R) Retos Project MAT2017-84385-R ; Ministerio de Ciencia e Innovación, Juan de la Cierva Incorporación Fellowship (grant agreement no. IJC2019-038894-I) MOFSEIDON project (PID2019-104228RB-I00) Ramón y Cajal, Grant Agreements 2014-15039 and 2015-18677 ; Fundación BBVA, IN[17]CBBQUI_0197 ; H2020 European Research Council, ERC Consolidator Grant REALNANO 815128 Grant Agreement no. 731019 (EUSMI) ; sygmaSB; |
Approved |
Most recent IF: 8.867 |
|
| |
Call Number |
EMAT @ emat @c:irua:179791 |
Serial |
6802 |
|
| Permanent link to this record |
| |
|
| |
|
Author |
Canioni, R.; Roch-Marchal, C.; Sécheresse, F.; Horcajada, P.; Serre, C.; Hardi-Dan, M.; Férey, G.; Grenèche, J.-M.; Lefebvre, F.; Chang, J.-S.; Hwang, Y.-K.; Lebedev, O.; Turner, S.; Van Tendeloo, G. |
|
| |
Title |
Stable polyoxometalate insertion within the mesoporous metal organic framework MIL-100(Fe) |
Type |
A1 Journal article |
| |
Year |
2011 |
Publication |
Journal of materials chemistry |
Abbreviated Journal |
J Mater Chem |
|
| |
Volume |
21 |
Issue |
4 |
Pages |
1226-1233 |
|
| |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
| |
Abstract |
Successful encapsulation of polyoxometalate (POM) within the framework of a mesoporous iron trimesate MIL-100(Fe) sample has been achieved by direct hydrothermal synthesis in the absence of fluorine. XRPD, 31P MAS NMR, IR, EELS, TEM and 57Fe Mössbauer spectrometry corroborate the insertion of POM within the cavities of the MOF. The experimental Mo/Fe ratio is 0.95, in agreement with the maximum theoretical amount of POM loaded within the pores of MIL-100(Fe), based on steric hindrance considerations. The POM-MIL-100(Fe) sample exhibits a pore volume of 0.373 cm3 g−1 and a BET surface area close to 1000 m2 g−1, indicating that small gas molecules can easily diffuse inside the cavities despite the presence of heavy phosphomolybdates. These latter contribute to the decrease in the overall surface area, due to the increase in molar weight, by 65%. Moreover, the resulting Keggin containing MIL-100(Fe) solid is stable in aqueous solution with no POM leaching even after more than 2 months. In addition, no exchange of the Keggin anions by tetrabutylammonium perchlorate in organic media has been observed. |
|
| |
Address |
|
|
| |
Corporate Author |
|
Thesis |
|
|
| |
Publisher |
|
Place of Publication |
Cambridge |
Editor |
|
|
| |
Language |
|
Wos |
000286110400042 |
Publication Date |
2010-11-25 |
|
| |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
| |
Series Volume |
|
Series Issue |
|
Edition |
|
|
| |
ISSN |
0959-9428;1364-5501; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
| |
Impact Factor |
|
Times cited |
158 |
Open Access |
|
|
| |
Notes |
|
Approved |
Most recent IF: NA |
|
| |
Call Number |
UA @ lucian @ c:irua:88642 |
Serial |
3145 |
|
| Permanent link to this record |