Abstract: The patterns of Ni release from Nitinol vary depending on the type of material (NiTi alloys with low or no processing versus commercial wires or sheets). A thick TiO2 layer generated on the wire surface during processing is often considered as a reliable barrier against Ni release. The present study of Nitinol wires with surface oxides resulting from production was conducted to identify the sources of Ni release and its distribution in the surface sublayers. The chemistry and topography of the surfaces of Nitinol wires drawn using different techniques were studied with XPS and SEM. The distribution of Ni into surface depth and the surface oxide thickness were evaluated using Auger spectroscopy, TEM with FIB and ELNES. Ni release was estimated using either ICPA or AAS. Potentiodynamic potential polarization of selected wires was performed in as-received state with no strain and in treated strained samples. Wire samples in the as-received state showed low breakdown potentials (200 mV); the improved corrosion resistance of these wires after treatment was not affected by strain. It is shown how processing techniques affect surface topography, chemistry and also Ni release. Nitinol wires with the thickest surface oxide TiO2 (up to 720 nm) showed the highest Ni release, attributed to the presence of particles of essentially pure Ni whose number and size increased while approaching the interface between the surface and the bulk. The biological implications of high and lasting Ni release are also discussed.

Abstract: Black corals (Cnidaria, Antipatharia) from three different sources were investigated with the aim of detecting inorganic components and their morphology. In general, the skeleton of black corals was composed of the chitin fibrils admixed with peptides and the chitin presence was confirmed by the X-ray diffraction (XRD), Fourier Transformed Infrared Spectrometry (FTIR) and microRaman Microscopy, the latter giving the opportunity of tracing single fibrils and their location. The composition and concentrations of the inorganic components of the black corals were measured, using a scanning electron microprobe and micro-Particle Induced X-ray Emission (µ-PIXE). The application of such instruments enabled the estimation of the constituent distributions in a microscale. The mapping option was the most useful technique of making analyses in these studies, just to reveal the composition of chamber-like cells. Analysis of the morphology and microstructure showed that there were three distinct regions within the coral: a core and the cells encircled with adjacent interface gluing strips. The majority of the elements analyzed were selectively distributed and segregated in a striking way in mentioned distinctive zones of the skeleton and it was detected for the first time. The core area was characterized by the relatively elevated concentrations of Ca. The measurements gave extremely clear images of the distribution of particular elements in the skeletal tissue, with I, Ca, K and Fe much more concentrated in the gluing zones, while C, N, Na and Mg present in the interiors of particular skeletal cells. The distribution of some elements (Mg, Fe) and some compounds (chitin) and functional groups (SS, CI) allows differentiating the biological and mechanical functions of particular fragments of the rods. The kinds of elements and their concentrations measured were essentially in compliance with rare data available in the literature. The Raman technique gave the additional qualitative information about the structure of gluing zone and the chitin fibrils and surrounding matrix inside the cell interior.

Abstract: Molecular dynamics simulations were used to investigate the size-dependent melting mechanism of nickel nanoclusters of various sizes. The melting process was monitored by the caloric curve, the overall cluster Lindemann index, and the atomic Lindemann index. Size-dependent melting temperatures were determined, and the correct linear dependence on inverse diameter was recovered. We found that the melting mechanism gradually changes from dynamic coexistence melting to surface melting with increasing cluster size. These findings are of importance in better understanding carbon nanotube growth by catalytic chemical vapor deposition as the phase state of the catalyst nanoparticle codetermines the growth mechanism.

Abstract: A study was undertaken to determine causes and effects of corrosion processes in ballast tanks. Part 1 of this article (October 2009 MP) described the data collection. Part 2 describes the development of a corrosion index (CI) derived from the general International Association of Classification Societies corrosion assessment methods. The CI can be used in situ to assess ballast tank corrosion. An average timeline for-corrosion of tanks is presented.

Abstract: The effect of the size of the GaAs barrier and the Ga1−xInxAs well on the structural properties of a Ga1−xInxAs/GaAs multiple quantum well structure is investigated using the Metropolis Monte Carlo approach based on a well-parametrized Tersoff potential. It is found that within the well the Ga-As and In-As bond lengths undergo contractions whose magnitude increases with increasing In content in sharp contrast with bond-length variations in the bulk Ga1−xInxAs systems. For fixed barrier size and In content, the contraction of the bonds is also found to increase with increasing size of the well. Using the local atomic structure of the heterostructures, a more local analysis of the strain state of the systems is given and comparison with the prediction of macroscopic continuum elasticity theory shows deviations from the latter.

