Abstract: AlGaN/GaN heterostructures were grown on “on-axis” and 2° off (0001) 4H-SiC substrates by metalorganic vapor phase epitaxy (MOVPE). Structural characterization was performed by transmission electron microscopy. The dislocation density, being greater in the on-axis case, is gradually reduced in the GaN layer and is forming
dislocation loops in the lower region. Steps aligned along [11̅00] in the off-axis case give rise to simultaneous defect formation. In the on-axis case, an almost zero density of steps is observed, with the main origin of defects probably being the orientation mismatch at the grain boundaries between the small not fully coalesced AlN grains. V-shaped formations are observed in the AlN nucleation layer, but are more frequent in the off-axis case, probably enhanced by the presence of steps. These V-shaped formations are completely overgrown by the GaN layer, during the subsequent deposition, presenting AlGaN areas in the walls of the defect, indicating an interdiffusion between the layers. Finally, at the AlGaN/GaN heterostructure surface in the on-axis case, V-shapes are observed, with the AlN spacer and AlGaN (21% Al) thickness on relaxed GaN exceeding the critical thickness for relaxation. On the other hand, no relaxation in the form of V-shape creation is observed in the off-axis case, probably due to the smaller AlGaN thickness (less than 21% Al). The AlN spacer layer, grown in between the heterostructure, presents a uniform thickness and clear interfaces.

Abstract: The high temperature phase of Ni1-xS has the NiAs-type structure. The coexistence of two superstructures, ''3a3a3c'' and ''2a2a3c'' with the basic phase is confirmed by means of electron diffraction. The 2a2a3c superstructure is studied by means of electron diffraction and high resolution electron microscopy. A structure model is proposed based on the periodic insertion of stacking faults in the NiAs-type basic structure and the ordering of vacancies in alternate metal-atom layers. Microtwinning in very narrow slabs is found to be a main feature of the 2a2a3c regions and two defect models are discussed.