Abstract: The influence of 0.25, 2 and 5 wt.% alumina addition on the mechanical properties and low temperature degradation (LTD) of 3, 2.5 and 2 mol% yttria-stabilized TZP ceramics was investigated. The amount of alumina addition was observed to have a crucial impact on the degradation of Y-TZP ceramics. Independent on the yttria stabilizer content, 0.25 wt.% alumina had a higher degradation retarding effect to Y-TZP ceramics than 2 and 5 wt.% of alumina addition, which had a comparable effect. The apparent activation energy for the degradation process was increased by adding alumina, but it was the same for 0.255 wt.% alumina doped 3Y-TZP ceramics. For Y-TZPs containing a small amount of alumina addition, only the segregated Al3+ at the grain boundaries of the zirconia grains was effective to retard the degradation of Y-TZPs. The secondary phase Al2O3 grains increased the degradation kinetics, which might be attributed to the residual stresses.

Abstract: Different factors such as the way of incorporating the Y2O3 stabilizer, alumina addition and sintering temperature were assessed with the goal to improve the low temperature degradation (LTD) resistance of 3Y-TZP without compromising on the mechanical properties. The degradation of hydrothermally treated specimens was studied by X-ray diffraction, micro-Raman spectroscopy and scanning electron microscopy. Decreasing the sintering temperature decreased the LTD susceptibility of 3Y-TZPs but did not allow to obtain a LTD resistant 3Y-TZP with optimized mechanical properties. Alumina addition along with the use of Y2O3 stabilizer coated starting powder allowed to combine both an excellent toughness and LTD resistance, as compared to alumina-free and stabilizer co-precipitated powder based equivalents. Transmission electron microscopy revealed that the improved LTD resistance could be attributed to the segregation of Al3+ at the grain boundary and the heterogeneously distributed Y3+ stabilizer.

Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)

Impact Factor: 3.411

Times cited: 48

DOI: 10.1016/j.jeurceramsoc.2014.02.026

Additional Links: UA library record; WoS full record; WoS citing articles

Permanent link

| Save citation: RTF PDF LaTeX

| Export record: BibTeX Endnote ISI RIS Word XML

	NANOlab Center of Excellence literature database Home \| Show All \| Simple Search \| Advanced Search	Login Quick Search: Field: contains: ...
	1–2 of 2 records found matching your query (RSS):

	“Critical influence of alumina content on the low temperature degradation of 2-3 mol% yttria-stabilized TZP for dental restorations”. Zhang F, Vanmeensel K, Inokoshi M, Batuk M, Hadermann J, Van Meerbeek B, Naert I, Vleugels J, Journal of the European Ceramic Society 35, 741 (2015). http://doi.org/10.1016/j.jeurceramsoc.2014.09.018 Abstract: The influence of 0.25, 2 and 5 wt.% alumina addition on the mechanical properties and low temperature degradation (LTD) of 3, 2.5 and 2 mol% yttria-stabilized TZP ceramics was investigated. The amount of alumina addition was observed to have a crucial impact on the degradation of Y-TZP ceramics. Independent on the yttria stabilizer content, 0.25 wt.% alumina had a higher degradation retarding effect to Y-TZP ceramics than 2 and 5 wt.% of alumina addition, which had a comparable effect. The apparent activation energy for the degradation process was increased by adding alumina, but it was the same for 0.255 wt.% alumina doped 3Y-TZP ceramics. For Y-TZPs containing a small amount of alumina addition, only the segregated Al3+ at the grain boundaries of the zirconia grains was effective to retard the degradation of Y-TZPs. The secondary phase Al2O3 grains increased the degradation kinetics, which might be attributed to the residual stresses. Keywords: A1 Journal article; Electron microscopy for materials research (EMAT) Impact Factor: 3.411 Times cited: 37 DOI: 10.1016/j.jeurceramsoc.2014.09.018 Additional Links: UA library record; WoS full record; WoS citing articles Permanent link \| Save citation: RTF PDF LaTeX \| Export record: BibTeX Endnote ISI RIS Word XML
	“3Y-TZP ceramics with improved hydrothermal degradation resistance and fracture toughness”. Zhang F, Vanmeensel K, Inokoshi M, Batuk M, Hadermann J, Van Meerbeek B, Naert I, Vleugels J, Journal of the European Ceramic Society 34, 2453 (2014). http://doi.org/10.1016/j.jeurceramsoc.2014.02.026 Abstract: Different factors such as the way of incorporating the Y2O3 stabilizer, alumina addition and sintering temperature were assessed with the goal to improve the low temperature degradation (LTD) resistance of 3Y-TZP without compromising on the mechanical properties. The degradation of hydrothermally treated specimens was studied by X-ray diffraction, micro-Raman spectroscopy and scanning electron microscopy. Decreasing the sintering temperature decreased the LTD susceptibility of 3Y-TZPs but did not allow to obtain a LTD resistant 3Y-TZP with optimized mechanical properties. Alumina addition along with the use of Y2O3 stabilizer coated starting powder allowed to combine both an excellent toughness and LTD resistance, as compared to alumina-free and stabilizer co-precipitated powder based equivalents. Transmission electron microscopy revealed that the improved LTD resistance could be attributed to the segregation of Al3+ at the grain boundary and the heterogeneously distributed Y3+ stabilizer. Keywords: A1 Journal article; Electron microscopy for materials research (EMAT) Impact Factor: 3.411 Times cited: 48 DOI: 10.1016/j.jeurceramsoc.2014.02.026 Additional Links: UA library record; WoS full record; WoS citing articles Permanent link \| Save citation: RTF PDF LaTeX \| Export record: BibTeX Endnote ISI RIS Word XML