Abstract: An instrumental neutron activation method for V, Mn and W in alloy steels with a 241 Am/Be isotopic neutron source is described. The samples were irradiated to induce the nuclear reactions 51V(n, γ) 52V, 55Mn(n, γ)56Mn, and 186W(n, γ)187W. The activities were measured with a NaI(TI) detector. Interferences on the measured photopeaks were shown to be negligible by measuring the half-lives of 62V, 56Mn and 187W.These thre elementes were determined in the range 1.512.9% in special steels; manganese in the range 0.51.6% was measured in cast irons. Calibration was done by comparison with results from wet chemistry and x-ray fluorescence spectrometry. The processing times for the vanadium, manganese and tungsten determinations were 11 min, 3 h and 26.3 h, respectively, but these were reduced greatly by intoruding a scheme wherein six samples were simultaneously irradiated and the 56Mn and 187W nuclides were measured sequentially for a series of 66 samples. The average processing time was reduced to 45 min for tungsten with a precision of 4.0% and accuracy of 3.4% and 22.8 min for manganese with a precision of 3.8% and accuracy of 3.1%.

Abstract: Various bulk and surface analytical techniques were used to study the chemical deterioration of the 13th-to-15th century limestone cathedral in Mechelen, Belgium. The weathering crust on the walls was found to be rich in sulfate, regardless of the geographic orientation. Nitrate and chloride were only detected in minor amounts in the crust and run-off samples. Attack by gaseous sulfur compounds seems to play a dominant role in the stone deterioration mechanism. Electron microprobe analysis showed predominantly bar-shaped gypsum crystals in the crust, and laser microprobe mass spectrometry showed that carbon seems to be responsible for the blackness of most crust samples. Automated electron microprobe analysis also indicated significant differences in the analytical composition of suspensions in run-off water and in rain-water.

Abstract: The potential of laser microprobe mass analysis (LAMMA) as a sensitive microanalytical technique was explored in applications relevant to nephrology. Aluminum and associated elements, such as iron, were localized in fresh tissue biopsies obtained from uremic patients treatment by chronic hemodialysis. The LAMMA was applied to serum, liver, bone, and parathyroid glands of such patients. In addition, we used LAMMA to evaluate the specificity and sensitivity of routine histochemistry, in particular on human bone sections stained by the aluminon method. The high, multielemental sensitivity and molecular microprobe potential of LAMMA established important advantages over other microchemical methods forin situ analysis at the micron level in histological sections.

Abstract: Laser microprobe mass analysis (LAMMA) was applied to particulate matter from the Atlantic Ocean. Inferring information about the surface layer by LAMMA was not probe X-ray microanalysis (EPXMA). Geochemically relevant groups of particles had been identified by EPXMA and cluster analysis. For both locations, the most abundant ones appeared to be those rich in silicon and the alumino-silicates. Afterwards LAMMA was applied to obtain more information about the trace element composition and surface characteristics. The iron-rich phase appeared to contain significant amounts of heavy metals and of phosphate. Lead appeared to be associated in detectable amounts with alumino-silicates in the Scheldt but not with those in the Atlantic Ocean. Inferring information about the surface layer by LAMMA was not always unambiguous.

Abstract: A total of 82 samples of wet and total deposition were sampled near the limestone cathedral at Mechelen, Belgium, which is presently being affected seriously by air pollution, and at a reference site. Most of these samples were analyzed for 10 major and 7 trace ions in solution and for 15 elements in suspension. It appeared that calcite, released from the building, effectively neutralizes the rainwater in the near vicinity and produces high Ca and bicarbonate concentrations. Heavy metal concentrations are hardly affected by the building.

Abstract: Different trace- and microanalytical techniques were used in an extensive study to elucidate the chemical deterioration process of the sandy-limestone St Rombouts Cathedral in Mechelen, Belgium. Samples of stones, mortar joints, slates, atmospheric aerosols and gases, total and wet deposition, and water that had run down the cathedral walls, were all thoroughly characterized. At the east side, usually not exposed to precipitation, a 3001000-μm thick outer crust of microcrystalline gypsum was observed, while at the west side, this surface layer was mostly eroded away due to precipitation. At the north and south sides, the crust contains varying amounts of gypsum and calcite. The gypsum is mostly present in a bar-shaped morphology and carbonaceous fly-ash particles were rarely found in the weathering crust. Local stone characteristics seem to be extremely important in relation to the gypsum content of the crust; black samples always have a much higher sulphate content than the corresponding white samples, irrespective of the predominant direction of orientation. The relative contribution of nitrogen- and chlorine-containing pollutants to the total decay process is much smaller than that of sulphur-containing pollutants. Deposition samples collected at the site of the cathedral mostly had a pH of > 5.6, due to the neutralization of the rainwater by alkaline atmospheric constituents. Runoff water and washdown water were enriched in all ions, especially Ca2+ and SO42−, indicating that, indeed, gypsum is the most important weathering product. The suspension in deposition samples and black-well leaching water was highly enriched in silicon-containing particles, while runoff water and white-wall leaching water contained a predominant calcium-rich suspension.