Abstract: In this article, results using confocal µ-Raman to analyse the cross-section of paint samples are presented. Results obtained with light microscopy, scanning electron microscopy (SEM) combined with an energy dispersive X-ray analysis (EDX) and micro-X-ray fluorescence (µ-XRF) are mentioned and compared to the ones obtained with confocal (MRS). In some cases, pigment identification was possible only by combining analytical results from different techniques. The samples were drawn from five paintings belonging to the Academy of Fine Arts of Antwerp, which are part of a collection of 34 paintings made by students from the Academy between 1819 and 1920. Since, on the one hand, the painting techniques and materials, especially pigments, used in this period are still not completely known, and on the other hand, this collection constitutes a very important and reliable resource of information, these paintings were chosen for a systematic investigation. They represent the evolution of painting in Belgium over approximately a century.

Abstract: On several paintings of James Ensor (1860−1949), a gradual fading of originally bright yellow areas, painted with the pigment cadmium yellow (CdS), is observed. Additionally, in some areas exposed to light, the formation of small white-colored globules on top of the original paint surface is observed. In this paper the chemical transformation leading to the color change and to the formation of the globules is elucidated. Microscopic X-ray absorption near-edge spectroscopy (ì-XANES) experiments show that sulfur, originally present in sulfidic form (S2−), is oxidized during the transformation to the sulfate form (S6+). Upon formation (at or immediately below the surface), the highly soluble cadmium sulfate is assumed to be transported to the surface in solution and reprecipitates there, forming the whitish globules. The presence of cadmium sulfate (CdSO4·2H2O) and ammonium cadmium sulfate [(NH4)2Cd(SO4)2] at the surface is confirmed by microscopic X-ray diffraction measurements, where the latter salt is suspected to result from a secondary reaction of cadmium sulfate with ammonia. Measurements performed on cross sections reveal that the oxidation front has penetrated into the yellow paint down to ca. 1−2 ìm. The morphology and elemental distribution of the paint and degradation product were examined by means of scanning electron microscopy equipped with an energy-dispersive spectrometer (SEM-EDS) and synchrotron radiation based micro-X-ray fluorescence spectrometry (SR ì-XRF). In addition, ultraviolet-induced visible fluorescence photography (UIVFP) revealed itself to be a straightforward technique for documenting the occurrence of this specific kind of degradation on a macroscale by painting conservators.

Abstract: Iron mineral containing sensory dendrites in the inner lining of the upper beak of homing pigeons [1] and various bird species [2] are the first candidate structures for an avian magnetic field receptor. A new concept of magnetoreception [3, 4] is based on detailed ultra-structural optical and electron microscopy analyses in combination with synchrotron radiation microscopic X-ray fluorescence analysis (micro-XRF) and microscopic X-ray absorption near edge structures (micro-XANES). Several behavioral experiments [5, 6] and first mathematical simulations [6] affirm our avian magnetoreceptor model. The iron minerals inside the dendrites are housed in three different subcellular compartments (bullets, platelets, vesicles), which could be clearly resolved and identified by electron microscopy on ultrathin sections [1, 3]. Micro-XRF and micro-XANES data obtained at HASYLAB beamline L added information about the elemental distribution and Fe speciation [3], but are averaged over the complete dendrite due to limited spatial resolution. Here we present recently performed micro-XRF maps with sub-micrometer resolution (ESRF ID21), which reveal for the first time subcellular structural information from almost bulk-like dendrite sample material. Due to the thickness of 30 μm the microarchitecture of the dendrites can be considered as undisturbed and artefacts introduced by sectioning might be widely reduced.

Abstract: A combination of synchrotron radiation based X-ray microscopic techniques (ì-XRF, ì-XANES, ì-XRD) applied on single depleted uranium (DU) particles and semi-bulk leaching experiments has been employed to link the potential bioavailability of DU particles to site-specific particle characteristics. The oxidation states and crystallographic forms of U in DU particles have been determined for individual particles isolated from selected samples collected at different sites in Kosovo and Kuwait that were contaminated by DU ammunition during the 1999 Balkan conflict and the 1991 Gulf war. Furthermore, small soil or sand samples heavily contaminated with DU particles were subjected to simulated gastrointestinal fluid (0.16 M HCl) extractions. Characteristics of DU particles in Kosovo soils collected in 2000 and in Kuwait soils collected in 2002 varied significantly depending on the release scenario and to some extent on weathering conditions. Oxidized U (+6) was determined in large, fragile and bright yellow DU particles released during fire at a DU ammunition storage facility and crystalline phases such as schoepite (UO3·2.25H2O), dehydrated schoepite (UO3·0.75H2O) and metaschoepite (UO3·2.0H2O) were identified. As expected, these DU particles were rapidly dissolved in 0.16 M HCl (84 ± 3% extracted after 2 h) indicating a high degree of potential mobility and bioavailability. In contrast, the 2 h extraction of samples contaminated with DU particles originating either from corrosion of unspent DU penetrators or from impacted DU ammunition appeared to be much slower (2030%) as uranium was less oxidized (+4 to +6). Crystalline phases such as UO2, UC and metallic U or UTi alloy were determined in impacted DU particles from Kosovo and Kuwait, while the UO2,34 phase, only determined in particles from Kosovo, could reflect a more corrosive environment. Although the results are based on a limited number of DU particles, they indicate that the structure and extractability of DU particles released from similar sources (metallic U penetrators) will depend on the release scenarios (fire, impact) and to some extent environmental conditions. However, most of the DU particles (7396%) in all investigated samples were dissolved in 0.16 M HCl after one week indicating that a majority of the DU material is bioaccessible.