Abstract: Environmental parameters such as temperature, relative humidity, visible light, UV radiation and pollution influence the deterioration rate of heritage items. To judge on the environmental appropriateness for heritage conservation, it is therefore important to monitor the environment. Often, an incomplete set of environmental parameters is measured, or sporadic or time-averaged measurements are performed. As a result, a wide range of undesirable situations and hazards remain unnoticed. This might lead to an underestimation of environmental dangers (i.e., inaccurate judgement) or to inappropriate mitigation measures (i.e., inaccurate decision making). We present an innovative and user-friendly monitoring device that simultaneously and continuously measures (1) environmental parameters and (2) material behavior. An extended combination of off-the-shelf sensors for temperature, relative humidity, air speed, CO2, NO2, O-3 and particulate matter are connected to a multipurpose datalogger. In-house developed sensors for the shrinkage and expansion behavior of wood, as well as sensors for metal corrosion rates are connected to the same datalogger. Such extended monitoring shows the identification of a wider range of undesirable situations, and it facilitates the search for correlations between such situations and the sources that cause them, i.e., the hazards.

Abstract: This study demonstrates that the mechanism responsible for the transformation of glass into a degradation layer is pH-dependent. In acid conditions, the transformed glass is homogeneous and brittle. In mild alkaline conditions, transformed glass is heterogeneous due to the presence of lamellae composed of silica nanoparticles and the occurrence of Ca-rich inclusions. The fundamental difference between acid and alkaline conditions cannot be explained by the currently accepted degradation mechanism based on ion exchange. To explain this critical observation, we propose a refined degradation mechanism based on existing knowledge that involves several inwardly moving reaction fronts. The fronts responsible for the transformation of the silicate network into amorphous silica are also responsible for the morphology of the transformed glass. We have identified the feedback mechanism that explains the formation of lamellae in alkaline conditions.

Abstract: Climate change will affect the preservation conditions of our cultural heritage. Therefore, well-considered mitigation actions should be implemented to safeguard our heritage for future generations. Environmental monitoring is essential to follow up the change in preservation conditions and to evaluate the effectiveness of performed mitigation actions. To support heritage guardians in the processing and evaluation of monitored data, an indoor air quality (IAQ) index for heritage applications is introduced. The index is calculated for each measured point in time and is visualized in a user-friendly and intuitive way. The current paper describes the backbone of the IAQ-calculating algorithm. The algorithm is subsequently applied on a case study in which a mitigation action is implemented in a church.

Abstract: The world famous Alhambra monument in Granada, Southern Spain, listed as UNESCO world cultural heritage since 1984, represents probably the most beautiful example of Islamic art and architecture from the Middle Ages in Europe. It is visited by ca. 2 million people annually. Granada is situated in a natural basin, surrounded by mountains with altitudes up to 3500 m. Due to this topography and the prevailing low wind speeds, pollution-derived and especially traffic-derived particulate matter often accumulates in the urban air. In order to evaluate the potential conservation risks from the surrounding air, the atmospheric composition in the Alhambra monument was evaluated. Indoor temperature and relative humidity fluctuations were evaluated for their potential degenerative effects. Furthermore, the atmospheric composition in the Alhambra was analyzed in terms of inorganic gases (NO2, SO2, O3, and NH3) and black carbon. It was found that the open architecture protected the indoor environments from developing a potentially harmful microclimate, such as the build-up of humidity resulting from the huge number of daily tourists. On the downside, the strong ventilation made the indoor air hardly different from outdoor air, as characterized by strong diurnal temperature and relative humidity gradients and high traffic-derived pollutant levels.

Abstract: There is a long tradition in evaluating industrial atmospheres by measuring the corrosion rate of exposed metal coupons. The heritage community also uses this method, but the interpretation of the corrosion rate often lacks clarity due to the low corrosivity in indoor museum environments. This investigation explores the possibilities and drawbacks of different silver corrosion rate assessments. The corrosion rate is determined by three approaches: (1) chemical characterization of metal coupons using analytical techniques such as electrochemical measurements, SEM-EDX, XRD, and µ-Raman spectroscopy, (2) continuous corrosion monitoring methods based on electrical resistivity loss of a corroding nm-sized metal wire and weight gain of a corroding silver coated quartz crystal, and (3) characterization of the visual degradation of the metal coupons. This study confirms that subtle differences in corrosivity between locations inside a museum can be determined on condition that the same corrosion rate assessment is used. However, the impact of the coupon orientation with respect to the prevailing direction of air circulation can be substantially larger than the impact of the coupon location.

