Records |
Links |
|
Author |
Penders, A.; Konstantinovic, M.J.; Van Renterghem, W.; Bosch, R.W.; Schryvers, D. |
|
| |
Title |
TEM investigation of SCC crack tips in high Si stainless steel tapered specimens |
Type |
A1 Journal article |
| |
Year  |
2021 |
Publication |
Corrosion Engineering Science And Technology |
Abbreviated Journal |
Corros Eng Sci Techn |
|
| |
Volume |
|
Issue |
|
Pages |
|
|
| |
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
|
| |
Abstract |
The stress corrosion cracking (SCC) mechanism is investigated in high Si duplex stainless steel in a simulated PWR environment based on TEM analysis of FIB-extracted SCC crack tips. The microstructural investigation in the near vicinity of SCC crack tips illustrates a strain-rate dependence in SCC mechanisms. Detailed analysis of the crack tip morphology, that includes crack tip oxidation and surrounding deformation field, indicates the existence of an interplay between corrosion- and deformation-driven failure as a function of the strain rate. Slow strain-rate crack tips exhibit a narrow cleavage failure which can be linked to the film-induced failure mechanism, while rounded shaped crack tips for faster strain rates could be related to the strain-induced failure. As a result, two nominal strain-rate-dependent failure regimes dominated either by corrosion or deformation-driven cracking mechanisms can be distinguished. |
|
| |
Address |
|
|
| |
Corporate Author |
|
Thesis |
|
|
| |
Publisher |
|
Place of Publication |
|
Editor |
|
|
| |
Language |
|
Wos |
000695956400001 |
Publication Date |
2021-09-14 |
|
| |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
| |
Series Volume |
|
Series Issue |
|
Edition |
|
|
| |
ISSN |
1478-422x |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
| |
Impact Factor |
0.879 |
Times cited |
|
Open Access |
OpenAccess |
|
| |
Notes |
|
Approved |
Most recent IF: 0.879 |
|
| |
Call Number |
UA @ admin @ c:irua:181533 |
Serial |
6892 |
|
| Permanent link to this record |
| |
|
| |
|
Author |
Penders, A.; Konstantinovic, M.J.; Bosch, R.W.; Schryvers, D. |
|
| |
Title |
Crack initiation in tapered high Si stainless steel specimens : stress threshold analyses |
Type |
A1 Journal article |
| |
Year |
2020 |
Publication |
Corrosion Engineering Science And Technology |
Abbreviated Journal |
Corros Eng Sci Techn |
|
| |
Volume |
|
Issue |
|
Pages |
1-8 |
|
| |
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
|
| |
Abstract |
Tapered specimens were used for an accelerated test technique to study the crack initiation of high Si stainless steel by means of constant elongation rate tensile testing in a simulated pressurised water reactor environment. Detailed crack density distributions were obtained by applying an advanced crack detection algorithm on iteratively displaced scanning electron microscopy pictures featuring stress corrosion cracks along the specimen's gauge length. By means of finite-element analysis, prominent peaks in the crack density graphs are demonstrated to be related to stress relief and stress build-up during the crack initiation phase. Intrinsic scatter related to the crack detection suggests that stress corrosion cracking is independent of the strain-rate for strain-rates lower than 10(-6 )s(-1). Based on the extrapolation to constant load conditions, the critical threshold value for the duplex high Si stainless steel is estimated to be around 580 MPa. |
|
| |
Address |
|
|
| |
Corporate Author |
|
Thesis |
|
|
| |
Publisher |
|
Place of Publication |
|
Editor |
|
|
| |
Language |
|
Wos |
000549651600001 |
Publication Date |
2020-06-30 |
|
| |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
| |
Series Volume |
|
Series Issue |
|
Edition |
|
|
| |
ISSN |
1478-422x |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
| |
Impact Factor |
1.8 |
Times cited |
1 |
Open Access |
Not_Open_Access |
|
| |
Notes |
; We would like to acknowledge ENGIE Electrabel for the financial support of this work under the contract number BSUEZ5500. ; |
Approved |
Most recent IF: 1.8; 2020 IF: 0.879 |
|
| |
Call Number |
UA @ admin @ c:irua:171292 |
Serial |
6478 |
|
| Permanent link to this record |
| |
|
| |
|
Author |
Potgieter-Vermaak, S.S.; Mmari, A.; Van Grieken, R.; McCrindle, R.I.; Potgieter, J.H. |
|
| |
Title |
Degradation of galvanised iron roofing material in Tanzania by atmospheric corrosion |
Type |
A1 Journal article |
| |
Year |
2011 |
Publication |
Corrosion engineering science and technology |
Abbreviated Journal |
|
|
| |
Volume |
46 |
Issue |
5 |
Pages |
642-650 |
|
| |
Keywords |
A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation) |
|
| |
Abstract |
Galvanised iron is popular in many applications, particular as a roofing material. However, just like other materials, especially metallic ones, it is prone to degradation by corrosion. In this particular study, the degradation of galvanised roof sheets was investigated at a coastal, urban and rural site in Tanzania, Africa. Samples were exposed to various outdoor environments over a period of 3 years. In addition, some accelerated laboratory investigations were conducted in different simulated air pollution environments in an artificial corrosion chamber constructed for this purpose to supplement the outdoor exposure tests. It was found that the combination of the tropical climate and increasing air pollution due to industrial development in the capital Dar-es-Salaam resulted in substantial atmospheric corrosion of the roof sheets, which eventually leads to failure and the necessity for replacement. The rural site had the lowest degree of atmospheric corrosion as expected. A combination of different corrosion products was identified as a result of the atmospheric corrosion by Raman and EDX analyses. The information gained from this investigation could be utilised to construct more durable structures requiring less frequent replacement and maintenance in future. |
|
| |
Address |
|
|
| |
Corporate Author |
|
Thesis |
|
|
| |
Publisher |
|
Place of Publication |
|
Editor |
|
|
| |
Language |
|
Wos |
000294421100008 |
Publication Date |
2010-04-12 |
|
| |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
| |
Series Volume |
|
Series Issue |
|
Edition |
|
|
| |
ISSN |
1478-422x |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
| |
Impact Factor |
|
Times cited |
|
Open Access |
|
|
| |
Notes |
|
Approved |
no |
|
| |
Call Number |
UA @ admin @ c:irua:92094 |
Serial |
7758 |
|
| Permanent link to this record |