Abstract: The ternary oxides Ba8Ta4Ti3O24 and Ba10Ta7.04Ti1.2O30 were synthesized and their crystal structures and defects were studied by means of X-ray powder diffraction, electron diffraction, and high resolution electron microscopy. The crystal structure of Ba8Ta4Ti3O24 is based on the 8H (cchc)(2) close-packed stacking (a 10.0314 Angstrom, c = 18.869 Angstrom, SG P6(3)/mcm, Z = 3) and that of Ba10Ta7.04Ti1.2O30 and on the 10H (cchcc)(2) close-packed stacking (a = 5.7981 Angstrom, c = 23.755 Angstrom, SG P6(3)/mmc, Z = 1) of BaO3 layers. The structural refinements gave the following values for the R factors for Ba8Ta4Ti3O24 (Ba10Ta7.04Ti1.2O30) R(I) = 0.041 (0.039), R(P) = 0.108 (0.118), and R(wP) = 0.094 (0.099). The main feature of both structures is the presence of two types of face-sharing octahedra (FSO) with different occupancies by Ta atoms, Ti atoms, and vacancies, which results in the formation of a superstructure. It was shown that in the Ba8Ta4Ti3O24 structure these pairs of FSO occur in an ordered fashion and in the Ba10Ta7.04Ti1.2O30 structure in a disordered fashion. The existence of the wide range of solid solutions was shown to be also a consequence of the presence of one of the two types of face-sharing octahedra. (C) 1995 Academic Press, Inc,

Abstract: Superconducting Cu mixed oxyfluoride, Sr,Cu(O, F)(4+delta), was Obtained via fluorination of Sr2CuO3 by XeF2 in the 100-250 degrees C temperature range in a closed Ni container. The prepared samples exhibited a lower T-c in comparison with earlier reported values. Different samples in the Sr-Cu-O-F system were prepared by a solid-state reaction at 220-400 degrees C, but no formation of the oxyfluoride was detected even with an addition of xenon difluoride. These data allow one to draw conclusions on the metastability of the oxyfluoride under the conditions used, Electron microscopy and X-ray powder diffraction studies revealed large amounts of badly crystallized SrF2; this could be a reason for the small superconducting volume fraction as well as for the inhomogeneous distribution of the anions.