Abstract: It is known that the neutral image tone of a developed photographic film becomes brownish when the thickness of the original silver halide tabular crystals is reduced. We investigate by electron microscopy to what extent the silver filament structure has changed and how it induces the shift in image tone. Therefore, two samples of AgBr {111} tabular crystals with average thicknesses of 160 nm and 90 nm respectively, are compared. It is shown that the dimensions and defect structure of the filaments are comparable, but that the 90 nm crystals result in a more widely spaced structure, which explains the shift in image tone on a qualitative level. The influence of the addition of an image toner, i.e., phenylmercaptotetrazole, on the filament structure is also investigated. An even more open filament structure of longer, but smaller filaments was observed.

Abstract: A two-step process for the formation of sensitivity centers different from earlier described two-step processes was found for sulfur sensitized emulsions. After deposition of sulfur in the first step, it was found that the second step does not consist of rearrangement of sulfur over the surface, but of the supply of silver interstitial ions towards the deposited sulfur clusters. The two processes could be separated by adsorbing and desorbing TAI (4-hydroxy-1, 3,3a, 7-tetraazaindene) at/from the silver halide surface. When 1.5 mmol TAI/mol Ag is added before the sulfur reaction, the silver interstitials are immobilized but sulfur still can be deposited at the same level. By lowering the pH to 2.50 after this sulfur reaction, TAI is desorbed from the surface and the released interstitials then cause a restoration of the properties of a sulfur system without TAI. These effects could be demonstrated via diffuse reflectance spectroscopy (DRS), sensitometry and dielectric loss measurements. We could also confirm the isolation of silver sulfide clusters by TAI from other chemicals in the solution, by adsorption of TAI on the clusters.