Abstract: In the present study ultra-fine fly ash as a novel by-product obtained by a dry and closed separation process was investigated as cement replacement in concrete. The impact of ultra-fine fly ash on material properties was investigated following an upscaling as an approach considering paste, mortar and concrete properties. Two types of cement, Portland cement (CEMI) and slag cement (CEMIII), two types of ultra-fly ashes, one with particle size d90< 9.3lm (FA1) and second with d90< 4.6lm (FA2) were used.At paste- and mortar- level, cement was replaced at 0%, 15%, 25%, 35% and 50% with FA1 and FA2. At concrete- level, cement was replaced at 0%, 15% and 25% with different ratios of FA1 and FA2. The results at paste- and mortar- level showed that an increased fineness of the fly ash (FA2) contributes to better workability of the mix. For CEMI, the compressive strength of concrete with FA2 at 25% cement replacement was already equal to the reference 0% replacement concrete at the age of 28 days. For CEMIII, the compressive strength of concrete mix with FA1 with 15% and FA2 with 25% cement replacements reached the reference concrete value at the age of 91 days. Regarding the durability, replacing cement with ultra-fine fly ash (FA2) had a positive influence on the resistivity, chloride migration coefficient and alkali-silica reaction (ASR), and a negative influence on the carbonation resistance.

Abstract: Diesel soot emissions deteriorate the appearance of architectural building materials by soot fouling. This soot deposition devalue the aesthetic value of the building. A solution to counteract this problem is applying titanium dioxide on building materials. TiO2 can provide air-purifying and self-cleaning properties due to its photocatalytic activity. In literature, photocatalytic soot oxidation is observed on glass or silicon substrates. However, degradation of soot by photocatalysis was not yet investigated on cementitious samples (mortar, concrete) although it is one of the most frequently used building materials. In this study, photocatalytic soot oxidation by means of TiO2 coated cementitious samples is addressed. The soot removal capacity of four types of TiO2 layers, coated on mortar samples, is evaluated by means of two detection methods. The first method is based on colorimetric measurements, while the second method uses digital image processing to calculate the area of soot coverage. The experimental data revealed that cementitious materials coated with commercially available TiO2 exhibited self-cleaning properties as it was found that all coated samples were able to remove soot. The P25 coating gave the best soot degradation performance, while the Eoxolit product showed the slowest soot degradation rate. In addition, gas chromatography measurements in a closed chamber experiment with P25 confirmed that complete mineralization of about 60% of the soot was obtained within 24 hours since CO2 was the sole observed oxidation product. Due to its realistic approach, this study proves that photocatalytic soot removal on TiO2 coated cementitious surfaces is possible in practice, which is an important step towards the practical application of self-cleaning building materials.