Abstract: Many historical ‘silver’ objects are composed of sterling silver, a silver alloy containing small amounts of copper. Besides the dramatic impact of copper on the corrosion process, the chemical composition of the corrosion layer evolves continuously. The evolution of the surface during the exposure to a Na2S solution was monitored by means of visual observation at macroscopic level, chemical analysis at microscopic level and analysis at the nanoscopic level. The corrosion process starts with the preferential oxidation of copper, forming mixtures of oxides and sulphides while voids are being created beneath the corrosion layer. Only at a later stage, the silver below the corrosion layer is consumed. This results in the formation of jalpaite and at a later stage of acanthite. The acanthite is found inside the corrosion layer at the boundaries of jalpaite grains and as individual grains between the jalpaite grains but also as a thin film on top of the corrosion layer. The corrosion process could be described as a sequence of 5 subsequent surface states with transitions between these states.

Abstract: It is commonly known that the conservation state of works of arts exhibited inside museums is strongly influenced by the indoor environmental quality (IEQ). Heritage institutions traditionally record and evaluate their IEQ by monitoring temperature, relative humidity, and -more rarely-light. However, smart use of technology enables monitoring other parameters that give a more complete insight in environmental air aggressiveness. One of this parameters is particulate matter (PM) and especially its concentration, size distribution and chemical composition. In this work, we present a selection of data sets which were obtained in a measuring campaign performed in the War Heritage Institute in Brussels, Belgium. A continuous monitoring of PM concentration with a light scattering based particle counter was performed. In addition the daily mass concentration and size distribution of airborne PM was monitored by means of Harvard impactors. The chemical composition of sampled PM was inferred from the results of XRF and IC analysis. The insights from these datasets are combined with the results of traditional environmental monitoring (temperature, relative humidity and light intensity), and assessed against the recommended guidelines for conservation environments. By using an integrated approach based on the calculation of an IEQ-index, we present a straightforward methodology to evaluate and visualize the IEQ including also continuous PM monitoring. It is clear from the results of this study how including PM in IEQ analysis allows to identify potential risks for museum collections that remain invisible when only traditional parameters are considered.

Abstract: Chemical transformations in paintings often induce discolorations, disturbing the appearance of the image. For an appropriate conservation of such valuable and irreplaceable heritage objects, it is important to have a good know-how on the degradation processes of the (historical) materials: which pigments have been discolored, what are the responsible processes, and which (environmental) conditions have the highest impact on the pigment degradation and should be mitigated. Pigment degradation is already widely studied, either by analyzing historical samples or by accelerated weathering experiments on dummies. However, in historic samples several processes may have taken place, increasing the complexity of the current state, while aging experiments are time-consuming due to the often extended aging period. An alternative method is proposed for a fast monitoring of degradation processes of semiconductor pigments, using an electrochemical setup mimicking the real environment and allowing the identification of harmful environmental parameters for each pigment. Examples are given for the pigments cadmium yellow (CdS) and vermilion (α-HgS).

Abstract: During the study of a large number of archaeological glass fragments, manganese-rich inclusions in leached layers were observed in a limited number of cases. This phenomenon occurs only in black-coloured leached layers. Since the formation mechanism of such manganese-rich inclusions is still unclear, a combination of several analytical techniques was used in order to investigate this phenomenon and, more specifically, to obtain more information on (a) the composition and morphology of the inclusions, (b) the chemical state of Mn and (c) the 3D morphology of the inclusions. A mechanism that might explain the formation of these inclusions is proposed.

Abstract: The chemical composition, as determined by electron probe X-ray microanalysis of a series of ca. 100 archaeological glass fragments, excavated at the Raversijde site (Belgium) is discussed. In the 15th-16th century, Raversijde was a flourishing fishermen town located on the shore of the North Sea, close to the city of Ostend. As a consequence of several battles that were fought in its vicinity, the site was abandoned in the 16th century and was not occupied since then. It is one of the rare archaeological sites in Europe that contains a significant amount of information on the daily life inside a small but affluent medieval community. A comparison of the chemical composition of fragments of vessels and window glass encountered in Raversijde to those found in urban centres in Belgium and to literature date on German and French archaeological finds shows that glass made with wood ash dominates. Usually, it concerns artifacts with a predominantly utilitarian use. A few objects made with sodic (i.e., Na-rich) glass were also encountered, likely to have been imported from Venice during the 15th century or in later periods from an urban centre such as Antwerp, where Facon-de-Venice glass manufacturing activities were established near the start of the 16th century. (C) 2004 Elsevier B.V. All rights reserved.