Abstract: The recent infatuation for LiFePO4 as positive electrode material in Li-ion batteries has prompted a renewed interest in olivine-type structures, with a view to enhance their conduction proper-ties. We show that the dual substitution of Li for Fe and of P for Si in the olivine LiFePO4 phase leads to a complete solid solution Li1-xFe1+xP1-xSixO4 as deduced from combined X-ray diffraction, Mossbauer, and NMR experiments. Our findings challenge the common belief that the anionic network cannot be substituted. Moreover. it is found that such a substitution promotes Li intersite mixing between the olivine M1 and M2 sites. Such mixing, together with the worsening of the conducting properties of the dually substituted samples, is believed to be responsible for the poor electrochemical performances of the member's series. Beyond x = 0.20, the samples were electrochemically inactive. While the current materials are disappointing application-wise, such a study provides clues to the rich chemistry remaining to be unveiled with olivine-type structures in particular and polyanionic compounds in general.

Abstract: A new Tl-doped strontium ferrite Fe2(Sr2-Tl)Sr3Fe4O14.65, with an original structure, has been synthesized and structurally characterized by powder X-ray diffraction and transmission electron microscopy. The TGA and Mssbauer studies evidence a mixed valence of iron. The structure exhibits a commensurate modulation, with a F-type subcell a ≈ b ≈ 5.4 Å (≈ ap√2), c ≈ 42 Å with a modulation vector q = αa* with α = 0.4. The supercell parameters have been refined as a= 27.1101(8) Å, b= 5.5187(2) Å and c= 42.0513(9) Å, in the space group Fmmm. The electron diffraction and electron microscopy data of this novel ferrite show that it can be described as a FeTl-2234-type structure corresponding to the intergrowth of a quadruple perovskite slice [(SrFeO2.8)4], with a complex rock salt related slice [Fe2(Sr2-Tl)O3.4]∞, built up of one double iron layer [Fe2O2.4] sandwiched between two [SrO] layers. The HRTEM images show that the oxygen atoms and vacancies are randomly distributed in the perovskite layers while the HAADF STEM images evidence the absence of Tl segregation in the matrix. Fe2(Sr2-Tl)Sr3Fe4O14.65 exhibits a very large value of χ (11emu/mol) at 5 K, which remains large at 400 K; the M(H) loop presents a shape characteristic of ferrimagnetism, with a large coercive field of 0.3 T. The value of magnetization saturates at 400 K at 0.68 μB/Fe. At 10 K, the value of magnetization reaches a maximum of 2 μB/Fe. The resistivity presents a semiconducting-like behavior, with ρ 800 Ω·cm at 300 K.

Abstract: Soil samples from an abandoned uranium mine have been investigated in order to determine the molecular phases of uranium compounds. The experiments were carried out with soil particulate matter, collected randomly from the area of the formerly exploited ore. To select the particles rich with uranium, scanning electron microscopy with energy-dispersive X-ray attachment (SEM/EDX) was applied first. Afterwards, the particles were relocated and measured by l-Raman spectrometry (MRS). Residues of the main deposit, uraninite UO2, were detected, along with its alteration products. In terms of Raman scattering properties, uranium oxides are quite sensitive to the laser beam wavelength, which results in very specific features of their Raman spectra. In this paper the Raman spectra of uranium oxides of different origin and oxidation states, measured with 514 and 785 nm lasers, are also presented

Abstract: Electron transport through multiterminal rectangular arrays of quantum rings is studied in the presence of Rashba-type spin-orbit interaction (SOI) and of a perpendicular magnetic field. Using the analytic expressions for the transmission and reflection coefficients for single rings we obtain the conductance through such arrays as a function of the SOI strength, of the magnetic flux, and of the wave vector k of the incident electron. Due to destructive or constructive spin interferences caused by the SOI, the array can be totally opaque for certain ranges of k, while there are parameter values where it is completely transparent. Spin resolved transmission probabilities show nontrivial spin transformations at the outputs of the arrays. When pointlike random scattering centers are placed between the rings, the Aharonov-Bohm peaks split, and an oscillatory behavior of the conductance emerges as a function of the SOI strength.